Electric Properties of SBT Thin Films with various Annealing Conditions

다양한 열처리 조건에 따른 SBT 박막의 전기적 특성

The $Sr_{0.7}Bi_{2.3}Ta_2O_9$(SBT) thin films are deposited on Pt-coated electrode(Pt/TiO2/SiO2/Si) using RF magnetron sputtering method. The structural and electric properties of SBT capacitors were influenced with annealing atmosphere. In the XRD pattern, the SBT thin films in all annealing atmosphere had (105) orientation. In the SEM images, Bi-layered perovskite phase was crystallized in all annealing atmosphere and grains largely grew in oxygen annealing atmosphere. The maximum remanent polarization and the coercive electric field in oxygen annealing atmosphere are $12.40{\mu}C/cm^2$ and 48kV/cm respectively. The dielectric constant and leakage current density annealing in oxygen atmosphere are 340 and $6.81{\times}10^{-10}A/cm^2$ respectively. The fatigue characteristics of SBT capacitors did not change up to $10^{10}$ switching cycles.