• Journal of the Korean Wood Science and Technology
• /
• 제46권2호
• /
• pp.155-165
• /
• 2018

The objective of the research was to evaluate the effect of particle pre-treatment on physical, mechanical, and durability of jatropha fruit hulls (JFH) particleboard. The pre-treatments included were immersing in cold water, hot water, and acetic acid solution. After each treatment, the particles were dried up to 3% moisture content. Urea-formaldehyde (UF) resin was used to fabricate particleboards with board size, thickness and density target of 25 cm by 25 cm, 0.80 cm, and $0.70g/cm^3$, respectively. Board pressed at $130^{\circ}C$ for 10 minutes, and $25kg/cm^2$ pressure. The evaluation of particleboard followed the JIS A 5908-2003. Whilist their resistance to subterranean termite test (mass loss, mortality, antifeedant value and feeding rate) refers to the Indonesian standard (SNI 01.7207-2006). The physical and mechanical properties of particleboards showed that all pre-treatments decreased the pH of particles. Overall, all particle immersing treatments resulted of better physical and mechanical properties of particleboard than those of untreated ones. The acetic acid treatment resulted the best physical and mechanical properties of particleboard. Based on the mass loss of JFH particleboard, hot water and acetic acid treated particleboards were classified into weak resistance to subterranean attack. The other two treatments were classified into very weak resistance. Hot water treated particleboard provided the highest mortality and antifeedant as much as 87.40% and 34.20%, respectively. Based on antifeedant classification, hot water treated particleboards were classified into moderately strong resistance, while other treatments were categorized into weak resistance. The lowest feeding rate value ($45.30{\mu}g/termite/day$) was attained by hot water treatment.

• Composites Research
• /
• 제15권2호
• /
• pp.32-39
• /
• 2002

본 연구에서는 자가치료제를 저장할 수 있는 마이크로캡슐을 제조하기 위만 공정절차를 제시하고 자가치료제가 저장된 마이크로캡슐을 제조하였다. 이때 자가치료제는 DCPD(dicyclopentadiene), 마이크로캡슐은 요소-포름알데히드 수지로 구성되어 있으며 레이저 회절법을 이용한 입도분석기를 통해 마이크로캡슐의 크기와 입도분포를 측정하였다. 또만 DSC를 통해 자가치료제, 마이크로캡슐 박막을 형성하는 요소-포름알데히드의 수지, 자가치료제가 저장된 마이크로캡슐 등에 대한 열분석을 수행하였으며 자가치료제가 저장된 마이크로캡슐에 대해 TGA를 통해 연속적인 온도증가 및 일정한 온도 조건 하에서의 열안정성을 평가하였다. 연구결과에 따르면 자가치료제가 저장된 마이크로캡슐은 마이크로캡슐의 박막이 연소되기 전까지는 박막 자체가 자가치료제의 증발을 막아 주어 자가치료제를 안정적으로 저장할 수 있음을 알 수 있었다.

• Journal of Forest and Environmental Science
• /
• 제31권2호
• /
• pp.119-125
• /
• 2015

This study examined the effects of rice straw steaming time and mixing ratio between rice straw and wood particle on the properties of mixed particle board from Acacia mangium Willd wood and rice straw. Rice straw and Acacia mangium Willd wood were collected in Hanoi, Vietnam. The particle board was three-layer particle board with the structural ratio of 1:3:1. The thickness, density and board size of the particle board were 18 mm, $0.7g/cm^3$, and $800{\times}800{\times}18$ (mm, including trimming), respectively. A resin mixture between commercial Urea-formaldehyde (U-F) adhesive and methylene diphenyl isocyanate (MDI) adhesive was used with a dosage of 12% for the core layer and 14% for the surface layer. In this experimental design, the steaming time for rice straw was 15, 30, 45, 60, and 75 minutes at $100^{\circ}C$. The rice straw-wood mixing ratio was 10, 20, 30, 40, and 50%. The results showed that both mixing ratio and steaming time affect the properties of the particleboard, but the mixing ratio has a stronger impact. A higher mixing ratio and a longer steaming time resulted in a better quality of particleboard. The optimal steaming time for rice straw was 46.12 minutes with the straw-wood mixing ratio of 29.85% with the following characteristics of the particle board: the modulus of rupture (MOR) of 14.64 MPa, internal bond strength (IB) of 0.382 MPa, thickness swelling (TS) of 8.83%, and board density of $0.7-0.7g/cm^3$.

