• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.22 no.1
• /
• pp.64-72
• /
• 1998

This paper was undertaken to develop the fracture toughness testing method using small and single specimen compared to the conventional method in evaluating elastic-plastic fracture toughness of the superconducting magnet structural material at cryogenic temperature. The elastic-plastic fracture toughness test was conducted by using the unloading compliance method recommended by ASTM E813-89 to accomplish the above purpose. And, the 20% side-grooved 0.5TCT and 1TCT specimens were used to evaluate the fracture toughness by using as possible as miniaturized CT specimen. The unloading compliance method was a very useful method in evaluating elastic-plastic fracture toughness at cryogenic temperature. It could be taken valid fracture toughness values by using 20% side-grooved 0.5TCT specimen recommended by ASTM E813-89.

• Journal of Ocean Engineering and Technology
• /
• v.9 no.1
• /
• pp.111-119
• /
• 1995

The elastic-plastic fracture toughness($J_{IC}$) and fracture resistance (J-R curve) of SA508-3 alloy steel used for nuclear reactor pressure vessel are investigated by using CT-type specimens. Fracture toughness tests are conducted by unloading compliance method and multiple specimen method at room temperature, -2$0^{\circ}C$ and 20$0^{\circ}C$. The apparent negative crack growth phenomenon which usually arises in partial unloading compliance test is well known. The negative crack growth phenomenon in determining J sub(IC) or J-R cure from partial unloading compliance experiments may be eliminated by the offset technique. In this study, the evaluation of $J_{IC}$ multiple specimen method recommended by the JSME gives the most reliable results by using half-size CT(similar-type) specimens.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.12
• /
• pp.3010-3017
• /
• 2000

For integrity evaluation of cracked or damaged structures, fracture toughness test results in ASTM are widely used. The fracture toughness values of the structures are used as an effective design criterion in nuclear plants and aircraft structures. Sometimes the difference of P-$\delta$ curve trend during the unloading /reloading cycle in the fracture toughness test using partial unloading compliance was observed. The phenomenon as a possible source of error in determining fracture toughness may be caused by the residual stress during unloading work-hardening and bucking of a specimen. Therefore, we evaluate the effect of bucking and compressive residual stress during the K-R and J-R testing using a finite element method.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.1
• /
• pp.113-120
• /
• 2002

Experimental procedure to measure fracture toughness (J$_{c}$) under mixed mode loading using CTS(Compact Tension-Shear) specimens is described. It\`s loading angle ranges from 0$^{\circ}$ to 45$^{\circ}$ with interval of 157. The general outline of experimental procedure is similar to that of ASTM E8l3-89 fur mode I fracture. Equations fur determining J-integral is quoted from the authors' previous works. The relation between unloading compliance and physical crack size was calibrated. As an example, fracture toughness of aluminum alloy 2024p-7361 was measured and some reasonable results of J$_{c}$ with various loading angles were obtained.

• Journal of Mechanical Science and Technology
• /
• v.15 no.1
• /
• pp.26-34
• /
• 2001

Most research to date concerning the cryogenic toughness of austenitic stainless steels has concentrated on the base metal and weld metal in weldments. The most severe problem faced on the conventional austenitic stainless steel is the thermal aging degradation such as sensitization and carbide induced embrittlement. In this paper, we investigate the cryogenic toughness degradation which can be occurred for austenitic stainless in welding. The test materials are austenitic stainless JN1, JJ1 and JK2 steels, which are materials recently developed for use in nuclear fusion apparatus at cryogenic temperature. The small punch(SP) test was conducted to detect similar isothermally aging condition with material degradation occurred in service welding. The single-specimen unloading compliance method was used to determine toughness degradation caused by thermal aging for austenitic stainless steels. In addition, we have investigated size effect on fracture toughness by using 20% side-grooved 0.5TCT specimens.

