• Progress in Superconductivity
• /
• v.3 no.1
• /
• pp.130-133
• /
• 2001

A multifilamentary Bi-2223 HTS tape for superconducting power applications was studied through the fabrication of 250-meter long tapes by the PIT(powder in tube) process. To fabricate continuous long wire, a drawing machine, a two-drum bull block and a rolled tape winding machine were developed. Especially, 250-meter long tapes were heat treated in the shape of pancake coil to reduce the heat affect zone and to achieve the high critical current. Engineering critical current density was improved through both the enhancements of critical current density by control of thermal process and the increase of filling factor by using thin Ag alloy sheath tubes less than 1.5 mm in thickness. We have made successfully 250-meter long 37 filamentary tapes with high filling factor up to 31 % employing the modified drawing and rolling technique. The critical current of 250-meter long tapes with pancake coil type was measured by transport method at self-field up to 250 gauss of center field. The measured values, based on the transport critical current at self-field, $I_{c}$ -B characteristics and magnetic field analysis, are 34 A of I$_{c}$ and 4.0 $kA/\textrm{cm}^2$ of $J_{e}$ at 250 m, 77 K, and 0 T. We also have achieved the 56 A of I$_{c}$ and 7.0 $0 kA/\textrm{cm}^2$ of$ J_{e}$ in short tapes at 77K, self-field, and 1$mutextrm{V}$/cm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.5
• /
• pp.418-423
• /
• 2003

AC loss is an important issue in the design of high-T$\sub$c/ superconducting power cables which consist of a number of Bi-2223 tapes wound on a former. In the cables, the tapes have different critical currents intrinsically. And they are electrically connected to each other and current leads. These make loss measurements considerably complex, especially for short samples of laboratory size. So special cautions are required in the positioning of voltage leads for measuring the true loss voltage. In this work we have prepared a conductor composed of three Bi-2223 tapes with different critical currents. The critical current and AC loss characteristics in the conductor have experimentally investigated. The results show that for uniform current distributions the conductor's critical current is proportional to the critical current of the Bi-2223 tape to which a voltage lead is attached. However it depends on the current non-uniformity parameter in the conductor rather than the tape's critical currents for nonuniform current distributions. The loss tests indicate that the AC loss is dependent on arrangements of voltage leads but not on their contact positions. The measured losses in the conductor also agree well with the sum of the transport losses measured in each Bi-2223 tape.

• Progress in Superconductivity
• /
• v.5 no.2
• /
• pp.89-93
• /
• 2004

We have studied alternating transport current losses in the vertically stacked high temperature superconducting tapes(HTS) using numerical techniques. In the case of stacked conductors, HTS tapes are exposed to self-field generated by transport current itself and also experienced external magnetic field around adjacent tapes. It is well known that magnetic interactions between neighbored tapes have significant effect on their properties of superconducting tapes such as current distribution, AC loss, and critical current. In this paper, we investigated the transport current losses in stacked conductors consisting of a few of the HTS tapes using numerical analysis. Current distributions are calculated in HTS tape cross-section taking account of magnetic field dependencies, which are represented superconducting nonlinear properties. Dissipated losses in tape and stacked conductors were integrated with current distribution and electric field intensity in the whole conductor region. Finally estimated results were discussed and verified through the analytical theory.

• Progress in Superconductivity and Cryogenics
• /
• v.16 no.1
• /
• pp.27-31
• /
• 2014

2G HTS tapes are widely used for various electric machines. In addition, stacked or parallel connected HTS tapes are essentially used to raise transport current level for large capacity electric machines. Therefore, critical current characteristic of stacked tapes need to be studied. Recently developed 2G HTS tapes are fabricated with various defects doping so that tapes possess pinning center to improve the critical current characteristic. During this process, the critical current is determined minimum value in not perpendicular magnetic field but a specific magnetic field angle according to the reported research. However, the effects of magnetic field angle to critical current of multi-stacked 2G HTS tapes have not been examined. In this paper, field coil which is a race-track coil wound by using an HTS tape with iron-core was fabricated to apply angle adjustable magnetic field to the 2G HTS tape samples. We measured critical current of single and multi-stacked two tapes that have different characteristic depending on various magnetic field angle and magnitude in liquid nitrogen environment. Furthermore, results of single and multi-stacked tapes were compared and analyzed.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.2
• /
• pp.20-24
• /
• 2004

Bi-2223 wire, the first-generation high temperature superconducting (HTS) wire, was successfully commercialized and various electrical machinery and equipment are actively being developed in many countries. Because its critical current is too small to realize the lossless conducting part of electric power system with a HTS wire, multi-HTS paths are used to enlarge the critical current of HTS system. Though the resistance generated in HTS wire by transport current is very small, the difference of it in multi-path is the additional reason which causes the non-uniform current sharing in multi-HTS path except the well known reason, the difference of inductance between each path. In this paper, experimental research on current sharing of multi-strand and multi-stacked HTS wire was implemented. The whole critical current of multi-HTS paths is not equal to sum of critical current of each path because of non-uniform current sharing occurred in this paths. It was verified experimentally that Bi-2223 wires have different resistance generated by same transport current even if they was manufactured in same progress of work. Current sharing phenomenon was affected by difference of resistance and self and mutual inductance.

