This study focuses on the fabrication of a WC/Co composite powder from the oxide of WC/Co hardmetal scrap using solid carbon in a hydrogen gas atmosphere for the recycling of WC/Co hardmetal. Mixed powders are manufactured by mechanically milling the oxide powder of WC-13 wt% Co hardmetal scrap and carbon black with varying powder/ball weight ratios. The oxide powder of WC-13 wt% Co hardmetal scrap consists of $WO_3$ and $CoWO_4$. The mixed powder mechanically milled at a lower powder/ball weight ratio (high mechanical milling energy) has a more rapid carbothermal reduction reaction in the formation of WC and Co phases compared with that mechanically milled at a higher powder/ball weight ratio (lower mechanical milling energy). The WC/Co composite powder is fabricated at $900^{\circ}C$ for 6 h from the oxide of WC/Co hardmetal scrap using solid carbon in a hydrogen gas atmosphere. The fabricated WC/Co composite powder has a particle size of approximately $0.25-0.5{\mu}m$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.298.2-298.2
• /
• 2016

가공이 까다로운 소재를 가공하기 위한 공구에 적용하기 위해서 Al의 함량이 높은 AlTiN 소재가 개발되어 적용되고 있으며, 이 소재는 공구의 수명향상을 위한 표면처리 소재로 각광을 받고 있다. 본 연구에서는 음극 아크 증착 시 거대입자가 박막에 증착되어 결함을 만들기 때문에 그 밀도를 낮추기 위해서 음극 아크 증착을 이용하여 공정 변화에 따른 AlTiN 박막의 표면형상을 관찰하고 특성을 평가하였다. 또한 빗각 증착을 적용하여 제작한 AlTiN 박막의 특성을 평가하였다. Al-25 at.%Ti 합금타겟을 음극 아크 소스에 장착하여 AlTiN 박막을 코팅하였다. 시편은 스테인리스 강판(SUS304)과 초경(tungsten carbide; WC)을 사용하였다. 음극 아크 소스에 인가되는 전류가 낮을수록 AlTiN 박막 표면에 거대입자의 밀도가 낮아졌으며, 기판 전압과 공정압력이 높을수록 AlTiN 박막의 표면에 존재하는 거대입자의 밀도가 낮아지는 경향을 보였다. 이를 통하여 거대입자밀도를 낮추는 기초공정을 도출하였다. AlTiN 박막 제작 시 빗각을 적용한 결과 $60^{\circ}$의 빗각을 적용한 다층 박막에서 약 33 GPa의 경도를 보였다. 본 연구를 통해 음극 아크 증착을 이용하여 거대입자의 밀도가 낮은 박막을 제작할 수 있는 공정을 도출하였고, 빗각증착을 적용하면 경도가 향상되는 결과를 확인하였다. 이를 통해 절삭공구 등과 같이 고경도의 코팅물성 유지를 위한 코팅분야에 응용이 가능할 것으로 판단된다.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.3
• /
• pp.249-256
• /
• 2015

PURPOSE. The aim of this study was to evaluate the effects of atmospheric plasma (APL) versus conventional surface treatments on the adhesion of self-adhesive resin cement to Ti-6Al-4V alloy. MATERIALS AND METHODS. Sixty plates of machined titanium (Ti) discs were divided into five groups (n=12): 1) Untreated (CNT); 2) Sandblasted (SAB); 3) Tribochemically treated (ROC); 4) Tungsten CarbideBur (TCB); 5) APL treated (APL). SEM analysis and surface roughness (Ra) measurements were performed. Self-adhesive resin cement was bonded to the Ti surfaces and shear bond strength (SBS) tests, Ra and failure mode examinations were carried out. Data were analyzed by one-way analysis of variance and chi-squared test. RESULTS. The lowest SBS value was obtained with CNT and was significantly different from all other groups except for APL. The ROC showed the highest SBS and Ra values of all the groups. CONCLUSION. It was concluded that the effect of APL on SBS and Ra was not sufficient and it may not be a potential for promoting adhesion to titanium.

• Design & Manufacturing
• /
• v.6 no.2
• /
• pp.90-95
• /
• 2012

The sheet metal forming proceccing is very important and indispensable in the automotive industry because the accuracy of prsee worked parts is directly related to the automotive quality. But when making mold it is difficult and expensive to modify mold. mold design technology is a critical technology in press plastic working. When design the mold there are lots of variables in press plastic working according to worked material, mold materials, conditions of heat treatment, clearance and so on. Abrasion of mold depends on these kind of conditions and sheared surface which is crucial for quality of product also depends on them. In this study, we conduct research on abrasion loss of mold according to 8, 10 and 12% of clearance for thickness of 1.0mm of worked material out of mold design variables of the products whose worked materials are high carbon steel and carbon tool steel by a practical experiment and perform a comparative evaluation of difference of abrasion loss mold with the alloy tool steel (STD11) and Tungsten Carbide (WC).

• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.1
• /
• pp.55-65
• /
• 1999

Graphitization of cementite in high carbon steels at subcritical temperature is reported. We have studied about the effects of Ni in these steels on graphitization. The chemical compositions of the specimens were Fe-(0.54, 0.7)%-C-1.0%Si-0.1%Mn-(0.2~1.0)%Ni. After annealing at $650^{\circ}C$, $680^{\circ}C$ and $700^{\circ}C$ during various time the microstructures and hardness change were observed. In order to recover the initial hardness of high carbon steel, dissolution treatment of graphite was performed at $870^{\circ}C$. In case of 0.7%C steel, graphitization was accelerated rather 1.0%Ni addition steel than 0.2% and 0.54%Ni addition steels but the graphite is coarser. In case of 0.54%C-0.2%Ni steel, graphite particles were distributed relatively homogeniously and finely. Nickel addition promotes graphitization of these steels but makes graphite blocky.

• Journal of the Korean Society for Precision Engineering
• /
• v.26 no.8
• /
• pp.47-54
• /
• 2009

In this study, a simple and effective method was proposed to minimize electrolytic corrosion on the workpiece during ED-drilling using water as a working fluid. The adhesion of a cover plate onto the surface of the workpiece was greatly effective for suppressing electrolytic corrosion during ED-drilling. The experiment revealed that the adhesion of the cover plate prevented corrosion without causing significant changes in machining characteristics. Using the machining method proposed in this paper, electrolytic-corrosion-free holes can be machined without change in the machinery system. By using corrosion-free hole as a start hole for wire EDM, a lead frame die with high quality was fabricated successfully.

• Journal of Electrical Engineering and Technology
• /
• v.12 no.6
• /
• pp.2256-2261
• /
• 2017

Carbon nanotube (CNT) and alumina ($Al_2O_3$) are synthesized into hybrid composites, and an advanced electrical discharge machining (EDM) system is developed for the machining of hard and conductive materials. CNT nanoparticles are mixed with $Al_2O_3$ powder and the $Al_2O_3$/CNT slurry is sintered by spark plasma. The hardness and the electrical conductivity of the $Al_2O_3$/CNT hybrid composite were investigated. The electrical discharge is controlled by a capacitive ballast circuit. The capacitive ballast circuit is applied to the tungsten carbide and the $Al_2O_3$/CNT hybrid composite. The voltage-current waveforms and scanning electron microscope (SEM) images were measured to analyze the characteristics of the boring process. The developed EDM process can manufacture the ceramic based hybrid composites, thereby expecting the variety of applications.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.6
• /
• pp.482-487
• /
• 2013

The new recycling technology for aged aluminum wires in overhead conductor have been carried out. We are attempting to develop remanufacturing method for them for more effective way of recycling in stead of its conventional remelting process. The drawing process of aged aluminum wires play a role in remanufacture process. Drawing process was performed under lubricant. The speed of drawing was between 500 m/min and 1,000 m/min. These machines have 11 or 12 dies house for breakdown of the feedstock. Material of the die is tungsten carbide and they have generally 25% reduction ratio. The paper investigates the mechanical properties during drawing process of aged aluminum wire. The results of tensile tests and microscopic analysis were discussed to underscore the hardening features of drawing aluminum wire. Various graphs are presented accompanied by discussion about their relevance on the process.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.1744-1748
• /
• 2007

In this study, the Johnson-Kendall-Roberts (JKR) theory was combined with the instrumented indentation technique (IIT) to evaluate work of adhesion and modulus of elastomeric polymer. Indentation test was used to obtain the load-displacement data for contacts between Tungsten Carbide indenter and elastomeric polymer. And the JKR contact model, contrived to take viscoelastic effects of polymer into account, was applied to compensate the contact area and the elastic modulus which Hertzian contact model would underestimate and overestimate, respectively. Besides, we could obtain the thermodynamic work of adhesion by considering the surface energy in this contact model. In order to define the relation between JKR contact area and applied load without optical measuring of contact area, we used the relation between applied load and contact stiffness by examining the correlation between JKR contact area and stiffness through dimensional analysis with 14 kinds of elastomeric polymer. From this work, it could be demonstrated that the interfacial work of adhesion and elastic modulus of compliant polymer can be obtained from a simple instrumented indentation testing without area measurement, and provided as the main algorithm of compliant polymer characterization.

• Korean Journal of Crystallography
• /
• v.5 no.1
• /
• pp.39-50
• /
• 1994

Diamond thin films were deposited on silicon, molybdebum, titanum and tugsten substrates, and were chlwntnizen using scanning electron microscopy, X-ray diffraction analysis and Raman spectroscopy. From the result of experiment in various deposition periods, it was found that found that were nucleated and grown on interlayed carbide layers, which were formed on refractory metal substrates at the initial stage of.