• Journal of the Korean Society of Safety
• /
• v.13 no.4
• /
• pp.19-24
• /
• 1998

Elastic-plastic fracture toughness($J_{IC}$) by ultrasonic method is evaluated in terms of width and thickness. Widths of specimen in 6061-T6 aluminum alloy are 50mm and 100mm, thicknesses of those are 20mm and 25mm, respectively. Elastic-plastic fracture toughness by ultrasonic method is independent of specimen thickness and side groove. Angle beam probe which are placed on the end of the compact specimen detect the maximum crack extension effectively. Comparing with elastic-plastic fracture toughness by ultrasonic method and that of unloading compliance method, $J_{IC}$ of ultrasonic method are underestimated to that of unloading compliance method. Elastic-plastic fracture toughness of width 100mm specimen are underestimated to that of width 50mm specimen about 20%.

• Journal of Ocean Engineering and Technology
• /
• v.8 no.2
• /
• pp.157-165
• /
• 1994

Effect of an accelerated iso-thermal aging (375 degree C x 66days, 375 degree C x 200days) on elastic-plastic fracture resistance curve were examined in SA533B low alloy steel. Fracture toughness test are conducted by unloading compliance method at room temperature. But the apparent negative crack growth phenomenon, usually arise in partial unloading compliance test. The phenomenon of negative crack growth may be eliminated by the offset technique. There is no effect of aging on J sub(IC) and dJ/da in iso-thermal aged (375 degree C x 66 days) specimen, but there is very little effect in iso-thermal aged (375 degree C x 200 days) specimen.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.22 no.2
• /
• pp.343-351
• /
• 1998

This paper was investigated degradation of the fracture toughness caused by sensitizing heat-treatment of the cryogenic structural material JN1 base metal using unloading compliance method reported as useful a method in evaluating the elastic-plastic fracture toughness at cryogenic temperature. The specimens used in this paper were 20% side-grooved 0.5T-CT specimens which were machined in the JN1 base metal. Also, to investigate cryogenic fracture toughness of the fusion line region in the JN1 GTA weldments, it was also used 20% side-grooved 0.5T-CT specimens that was machined fusion line to located in the middle of the specimen. The cryogenic fracture toughness values of the JN1 base metal were significantly decreased with increasing the time and temperature of the heat treatment. The fracture toughness value obtained from the fusion line specimen was invalid, but it was lower value than that of the JN1 base metal. Especially, this value was approximately equal with that obtained from the JN1 650.deg. C-5h heat-treated material.

• Nuclear Engineering and Technology
• /
• v.19 no.1
• /
• pp.1-9
• /
• 1987

The fracture toughness of SA 533 Grade B Class 1 steel has been studied with the Charpy impact test specimens in a range of temperature between -4$0^{\circ}C$ and 288$^{\circ}C$. The dynamic fracture toughness is measured by the instrumented precracked Charpy impact test while the static fracture toughness is by the 3-point bend test based on the unloading compliance method. The results are compared with the data obtained from the large specimens. It is known through the studies that temperature dependence of the appropriate (a low bound) value of the fracture toughness can be estimated by taking the static fracture toughness above the transition temperature and the dynamic fracture toughness below the temperature and it is also shown that the tests are satisfied with the requirements of ASTM E 813 when the side-groove is more than 14%.

• Journal of Ocean Engineering and Technology
• /
• v.15 no.3
• /
• pp.63-68
• /
• 2001

SG-365 steel is an important material and used for manufacturing a pressure vessel which the gas piping. In this investigation, the elastic plastic fracture toughness of this material is evaluated by the an unloading compliance method according to the ATM E813-97 method on the smooth and side groove 1CT specimens. The effect of smooth and side groove is studied on the elastic plastic fracture toughness. The side grooved specimen is very useful in estimation of the $J_IC. Because it is much easier than the smooth specimen to the onset of the ductile tearing by the R curve method. Besides, it improves the accuracy of toughness values, decreases the scattering of them and tunneling and shear lip by the side groove.