• Journal of Sensor Science and Technology
• /
• v.28 no.4
• /
• pp.256-261
• /
• 2019

In this study, mid-infrared transparent zinc sulfide (ZnS) ceramics were fabricated through hydrothermal synthesis with different molar ratios of S/Zn (S/Zn = 0.8, 1.0, 1.2, 1.4, and 1.6). The ZnS ceramics were sintered at a relatively low temperature of $850^{\circ}C$ to prevent the occurrence of the hexagonal phase featuring optical anisotropy. The phase composition, microstructure, and optical properties of the ZnS ceramics were subsequently investigated by employing X-ray diffraction, scanning electron microscopy, and Fouriertransform infrared spectroscopy. The results obtained indicate that the ZnS nanoparticles feature the cubic phase, without the hexagonal phase. Moreover, with increasing S, the crystallinity and particle size of the ZnS nanoparticles increased. The crystallinity and density of the ZnS ceramics improved when the molar ratio of S was higher than the molar ratio of Zn, thereby enhancing the transmittance. Furthermore, the ZnS ceramic with an S/Zn value of 1.2 was found to exhibit the highest transmittance of approximately 69% owing to the reduced occurrence of the hexagonal phase and a high density of 99.8%.

• Korean Journal of Materials Research
• /
• v.27 no.1
• /
• pp.12-18
• /
• 2017

Transparent organic-inorganic hybrid hard coating films were prepared by the addition of $SiO_2$ or $ZrO_2$, as an inorganic filler to improve the hardness property, filler was highly dispersed in the acrylic resin. To improve the compatibility in the acrylic resin, $SiO_2$ or $ZrO_2$ is surface-modified using various silanes with variation of the modification time and silane content. Depending on the content and kind of the modified inorganic oxide, transparent modified inorganic sols were formulated in acryl resin. Then, the sols were bar coated and cured on PET films to investigate the optical and mechanical properties. The optimized film, which has a modified $ZrO_2$ content of 4 wt% markedly improved in terms of the hardness, haze, and transparency as compared to neat acrylate resin and acrylate resin containing modified $SiO_2$ content of 8 wt%. Meanwhile, the low transparency and high haze of these films slowly appeared at $SiO_2$ content above 10 wt% and $ZrO_2$ content of 5 wt%, but the hardness values were maintained at 2H and 3H, respectively, in comparison with the HB of neat acrylate resin.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.11
• /
• pp.722-727
• /
• 2017

Transparent ZnS ceramics were synthesized by hydrothermal synthesis ($180^{\circ}C$ for 70 h), and were sintered by a hot press process at $950^{\circ}C$. To confirm the optical properties of the ZnS ceramics after sintering for various sintering holding times, we performed X-ray diffraction analysis, scanning electron microscopy, and Fourier-transform-infrared spectroscopy. The ZnS nanopowders was found to be single-phase (cubic) without any hexagonal phase. However, the hexagonal phase is formed and increases in content with increasing sintering holding time. The density of the ZnS ceramics was above 99.7%, except for the unsintered one. The ZnS ceramics showed high transmittance (~70%) when sintered for more than 2 h.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2004.04b
• /
• pp.36.3-36.3
• /
• 2004

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.40.1-40
• /
• 2003

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.1
• /
• pp.50-54
• /
• 1999

Plasma display panel is a potential candidate for HDTV, due to the fact that the screen size can easily be increased by a thick film technology. In this study, transparent dielectric materials which satisfied the requirements of dielectrics for PDP was developed using lead alumina borosilicate glasses. The Paste which had thixotropic behavior suitable for screen printing was made of this glass composition. the paste became more thixotropic as the particle size decreased. After firing, the cross sectional area of the thick film was analyzed by SEM. The voids in the thick film were removed using bimodal particle system. The dielectric thick film showed good adhesion characteristics.

• Journal of the Korean Ceramic Society
• /
• v.43 no.10 s.293
• /
• pp.635-639
• /
• 2006

Dispersion behavior of the slurries consisted of Pb or Bi-based glass frits, which are used for the fabrication of green sheet as PDP front panel transparent dielectric, was examined in non-aqueous solvent system. Measurements of sedimentation height and viscosity were conducted to determine proper dispersion condition in the various solvent and dispersant system. Azotropic compound and ethyl acetate were used as the solvent and ammonium-type dispersant was applied to the slurries. All slurries were dispersed well in azotropic solvent system involving 20$\sim$50 vol% ethyl acetate at 2$\sim$3 wt% dispersant content. Especially, dispersion behavior was notably improved in the addition of ethyl acetate in the Bi-based frit slurry.

• Journal of the Korean Ceramic Society
• /
• v.45 no.1
• /
• pp.30-35
• /
• 2008

In this paper, CdS/Cd(Cu)S thin films and diodes were manufactured via a chemical bath deposition (CBD) process, and the effects of $NH_4Cl$ and TEA(triethylamine) on the properties of the films were examined. The addition of $NH_4Cl$ significantly increased the thickness of the CdS and Cd(Cu)S films, however, the addition of TEA decreased the thickness in both cases slightly. The addition of $NH_4Cl$ along with TEA increased the film thickness more effectively compared to the addition of only $NH_4Cl$. The thickness of the CdS film prepared from an aqueous solution of 0.007 M $CdSO_4$, 1.3 M $NH_4OH$, 0.03 M $SC(NH_2)_2$, 0.0001 M TEA and 0.03 M $NH_4Cl$ was 310 nm. Dark resistivity of the CdS film was $1.2{\times}10^3\;{\Omega}cm$ and the photo resistivity with $500\;W/cm^2$ irradiation of white light was $20{\Omega}cm$. The Cd(Cu)S/CdS thin film diodes prepared by CBD showed good rectifying characteristics.

• Journal of Ceramic Processing Research
• /
• v.13 no.spc2
• /
• pp.394-397
• /
• 2012

In this work, we studied the influence of the dopant elements concentration on the properties of SnO2 thin films deposited by pulsed laser deposition. X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), Hall effect measurement and UV-Vis studies were performed to characterize the deposited films. XRD results showed that the films had polycrystalline nature with tetragonal rutile structure. FE-SEM micrographs revealed that the as deposited films composed of dense microstructures with uniform grain size distribution. All the films show n-type conduction and the best transparent conductive oxide (TCO) performance was obtained on 6 wt% Sb2O5 doped SnO2 film prepared at pO2 of 60mtorr and Ts of 500 ℃. Its resitivity, optical transmittance, figure of merit are 7.8 × 10-4 Ω cm, 85% and 1.2 × 10-2 Ω-1, respectively.

• Journal of the Korean Ceramic Society
• /
• v.53 no.3
• /
• pp.338-342
• /
• 2016

ZnO thin film co-doped with F and Al was prepared on a glass substrate via simple non-alkoxide sol-gel spin coating. For a fixed F concentration, the addition of Al co-dopant was shown to reduce the resistivity mainly due to an increase in electrical carrier density compared with ZnO doped with F only, especially after the second post-heat-treatment in a reducing environment. There was no effective positive contribution to the reduction in resistivity due to the mobility enhancement by the addition of Al co-dopant. Optical transmittance of the ZnO thin film co-doped with F and Al in the visible light domain was shown to be higher than that of the ZnO thin film doped with F only.