• Korean Journal of Materials Research
• /
• v.19 no.1
• /
• pp.28-32
• /
• 2009

Silicon carbide (SiC) is a promising material for power device applications due to its wide band gap (3.26 eV for 4H-SiC), high critical electric field and excellent thermal conductivity. The Schottky barrier diode is the representative high-power device that is currently available commercially. A field plate edge-terminated 4H-SiC was fabricated using a lift-off process for opening the Schottky contacts. In this case, Ni/Ti dual-metal contacts were unintentionally formed at the edge of the Schottky contacts and resulted in the degradation of the electrical properties of the diodes. The breakdown voltage and Schottky barrier height (SBH, ${\Phi}_B$) was 107 V and 0.67 eV, respectively. To form homogeneous single-metal Ni/4H-SiC Schottky contacts, a deposition and etching method was employed, and the electrical properties of the diodes were improved. The modified SBDs showed enhanced electrical properties, as witnessed by a breakdown voltage of 635 V, a Schottky barrier height of ${\Phi}_B$=1.48 eV, an ideality factor of n=1.04 (close to one), a forward voltage drop of $V_F$=1.6 V, a specific on resistance of $R_{on}=2.1m{\Omega}-cm^2$ and a power loss of $P_L=79.6Wcm^{-2}$.

• Journal of radiological science and technology
• /
• v.16 no.1
• /
• pp.57-65
• /
• 1993

Asymetric system have been introduced in these years by KODAK company nam of Insight system for the purpose of improve the chest image. We have had a problem of chest radiology that it is very difficult to visualize the lung field and modiastinal region at one shot. That's why we are the RT using the technique of high voltage hard quality radiography in chest radiography. Also it is known the c-type wide latitude film can lift up the density of mediastinal structures. Authors investigated the photographic characteristics and physical structure of Insight system. Method 1. Investigated the structure of Emulsion layer. Calculated the particle size of Insight system using SEM(Scanning Electron Microscope). 2. Photographic characteristics has been compared the Insight system with the ortho KM/MG combination in $60{\sim}120kV$ range. Results 1. The particle size of backside film were investigated about 2 times larger that of front side film. 2. The front and backscreen's thickness ratio was detected 1 : 3.87, that the backscreen's thickness was thicker than frontscreen. 3. At the view point of photographic characteristics the frontside of insight system make up the contrast, backside make up the density at low exposure lesion.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.543-543
• /
• 2013

Thin-film transistors (TFTs) based on oxide semiconductors have been regarded as promising alternatives for conventional amorphous and polycrystalline silicon TFTs. Oxide TFTs have several advantages, such as low temperature processing, transparency and high field-effect mobility. Lots of oxide semiconductors for example ZnO, SnO2, In2O3, InZnO, ZnSnO, and InGaZnO etc. have been researched. Particularly, zinc-tin oxide (ZTO) is suitable for channel layer of oxide TFTs having a high mobility that Sn in ZTO can improve the carrier transport by overlapping orbital. However, some issues related to the ZTO TFT electrical performance still remain to be resolved, such as obtaining good electrical contact between source/drain (S/D) electrodes and active channel layer. In this study, the bottom-gate type ZTO TFTs with staggered structure were prepared. Thin films of ZTO (40 nm thick) were deposited by DC magnetron sputtering and performed at room temperature in an Ar atmosphere with an oxygen partial pressure of 10%. After annealing the thin films of ZTO at $400^{\circ}C$ or an hour, Cu, Mo, ITO and Ti electrodes were used for the S/D electrodes. Cu, Mo, ITO and Ti (200 nm thick) were also deposited by DC magnetron sputtering at room temperature. The channel layer and S/D electrodes were defined using a lift-off process which resulted in a fixed width W of 100 ${\mu}m$ and channel length L varied from 10 to 50 ${\mu}m$. The TFT source/drain series resistance, the intrinsic mobility (${\mu}i$), and intrinsic threshold voltage (Vi) were extracted by transmission line method (TLM) using a series of TFTs with different channel lengths. And the performances of ZTO TFTs were measured by using HP 4145B semiconductor analyzer. The results showed that the Cu S/D electrodes had a high intrinsic field effect mobility and a low effective contact resistance compared to other electrodes such as Mo, ITO and Ti.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.30A no.12
• /
• pp.51-59
• /
• 1993

