• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.236-236
• /
• 2011

Silicon oxynitride (SiON) was deposited for gas barrier film on polyethylene terephthalate (PET) using octamethylycyclodisiloxane (Si4O4C8H24, OMCTS) precursor by plasma enhanced chemical vapor deposition (PECVD) at low temperature. The ion flux and substrate temperature were measured by oscilloscope and thermometer. The chemical bonding structure and barrier property of films were characterized by Fourier transform infrared (FT-IR) spectroscopy and the water vapor transmission rate (WVTR), respectively. The deposition rate of films increases with RF bias and nitrogen dilution due to increase of dissociated precursor and nitrogen ion incident to the substrate. In addition, we confirmed that the increase of nitrogen dilution and RF bias reduced WVTR of films. Because, on the basis of FT-IR analysis, the increase of the nitrogen gas flow rate and RF bias caused the increase of the C=N stretching vibration resulting in the decrease of macro and nano defects.

• Journal of the Korean Ceramic Society
• /
• v.49 no.4
• /
• pp.301-307
• /
• 2012

SiAlON glasses are silicates or alumino-silicates, containing Mg, Ca, Y or rare earth (RE) ions as modifiers, in which nitrogen atoms substitute for oxygen atoms in the glass network. These glasses are found as intergranular films and at triple point junctions in silicon nitride ceramics and these grain boundary phases affect their fracture behaviour. This paper provides an overview of the preparation of M-SiAlON glasses and outlines the effects of composition on properties. As nitrogen substitutes for oxygen in SiAlON glasses, increases are observed in glass transition temperatures, viscosities, elastic moduli and microhardness. These property changes are compared with known effects of grain boundary glass chemistry in silicon nitride ceramics. Oxide sintering additives provide conditions for liquid phase sintering, reacting with surface silica on the $Si_3N_4$ particles and some of the nitride to form SiAlON liquid phases which on cooling remain as intergranular glasses. Thermal expansion mismatch between the grain boundary glass and the silicon nitride causes residual stresses in the material which can be determined from bulk SiAlON glass properties. The tensile residual stresses in the glass phase increase with increasing Y:Al ratio and this correlates with increasing fracture toughness as a result of easier debonding at the glass/${\beta}-Si_3N_4$ interface.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.2
• /
• pp.93-100
• /
• 2000

Effects of Ti content and Ti underlayer on the pitting behavior of TiN coated AISI 304 stainless steel have been studied. The stainless steel containing 0.1~1.0wt% Ti were melted with a vacuum melting furnace and heat treated at $1050^{\circ}C$ for 1hr for solutionization. The specimen were coated with l$\mu\textrm{m}$ and 2$\mu\textrm{m}$ thickness of Ti and TiN by E-beam PVD method. The microstructure and phase analysis were conducted by using XRD, XPS and SEM with these specimen. XRD patterns shows that in TiN single-layer only the TiN (111) Peak is major and the other peaks are very weak, but in Ti/TiN double-layer TiN (220) and TiN (200) peaks are developed. It is observed that the surface of coating is covered with titanium oxide (TiO$_2$) and titanium oxynitride ($TiO_2$N) as well as TiN. Corrosion potential on the anodic polarization curve measured in HCl solution increase in proportion to the Ti content of substrate and by a presence of the Ti underlayer, whereas corrosion and passivation current densities are not affected by either of them. The number and size of pits decrease with increasing Ti content and a presence of the coated Ti film as underlayer in the TiN coated stainless steel.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.132-132
• /
• 2010

In the nano-scale Si processing, patterning processes based on multilevel resist structures becoming more critical due to continuously decreasing resist thickness and feature size. In particular, highly selective etching of the first dielectric layer with resist patterns are great importance. In this work, process window for the infinitely high etch selectivity of silicon oxynitride (SiON) layers and silicon nitride (Si3N4) with EUV resist was investigated during etching of SiON/EUV resist and Si3N4/EUV resist in a CH2F2/N2/Ar dual-frequency superimposed capacitive coupled plasma (DFS-CCP) by varying the process parameters, such as the CH2F2 and N2 flow ratio and low-frequency source power (PLF). It was found that the CH2F2/N2 flow ratio was found to play a critical role in determining the process window for ultra high etch selectivity, due to the differences in change of the degree of polymerization on SiON, Si3N4, and EUV resist. Control of N2 flow ratio gave the possibility of obtaining the ultra high etch selectivity by keeping the steady-state hydrofluorocarbon layer thickness thin on the SiON and Si3N4 surface due to effective formation of HCN etch by-products and, in turn, in continuous SiON and Si3N4 etching, while the hydrofluorocarbon layer is deposited on the EUV resist surface.

