• 한국건설순환자원학회논문집
• /
• 제3권1호
• /
• pp.80-86
• /
• 2007

In this study we experimented setting time and basic properties as waste wood fiber and sodium silicate substitution rate to reuse waste wood fiber produced in construction field to wood chip board. To do this construction waste woods were crushed with the size less than 10mm, mixed with the rate of 1:2, 2.5, 3, and added sodium silicate with the rate of 0, 5% of cement content. The results are as follows. As the substitution rate of construction waste wood was increased delay of setting time was also increased, and the batch of adding 5% accelerator had a 13~17 hours faster setting time than non accelerator batch. The compressive strength was lower as wood substitution rate was higher, and as the specific gravity was higher, the strength was also higher. As wood substitution rate was higher, heat conductivity was lower, and as specific gravity was higher, heat conductivity also was higher.

• 토지주택연구
• /
• 제3권3호
• /
• pp.299-305
• /
• 2012

음식물쓰레기 발효 소멸용 목질바이오칩의 종류별로 세공구조에 따른 음식물쓰레기 무게 감량율 및 미생물 활동성을 비교분석 하였다. 목질바이오칩을 이용한 음식물쓰레기 발효 소멸실험을 온도 $30{\sim}50^{\circ}C$, 습도 30~70% 조건의 발효 소멸 반응조에 15일간 매일 700~1,500g의 음식물쓰레기를 투입하며 실시하였다. 이 때 1,500g의 목질바이오칩을 발효 소멸 반응조에 초기에 투입하였다. 실험에 사용한 목질바이오칩의 세공구조는 미생물 혼합형(A 바이오칩), $2{\mu}m$ 마크로 세공형(B biochip), $0.1{\mu}m$ 미세공형(C 바이오칩), 점성구조형(D 바이오칩)으로 4가지 유형이었다. 실험결과, A, B, C, D 바이오칩별 발효 소멸에 의한 음식물쓰레기 무게감량율은 각각 85%, 63%, 92%, 73%이었고, C 바이오칩의 경우가 음식물쓰레기 감량율 92%로 최고값을 나타내었다. 또한, C 바이오칩은 ATP/COD $3.00{\times}10^{-10}$, ATP/TN $2.31{\times}10^{-11}$로 상대적으로 타 종류의 바이오칩보다 높은 결과를 나타내었다. 이는 발효 소멸반응에서 발생되는 미생물의 서식지를 충분히 제공하여 ATP/COD 및 ATP/TN이 높아졌고 미생물의 활동성이 강화되어 발효 소멸반응이 원활하게 진행된 결과에 기인하는 것으로 분석되었다.

• Journal of the Korean Wood Science and Technology
• /
• 제29권3호
• /
• pp.68-72
• /
• 2001

In order to effectively use the waste wood, two types of woodceramics chip tile were made from woodceramics chip, gravel, zeolite and additions. The woodceramics chip was made from branch of apple tree (Malus pumila Mill.) Snow melting property, bending strength and compressive strength of woodceramics chip tile were tested according to the mixing rate of woodceramics chip. Snow melting properties of woodceramics chip tile increased after additions treatment but mechanical properties were reduced significantly after additions treatment. The results indicate that the additions are effective for snow melting property but negative effect on mechanical properties.

• Journal of the Korean Wood Science and Technology
• /
• 제25권4호
• /
• pp.29-38
• /
• 1997

The effect and control of wood property of reconstituted composite panels for improved board properties by wood-waste materials and development of combination method for heterogeneous materials have been of interest to the wood science researchers. The purpose of this study is to consider the properties in relation to hot pressing conditions and to develope the optimum hot pressing condition with waste wood and waste tire for the manufacturing of composite boards. The study of composite boards for recycling of wood and waste tire is nothing up to the present. Physical and mechanical properties such as specific gravity, moisture content, swelling coefficient, modulus of rupture and modulus of elasticity in bending test were studied. The condition of 3-stage press time for the lowest moisture content of composite board was $4{\rightarrow}3{\rightarrow}3$ minutes. Specific gravity of composite panels was affected mainly by the amount of rubber chip. Because of the low rigidity and high elasticity in rubber chip, it is considered the composite panel was adequate material in the place of compression load, but not bending load. Therefore, it was concluded that a use of rubber-based wood composite panel is proper to the interior materials such as floor a room than exterior materials. From the test results, the most optimum hot pressing conditions were $4{\rightarrow}3{\rightarrow}3$ minutes for 3-stage press time and $45{\rightarrow}20{\rightarrow}5kg/cm^2$ for 3-stage press pressure. The rubber-based wood composite panel was very excellent in elasticity by combination of rubber chip in comparison with existing other wood-based materials. Therefore, it was considered that rubber-based wood composites can be applicable to every interior materials such as floor a room and will be expected to effective reuse and recycle of waste tires and wood-waste materials, and will be contribute to protection of environment pollution in earth.

• 대한환경공학회지
• /
• 제32권4호
• /
• pp.363-368
• /
• 2010

본 연구에서는 아데노신3인산의 측정을 통하여 음식물 쓰레기의 발효-소멸반응에서의 미생물이 발생 및 활성정도를 총괄할 수 있는 인자를 도출할 수 있었다. 목질바이오칩을 이용한 음식물 쓰레기의 발효-소멸에서 무게감량 및 유기물 분해율이 높아질수록 아데노신3인산의 농도가 증가하였다. 아데노신3인산은 목질바이오칩의 종류별 유기물 분해 및 무게 감량에 대한 성능 선택성 설정에 유용한 인자로 활용 기대된다.

