• Corrosion Science and Technology
• /
• 제4권5호
• /
• pp.191-200
• /
• 2005

Two azole compounds viz., Imidazole (IM) and 2-Methylimidazole (2-MIM) were studied to investigate their inhibiting action on corrosion of mild steel in phosphoric acid ($H_3PO_4$) solution by mass loss and polarization techniques at 302K-333K. It has been found that the inhibition efficiency of the all inhibitors increased with increase in inhibitor concentration and decreases with increasing temperature and also with increase in acid concentrations. The inhibition efficiency of these compounds showed very good inhibition efficiency. At 0.5% of IM and 2-MIM in 1N and 5N phosphoric acid solution at 302K to 333K for 5 hours immersion period, the inhibition efficiency of 2-Methylimidazole found to be higher than Imidazole. The adsorption of these compounds on the mild steel surface from the acids has been found to obey Tempkin's adsorption isotherm. The values of activation energy ($E{\alpha}$) and free energy of adsorption (${\Delta}G{\alpha}ds$) were also calculated. The plots of log $W_f$ against time (days) at 302K give straight line which suggested that it obeys first order kinetics and also calculate the rate constant k and half life time $t_{1/2}$. Surface was analyzed by SEM and FITR spectroscopy.

• 수산해양기술연구
• /
• 제39권4호
• /
• pp.291-297
• /
• 2003

Al-brass is usually used as the tube material of vessel's heat exchanger for seawater cooling system because it has high thermal conductivity and good mechanical properties and high corrosion resistance due to cuprous oxide (Cu20) layer against seawater. However, Al-brass tubes of heat exchanger for vessel at the actual environment is reported that local corrosion such as stress corrosion cracking occurred by synergism effect between mechanical factor and corrosion environment In this paper, the effect of corrosion environment on the stress corrosion cracking of Al-brass in various NH4OH of 3.5% NaCl solution, under flow by constant displacement tester. Based on the test results, the behavior of polarization, stress corrosion crack propagation and dezincification phenomenon of Al-brass are investigated. The main results are as follows：(1) Increasing range of potential from open circuit potential to repassivation gets lower, as the contain rate of NH4OH gets higher. (2) As contain rate of NH4OH gets higher, SCC of Al-brass is become activation but the protection film(Cu20) of Al-brass is created in 3.5% NaCl solution. (3) According as content of NH4OH increases in 3.5% NaCl solution, the dezincifiction area is spread. It is concluded that dezincification occurred by localized preferential anodic dissolution at stress focusing region.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.656-658
• /
• 2004

Pb$(Zr_{0.8}Ti_{0.2})TiO_3$ powder were prepared by the sol-gel method using a solution of Pb-acetate, Zr n-propoxide and Ti iso-propoxide. PZT thick film were fabricated by the screen printing method, and the structural and ferroelectric properties asafunting of the sintering temperature were studied. PZT film thickness, obtained by four screen printing, was approximately $70\sim90{\mu}m$. The relative dielectric constant and the dielectric loss of the PZT thick film sintered at $1050^{\circ}C$t were approximately 676 and 1.4%, respectively. The remanent polarization and the coercive field of the PZT thick film sintered at $1050^{\circ}C$ were $21.15{\mu}C/cm^2$ and 10.1 kV/cm, mapetively

• 한국지구물리탐사학회:학술대회논문집
• /
• 한국지구물리탐사학회 2003년도 Proceedings of the international symposium on the fusion technology
• /
• pp.383-389
• /
• 2003

Clay minerals show a distinct induced-polarization phenomenon, which is one of the most important factors for predicting groundwater flow and contaminant transport. This paper presents a step-by-step process to estimate Cole-Cole parameters from spectral induced-polarization (IP) data measured on the surface of three-dimensional earth. First, the inversion of low-frequency resistivity survey data is made to identify the dc resistivity ${\rho}_dc$ of a volume having IP effects. The other parameters, chargeability m, time constant $\tau$, and frequency dependence c, are sought for the polarizable volume. Next, using multi-frequency data, c can be obtained as high or low asymptotes of the slope of log phase vs. log frequency. Further, for low m, intrinsic $\tau$ is approximated by apparent one, ${\tau}_a$, which is derived from the relation ${{\omega}{\tau}}_a$=1 at an angular frequency $\omega$, where the imaginary component of spectral IP data has an extreme value. Finally, to obtain intrinsic m a two-step linearized procedure has been derived. For a body of given $\tau$ and c, forward modeling with a progression of m values yields a plot of observed vs. intrinsic imaginary components for a frequency. Since this plot is essentially linear, to extract the intrinsic imaginary component is quite simple with an observed value. Using the plot of intrinsic imaginary component vs. m, intrinsic m is determined. We present a synthetic example to illustrate that the Cole-Cole parameters can be recovered from spectral IP data.

• E2M - 전기 전자와 첨단 소재
• /
• 제8권2호
• /
• pp.190-195
• /
• 1995

Temperature dependences of the dielectric constant K(T), remanent polarization $P_{r}$, (T), effective birefringence overbar .DELTA.n(T), transmitted light intensity and quadratic electro optic coefficient R(T) of the two-stage sintered xBa(L $a_{1}$2/N $b_{1}$2/) $O_{3}$-(1-x)Pb(Z $r_{y}$ $Ti_{1-y}$) $O_{3}$(x=0.085, 0.09, 0.40.leq.y.leq.0.70) ceramics were investigated. Increasing the PbZr $O_{3}$ contents, the crystal structure of a specimen was changed from a tetragonal phase to a rhombohedral and cubic phase, and the phase transition was showed a diffuse phase transition(DPT) characteristics. In the compositions which located on the PE-FE phase boundary, the discrepancy was observed between the Curie temperature and temperature which a microscopic polarization and effective birefringence were disappeared.red.d.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집 Vol.3 No.2
• /
• pp.589-592
• /
• 2002