• Journal of the Korean Wood Science and Technology
• /
• 제1권2호
• /
• pp.3-10
• /
• 1973

This study was carried out to examine the characeristics of waste sanders(S)from. plywood and pre-finishing plywood surface sanding and double saw finishing, as a new extander in urea-formaldehyde resin(UFR) in plywood adhesive, and to focus, adhesive strength using the glue extended with milled sanders(MS) as extender, leveling the optimum amount of MS to be added, and examining the physical properties of glue extended MS & S. Also economical good feasibility of substitution for wheat flour(WF) with MS as a new extender is analyzed and presented in details. Selecting three standard samples of 80, 100 and 180 mesh, sorking them in distilled water at $20^{\circ}C$, 24 hours, redrying at $105^{\circ}C$ and rescreening the sample with standard screen, again, the 3 samples of 80, 100, and 180 mesh are passed 23 percent through 80 mesh sander standard sample 27 percent through on 100 mesh and only 10.9 percent through 180 mesh, respectively. The particle size of retained parts are greater in size of redried form. It seems undoubtly that particles to be extended in glue are got swollen and become greater in size and coarser in shape. The shape of fresh S particles are irregular thin needle with small scale, as shown in Figure 5. PFS are so finer than plywood S that only 9.8 percent of the S retained on 100 mest screen, 24. 30 percent on 100-160 mesh, and 65.9% on 160-180 mesh. But particle size of the fresh S is large enough to make the viscosity of glue direct extended with S too high to apply it glue spreader. The glue extended with milled sanders(MS). 3 hours milled PFS or 6 hours milled plywood S, having particle sizes shown in Tables 7 and 8, as ratio of Reain/MS/WF/water: 100/8/8/10, indicate good viscosity of 16 to 24 ps, as shown in Figure 5, for applying direct to glue spreader, have high tensile-shear strength (adhesive strength), 102.4 kp/$cm^2$, and 94 percent wood failure.

• 한국가구학회지
• /
• 제11권2호
• /
• pp.45-53
• /
• 2000

This study was carried out to determine the suitability of 3 months old bamboo species of Phyllostachys bambusoides S. et Z., Phyllostachys Pubescens Mazel and Phyllostachys nigra var henonis Stapf as raw materials for the manufacture of strandboard. Total of 108 strandboards were made using urea-formaldehyde resin content level of 12% and one percent of liquid wax emulsion. The strandboard consisted of three layers the top and the bottom layer of which were oriented to the same direction and weighted 25% of the strandboard each. The middle core layer weighed 50% of the board and was perpendicular to the outer top and bottom layers. Analysis was performed to determine the effect of strand lengths and Uowing years of 3 months, 2 years and 3 years on strandboard properties. The physical and mechanical properties of bamboo species and boards were measured and compared to the standard requirements of strandboards. The results are as follows; 1. The more the growing years the higher the density of bamboo. Top part of bamboo indicated higher density value than that of bottom part. 2. Bamboo showed higher static bending strength compared to the main wood species. Longer growing years of bamboo generally inclosed the static tending strength out there were no statistical significancies for Phyllostachys bmbusoides S. et Z. and Phyllostachys pubescens Mazel. 3. Strand length indicated no difference on density and moisture content of strandboard. 5 cm of strand length gave the best static bending strength and internal bonding strength. Bamboo strandboard exhibited lesser extents of thickness swelling than that of CSA standard. 4. 3 months old bamboo gave higher static bending strength of strandboard than those of 2 years and 3 years old bamboo. In case of Phyllostachys nigra var henonis Stapf, 3 months old bamboo indicated higher internal bonding strength than those of 2 years and 3years old bamboo. but in Phyllostachys bambusoides S. et Z., Phyllostachys pubescens Mazel, there were no difference among growing years. Growing years showed no different physical properties of bamboo strandboard.

