• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.4
• /
• pp.23-29
• /
• 2000

We demonstrate the fabrication method of high-density and high-quality solder bump solving a copper (Cu) cross-contamination in Si-LSI laboratory. The Cu cross-contamination is solved by separating solder-bump process by two steps. Former is via-formation process excluding Cu/Ti under ball metallurgy (UBM) layer sputtering in Si-LSI laboratory. Latter is electroplating process including Ti-adhesion and Cu-seed layers sputtering out of Si-LSI laboratory. Thick photoresist (PR) is achieved by a multiple coating method. After TiW/Al-electrode sputtering for electroplating and via formation in Si-LSI laboratory, Cu/Ti UBM layer is sputtered on sample. The Cu-seed layer on the PR is etched during Cu-electroplating with low-electroplating rate due to a difference in resistance of UBM layer between via bottom and PR. Therefore Cu-buffer layer can be electroplated selectively at the via bottom. After etching the Ti-adhesion layer on the PR, Sn/Pb solder layer with a composition of 60/40 is electroplated using a tin-lead electroplating bath with a metal stoichiometry of 60/40 (weight percent ratio). Scanning electron microscope image shows that the fabricated solder bump is high-uniformity and high-quality as well as symmetric mushroom shape. The solder bumps with even 40/60 $\mu\textrm{m}$ in diameter/pitch do not touch during electroplating and reflow procedures. The solder-bump process of high-uniformity and high-density with the Cu cross-contamination free in Si-LSI laboratory will be effective for electronic microwave application.

• Journal of Sensor Science and Technology
• /
• v.11 no.6
• /
• pp.342-349
• /
• 2002

New formation technique of metal oxide sensing film was proposed m this paper. Silicon wafer with Pt electrodes was used as a substrate for depositing metal Sn film. Metal Sn was deposited in the state of not continuous film but only island state. The samples were prepared to obtain the optimal condition of metal Sn deposition. The resistances of deposited Sn onto Pt electrodes amounted to $1\;k{\Omega}$, $5\;k{\Omega}$, $10\;k{\Omega}$ and $50\;k{\Omega}$, respectively. Also The sample with $1,500\;{\AA}$ thickness of Sn was prepared m order to compare sensing properties between conventional type and proposing type. After deposition of metal Sn, $SnO_2$ was formed by thermal oxidation method for 3 hrs. in $O_2$ ambient at $700^{\circ}C$. Surface morphology, crystal structure and surface roughness of oxidized-sensing film were examined by SEM, XRD, and AFM, respectively. From the results of these analyses, the optimal deposition condition of Sn was that the Pt electrode resistance became $10\;k{\Omega}(300\;{\AA})$. Also, the sensing characteristics of fabricated sensing film for various concentrations of butane, propane and carbon monoxide gases were measured at he operating temperatures of $250^{\circ}C$, $300^{\circ}C$ and $350^{\circ}C$, respectively. Although catalyst as not added to the sensing film, it has exhibited the high sensitivity to all the test gases.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.4
• /
• pp.347-353
• /
• 2002

A structure of a glass electrode-type pH sensor for measuring any concentration of $H^+$ in an aqueous solution was embodied with bulk micromachining technology. Two open well structures were formed, and a reference electrode was secured by the Ag/AgCl thin film in the sloped side of the etched structure. A sensitive membrane of an indicator electrode for generating a potential by an exchange reaction to $H^+$ was made with a glass containing Na 20% or more finely so that its thickness might be $100{\mu}m$ or so, and then it was bonded to one pyramidal structure. A liquid junction for a current path was formed by filling an agar in the anisotropically etched part of the Si wafer, which had a size of $50{\mu}m{\times}50{\mu}m$, and then bonded it to the other. After complete fabrication of each part, it was filled with a 2M KCl reference solution and encapsulated the sensor structure with a cold expoxy. The potential value of fabricated pH sensor was about 90mV/pH in the standard pH solutions.