• Proceedings of the KIEE Conference
• /
• 2001.11b
• /
• pp.96-100
• /
• 2001

Bi-2223 tapes have been developed for low-field power applications at liquid nitrogen temperature. When the Bi-2223 tapes are used in an application such as a power transmission cable or a power transformer, they are supplied with an AC transport current and exposed to an external magnetic field generated by neighboring tape's AC currents simultaneously. AC loss taking into account such real applications is a crucial issue for power applications of the Bi-2223 tapes to be feasible. In this paper, the transport losses for different AC current levels and arrangements of the neighboring tapes have been measured in a 1.5 m long Bi-2223 tape. The significant increase of the transport losses due to neighboring tape's AC currents is observed. An increase of the transport losses caused by a decrease of the Bi-2223 tape's critical current is a minor effect. The measured transport losses could not be explained by a dynamic resistance loss based on DC voltage-current characteristics in combination with the neighboring tape's AC currents. The transport losses do not depend on the frequency of the neighboring tape's AC currents but its arrangements in the range of small current especially.

• Progress in Superconductivity and Cryogenics
• /
• v.17 no.1
• /
• pp.17-20
• /
• 2015

Coated conductor is an important candidate for power cable applications due to its high current density. Even for DC power cable transmission, we must study the transport properties of HTS tapes after slow and fast discharge. In order to evaluate relation of the magnetic field with applied current we developed a scanning magnetic field measurements system by employing a Hall probe. This work presents the measurements of the magnetic fields above a coated conductor by varying applied current pattern. In the work, a transport current of 100 A, less than the critical current, is applied to YBCO coated conductor. We measured the residual magnetic field distributions after cut off the transport current with slow and fast operations. The results show differences of the magnetic field profiles and the corresponding current profiles by an inverse solution from the magnetic field measurement between these two operations because of the hysteresis of coated conductor excited by the transport current.

• Progress in Superconductivity and Cryogenics
• /
• v.23 no.4
• /
• pp.10-13
• /
• 2021

Recently, cable conductors composed of numerous coated conductors have been developed to transport huge current for large-scale applications, for example accelerators and fusion reactors. Various cable conductors such as CORC (Conductor on round core), Roebel Cable, and TSTC (Twisted stacked tape cable) have been designed and tested to apply for large-scale applications. But, these cable conductors cannot improve the engineering critical current density (J_e) because they are made by simple stacking of coated conductors. In this study, multi-HTS (High temperature superconductor) layers on one substrate (MHOS) wire was fabricated to increase the engineering critical current density by using the exfoliation of superconducting layer from substrate and silver diffusion bonding method. By the repetition of these processes, the 10 m long 6-layer MHOS conductor was successfully fabricated without any intermediate layers like buffer or solder. 6-layer MHOS conductor exhibited a high critical current of 2,460A/12mm-w. and high engineering critical current density of 1,367A/mm² at liquid nitrogen temperature.

• Progress in Superconductivity and Cryogenics
• /
• v.12 no.3
• /
• pp.16-20
• /
• 2010

For large scale power applications of HTS conductor, it is getting more important to have a stacked HTS coated conductor with low loss and large current capacity. But it was not easy to measure some electric properties. Stabilizer free YBCO CC for striated/ stacked conductors is easily burned out during the measurement of the critical current density because it has no stabilizer and it is difficult to set-up the current lead and voltage taps because it has many pieces of YBCO CC in a conductor. Instead of direct measuring the critical current of a stacked HTS coated conductor, indirect estimation from measuring a magnetization loss of HTS coated conductor could be useful for practical estimation of the critical current. The magnetization loss of a superconductor is supposed to be affected by a full penetrating magnetic field, and it tends to show an inflection point at the full penetrating magnetic field when we generate the graph of magnetization loss vs. external magnetic field. The full penetrating magnetic field depends on the shape of the conductor and its critical current density, so we can estimate the effective critical current density from measuring the magnetization loss. In this paper, to prove the effectiveness of this indirect estimation of the critical current, we prepared several different kinds of YBCO CC(coated conductor) including a stacked conductor short samples and measured the magnetization losses and the critical currents of each sample by using linked pick up coils and direct voltage measurement with transport current respectively.

• 연구논문집
• /
• s.27
• /
• pp.175-181
• /
• 1997

Superconducting joints between Bi-2223/Ag tapes are fabricated by a press & reaction anneal and a multiple press & anneal. The silver sheath was mechanically or chemically removed from one side of each tape without altering the superconducting core. The exposed superconducting core of the two tapes were brought into contact and pressed so as to form a lap joint. The joined tapes were then subjected to a series of different thermomechanical treatments to achieve optimum heat treatment condition. The result from transport measurements shows that critical current ($I_c$) transmitting through joined area reaches 9A, approximately 60% of the current capacity of the tapes themselves. The critical current through joined area was improved by repeated press and reaction annealing. Measurements of the current-voltage relationship were made with several configuration of the voltage probes to characterize the critical current variation and I-V curve along the joint. Also discussed are microstructural aspects of the superconducting joint.