• Journal of the Korean Wood Science and Technology
• /
• 제21권2호
• /
• pp.57-65
• /
• 1993

The aim of this research was to manufacture sludge-particle board using paper sludge with wood particle and to investigate physical and mechanical properties of various sludge-particle boards, fabricated with ratios of sludge to particle of 10 to 90, 20 to 80, 30 to 70, 40 to 60 and 50 to 50(oven dry weight based). Sludge-particle boards were manufactured by urea-formaldehyde resin, 0.8 target specific gravity, and 10mm thickness. It was possible to manufacture sludge-particle board as the same processing in the present particleboard manufacturing system. This sludge-particle board have different properties as composition ratios of sludge and particle. And sludge-particle board made from 10 percent to 20 percent of sludge mixing ratio have similar mechanical properties compared with control particleboard. Especially, the sludge-particle board made from 10 percent to 40 percent mixing ratios of sludge have superior to control particleboard in internal bond, screw withdrawal holding strength and modulus of elasticity. In the case of dimensional stability, water absorption was increased and thickness swelling was decreased as increased with sludge mixing proportion. The sludge-particle board made of different mixing ratios of our laboratory design was able to concluded that there is possibility of partial substitution of wood particle materials.

• Korean Chemical Engineering Research
• /
• 제56권4호
• /
• pp.577-584
• /
• 2018

본 연구는 목질계 섬유판 제조에 있어 목섬유에 대한 도계부산물인 닭털의 부분적 대체화 가능성을 검토하기 위하여 수행하였다. 닭털은 주로 케라틴계 단백질로 구성되어 있으며, 외형적으로 목섬유와 큰 차이는 없었다. 닭털의 전처리 방법에 따른 포름알데히드 흡착능을 비교한 결과, 닭털을 고온/고압에서 처리하고 분쇄한 우모분에서 가장 높았다. 한편 일반 가위로 절단한 닭털과 이를 가정용 믹서로 고해시킨 닭털의 폼알데히드 흡착량을 dinitrophenylhydrazine법으로 측정한 결과 차이는 없었다. 닭털, 고해 닭털, 우모분을 각각 목섬유의 전건무게를 기준으로 5 wt%로 혼합하여 제조한 중밀도섬유판(MDF)의 물성과 폼알데히드방출량은 닭털의 전처리 조건에 영향을 받지 않았다. 그러나 이 측정치를 목섬유만으로 제조한 MDF와 비교하였을 때, 두께팽윤율과 폼알데히드방출량은 크게 개선되었다. 따라서 현재 생산 현장에서 적용되고 있는 요소수지를 이용한 MDF 제조에 있어 목섬유와 함께 일정한 양의 닭털, 고해 닭털 또는 우모분을 첨가할 경우 치수안전성과 폼알데히드방출량이 개선된 MDF의 제조가 가능할 것으로 예상된다. 그러나 MDF제조에 있어 닭털의 사용은 현재 상황에서 목섬유와 비교하여 원료 확보의 어려움과 높은 단가로 경제성이 낮은 것으로 조사되었다. 경제성 향상을 위하여 중소형 도계장에서 발생하는 닭털을 이용하거나, 동물성 사료의 금지에 대한 대비책 및 인플루엔자 감염 조류에 대한 환경적 처리 방안으로 닭털의 섬유판 원료에 대한 부분적 대체화 기술은 향후 사용 가능성이 충분할 것으로 판단된다.

• Journal of the Korean Wood Science and Technology
• /
• 제24권4호
• /
• pp.56-63
• /
• 1996

This study was to manufacture thinned wood of Larix leptolepis Gordon into Oriented Strand Board(OSB) with Urea-Formaldehyde Resin. The OSB was made of four kinds of strand in slenderness ratio 150 ; thickness $0.3{\pm}0.05mm$, $0.4{\pm}0.05mm$, $0.5{\pm}0.05mm$ and $0.6{\pm}0.05mm$, respectively length 45mm, 60mm, 75mm and 90mm. Target densities were 0.65gr/$cm^3$, 0.75gr/$cm^3$ and 0.85gr/$cm^3$. The stepwise 9 minutes-multi-pressing schedule in the maximum pressure 40kgf/$cm^2$, the minimum pressure 10kgf/$cm^2$ was applied for $400mm{\times}390mm{\times}12mm$ board at the temperature of $150^{\circ}C$ in a hot press. In MOR The OSB of thin strand thickness $0.3{\pm}0.05mm$(length 45mm) and density 0.85gr/$cm^3$ was the highest. The strand thickness had more effect on MOR than the strand length. In strand thickness $0.4{\pm}0.05mm$(length 60mm) and density 0.85gr/$cm^3$ was the highest MOE. The strand thickness and length had adverse effects on MOE each other. At internal bonding. The OSB of strand thickness $0.3{\pm}0.05mm$(length 45mm) and board density 0.75gr/$cm^3$ showed the highest value. OSB had higher IB value with thinner strand thickness. The thinner strand thickness showed the lower thickness swelling in turn $0.3{\pm}0.05mm$(length 45mm), $0.4{\pm}0.05mm$(length 60mm), $0.5{\pm}0.05mm$(length 75mm). $0.6{\pm}0.05mm$(length 90mm). Target densities 0.75gr/$cm^3$ 0.65gr/$cm^3$, 0.85gr/$cm^3$ showed in turn lower value. Finally, The OSB made of thinned wood of Larix leptolepis Gordon showed good results in laboratory experiment.