• Korean Journal of Materials Research
• /
• v.10 no.9
• /
• pp.601-606
• /
• 2000

Nickel mono-silicide(NiSi) shows no increase of resistivity as the line width decreases below 0.15$\mu\textrm{m}$. Furthermore, thin silicide can be made easily and restrain the redistribution of dopants, because NiSi in created through the reaction of one nickel atom and one silicon atom. Therefore, we investigated the deposition condition of Ni films, heat treatment condition and basic properties of NiSi films which are expected to be employed for sub-0.15$\mu\textrm{m}$ class devices. The nickel silicide film was deposited on the Si wafer by using a dc-magnetron sputter, then annealed at the temperature range of $150~1000^{\circ}C$. Surface roughness of each specimen was measured by using a SPM (scanning probe microscope). Microstructure and qualitative composition analysis were executed by a TEM-EDS(transmission electron microscope-energy dispersive x-ray spectroscope). Electrical properties of the materials at each annealing temperature were measured by a four-point probe. As the results of our study, we may conclude that; 1. SPM can be employed as a non-destructive process to monitor NiSi/NiSi$_2$ transformation. 2. For annealing temperature over $800^{\circ}C$, oxygen pressure $Po_2$ should be kept below $1.5{\times}10^{-11}torr$ to avoid oxidation of residual Ni. 3. NiSi to $NiSi_2$ transformation temperature in our study was $700^{\circ}C$ from the four-point probe measurement.

• Journal of the Korean Vacuum Society
• /
• v.16 no.2
• /
• pp.99-104
• /
• 2007

Porous silicon exhibiting dual optical properties, both $Febry-P{\acute{e}}rot$ fringe (optical reflectivity) and photoluminescence had been developed and used as chemical sensors. Porous silicon samples were prepared by an electrochemical etch of p-type silicon wafer (boron-doped, <100> orientation, resistivity ; $1-10{\Omega}cm$). Two different types of porous silicon, fresh porous silicon (Si-H terminated) and oxidized porous silicon (Si-OH terminated)by the thermal oxidation, were prepared. Then the samples were exposed to the vapor of various organics, such as methanol, acetone, hexane, and toluene. Both reflectivity and photoluminescence were simultaneously measured under the exposure of organic vapors for sensing VOC's. These surface-modified samples showed unique respond in both reflectivity and photoluminescence with various organic vapors. While polar molecules exhibit greater quenching photoluminescence, molecules having higher vapor pressure show greater red shift for reflectivity.

• Resources Recycling
• /
• v.21 no.5
• /
• pp.31-37
• /
• 2012

As a recovery of elemental silicon from the sludge of Si wafer process, a process of mechanical separation-chlorine roasting-electrolysis has been suggested. The silicon sludge consisted of Si, SiC, machine oil, and metallic impurities. The oil and metal impurities was removed by mechanical separation. The Si-SiC mixture was converted to silicon chloride by chlorine roasting at $1000^{\circ}C$ for 1 hr and the silicon chloride was dissolved into an ionic liquid of $[Bmpy]Tf_2N$ as an electrolyte. Cyclic voltammetry results showed an wide voltage window of pure $[Bmpy]Tf_2N$ and a reduction peak of elemental Si from $[Bmpy]Tf_2N$ dissolved $SiCl_4$ on Au electrode, respectively. The silicon deposits could be prepared on the Au electrode by the potentiostatic electrolysis of -1.9 V vs. Pt-QRE. The elemental silicon uniformly electrodeposited was confirmed by various analytical techniques including XRD, FE-SEM with EDS, and XPS. Any impurity was not detected except trace oxygen contaminated during handling for analysis.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.27 no.5
• /
• pp.375-382
• /
• 2007

Nondestructive testing (NDT) by using the electromagnetic methods are useful for detecting cracks on the surface and subsurface of the metal. However, when the material contains both ferromagnetic and paramagnetic materials, it is difficult for NDT to detect and analyze cracks using this method. In addition the existence of a partial ferromagnetic material can be incorrectly characterized as a crack in the several cases. On the other hand a large crack has sometimes been misunderstood as a partially magnetized region. Inconel 600 is an important material in atomic energy plant. A nickel film is coated when a crack a appears on an Inconel substrate. Cracks are difficult to detect on the combined material of an Inconel substrate with a nickel film, which are paramagnetic and ferromagnetic material respectively. In this paper, a scan type magnetic camera, which uses a complex induced current-magnetic flux leakage (CIC-MFL) method as a magnetic source and a linearly integrated Hall sensor array (LIHaS) on a wafer as the magnetic sensors, was examined for its ability to detect cracks on the combined material. The evaluation probability of a crack is discussed. In addition the detection probability of the minimum depth was reported.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.448-448
• /
• 2013

