• KOREAN JOURNAL OF PACKAGING SCIENCE & TECHNOLOGY
• /
• v.5 no.2
• /
• pp.9-16
• /
• 1999

Edible films were prepared from proteins extracted from soybean curd residue by alkaline extraction and isoelectric precipitation. Effects of film forming solution pH and plasticizers on mechanical and barrier properties of edible films were studied. films were formed within pH $7{\sim}11$ with tensile strength (TS) of $2.9{\sim}3.3$ MPa. Films produced under pH 10 had the highest TS and Elongation (E) (3.3 MPa and 60.1%) but no significant difference was observed among water vapor permeabilities (WVP) of film. Glycerol, sorbitol and its mixture (1:1, w/w) were added as plasticizers. The concentration and mixing ratio of plasticizers also affected the TS, E and WVP of films. TS of films decreased from 15.0 MPa to 2.9 MPa as plasticizer concentration increased from 0.4 to 0.8 g plasticizer/g protein. At a plasticizer concentration, the highest TS was observed when sorbitol was used whereas the highest E was measured when mixture of glycerol and sorbitol was used as plasticizer WVP of films increased as the plasticizer concentration increased. Films plasticized with glycerol showed the highest WVP among the films with the same plasticizer concentrations. Edible films prepared from soybean curd residue protein showed very low oxygen permeabilities ($29.5{\sim}61.1aL{\cdot}m/m^2{\cdot}s{\cdot}Pa$) and oil resistance at all plasticizer concentration level tested.

• International Journal of Highway Engineering
• /
• v.8 no.2 s.28
• /
• pp.23-30
• /
• 2006

Emulsified Asphalt Mixture(EAM) is more environmentally-friendly and cost-effective than typical Hot Mix Asphalt (HMA) because EAM does not produce carcinogenic substances, e.g., naphtha, kerosene, during the both of manufacturing and roadway construction process. Also, it does not require heating the aggregates and asphalt binder. However, EAM has some disadvantages. Generally EAM has a less load bearing capacity and more moisture susceptibility than conventional HMA. The study evaluated a Fiber modified EAM (FEAM) to increase load bearing capacity and to decrease moisture susceptibility of EAM. Modified Marshall mix design was developed to find Optimum Emulsion Contents (OEC), Optimum Water Contents (OWC), and Optimum Fiber Contents (OFC). A series of test were performed on the fabricated specimen with OBC, OWC, and OFC. Tests include Marshall Stability, Indirect Tensile Strength, and Resilient modulus test. Comparison analyses were performed among EAM, Fiber modified EAM (FEAM), and typical HMA to verify the applicability of EAM and FEAM in the field. Test results indicated that both of EAM and FEAM have an enough capability to resist medium traffic volume based on the Marshall mix design criteria. Also the study found that fiber modification is effective to increase the load bearing capacity and moisture damage resistance of EAM.

• Journal of Korean Society of Steel Construction
• /
• v.26 no.4
• /
• pp.299-309
• /
• 2014

HSA800 is a new high strength steel (HSS) plate for building structures developed by POSCO and RIST in 2011. It has upper and lower bounds for yield ($F_y$) and tensile ($F_u$) strength as of 650-770MPa and 800-950MPa, respectively, with yield ratio ($F_y/F_u$) limit as of 0.85 which make steel quality more reliable and enhance the seismic resistance of structures. As made by TMCP, it has a good weldability without increasing carbon percentage. The objective of this study is to provide alternative design of mega-structural members of the Lotte World Tower (555m, 123 story), a first super-tall building in Korea, using HSS considering structural safety, constructability, and cost-effectiveness. Steel outrigger trusses, belt-trusses and steel exterior columns were selected and analyzed to evaluate the structural performance between original and alternative designs using HSS. The results show that HSS can be applied to the members which do not affect lateral stiffness of a building and, in this study, approximately 1100tons of steel were saved. It implies that HSS can save overall construction costs - manufacturing, delivery, and erection costs - by reducing mega structural member size. HSA800 was very first applied to the Lotte World Tower based on the results of this study.