• 대한토목학회논문집
• /
• 제31권3D호
• /
• pp.413-420
• /
• 2011

건설현장에서 나오는 폐목재 또는 활용가치가 낮은 벌목지에서 발생하는 나무뿌리와 가지 등의 임목폐기물을 분쇄한 목재 칩을 우레탄 수지로 결합시킨 보도용 포장재를 제안하기 위한 실험을 실시하였다. 시험체는 재료혼합비율로서 건설폐목재 칩 및 임목폐기물 칩에 대한 우레탄 수지의 질량비를 0.5, 0.75, 1.0의 3수준으로 정하고 재료 계량 후 믹서로 혼합, 성형한 다음 7일이 경과하였을 때 인장강도 시험, 골프공과 스틸볼을 이용한 탄력성 시험, 투수계수 측정 및 가연성 시험을 실시하였다. 실험결과 공기중 건조상태에서 시험체의 인장강도는 0.2~1.1MPa의 범위를 나타냈으며 재령 7일 이후의 강도 변화는 나타나지 않았다. 그러나 침수시켰을 때 강도가 저하되었으며 그 강도의 저하비율은 우레탄 수지의 사용량이 적을수록 크게 되므로 강우 등에 의한 수분 침투를 고려하여 폐목재 칩에 대한 수지의 질량비는 0.75 이상으로 하는 것이 바람직하다고 판단된다. 탄력성 시험결과로서 폐목재 칩과 우레탄 수지를 사용한 시험체의 GB계수와 SB계수는 20% 이하의 낮은 값으로 측정되어 보도용 포장재로서 우수한 특성을 나타냈다. 또한 투수계수는 모든 배합의 시험체에서 0.5mm/sec 이상으로, 투수성 포장재에 있어서 시공 후 요구되는 일반적인 투수계수의 기준값을 상회하였으며, 목질계 포장재의 가연성은 실용상 특별히 문제가 되지는 않을 것으로 판단되었다.

• 한국연소학회지
• /
• 제4권2호
• /
• pp.11-22
• /
• 1999

Combustion characteristics of the wood chips(balsa chips) were experimentally investigated with respect to the thermal recycle system of the urban waste. The urban waste contains plastics, vegetable and wood materials. Wood was chosen as an example of the one of the component of urban dust. A small wood chip was burned in a electric furnace by the micro-electric balance. The mass reduction rate was normalized by the initial mass of test piece and the time of volatile combustion end. When the mass of the wood chips(balsa chips) was larger than 0.5g, the combustion similarity was found on the normalized mass reduction rate.

• 한국건설순환자원학회지
• /
• 제8권4호
• /
• pp.33-37
• /
• 2013

• 공업화학
• /
• 제22권1호
• /
• pp.87-90
• /
• 2011

열 중량 분석기를 이용하여, 상온에서부터 $600^{\circ}C$까지 10, 20, and $30^{\circ}C/min$의 승온 속도로 바이오매스/플라스틱 혼합물의 혼합열분해를 수행하였다. 바이오매스는 폐목재 우드칩(WWC)을 사용하였고, 플라스틱은 선형저밀도 폴리에틸렌(LLDPE)을 시료로 사용하였다. LLDPE 단독 분해시 $430{\sim}550^{\circ}C$, WWC 단독 분해시는 $230{\sim}600^{\circ}C$에서 분해되었으나, 두 가지 시료를 혼합하여 혼합열분해 한 결과, WWC에 해당하는 분해 온도는 일정한 반면 LLDPE 분해구간의 분해온도가 상승하였다. 이러한 실험결과는 높은 온도범위에서 LLDPE와 WWC이 혼합열분해 되는 동안에 상호작용이 일어났음을 의미한다.

• Journal of the Korean Wood Science and Technology
• /
• 제41권6호
• /
• pp.490-496
• /
• 2013

폐목재의 재활용으로 인한 보드의 물리 기계적 특성이 하락하는 경향이 있다. 그 원인으로는 가공되어 있던 재료를 재활용함에 있어 그 형상이 불균질하고 기존의 접착제 성분과 이물질로 인한 보드 품질의 불균일과 저하를 초래한다. 또한 접착제에 포함되어 있는 포름알데히드로 인해 높은 방산량을 가지게 된다. 이러한 제품의 질적 하락이 수입되는 파티클보드와의 가격 및 품질 경쟁력 약화로 이어져 국내 보드 산업의 문제점으로 대두되고 있다. 따라서 본 연구에서는 최근 파티클보드의 원재료로 사용되고 있는 합판 정재단 부산물을 이용한 보드를 제조하고 각각의 제조 조건별 물리 기계적 특성을 평가하였다. 그 평가결과로 베니어 적층 복합보드를 EMDI 수지를 이용하여 4~16 mesh의 일반적인 chip 크기로 중층을 제작했을 때 휨강도가 57.7 $N/mm^2$로 OSB 측정결과 26.8 $N/mm^2$에 비해 215% 높은 휨강도를 나타냈으며 7.1~17.3%의 두께팽창률은 내수성을 지닌 보드로서 적합함을 보였다. 또한 0.7 ppm의 포름알데히드 방산량은 E1등급의 평균값 1.5 ppm과 E0 등급 최대값 0.7 ppm의 조건에 충족하며 이러한 결과는 바닥 깔개용 OSB를 대체 가능할 것으로 사료된다.