최근 생물학적 분석 기구에서 시료를 처리, 분리, 검출, 샘플링 또는 분석하기 위해 사용되는 마이크로펌프(Micropump)에 대한 관심이 높아지고 있다. 또한 전자소자의 성능과 신뢰성의 증진을 위한 전자소자의 열 문제를 해결하기 위해 냉각장치로 마이크로 펌프가 적용되기도 한다. 그 외에도 마이크로펌프는 다양한 분야에 응용이 가능하다. 마이크로펌프는 작동 방식에 따라 압전형, 공압형, 열공압형, 연동형 등의 여러 종류로 분류되고 있다. 그중에서도 최근에는 연동형 마이크로 펌프의 개발이 각광받고 있다. 기존의 연동형 펌프들은 다중 챔버를 가지고 있으며, 각각의 챔버 내에서 Dead volume이 많이 발생할 뿐만 아니라 이상적인 연동운동과는 차이가 많이 나는 문제점을 가지고 있다. 또한 압전방식과 열공압방식은 느린 응답성으로 인해 효율적인 유체 이동이 어렵다. 본 논문에서는 이상적인 연동운동을 구현하기 위하여 기존의 연동형 펌프의 단점을 보완하고, 하나의 챔버에 다중전극 구조를 가지는 정전기력방식의 연동형 펌프를 개발하였다. 정전기력방식으로 펌프를 구동함으로써, 저전력으로 펌프구동이 가능하며, 하나의 챔버에 다중전극을 설치함으로써 이상적인 연동운동을 재현하였다. 그리고 Dead volume을 최소화 하였다. 또한, 빠른 반응속도로 인해 효율적인 유체 이동을 실현시킬 수 있었다. 본 연구에서 제안된 마이크로 펌프의 구성은 크게 챔버, 박막, Inlet/outlet hole으로 구성되었다. 챔버는 Si-wafer에 wet etching 공정으로 제작 하였고 그 위에 알루미늄 박막을 200 nm 증착시켰다. 챔버는 가로 32 mm, 세로 5 mm, 깊이는 $15{\mu}m$, 부피는 $200{\mu}l$으로 제작되었다. 박막은 폴리이미드(polyimide)를 사용하여 $3{\mu}m$의 두께로 제작 되었으며, 폴리이미드 박막 사이에는 200 nm 두께의 4개의 알루미늄 박막 전극을 삽입시켰다. 삽입된 4개의 전극에 개별적인 전기신호를 보냄으로써 연동운동이 가능하다. Inlet/outlet hole은 직경 2 mm의 크기로 제작되었으며, 튜브를 연결하여 유체가 흐를 수 있는 체널을 형성하였다. 제작된 마이크로 펌프의 구동전압은 115 V이며, 인가되는 주파수를 1 Hz~100 KHz까지 변화시켜 유량을 측정하였다. 작동 유체는 공기이며, 유량측정은 튜브 내에 물방울을 삽입하여 시간에 따른 이동거리를 관측하였다. 측정결과 2.2 KHz에서 2.4 mm/min의 가장 높은 유량을 확인할 수 있었다. 본 연구를 통해 제안된 연동형 마이크로펌프는 이상적인 연동운동이 가능함으로써 기존의 연동형 방식의 문제점을 보완하였으며, 생명과학, 의학, 화학 등의 분야에서 적용이 가능하리라 기대된다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.399-399
• /
• 2013