• Applied Chemistry for Engineering
• /
• v.17 no.3
• /
• pp.267-273
• /
• 2006

We have prepared PP/Ba-ferrite composite fabrics by a melt-blown spinning method and investigated the relationship between the properties of PP/Ba-ferrite composite fabrics and melt-blown processing factors. A PP composite containing Ba-ferrite as a magnetic particulate filler was prepared in the form of pellet from PP resin and Ba-ferrite powder by melt compounding using a single extruder. Screw turning force (rpm), DCD (die-to-collector distance), and Ba-ferrite content were changed. We measured diameters of fiber, mechanical, thermal, and magnetic properties for the composited PP fabrics. The elongation was increased and a fiber diameter and tensile strength were decreased as the spinning distance increased or screw turning force decreased. The crystallinity was increased with increasing spinning distance according to XRD. It was assumed that the orientation of crystalline domain in the neat PP without ferrite was increased by drawing in mechanical direction, however, the orientation in the PP composite was decreased according to XRD analysis. We measured a magnetic property of PP nonwoven fabric containing Ba-ferrite powder. A coercive force, maximum magnetization, and residual magnetization are reduced with the spinning distance. According to the result of TGA measurement, the heat resistance was increased with the Ba-ferrite powder content and with decreasing the spinning distance.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.5
• /
• pp.55-63
• /
• 2018

Recently, the use of duplex stainless steel which with a two-phase microstructure (equal mixture of ferrite and austenite) has been increased in a variety of industrial fields due to higher strength leading to weight saving, greater corrosion resistance(particularly, stress corrosion cracking) and lower price. However, currently, stainless steels are not included in the structural materials of Korean Building Code and corresponding design standards are not specified. In this paper, experimental studies have been performed to investigate the structural behaviors of duplex stainless steel (STS329FLD) bolted connection with two bolts for providing the design data. Main variables are shear connection type (single shear and double shear) and end distance parallel to the direction of applied force. Fracture modes at the final step of test were classified into typical block shear fracture, tensile fracture and curling. Curling occurrence in single shear connection led to ultimate strength drop by up to 20%. Test strengths were compared with those by current design specifications such as AISC/AISI/KBC, EC3 and AIJ and proposed equations by existing studies. For specimens with no curling, Clement & Teh's equation considering the active shear plane provided a higher strength estimation accurancy and for specimens with curling, Kim & Lim's equation considering strength reduction by curling was also overly unconservative to predict the ultimate strength of curled connections.

• Applied Chemistry for Engineering
• /
• v.7 no.3
• /
• pp.597-604
• /
• 1996

Resin-type neutron shielding materials, KNS-115A, 115B and 115C have been fabricated to be used for spent fuel shipping cask. The base material is epoxy resin, and polypropylene, aluminium hydroxide and boron carbide are added. These shielding materials offer good fluidity at processing, which makes it possible to apply this resin shield to complicated geometric shapes such as shipping cask. Several measurements were made for the shielding materials to evaluate the shielding property, combustion characteristics, fire resistance, thermal and mechanical properties. The neutron shielding ability of the shielding materials is estimated to be better than that of foreign's shielding material, NS-4-FR, due to higher hydrogen atomic density. Other properties of the shielding materials are as follows: Onset temperatures; $267{\sim}270^{\circ}C$, thermal conductivities; $0.62{\sim}0.72W/m{\cdot}K$, combustion characteristics; <$800^{\circ}C$, ATB(average time of burning); <5sec, AEB(average extent of burning) ; <5mm, tensile strengths; $2.3{\sim}3.0kg/mm^2$, compressive strengths; $5.3{\sim}13.3kg/mm^2$, flexural strengths; $4.4{\sim}5.4kg/mm^2$.

