• Journal of Periodontal and Implant Science
• /
• v.37 no.3
• /
• pp.585-597
• /
• 2007

The present study was performed to evaluate the effect of Tetracycline-HCI and Saline on the change of implant surface microstructure and surface roughness according to application time. Implants with resorbable blasting media surface were utilized. Before test all 13 implants were measured surface roughness. Among them, 6 implants were rubbed with 50mg/ml Tetracycline-HCl solution and other 6 implants with saline for $\frac{1}{2}$min., 1min., $1\frac{1}{2}$min., 2min., $2\frac{1}{2}$min and 3min. Then, specimens were processed for scanning electron microscopic observation and surface roughness after test. The results of this study were as follows. 1. Control group showed a few irregular, rough, uneven surface with crater-like depression. 2. The test group with Tetracycline-HCl conditioning showed an altered surface when Tetracycline-HCl was applied for 30secs, and showed a various surface alteration as application times go on. 3. The test group with Saline conditioning showed no significant surface differences and surface roughness. 4. The significant increase of Ra value was showed when Tetracycline-HCl was applied for 30secs. In conclusion, the 50mg/ml Tetracycline-HCl must not be applied for the RBM surface implant for surface treatment.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.40-44
• /
• 2008

The interfacial adhesion energy between resist and a substrate is very important due to resist pull-off problems during separation of mold from a substrate in nanoimprint process. And effect of substrate surface roughness on interfacial adhesion energy is very important. In this paper, we have treated glass wafer surface using $CF_4$ gas for increase surface roughness and it has tested interfacial adhesion properties of UV resin/glass substrate interfaces by 4 point bending test. The interfacial adhesion energies by bare, 30, 60 and 90 sec surface treatments are 0.62, 1.4, 1.36 and 2 $J/m^2$, respectively. The test results showed quantitative comparisons of interfacial fracture energy (G) effect of glass wafer surface roughness.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.6
• /
• pp.216-226
• /
• 2005

Pb-Free Technology was born with environmental problems of electronic component, Being connected by big and small project of every country. Also, in each country environment is connected and various standards of IEC, ISO, MIL, JIS, KS, JEDEC, EIAJ etc. All products can divide at solder part and finishing part These can tested each and synthetically divide. This research is reliability evaluation for three kind of ph-free SnCu solder plating solution and it's deposit. First, executed analysis about Pure Sn, SnCu solutions and plating surface by way similar to other plating solution analysis. Next, executed reliability about test method and equipment for reliable analyzer system construction. Next, data comparison and estimation, main estimation test method and item's choice. In this paper the systematic surface analysis and reliability for plating solutions and it's deposit in metal surface finishing processes could be shown.

• Tribology and Lubricants
• /
• v.38 no.3
• /
• pp.115-119
• /
• 2022

This paper selected three kinds of grease with the same type but different consistency for the experiment. The purpose of the experiment is tested the effect of different consistency of grease on the wear of the gear surface. Different torque test groups were selected in the test, and the lubrication effect of different greases was tested in the test groups with the same torque. After each set of tests, the wear of the gear surfaces was observed and recorded. The data recorded in the experiment included the area of the wear area on the gear surface, the type of wear and the volume of wear. After the test, the gear surface roughness was measured. By calculating the wear volume, the effects of different concentrations of grease on the gear surface wear were compared. The experimental results show that under different stress conditions, the consistency of the grease has a great influence on the lubricating effect of the gear surface and the gear wear. Under the condition with low speed and high torque, different grease consistency affect the gear surface wear, the high consistency grease can reduce the wear of the gear surface, so that the gear can get better lubrication effect during the work.

• The Journal of Korean Society for Neurotherapy
• /
• v.22 no.3
• /
• pp.19-23
• /
• 2018

Purpose The purpose of this study was to investigate the change of balance ability by performing closed chain exercise on stable support surface and unstable support surface in twenties. Methods This study randomly selected 15 students in the closed chain exercise group on the stable support side and 15 on the closed chain exercise group on the unstable support side. Balance ability was measured before and after the start of exercise and static balance was measured by OLT(One Leg Standing Test) and FRT (Functional Reach Test). Result The changes of the function reach test of the closed chain movement according to the ground type were significant in the unstable and stable support surfaces and the change of function reach test after the intervention in the two groups was significantly improved compared with the closed chain movement respectively. The one leg standing test changes of the closed chain movement according to the ground type showed significant results on the unstable and stable support surfaces, but there was no significant difference in the one leg standing test changes after intervention between the two groups. Conclusion The effect of closed chain training on ground type is unstable. The change of function reach test and one leg standing test of the closed chain exercise group on the stable support surface resulted in significant changes after exercise, but there was a significant difference in the balance ability of function reach test change after intervention between the groups.