• 보존과학회지
• /
• 제33권5호
• /
• pp.363-370
• /
• 2017

국립일제강제동원역사관에서 보존처리를 의뢰한 상의 2벌의 재질 분석을 실시하여 당시 의복의 특징을 파악하고, 보존처리를 위한 기초 데이터 구축을 목적으로 한다. 시료의 섬유 짜임 관찰을 위해 실체현미경을 사용하였다. 또한, 섬유 동정을 위해 푸리에변환 적외선 분광광도계(FT-IR), 전자현미경(SEM-EDS)을 이용하였다. 의복 A는 겨드랑이의 구멍, 문양이 있는 레이온제의 흰색 동정, 전체적으로 문양이 없는 소재 등으로 유추하여 보아 여성이 입었던 일본식 속옷 형식의 상의(半襦袢)로 보인다. 몸통 부분의 현미경 관찰 결과 단면 기공이 관찰되며 전체적으로 섬유 꼬임이 관찰 되며, 재질 분석 결과 면이었다. 흰색 동정은 섬유 길이 방향으로 세로선이 관찰되며 단면에 기공은 관찰되지 않으며 재질 분석 결과 레이온 이었다. 의복 B는 오사카 지창에서 검수하고 직인한 작업자용 상의로 보인다. 현미경 관찰 결과, 섬유 꼬임과 단면 기공이 관찰 되었으며, 재질 분석 결과 면이었다. 단추는 분석 결과 초기 플라스틱의 하나인 요소수지로 보인다.

• Journal of the Korean Wood Science and Technology
• /
• 제46권1호
• /
• pp.67-72
• /
• 2018

본 연구에서는 주요 조림수종으로 선정된 백합나무를 이용하여 파티클보드(PB)와 배향성 스트랜드보드(OSB)를 제조하여 보드 원료로서의 가능성을 확인하였다. 두께 15 mm, 밀도 $0.7g/cm^3$의 파티클보드와 두께 10 mm, 밀도 $0.65g/cm^3$의 OSB를 제조하였으며, 파티클보드 공장에서 상용하고 있는 $E_1$ 등급의 요소 폼알데하이드 수지와 왁스, 경화제를 첨가하여 실제 생산, 유통하는 보드제품과 최대한 유사하게 제작조건을 맞추었다. 제조된 보드의 품질시험 결과, PB의 경우, 평균두께 15.8 mm, 평균밀도 $0.71g/cm^3$, 함수율은 5.8% 기준에 적합하였다. 휨강도는 KS 규격(KS F 3104)의 13형 이상($13.0N/mm^2$ 이상), 박리강도는 18형 이상($0.3N/mm^2$ 이상), 나사못 유지력은 평면에서는 18형 이상(700 N 이상), 측면 15형 이상(300 N 이상)의 품질을 만족시켰다. 그러나 휨강도가 박리강도, 나사못유지력에 비해서 낮은 강도를 나타내는데 이것은 파티클 길이/두께의 비율(Slenderness ratio)이 영향을 미친 것으로 판단된다. OSB의 경우, 평균두께 10.7 mm, 평균밀도 $0.68g/cm^3$, 함수율은 6.3%로 KS F 3104 기준에 적합하였으며, 휨강도 18형 이상($18.0N/mm^2$ 이상), 나사못유지력 18형 이상(700 N 이상), 박리강도 13형 이상($0.20N/mm^2$ 이상)의 품질을 만족시켰다.