• Journal of Adhesion and Interface
• /
• v.10 no.4
• /
• pp.155-161
• /
• 2009

The most upcoming technical issue of automotive coating is the compact coating process. Pre-primed coating is the outstanding technology eliminating electro-deposition and primer coating process. The main properties of pre-primed coating for automotive are flexibility, corrosion resistance, and weldability. Therefore, we synthesized the conventional polyester, elastomeric polyester and polyvinylidene fluoride resins and evaluated their properties to use as weldable pre-primed automotive coatings. As the results of flexibility and curing behavior, the elastomeric polyester coating was most appropriate to use for the pre-primed automotive coatings.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.34 no.6
• /
• pp.1677-1685
• /
• 2014

Short discrete fibers compounded with concrete can enhance the tensile resistance and ductility of concrete. Recently, the effectiveness of the reinforcement has increased according to the increasing length of steel fiber. However, the lengthening of steel fiber requires reducing the ratio of the fiber content to remain the workability and quality of concrete. Thus, the present study evaluated the flexural performance of fiber reinforced concrete with less than l.0% fiber volume ratios of steel fiber, 30mm and 60mm long, and polypropylene fiber, being evaluated as a good reinforcing material with chemical stability, long-term durability, and cost effectiveness. Concrete with more than 0.25% steel and 0.5% polypropylene fibers improved the brittle failure of concrete after reaching cracking strength. Concrete reinforced with polypropylene exhibited deflection-softening behavior, but that with more than 0.5% polypropylene delayed stress reduction and recovered flexural strength by 60 to 80% after cracking strength. In conclusion, concrete reinforced with more than 0.75% polypropylene could improve structural flexural performance. In particular, energy absorption capacity of reinforced concrete with 1.0% polypropylene fiber was similar to that with 0.5% and 0.7% steel fibers.

• Journal of the Korea Concrete Institute
• /
• v.17 no.6 s.90
• /
• pp.923-930
• /
• 2005

This paper was to evaluate the high strength lightweight self-compacting concrete(HLSCC) manufactured by Nan-Su, which main factor, Packing Factor(PF) for mixing design, has been modified and improved. We have examined HLSCC performance at its fresh condition as well as its mechanical properties at the hardened condition. The evaluation of HLSCC fluidity has been conducted per the standard of second class rating of JSCE, by three categories of flowability(slump-flow), segregation resistance ability(time required to reach 500mm of slump-flow and time required to flow through V-funnel) and filling ability(U-box test) of fresh concrete. The compressive strength of HLSSC at 28 days has come out to more than 30MPa in all mixes. The relationship between the compressive strength-splitting tensile strength and compressive strength-modulus of elasticity of HLSSC were similar those of typical lightweight concrete. Compressive strength and dry density of HLSCC at 28 days from the multiple regression analysis resulted as $f_c=-0.16LC-0.008LS+50.05(R=0.83)\;and\;f_d=-3.598LC-2.244LS+2,310(R=0.99)$, respectively.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.5
• /
• pp.449-457
• /
• 2020

Due to the improvement of living standards and avoidance of the 3D industry, it is difficult to find young and competent domestic workers at construction sites, and most foreign workers are contributing to the replacement, but the quality is still deteriorating due to lack of skilled workers and aging. Precast method is a method that make members in factory and assembles them on site, which can be expected to improve labor force and quality. This study is intended to provide basic data for the development of hang-type PC beams that can be applied to the determination of the field application of developed PC beams. The U-type connecting material is installed on both ends of the hang-up PC beam, and the role of the U-type connecting material is very important because it is a simple construction method through the U-type connecting material. In addition, the performance of the U-type connecting material will determine the performance of the hang-type PC beam as the final destruction occurs in the hang-type PC beam. The material properties of U-type connecting material were identified through structural experiments, and the end test corresponding to the partial experiment was conducted based on the material test results identified. Finally, the final design value of PC beams was proposed through structural experiments for application to the site.