• KSTLE International Journal
• /
• 제3권1호
• /
• pp.12-16
• /
• 2002

Micro/nano tribological and water wetting characteristics of ion beam treated PTFE (polytetrafluoroethylene) surfaces were experimentally studied. The ion beam treatment was performed with a hollow cathode ion gun at different argon ion dose conditions in a vacuum chamber to modify the topography of PTFE surface. Micro/nano tribological characteristics, water wetting angles and roughness were measured with a micro tribe tester, SPM (scanning probe microscope), contact anglemeter and profilometer, respectively. Results showed that surface roughness increased with the argon ion dose. Water wetting angle of the ion beam treated samples increased with the ion dose, so the surface shows an ultra-hydrophobic nature. Micro-adhesion and micro-friction depend on the wetting characteristics of the PTFE samples. However, nano-tribological characteristics showed different results. The scale effect of surface topography on tribological characteristics was discussed. Also, the water wetting characteristics of modified PTFE samples were discussed in terms of the surface topographic characteristics.

• Tribology and Lubricants
• /
• 제36권2호
• /
• pp.55-63
• /
• 2020

Recently, graphene has attracted considerable attention owing to its unique electrical, optical, thermal, and mechanical properties. The broad spectrum of applications from optics, sensors, and electronics to biodevice have been proposed based on these properties. In particular, graphene has been proposed as a protective coating layer and solid lubricant for microdevices and nanodevices because of its high mechanical strength, chemical inertness, and low friction characteristics. During the past decade, extensive efforts have been made to explore the tribological characteristics of graphene under various conditions and to expand its applicability. In addition to the experimental approaches, the molecular simulations performed provide fundamental insights into the friction and wear characteristics of graphene resulting from molecular interactions. This work is a review of the studies conducted over the past decade on the tribological characteristics of graphene using molecular simulation. These studies demonstrate the principal mechanisms of the superlubricity of graphene and help clarify the influences of surface conditions on tribological behavior. In particular, the investigation of the effects of the number of layers, strength of adhesion to the substrate, surface roughness, and commensurability provides deeper insights into the tribological characteristics of graphene. These fundamental understandings can help elucidate the feasibility of graphene as a protective coating layer and solid lubricant for microdevices and nanodevices.

• 한국정밀공학회지
• /
• 제16권5호통권98호
• /
• pp.145-150
• /
• 1999

We have studied on the tribological characteristics of surface modification by Arc Ion Implantation(AIP) coating method. Coating materials were deposited by the Titanium carbide(TiC) and Titanium nitride(TiN). An experimental process was established to determine the tribological characteristics of friction and wear behaviour with the variation of applied load, temperature and the time by the Falex friction and wear test machine. The results, It can be improved that when the surface modification of hard coatings(TiC, TiN) was deposited steel, the tribological characteristics become better. It is argued that improved because of excellence of the anti-wear, the extreme pressure properties and the heat stability.

• 한국산업융합학회 논문집
• /
• 제26권5호
• /
• pp.743-750
• /
• 2023

Aluminum alloy is a material widely used in the aircraft industry. However, since it has relatively low hardness, strength and tribological properties, it is necessary to improve these properties. In this paper, a TiN thin film was coated on the surface of AL7075-T7351 using DC magnetron sputtering. The coating was performed by setting different deposition pressure, deposition time, and applied power. Then, the tribological properties of the thin film were investigated. As a result of the experiment, the hardness of the thin film was higher than that of the base material, and the specimen with the highest hardness had excellent friction coefficient, wear amount, and adhesive strength characteristics. Through this study, it was confirmed that the tribological characteristics of aluminum alloy can be improved by depositing thin films using DC magnetron sputtering.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 proceedings of the second asia international conference on tribology
• /
• pp.339-340
• /
• 2002

Natural castor oil was chemically reconstructed to extend the carbon chains by means of iso-reaction so as to improve the rheological behavior, by way of increasing the viscosity index and decreasing the pour point. The rheological and tribological characteristics of the reconstructed castor oil were comparatively investigated with those of the natural castor oil and several other vegetable oils and a mineral oil. The friction and wear test results on a four-ball machine indicate that the chemically reconstructed castor oil has considerably improved rheological and tribological properties as compared with the natural castor oil. It shows a greatly increase viscosity index and largely decreased pour point, which makes it applicable to low temperature lubrication. The chemically reconstructed castor oil even shows better tribological behavior than pentaerythritol ester or di-iso-capryl sebacate. However, it is still needed to increase the oxidation stability of the reconstructed castor oil.