The $Sr_{0.7}Bi_{2.3}Ta_2O_9$(SBT) thin films are deposited on Pt-coated electrode(Pt/TiO2/SiO2/Si) using RF magnetron sputtering method. The structural and electric properties of SBT capacitors were influenced with annealing atmosphere. In the XRD pattern, the SBT thin films in all annealing atmosphere had (105) orientation. In the SEM images, Bi-layered perovskite phase was crystallized in all annealing atmosphere and grains largely grew in oxygen annealing atmosphere. The maximum remanent polarization and the coercive electric field in oxygen annealing atmosphere are $12.40{\mu}C/cm^2$ and 48kV/cm respectively. The dielectric constant and leakage current density annealing in oxygen atmosphere are 340 and $6.81{\times}10^{-10}A/cm^2$ respectively. The fatigue characteristics of SBT capacitors did not change up to $10^{10}$ switching cycles.

• E2M - 전기 전자와 첨단 소재
• /
• 제10권10호
• /
• pp.983-988
• /
• 1997

We investigated the structural and dielectric properties of PZT(20/80)/PZT(80/20) heterolayered thin films that fabricated by the alkoxide-based Sol-Gel method. PZT(20/80)/PZT(80/20) heterolayered thin films were spin-coated on the Pt/Ti/SiO$_2$/Si substrate with PZT(20/80) film of tetragonal structure and PZT(80/20) film of rhombohedral structure by turns. Each layers were dried to remove the organic materials at 30$0^{\circ}C$ for 30min and sintered at $650^{\circ}C$ for 1hr. This procedure was repeated several times to form PZT(20/80)/PZT(80/20) heterolayered films and thickness of the film obtained by one-times of drying/sintering process was approximately 80-90nm. PZt-1, 3, 5 films with top layer of PZT(20/80) film of tetragonal structure showed fine grain structure and PZT-2, 4, 6 films with top layer of PZT(80/20) film of rhombohedral structure showed the dense grain microstructure without rosette-type. Dielectric constant and dielectric loss of the PZT-6 film were approximaterly 1385 and 3.3% respectively. Increasing the number of coatings remanent polarization was increased and coercive field was decreased and the values of the PZT-6 film were 8.13$\mu$C/cm$^2$and 12.5kV/cm respectively.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제48권7호
• /
• pp.514-520
• /
• 1999

Ferroelectric PZT(30/70)/PZT(70/30) heterolayered thin films were fabricated by spin-coating method on the $Pt/Ti/SiO_2Si$ substrate alternately using(30/70) and PZT(70/30) alkoxide solutions prepared by sol-coating method. The coating and heating procedure was repeated six times to form PZT heterolayered films, and thickness of the film obtained by one-times drying/sintering process was about 40-50 nm. All PZT heterolayered films, showed dense and homogeneous structure without the presence of rosette sturctrue. The relative dielectric constant, remanent polarization and leakage current density of PZT heterolayered films were superior to those of single composition PZT(30/70) and PZT(70/30) films, and those values for the PZT-6 film were 975, $21 \muC/cm^2\; and\; 8\times10^{-9}\; A/cm^2$, respectively. And the PZT-6 heterolayered film showed fairly good fatigue characteristics of remanent polarization and coercive field after application of $10^8$ switching cycles.

• Transactions on Electrical and Electronic Materials
• /
• 제13권6호
• /
• pp.297-300
• /
• 2012

Lead-free (1-x)$(Na_{0.5}K_{0.5})NbO_3-xLiNbO_3$, i.e., NKN-LNx (x=0.0, 0.1, 0.2, 0.3, 0.4 mol) was prepared using the conventional solid state reaction method. The effects of LN mixing on the ferroelectric properties of NKN-LNx ceramics were studied using a dielectric constant and P-E (Polarization-electric field) measurements. Ferroelectricity was observed in the composition for x approximately varying between 0.0 and 0.4. Minimum remanent polarization $2P_r=5C/cm^2$ was achieved in the composition for x = 0.2. The ferroelectric phase transition temperature $T_C$ increased with increasing LN content. The ferroelectric phase transition of NKN-LNx ($x{\geq}0.1$) is a second-order phase transition, and that of NKN-LNx ($x{\leq}0.2$) is a first-order phase transition. These results indicate that the ferroelectric phase transition temperature of NKN-LNx change from that of second-order to weak first-order phase transition according to the LN content.

• Bulletin of the Korean Chemical Society
• /
• 제31권2호
• /
• pp.423-428
• /
• 2010

To reduce polarization of electrochemical capacitor based on carbon nanotube, titanium oxide nanoparticles were deposited by ultrasound. The pore distribution of $TiO_2$/CNT nanoparticle exhibited surface area of $341\;m^2g^{-1}$ when $TiO_2$ content was 4 wt %, which was better than that of pristine CNT with surface area of $188\;m^2g^{-1}$. The analyses indicated that titanium oxide (particle diameter < 20 nm) was deposited on the CNT surface. The electrochemical performance was evaluated by using cyclic voltammetry (CV), impedance measurement, and constant-current charge/discharge cycling techniques. The $TiO_2$/CNT composite electrode showed relatively better electrochemical behaviors than CNT electrode by increasing the specific capacitance from $22\;Fg^{-1}$ to $37\;Fg^{-1}$ in 1 M $H_2SO_4$ solution. A symmetric cell assembled with the composite electrodes showed the specific capacitance value of $11\;Fg^{-1}$ at a current loading of $0.5\;mAcm^{-2}$ during initial cycling.