• Journal of the Korean institute of surface engineering
• /
• v.31 no.6
• /
• pp.307-316
• /
• 1998

The effects of surface roughness on chromate conversion coating and the corrosion behavior of galvanized steel sheets were investigated. Surface roughness was differently given to the galvanized steel sheets tested and these were then chromated. Accelerated corrosion test was conducted under the condition of $30^{\circ}C$, 90%RH with flowing 200ppm $SO_2$ gas. The galvanized steels were also exposed to urban environment for 5 weeks. The corrosion rates were measured by weight gain method. The distribution of chromate film and corrosion product on the coating were examined which SEM/EDS. The chromate film formed preferentially at the convex sites rather than at the concave sites on the surface. The corrosion products were found at the concave sites where the chromate film formed rarely. The corrosion product on the coating were found at the concave sites where the chromate film formed rarely. The corrosion rates increased slightly with the surface roughness in accelerated corrosion test but significantly in field test.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.25 no.1
• /
• pp.61-70
• /
• 2001

As important factors determining human sensorial comfort, liquid moisture management and surface properties of heat resistant workwear materials were examined. To figure out liquid moisture management properties of the test materials, absorption capacity, rate of absorption, and evaporation properties were assessed. A modified GATS(Gravimetric Absorbency Testing System) was used to measure the liquid moisture accumulation associated with the wicking of liquid moisture from sweating skin. The GATS procedure measures demand wettability of materials to take up liquid in a direction perpendicular to the fabric surface and it was modified to incorporate a special test cell and cover to assess absorption behavior in the presence of evaporation. Fabric stiffness, smoothness, number and the length of surface fibers, and an estimate of the contact area between the skin and fabric surface were measured to characterize the mechanical and surface properties of the test materials. Also an estimate of the force with which a fabric clings to moist skin was made using as wet-cling index.

• Transactions of Materials Processing
• /
• v.17 no.6
• /
• pp.401-406
• /
• 2008

The frictional behavior of stamping process is a function of interface parameters such as sheet and tool material, lubricant, surface roughness, contact pressure, sliding speed etc. Among these parameters the thing that can be controlled by a steel maker is the surface roughness of sheet. In this study, effects of surface roughness on the frictional behavior of steel sheet for automotive were investigated to find out the way to improve the frictional characteristics of steel sheet. The cold rolled steel sheets with various surface roughnesses were prepared for the test. The flat type friction test was conducted with different lubricant conditions. The surface roughness effect on frictional behavior depends on the viscosity of lubricant. The frictional characteristic of steel sheet was influenced by the amplitude of roughness as well as the shape of that.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.29 no.5
• /
• pp.415-420
• /
• 2009

This paper reports the results of a case study for the evaluation of surface damage by using acoustic nonlinearity of surface wave. In this study, the experimental system was constructed to measure the acoustic nonlinear parameter of surface wave in an Aluminum 6061 T6 specimen of which surface was damaged by the three point bending fatigue test, and magnitudes of nonlinear parameter measured before and after the fatigue test were compared. Especially, since the surface fatigue damage by the three point bending is concentrated at the central position of loading, the change in the nonlinear parameter around this position was monitored. Experimental results showed that the measured nonlinear parameter at the outside of this position after the fatigue test was almost same as the initial value before the fatigue test, since the fatigue damage at this position was little. However, clear increase in the nonlinear parameter was noticed after the fatigue test at the central position of specimen where the surface fatigue damage is expected to be concentrated.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.3
• /
• pp.310-320
• /
• 2007

Statement of the problem. The fracture of acrylic resin dentures remains an unsolved problem. Therefore, many investigations have been performed and various approaches to strengthening acrylic resin, for example, the reinforcement of heat-cured acrylic resin using glass fibers, have been suggested over the years. But problems such as poor workability, rough surface, poor adhesion of glass fiber resin complex are not solved yet. Purpose. The aim of the present study was to investigate the effect of short glass fibers on the transverse strength of heat-polymerized denture base acrylic resin and roughness of resin complex after abrasion test. Material and methods. To avoid fiber bunching and achieve even fiber distribution, glass fiber bundles were mixed with acrylic resin powder in conventional mixer with a non-cutting blade, to produce the glass fiber($10{\mu}m$ diameter, 3mm length, silane treated) resin composite. Glass fibers were incorporated at 0%, 3%, 6% and 9% by weight. Transverse strength were measured. After abrasion test, surface roughness was evaluated and scanning electron microscope view was taken for clinical application. Results. 1. 6% and 9% incorporation of 3mm glass fibers in the acrylic resin enhanced the transverse strength of the test specimens(p<0.05). 2. Before abrasion test, incorporation of 0%, 3%, 9% glass fiber in the resin showed no dirrerence in roughness statisticaly(p>0.05). 3. After abrasion test, incorporation of 0%, 3%, 6% glass fiber in the resin showed same surface roughness value statistically(p>0.05). 4. In SEM, surface roughness increased as the percentage of the fibers increased. 5. In the areas where glass fiber bunchings are formated, a remarkably high roughness was noticed. Conclusion. 6% and 9% addition of silane-treated short glass fibers into denture base acrylic resin increased transverse strength significantly. Before and after abrasion test, incorporation of 0%, 3%, 6% glass fiber in the resin showed same surface roughness value statistically.