• 한국항공운항학회지
• /
• 제18권1호
• /
• pp.1-10
• /
• 2010

Structures under high temperature may have creep behavior and fatigue behavior. Durability study of the structures need the damage analysis with the creep-fatigue effects. In this paper, the damage analysis is studied for a turbine blade in the turbopump for a liquid rocket engine which is operated under high temperature condition. First of all, the load cycle is required for defining the operational characteristics of turbopump. The thermal stress analysis is done for a turbine blade of the turbopump. The stress analysis results are used to judge damage due to the creep and the fatigue. The strain-life method with miner rule is used for fatigue damage analysis. The Larson-Miller parameter master curve and robinson rule are used for the creep damage analysis. The linear damage summation method is used to consider creep-fatigue effects of turbopump turbine. Finally, the analysis results for fatigue and the influence are compared to figure out the damage phenomenon of the turbopump turbine.

• Geomechanics and Engineering
• /
• 제18권1호
• /
• pp.71-83
• /
• 2019

This investigation presented conventional triaxial and creep-permeability tests on sandstones considering thermally-induced damage (TID). The TID had no visible effects on rock surface color, effective porosity and permeability below $300^{\circ}C$ TID level. The permeability enlarged approximately two orders of magnitude as TID increased to $1000^{\circ}C$ level. TID of $700^{\circ}C$ level was a threshold where the influence of TID on the normalized mass and volume of the specimen can be divided into two linear phases. Moreover, no prominent variations in the deformation moduli and peak strength and strain appeared as TID< $500^{\circ}C$ level. It is interesting that the peak strength increased by 24.3% at $700^{\circ}C$ level but decreased by 11.5% at $1000^{\circ}C$ level. The time-related deformation and steady-state creep rate had positive correlations with creep loading and the TID level, whereas the instantaneous modulus showed the opposite. The strain rates under creep failure stresses raised 1-4 orders of magnitude than those at low-stress levels. The permeability was not only dependent on the TID level but also dependent on creep deformation. The TID resulted in large deformation and complexity of failure pattern for the sandstone.

• 대한기계학회논문집A
• /
• 제30권9호
• /
• pp.1034-1040
• /
• 2006

Due to the need of increasing thermal efficiency, supercritical pressure and temperature have been utilized in power plants. It is well known that 9Cr1Mo steel is suitable fer use in power plants operating at supercritical conditions. Therefore, to ensure the safety and the soundness of the power plant, creep characterization of the steel is important. In this study, the creep characterization of the gCr1Mo steel using small punch creep(SP-Creep) test has been described. The applied load and the central displacement of the specimen in SP-Creep test have been converted to bearing stress and strain of uc, respectively. The converted SP-Creep curves clearly showed the typical three-stage behavior of creep. The steady-state creep rate and the rupture time of the steel logarithmically changed with the bearing stress and satisfied the Power law relationship. Furthermore, the Larson-Miller parameter of the SP-Creep test agreed with that of the tensile creep test. From the comparison with low Cr-Mo steels, the creep characteristics of 9Cr1Mo steel proved to be superior. Thus, it can be confirmed that the 9Cr1Mo steel is suitable for supercritical power plant.

• 소성∙가공
• /
• 제14권6호
• /
• pp.502-508
• /
• 2005

Hypereutectic Al-Si alloys have been regarded attractive for automotive and aerospace application, due to high specific strength, good wear resistance, high thermal stability, low thermal expansion coefficient and good creep resistance. Spray casting of hypereutectic Al-Si alloy has been reported to provide distinct advantages over ingot metallurgy (IM) or rapid solidification/powder metallurgy (RS/PM) process in terms of microstructure refinement. In this study, hypereutectic Al-25Si-2.0Cu-1.0Mg alloy was prepared by OSPREY spray casting process. The change of strain rate sensitivity and Creep transition were analyzed by using the load relaxation test and constant creep test. High temperature deformation behavior of the hypereutectic Al-Si alloy has been investigated by applying the internal variable theory proposed by Chang et al. Especially, the creep resistance of spray casted hypereutectic Al-Si alloy can be enhanced considerably by the accumulation of prestrain.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2012년도 춘계 학술논문 발표대회
• /
• pp.255-256
• /
• 2012

In this study, strain properties of high strength concrete using light weight aggregate which is widely used in recent years are evaluated. For these purpose, thermal strain, transient creep were measured in prestressed condition as 0, 20, 40% of specimen strength at target temperature with 60MPa specimens which was using normal and light weight aggregate. As a result, light weight aggregate is more advantageous for the control of strain than normal aggregate because of its low thermal expansion.

• Journal of Welding and Joining
• /
• 제16권4호
• /
• pp.92-97
• /
• 1998

Because of the low melting temperature of solder, each temperature cycle initiates an irrecoverable creep deformation at the solder interconnection which connects the package body with the PCB. The crack starts and propagates from the position where the creep deformation is maximized. This work has tried to compare and analyze the thermal fatigue life of solder interconnection which is affected by the lead material, the size of die pad, chip thickness, and interface delamination of 48-Pin TSOP under the temperature cycle ($0^{\circ}C$~1$25^{\circ}C$). The crack initiation position and thermal fatigue life which are calculated by using FEA method are well matched with the results of experiments. The thermal Fatigue life of copper lead frame is extended around 3.6 times longer than that of alloy 42 lead frame. It is maximized when the chip size is matched with the length of the lead. It tends to be extended as the thickness of chip got thinner. As the interfacial delamination between die pad and EMC is increased, the thermal fatigue life tends to decrease in the beginning of delamination, and increase after the delamination grew after 45% of the length of die pad.