A 4${\times}10^{19}cm^{3}$ carbon-doped base AlGaAs/GaAs HBY was grown using carbontetracholoride(CCl$_4$) by atmospheric pressure MOCVD. Abruptness of emitter-base junction was characterized by SIMS(secondary ion mass spectorscopy) and the doping concentration of base layer was confirmed by DXRD(double crystal X-ray diffractometry). Mesa-type HBTs were fabricated using wet etching and lift-off technique. The base sheet resistance of R$_{sheet}$=550${\Omega}$/square was measured using TLM(transmission line model) method. The fabricated transistor achieved a collector-base junction breakdown voltage of BV$_{CBO}$=25V and a critical collector current density of J$_{O}$=40kA/cm$^2$ at V$_{CE}$=2V. The 50$\times$100$\mu$$^2$ emitter transistor showed a common emitter DC current gain of h$_{FE}$=30 at a collector current density of JS1CT=5kA/cm$^2$ and a base current ideality factor of ηS1EBT=1.4. The high frequency characterization of 5$\times$50$\mu$m$^2$ emitter transistor was carried out by on-wafer S-parameter measurement at 0.1~18.1GHz. Current gain cutoff frequency of f$_{T}$=27GHz and maximum oscillation frequency of f$_{max}$=16GHz were obtained from the measured Sparameter and device parameters of small-signal lumped-element equivalent network were extracted using Libra software. The fabricated HBT was proved to be useful to high speed and power spplications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.11-11
• /
• 2010

Thin-film-transistors (TFTs) that can be deposited at low temperature have recently attracted lots of applications such as sensors, solar cell and displays, because of the great flexible electronics and transparent. Transparent and flexible transistors are being required that high mobility and large-area uniformity at low temperature [1]. But, unfortunately most of TFT structures are used to be $SiO_2$ as gate dielectric layer. The $SiO_2$ has disadvantaged that it is required to high driving voltage to achieve the same operating efficiency compared with other high-k materials and its thickness is thicker than high-k materials [2]. To solve this problem, we find lots of high-k materials as $HfO_2$, $ZrO_2$, $SiN_x$, $TiO_2$, $Al_2O_3$. Among the High-k materials, $Al_2O_3$ is one of the outstanding materials due to its properties are high dielectric constant ( ~9 ), relatively low leakage current, wide bandgap ( 8.7 eV ) and good device stability. For the realization of flexible displays, all processes should be performed at very low temperatures, but low temperature $Al_2O_3$ grown by sputtering showed deteriorated electrical performance. Further decrease in growth temperature induces a high density of charge traps in the gate oxide/channel. This study investigated the effect of growth temperatures of ALD grown $Al_2O_3$ layers on the TFT device performance. The ALD deposition showed high conformal and defect-free dielectric layers at low temperature compared with other deposition equipments [2]. After ITO was wet-chemically etched with HCl : $HNO_3$ = 3:1, $Al_2O_3$ layer was deposited by ALD at various growth temperatures or lift-off process. Amorphous InGaZnO channel layers were deposited by rf magnetron sputtering at a working pressure of 3 mTorr and $O_2$/Ar (1/29 sccm). The electrodes were formed with electron-beam evaporated Ti (30 nm) and Au (70 nm) bilayer. The TFT devices were heat-treated in a furnace at $300^{\circ}C$ and nitrogen atmosphere for 1 hour by rapid thermal treatment. The electrical properties of the oxide TFTs were measured using semiconductor parameter analyzer (4145B), and LCR meter.

• Journal of Biomedical Engineering Research
• /
• v.19 no.1
• /
• pp.69-80
• /
• 1998

This research was designed to investigate how the exercise program affects paraplegic standing and walking employing functional electrical stimulation(FES). Emphasis was also given to fatigue of major lower extremity muscles induced by different types of electrical stimulation. We applied continuous and intermittent rectangular pulse trains to quadriceps of 10 normal subjects and 4 complete paraplegic patients. The frequencies were 20Hz and 80Hz, and the knee angle was fixed at 90$^{\circ}$and 150$^{\circ}$to investigate how muscle fatigue is related to muscle length. The knee extensor torque was measured and monitored. We have been training quadriceps and gastrocnemius of a male paraplegic patient by means of electrical stimulation for the past two year. FES standing was initiated when the knee extensors became strong enough to support the body weight, and then the patient started FES walking utilizing parallel bars and a walker. We used an 8-channel constant-voltage stimulator and surface electrodes. The experimental results indicated that paralyzed muscles fatigued rapidly around the optimal length contrary to normal muscles and confirmed that low frequency and intermittent stimulation delayed fatigue. Our exercise program increased muscle force by approximately 10 folds and decreased the fatigue index to half of the initial value. In addition, the exercise enabled the patient to voluntarily lift each leg up to 10cm, which was of great help to the swing phase of FES walking. Both muscle force and resistance to fatigue were significantly enhanced right after the exercise was applied every day instead of 6 days a week. Up to date, the patient can walk for more than two and half minutes at 10m/min while controlling the on/off time of the stimulator by pushing the toggle switch attached to the walker handle.