Metal silicides는 Si 기반의microelectronic devices의 interconnect와 contact 물질 등에 사용하기 위하여 그 형성 mechanism과 전기적 특성에 대한 연구가 많이 이루어지고 있다. 이 중 Rare-earth(RE) silicides는 저온에서 silicides를 형성하고, n-type Si과 낮은 Schottky Barrier contact (~0.3 eV)을 이룬다. 또한 낮은 resistivity와 Si과의 작은 lattice mismatch, 그리고 epitaxial growth의 가능성, 높은 thermal stability 등의 장점을 갖고 있다. RE silicides 중 ytterbium silicide는 가장 낮은 electric work function을 갖고 있어 n-channel schottky barrier MOSFETs의 source/drain으로 주목받고 있다. 또한 Silicon 기반의 CMOSFETs의 성능 향상 한계로 인하여 germanium 기반의 소자에 대한 연구가 이루어져 왔다. Ge 기반 FETs 제작을 위해서는 낮은 source/drain series/contact resistances의 contact을 형성해야 한다. 본 연구에서는 저접촉 저항 contact material로서 ytterbium germanide의 가능성에 대해 고찰하고자 하였다. HRTEM과 EDS를 이용하여 ytterbium germanide의 미세구조 분석과 면저항 및 Schottky Barrier Heights 등의 전기적 특성 분석을 진행하였다. Low doped n-type Ge (100) wafer를 1%의 hydrofluoric (HF) acid solution에 세정하여 native oxide layer를 제거하고, 고진공에서 RF sputtering 법을 이용하여 ytterbium 30 nm를 먼저 증착하고, 그 위에 ytterbium의 oxidation을 방지하기 위한 capping layer로 100 nm 두께의 TiN을 증착하였다. 증착 후, rapid thermal anneal (RTA)을 이용하여 N2 분위기에서 $300{\sim}700^{\circ}C$에서 각각 1분간 열처리하여 ytterbium germanides를 형성하였다. Ytterbium germanide의 미세구조 분석은 transmission electron microscopy (JEM-2100F)을 이용하였다. 면 저항 측정을 위해 sulfuric acid와 hydrogen peroxide solution (H2SO4:H2O2=6:1)에서 strip을 진행하여 TiN과 unreacted Yb을 제거하였고, 4-point probe를 통하여 측정하였다. Yb germanides의 면저항은 열처리 온도 증가에 따라 감소하다 증가하는 경향을 보이고, $400{\sim}500^{\circ}C$에서 가장 작은 면저항을 나타내었다. HRTEM 분석 결과, deposition 과정에서 Yb과 Si의 intermixing이 일어나 amorphous layer가 존재하였고, 열처리 온도가 증가하면서 diffusion이 더 활발히 일어나 amorphous layer의 두께가 증가하였다. $350^{\circ}C$ 열처리 샘플에서 germanide/Ge interface에서 epitaxial 구조의 crystalline Yb germanide가 형성되었고, EDS 측정 및 diffraction pattern을 통하여 안정상인 YbGe2-X phase임을 확인하였다. 이러한 epitaxial growth는 면저항의 감소를 가져왔으며, 열처리 온도가 증가하면서 epitaxial layer가 증가하다가 고온에서 polycrystalline 구조의 Yb germanide가 형성되어 면저항의 증가를 가져왔다. Schottky Barrier Heights 측정 결과 또한 면저항 경향과 동일하게 열처리 증가에 따라 감소하다가 고온에서 다시 증가하였다.

• Journal of Sensor Science and Technology
• /
• v.10 no.3
• /
• pp.148-155
• /
• 2001

A pressure sensor on the tip of a catheter which is utilized to measure the in-vivo pressure in a human body was fabricated and the characteristic of the pressure sensor as measured. To fit into a catheter with 1 mm caliber, samples of $150\;{\mu}m$(thickness) ${\times}$ (600, 700, 800, 900, 1000) ${\mu}m$(width) ${\times}2\;mm$(length) was fabricated. The thicker face with $450\;{\mu}m$ thickness of SDB wafer was made thin to $134\;{\mu}m$ thickness using KOH etchant and it made possible to fabricate sensor cell with the width shorter than 1 mm. Different to the whitstone bridge sensor, we formed one piezoresistor and one reference resistor in sensor. Therefore there are possibilities of reduction of the sensitivity, then by using the simulation tool ANSYS 5.5.1, the location and the type of the piezoresistor was optimized. Another piezoresistor type of sensor which contain one longitudinal and one transverse piezoresistor was fabricated at the same time, but the sensitivity was not improved very much. To get the output versus the pressure, a constant current source and a implementation amplifier was used. As a result, the maximum sensitivity of the sensor with one piezoresistor was $1.6\;{\mu}V/V/mmHg$.