• Journal of the Korean institute of surface engineering
• /
• v.30 no.4
• /
• pp.255-261
• /
• 1997

Thin film batteries can be used as a micro power source for electronic in which minute power is needed. In this study, lithium phosphorous oxynitride(LIPON) thin films were deposited as an eletrolyte for lithium ion batteries using RF magentron sputtering of lithium phosphate in N2. Ti was also added into the LIPON films as a second network former to enhance the ioinc conductivity of the films. The optimum conditions for LIPON film deposition were sought and the electrolyte with the conductivity of $2.5 \times 10^{-6}$S/cm was obtained at the condition of RF power 4.4 W/$\textrm{cm}^2$, process pressure 10 mtorr and pure nitrogen ambience. Furthermore, the conductivity of LIPON films was increased from $2.5 \times 10^{-6}$S/cm to $8.6 \times 10^{-6}$S/cm by the doping of 2.4at.% Ti. It was also found that by adding Ti to LIPON films, Li content was increased and nitrogen content that reported having the cross-linking effect on LIPON films was also increased as confirmed XPS.

• Journal of the Korean Electrochemical Society
• /
• v.11 no.2
• /
• pp.100-104
• /
• 2008

Titanium sheet metal substrates used in thin film batteries were wet etched and their surface area was increased in order to increase the discharge capacity and power density of the batteries. To obtain a homogeneous etching pattern, we used a conventional photolithographic process. Homogeneous hemisphere-shaped wells with a diameter of approximately $40\;{\mu}m$ were formed on the surface of the Ti substrate using a photo-etching process with a $20\;{\mu}m{\times}20\;{\mu}m$ square patterned photo mask. All-solid-state thin film cells composed of a Li/Lithium phosphorous oxynitride (Lipon)/$LiCoO_2$ system were fabricated onto the wet etched substrate using a physical vapor deposition method and their performances were compared with those of the cells on a bare substrate. It was found that the discharge capacity of the cells fabricated on wet etched Ti substrate increased by ca. 25% compared to that of the cell fabricated on bare one. High discharge rate was also able to be obtained through the reduction in the internal resistance. However, the cells fabricated on the wet etched substrate exhibited a higher degradation rate with charge-discharge cycling due to the nonuniform step coverage of the thin films, while the cells on the bare substrate demonstrated a good cycling performance.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 2000.06a
• /
• pp.1-33
• /
• 2000

Silicon carbide ceramics with sintering additives from the system AlN-Y$_2$O$_3$ can be gas-pressure sintered to theoretical density. While commonly a combination of sesquioxides is used such as Al$_2$O$_3$-Y$_2$O$_3$, the oxynitrid additives offer the advantage that only a nitrogen atmosphere is require instead of a powder. By starting form a mixture of ${\beta}$-SiC and ${\alpha}$-SiC, and by performing dedicated heat treatments after densification, anisotropic grain growth is obtained which leads to a platelet microstructure showing enhance fracture toughness. In the present work, recent improvement of the mechanical behaviour of these materials at ambient and high temperatures is reported. By means of a surface oxidation treatment in air it is possible to obtain four-point bending strengths in excess of 1 GPa, and the strength retention at high temperatures is significantly improved.

• Journal of Mechanical Science and Technology
• /
• v.18 no.3
• /
• pp.388-394
• /
• 2004

Composites of Si$_3$N$_4$-SiC containing up to 30 wt% of dispersed SiC particles were fabricated via hot-pressing with an oxynitride glass. To determine the effect of sintering time and SiC content on the mechanical properties and the cutting performance, the composites with fixed 8hr-sintering time and 20 wt% SiC content were fabricated and tested. Fracture toughness of the composites increased with increasing sintering time, while the hardness increased as the SiC content increased up to 20 wt%. The hardness of the composites was relatively independent of the grain size and the sintered density. For machining heat-treated AISI4140, the insert with 20 wt% SiC sintered for 8hr showed the longest tool life while the insert with 20 wt% SiC sintered for 12hr showed the longest tool life for machining gray cast iron. An effort was made to relate the mechanical properties, such as hardness, fracture toughness and wear resistance coefficient with the tool life. However, no apparent relationship was found between them. It may be stated that tool life is affected by not only the mechanical properties but also other properties such as surface roughness, density, grian size and the number of the inherent defects in the inserts.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.151-151
• /
• 2010

In this paper, the electrically properties of nonvolatile memory (NVM) using multi-stacks gate insulators of oxide-nitride-oxynitride (ONOn) and active layer of the low temperature polycrystalline silicon (LTPS) were investigated. From hydrogenated amorphous silicon (a-Si:H), the LTPS thin films with high crystalline fraction of 96% and low surface's roughness of 1.28 nm were fabricated by the metal induced crystallization (MIC) with annealing conditions of $650^{\circ}C$ for 5 hours on glass substrates. The LTPS thin film transistor (TFT) or the NVM obtains a field effect mobility of ($\mu_{FE}$) $10\;cm^2/V{\cdot}s$, threshold voltage ($V_{TH}$) of -3.5V. The results demonstrated that the NVM has a memory window of 1.6 V with a programming and erasing (P/E) voltage of -14 V and 14 V in 1 ms. Moreover, retention properties of the memory was determined exceed 80% after 10 years. Therefore, the LTPS fabricated by the MIC became a potential material for NVM application which employed for the system integration of the panel display.