• 폴리머
• /
• 제26권6호
• /
• pp.745-751
• /
• 2002

본 연구에서는 시료의 형광문제를 제거한 FT-Raman spectrometer을 이용하여 연신된 syndiotactic polypropylene의 비등방적 Raman 산란 특성을 측정하였다. 관찰된 Raman 피크를 해석하여 해당 symmetry species 분류를 목적으로, 입사 및 산란 복사선의 편광방향이 서로 다른 4 가지 편광실험을 수행하여 스펙트럼을 얻었다. 이 편광 Raman 실험 결과를 편광 infrared 실험에 의한 dichroism 결과 및 진동운동의 이론적 계산인 normal coordinate analysis 결과와 비교 분석하였다.

• 접착 및 계면
• /
• 제6권2호
• /
• pp.1-5
• /
• 2005

Single crystals of metallocene-catalyzed isotactic polypropylene (iPP) and/or syndiotactic PP (sPP) were prepared and preliminarily characterized. The crystallization was performed utilizing 0.1 % by weight concentrations of each PP in o-xylene in the range of temperature of $40{\sim}90^{\circ}C$. Following the XRD patterns, samples were ${\alpha}$-iPP and antichiral Cell III of sPP. The XRD pattern of iPP shows three ${\alpha}$-form peaks due to the (110), (040), (130) planes at $2{\theta}=14.2^{\circ}$, $17^{\circ}$, $18.8^{\circ}$, respectively. The XRD pattern of sPP is characterized by the presence of the (020) reflection at $16^{\circ}$. The melting point ($123^{\circ}C$ and $148^{\circ}C$, respectively) of the metallocene catalyzed iPP and sPP were generally lower than that of conventional PP ($160{\sim}170^{\circ}C$) due to the misinsertion of the monomer. When metallocene-catalyzed iPP samples were crystallized isothermally from solution grown at a lower temperature, lozenge shape single crystals were observed by transmission electron microscopy (TEM).

• 폴리머
• /
• 제27권6호
• /
• pp.509-520
• /
• 2003

입체규칙성이 다른 폴리프로필렌 (PP)의 결정화 거동을 비교하였다. 결정화 조건은 신디오택틱 폴리프로필렌 (sPP)과 아이소택틱 폴리프로필렌 (iPP)의 단위 결정 격자, 라멜라 구조, 구정의 성장에 영향을 주었다. 냉각속도가 증가할수록 결정 구조의 안정성이 감소하였으며, 냉각속도에 따른 구조적 변화는 iPP 가 sPP보다 크게 나타났다. sPP는 1 $^{\circ}C$/min 이하의 속도로 서냉될 때 body centered cell H의 fully antichiral packing 구조를 형성하였고 sPP가 primitive cellII구조를 형성할 때, 결정 격자와 라멜라 구조는 열이력의 영향을 작게 받은 것으로 확인되었다. 최대 결정화 온도에서 결정화 속도는 iPP가 sPP보다 빠르게 나타났다.

• Macromolecular Research
• /
• 제14권3호
• /
• pp.306-311
• /
• 2006

New unsymmetrical ($\alpha$-Diimine)nickel(II) catalysts having different pendent groups at the ortho positions on aromatic rings were synthesized and subjected to propylene polymerizations with MAO (methylaluminoxane). Structural analyses of the resulting polypropylenes by $^1H\;and\;^{13}C\;NMR$ showed that the ortho substituents on aromatic rings of ($\alpha$-diimine)nickel(II) catalyst affected significantly the polypropylene microstructure. While $C_s$ symmetric catalyst afforded a syndiotactic polypropylene (rr triad content=66%) due to the syndiospecific chain end control, $C_1$ symmetric catalysts produced much less stereoregular polypropylenes (rr triads content <50%), presumably because of collision of the isospecific site control with the syndiospecific chain end control.

• 폴리머
• /
• 제27권6호
• /
• pp.521-527
• /
• 2003

신디오택틱 폴리프로필렌 (sPP)과 아이소택틱 폴리프로필렌 (iPP)은 용융과정에서 결정의 재배열이 나타나며 이와 같은 재결정 현상을 해석하기 위하여 결정화도와 결정구조의 변화, 동역학적 물성을 고찰하였고 DSC, FT-IR, SAXS, DMA를 이용하였다. 본 연구에서 실험된 조건에서는 sPP의 재결정화 현상을 확인할 수 없었으며, iPP는 용융으로부터 냉각되는 속도가 빠르게 될 수록 재가열시 재결정화 현상이 두드러졌다. iPP의 재결정화가 진행되는 동안 tan $\delta$가 0.119에서 0.101로 감소하여 탄성율이 증가한 결과를 보이나 결정화도는 거의 일정하게 유지되었다. 더욱이 재결정 현상이 진행되는 동안 SAXS 산란피크의 반가폭이 약 30% 감소하여 라멜라의 질서가 증가하는 거동을 보였다.

• 폴리머
• /
• 제38권3호
• /
• pp.333-337
• /
• 2014

PVC 재질로 만들어진 기존의 수액백과 튜브는 가소제인 DEHP(diethylhexyl phthalate)를 함유하고 있어 정맥 주사 시에 가소제의 용출과 약물 흡착이라는 심각한 취약점을 내재하고 있다. 본 연구에서는 폴리올레핀 재질로 만들어진 non-PVC 수액튜브(가소제 미포함)를 개발하고, 이들 튜브 내면에서의 약물 흡착 거동을 기존의 PVC 및 PU 재질의 수액 튜브와 비교 검토하므로써, 수액 주사 시 약물 흡착으로 인한 약효 감소 효과를 최소화 가능한 방안을 도출하고자 한다. 4가지의 non-PVC 수액튜브는 폴리에틸렌(PE), 폴리프로필렌(PP), syndiotactic 1,2-폴리부타 다이엔(PB)과 스타이렌-에틸렌(SE)의 공중합 탄성체를 사용하여 압출하여 제조하였으며, 이들은 기존의 PVC 수액튜브의 기계적 특성과 동등한 물성을 나타내었다. 아울러 제조된 폴리올레핀 재질의 4가지 수액튜브들은 기존의 PVC 및 PU 재질의 수액튜브 대비 우수한 약물흡착 방지 효과를 나타내었다. 따라서 이들은 약물흡착 방지용 수액튜브뿐 아니라 DEHP의 용출 위험이 배제된 안전한 수액튜브로서 임상 적용 가능할 것이다.