• 수산해양기술연구
• /
• 제28권1호
• /
• pp.71-78
• /
• 1992

Zr-4 used for a cladding and an end plug of reactor component has creep deformation under operation at high temperature. Creep is regarded as the time dependent deformation of a material under constant applied stress. Although the major source of the deformation of zirconium component in water-cooled reactors is irradiation creep, the thermal creep may give a rise to significant deformation in reactor component especially at relatively high temperatures and at various constant stresses, and therefore it must be predicted accurately. Stress relaxation is the time dependent change of stress at constant strain and it is a process related intimately to creep. In this paper, the creep behavior and stress relaxation of Zr-4 is examined at the temperature of 50$0^{\circ}C$ that is 40% of the absolute melting temperature of Zr-4 under the stress below yield stress and under the various constant strains. The results obtained are summarized as follows: 1) With an increase of stress, the steady state creep rate increases and the creep rupture time decreases. 2) The steady state creep rate $\varepsilon$(%/s) for the stress $\sigma$sub(c) (kgf/mm super(2)) of Zr-4 increases outstandingly. All the empirical equations computed for Zr-4 increases outstandingly. All the empirical equations computed for Zr-4 are in accord with Norton's model equation($\varepsilon$=K$\sigma$ sub(c) super (n)). The constants of materials computed are as follows: K=3.9881$\times$10 super(-5), n=1.9608 3) The rupture time T sub(r) (hr) decreases linearly with the increase of stress on the log-log scaled graph. The empirical equations computed for Zr-4 are in accord with Bailey's model equation (T sub(r)=K sub(1)$\sigma$sub(c) super(m)). The constants of materials computed are as follows: K sub(1)=1.2875$\times$10 super(16), m=-3.467 4) It seems clear that the strain could be quantitatively dependent on the high temperature creep properties such as creep stress, rupture time, steady state creep rate and total creep rate. It is found that these relationships are linear on the log-log graph. 5) In stress relaxation test, as the critical constant strain that can be allowed to the specimen is larger, stress relaxation becomes more rapid, and as the constant strain is smaller, the stress relaxation becomes slower.

• 콘크리트학회논문집
• /
• 제23권6호
• /
• pp.723-730
• /
• 2011

콘크리트 중의 골재가 차지하는 비율은 약 70~80 vol%로서 콘크리트의 고온 역학적 성상에 큰 영향요소로 작용할 수 있다. 이 연구는 고온시 콘크리트의 역학적 특성을 평가하기 위한 일환으로써 다양한 환경조건, 즉 고온조건, 하중조건에 따른 역학적 특성을 비교하기 위하여 목표강도 60 MPa급 보통 골재 및 경량 골재 콘크리트를 대상으로 선정하였다. 사용된 시험체는 ${\phi}100{\times}200mm$로서 상온 압축강도의 0%, 20%, 40% 하중을 재하한 상태에서 고온에 따른 강도, 탄성계수, 열팽창 변형(thermal strain), 전체 변형(total strain), 내력저하수축(transient creep) 등 고온에서의 역학적 특성을 평가하였다. 시험 결과 골재의 열팽창계수가 작은 경량 콘크리트는 열팽창 변형이 일반 골재를 사용한 콘크리트에 비하여 전반적으로 작게 나타났으며, 고온조건인 $700^{\circ}C$에서도 압축강도 저하가 상온강도에 대하여 80% 수준으로 나타났다. 또한 재하에 의한 내력저하수축은 $500^{\circ}C$를 기준으로 콘크리트의 변형을 팽창에서 수축으로 전환시키는 영향요인으로써, 콘크리트와 골재의 열팽창 변형비(concrete /aggregate)가 수축의 경향이 큰 경우 콘크리트의 내력저하가 적은 경향을 확인할 수 있었다.

• Nuclear Engineering and Technology
• /
• 제49권5호
• /
• pp.1031-1043
• /
• 2017

A structural model for stress distributions of coated Zircaloy subjected to realistic incore pressure difference, thermal expansion, irradiation-induced axial growth, and creep has been developed in this study. In normal operation, the structural integrity of coating layers is anticipated to be significantly challenged with increasing burnup. Strain mismatch between the zircaloy and the coated layer, due to their different irradiation-induced axial growth, and creep deformation are found to be the most dominant causes of stress. This study suggests that the compatibility of the high temperature irradiation-induced strains (axial growth and creep) between zircaloy and the coating layer and the capability to undergo plastic strain should be taken as key metrics, along with the traditional focus on chemical protectiveness.

• Journal of Welding and Joining
• /
• 제15권2호
• /
• pp.64-71
• /
• 1997

In order to define the effects on shapes of welding joint, during Post Welding Heat Treatment (PWHT), we have carried out numerical analysis on the several test pieces by using computer program which was based on thermal-elasto-plastic-creep theories for the study. And then, welding residual stresses after PWHT were measured same test-pieces to compare with the results of numerical analysis. The main results obtained from this study is as follows: 1) The distribution modes of welding residual stresses are same on the all test pieces after and during PWHT by the both sides (measurement and numerical analysis). 2) The mechanical difference for change the thickness of plate and bevel angle are not appeared. 3) In a mechanical point of view (like material quality test, welding deformation etc.), manimum bevel angle (40$^{\circ}$.) is more suitable than maximum bevel angle (70$^{\circ}$).