Lowering surface reflectance of silicon wafer by texturization is one of the most important processes to improve the efficiency of silicon solar cells. Generally, the texturing of crystalline silicon was carried out using alkaline solution. The average reflectance of this method was 11% at the wavelength between 400 and 1,000 nm. In this study, the wafers were first texturing by NaOH solution at $80^{\circ}C$ for 35 min. Then the wafers were texturing by $SF_6$ and $O_2$ plasma in RIE (Reactive Ion Etching). The average reflectance of two step texturing was reduced to below 5% at the wavelength between 400 and 1,000 nm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.1
• /
• pp.58-61
• /
• 2012

In our report a relatively simple process for fast nano-texturing of p-type(100) CZ- silicon surface using silver catalyzed wet chemical etching in aqueous hydrofluoric acid (HF) and hydrogen peroxide solution($H_2O_2$) at room temperature. The wafers were saw-damaged by NaOH(6 wt%) at $60^{\circ}C$ for 150s. To obtain a nano-structured black surface, a thin layer of silver with thickness of 1 - 10 nm was deposited on the surfaces by evaporation system. After this process the samples were etched in HF : $H_2O_2$ : $H_2O$ = 1:5:10 at room temperature for 80s - 220s. Due to the local catalytic of the Ag clusters, this treatment results in the nano-scale texturing on the surface. This resulted in average reflectance values less than 9% after the silver on the surface of the wafers were removed.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.3
• /
• pp.138-143
• /
• 2007

The effects of texturing and anti-reflection coating on the reflection properties of multi-crystalline silicon solar cell have been investigated. The chemical solutions of alkaline and acidic etching solutions were used for texturing at the surface of multi-crystalline Si wafer. Experiments were performed with various temperature and time conditions in order to determine the optimized etching condition. Alkaline etching solution was found inadequate to the texturing of multi-crystalline Si due to its high reflectance of about 25%. The reflectance of Si wafer texturing with acidic etching solution showed a very low reflectance about 10%, which was attributed to the formation of homogeneous. Also, deposition of ITO anti-reflection coating reduced the reflectance of multi-crystalline si etched with acidic solution($HF+HNO_3$) to 2.6%.

• 한국태양에너지학회:학술대회논문집
• /
• 2011.04a
• /
• pp.111-115
• /
• 2011

Surface Texturing is an essential process for high efficiency in multi-crystalline silicon solar cell. In order to reduce the reflectivity, there are two major methods; proper surface texturing and anti-reflection coating. For texturization, wet chemical etching is a typical method for multi-crystalline silicon. The chemical solution for wet etching consists of HF, $NHO_3$, DI and $CH_3COOH$. We carried out texturization by the change of etching time like 15sec, 30sec, 45sec, 60sec and measured the reflectivity of textured wafers. As making the silicon solar cells, we obtained the conversion efficiency and relationship between texturing condition and solar cell characteristics. The reflectivity from 300nm to 1200nm was the lowest with 15 sec texturing time and 60 sec texturing time showed almost same reflectivity as bare one. The 45 sec texturing time showed the highest conversion efficiency.

• Journal of the Korean Society for Precision Engineering
• /
• v.31 no.5
• /
• pp.367-373
• /
• 2014

Surface texturing is a machining process on the surface to give engineering functions. The representative process of the surface texturing is lotus effect to give hydrophobic property by the lithography and chemical etching, which is the bio mimic from the nature. Surface texturing can be manufactured by a lot of processes, in particular using mechanical method such as a precise diamond turning, grinding, rolling, embossing, vibrorolling, and abrasive jet machining (AJM). Among them, the grinding process is notable in terms of the wide range of texturing area and fast processing time. The patterning by grinding is done by the grooved grinding wheel on the work piece. In this case, the pattern shape is determined by the grinding conditions as well as the wheel dressing conditions. In this paper, experimental study on the pattern shapes were done and provide the feasibility in use for the large area patterning.

• Journal of the Semiconductor & Display Technology
• /
• v.13 no.3
• /
• pp.21-25
• /
• 2014

The texturing is one of the most important processes for high efficiency crystalline silicon solar cells. The rear side flatness of silicon solar cell is very important for increasing the light reflectance and forming uniform back surface field(BSF) region in manufacturing high efficiency crystalline silicon solar cells. We investigated texturing difference between front and rear side of wafer by texturing of two adhered wafers. As a result, the flatter rear side was obtained by forming less pyramid size compared to the front side and improved reflectance of long wavelength and back surface field(BSF) region were also achieved. Therefore, the texturing of two adhered wafers can be expected to improve the efficiency of silicon solar cells due to increased short circuit current(Isc).

• Korean Journal of Metals and Materials
• /
• v.46 no.12
• /
• pp.835-840
• /
• 2008

Texturing for crystalline silicon solar cells is one of the important techniques to increase conversion efficiency by effective photon trapping. Generally, incoming wafers or alkali etched wafers are used for texturing. From this conventional etching process, $7{\sim}10{\mu}m$-sized random pyramids are formed. In this study, acid etching for removal of saw damages was practiced before texturing. This improved the resulting surface morphology, which consisted of $2{\sim}4{\mu}m$-sized pyramids. Because these pyramids covered the surface much more extensively, we obtained reduction of optical losses on the surface. In order to compare with conventional texturing, FE-SEM is used for observing surface morphology and reflectance data is analyzed by UV-VIS spectrophotometer.

• New & Renewable Energy
• /
• v.9 no.2
• /
• pp.30-39
• /
• 2013

Multi-crystalline silicon solar cells is not exist a specific crystal direction different from single crystalline silicon solar cells. In functional materials, therefore, isotropic wet etching of mc-Si solar cell is easy the acid solution rather than the alkaline solution. The reflectance of wet texturing process is about 25% and the reflectance of RIE texturing process is achieved less than 10%. In addition, wet texturing has many disadvantages as well as reflectance. So wet texturing process has been replaced by a RIE texturing process. In order to apply BIPV, RIE and wet textured multi-crystalline silicon solar cell modules was manufactured by different kind of EVA sheet. Moreover, in case of BIPV, the short circuit current characteristics according to the angle of incidence is more important, because the installation of BIPV is fixed location. In this study, we has measured SEM image and I-V curve of RIE and wet textured silicon solar cell and PV module. Also we has analyzed quantum efficiency characteristics of RIE and wet textured silicon solar cell for PV modules depending on incidence angle.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.2
• /
• pp.86-92
• /
• 2013

$SF_6/O_2$ inductively coupled plasmas were employed to texture Si surface as a pretreatment for nanocrystalline diamond film growth. It was found that the $SF_6/O_2$ plasma texturing provided a very wide process window where normalized roughness values in the range of 2~16 could be obtained. Significantly improved nucleation densities of ${\sim}6.5{\times}10^{10}cm^{-2}$ compared to conventional mechanical abrasion were achieved after seeding for the textured Si substrate.