• Tribology and Lubricants
• /
• 제26권1호
• /
• pp.7-13
• /
• 2010

This experimental study presents tribological characteristics under boundary lubrication contacts associated with electrorheolocal (ER) fluid. ER fluid is prepared by using phosphorated starch particles and silicone oil. Experimental apparatus of tribological tester is designed and constructed to evaluate tribological characteristics of pin specimens. Wear tests under boundary lubrication of ER fluid are experimentally performed under consideration of several operational factors such as normal load, sliding distance, sliding speed and specimen materials: steel, copper and aluminum. After wear test, microscopic surface changes of the worn pin specimens are analyzed in order to investigate measured wear characteristics by using the scanning electron microscope (SEM) as well as surface profilometer. In addition, the chemical wear characteristics are investigated by using energy dispersive x-ray spectroscopy (EDS). Moreover, friction coefficient measurements under different materials of pin specimens are conducted for the tribological investigations. In order to verify the effect of starch phosphate particles in ER fluid, the wear test results with ER fluid are compared with test results with only silicone oil. The results clearly present that the phosphorated starch based ER fluid shows the stabilized wear as well as friction characteristics after run-in operations, but the wear rate under ER fluid is increased.

• 한국산학기술학회논문지
• /
• 제8권3호
• /
• pp.432-436
• /
• 2007

자동차 구조용 재료에 대하여 물리적 증착 코팅방법에 의한 트라이볼로지 특성을 연구 하였다. 코팅 재료는 탄화티탄(TiC)과 질화티탄(TiN)이다. 실험은 펠렉스 마찰 마모시험기를 이용하여 하중과 온도에 다양한 조건을 적용하여 마찰과 마모 거동에 대하여 트라이볼로지 특성을 결정하고 평가하였다. 연구결과 코팅하지 않았을 때보다 코팅하였을 때가 윤활 특성이 향상 되었고, 특히 내마모성 및 극압성 그리고 열 안정성이 훌륭하였다.

• Journal of Advanced Marine Engineering and Technology
• /
• 제32권4호
• /
• pp.557-562
• /
• 2008

In this paper, experiments have been performed for the investigation of tribological characteristics of automobile gear oil with the addition of ZDDP and DEP by using the FALEX WEAR TEST MACHINE. The results are as follows. The wear characteristics of gear oil was improved by adding compound additives. The extreme pressure of gear oil increases and then decreases with the applied load. The maximum extreme pressure of gear oil with compound additive is bigger then that of pure gear oil. The friction coefficient of pure gear oil monotonically increases with the temperature, but that of gear oil mixed with the additives decreases at the high temperature.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1999년도 제29회 춘계학술대회
• /
• pp.53-60
• /
• 1999

As the flying height decreased, it is essential that hard disk drives perform reliable under various environmental conditions. In this paper the tribological characteristics of a head/disk interface are investigated under various temperature, relative humidity, altitude and outgas conditions. Specially, Contact-Start-Stop(CSS) tests were performed to assess the stiction, acoustic emission, slider take-off behavior, and track average amplitude(TAA). It is shown that the surface damage and head failure are accelerated by high temperature and humidity as well as low ambient pressure.

• Tribology and Lubricants
• /
• 제12권1호
• /
• pp.6-14
• /
• 1996

Experimental investigation on the tribological behavior of fiber-reinforced plastics(FRP) has been studied. It is shown that the frictional behavior of carbon FRP depends on the fiber-orientation while glass FRP does not. The friction coefficient values for carbon FRP were about 0.8, 0.3, and 0.2 for normal, 45$^{\circ}$ and 0$^{\circ}$ sliding directions respectively. Also, the applied load was found to affect the friction coefficient. In the case of this work, 50 gf resulted in the highest value while 200 gf resulted in the lowest value. The friction coefficients for higher loads fell in between the two extreme values.