• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.3
• /
• pp.511-518
• /
• 1997

The technique of fretting fatigue test was developed and fretting fatigue tests of A12024-T4 were conducted under several conditions. The newly developed calibration methods for measuring surface contact tractions showed good linearity and repeatability. The plate type specimen to which tow bridge type pads were attached and vision system was used to observe the crack behaviour. The oblieque cracks appeared in the early stage of crack growth and they became mode I cracks as they grow about 1 mm. The mode I transition points were found to be longer when surface tractions are higher or bulk stress is lower. Before the crack becomes mode I crack, 'well point' where crack grow about rate is minimum, was detected under every experimental condition. The crack behaviour was found to be affected by surface tractions, contact area, bulk stress. It was also found that partial slip and stick condition is most detrimental and the crack starts from the boundary of stick and slip. For gross slip crack started at the outside edge of pad. After crack mode transition, fretting fatigue cracks showed almost same behaviour of plain mode I fatigue cracks. Equivalent stress intensity factor was used to analyze the behaviour of fretting fatigue cracks and it was found that stress intensity factors can be applied to fretting fatigue cracks.

• Journal of Ocean Engineering and Technology
• /
• v.12 no.1
• /
• pp.39-49
• /
• 1998

In this work, fatigue tests by axial loading were carried out to investigate the effect of stress ratio on the growth behaviors of surface fatigue crack for SM45C steel and Al 2024-T4 alloy. The growth behaviors of surface crack have been monitored during fatigue process by measuring system attached CCTV and monitor. When the growth rates of surface crack were investigate by the concept of LEFM based on Newman-Raju's .DELTA.K, the dependence of stress ratio appears both SM45C steel and Al 2024-T4 alloy. Therefore, modified stress intensity factor range, .DELTA.K' [=(1+R)/sup n/.DELTA.K] are intorduced to eliminate the dependence of stress ratio. Using .DELTA.K', it is found that the dependence of stress ratio disappears both SM45C steel and Al 2024-T4 alloy.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.22 no.1
• /
• pp.160-169
• /
• 1998

The purpose of this study for the prediction of fatigue crack propagation behavior, Stress Intensity Factor(F) of round bar with 3-Dimensional half circular, semi-elliptical icro surface crack under rotary bending stress for the variable aspect, size, rotation angle was analyzed by Boundary Element Method (BEM). It is predicted that behavior of crack growth is half circular or circular crack (b/a.geq.1) and propagate to b/a.leq.0.85.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.10
• /
• pp.2495-2500
• /
• 1994

A method of prediction for the fatigue life of surface crack, that is, initial cracks grow and penetrate through the thickness, was presented in the previous study of the author. Effects of parameters such as the initial crack length, material factors, etc., for the life were discussed. In this paper, the probabilistic distribution of the life is calculated. Effects of the distribution of parameters for the distribution of life were also discussed.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.15 no.6
• /
• pp.1990-2001
• /
• 1991

The fatigue life and crack penetration behavior of high strength steel have been studied in detail both experimentally and analytically. The fatigue crack shape of a smooth specimen is almost semicircular, while a specimen with stress concentration becomes semielliptical according to stress concentration shape. The aspect ratio of smooth specimens calculated using the Newman-Raju's formular is smaller than the value obtained from the experiment. On the other hand, the aspect ratio of the stress concentration specimen shows a good agreement with experimental results. It is found that the crack growth behavior on the back surface after the penetration is unique and can be divided into three stages ; rapid growth region, constant growth region and acceleration growth region. By using the K value suggested in this study, the particular crack growth behavior and crack shape can be estimated quantitatively.

• Journal of Mechanical Science and Technology
• /
• v.16 no.1
• /
• pp.24-31
• /
• 2002

The leak-before-break (LBB) behaviors of a structural component under high and low fatigue loads are an important problem in nuclear power plants, liquid nitrogen gas tankers and chemical plants. This paper is an experimental study to evaluate the crack opening behavior after penetration for plate and pipe specimens. Crack opening displacement after penetration under low fatigue load could be satisfactorily determined at the center of the plate thickness regardless of the specimen size. In the case of high fatigue load, it is shown that the crack opening displacement at the center of a penetrated crack carl be derived using the gross stress, $\sigma$/sug G/, and the front surface crack length, a$\_$s/, together with the back surface crack length, a$\_$b/.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.2 no.4
• /
• pp.67-72
• /
• 2003

In this study, to investigate the effects of 2-step shot peening at the surface of spring steel, crack growth tests are conducted on spring steel and shot peened specimens. And then the residual stresses and fractographs are examined. The crack growth equation that can describe the whole crack growth behavior is used to evaluate the experiment results. The results show that fatigue crack glows slowly in the shot peened specimen than in the unpeened. And in the case of the 2-step shot peened specimen the initial stress intensity factor range and the fracture toughness is higher than the unpeened specimen due to the compressive residual stress. Fractographs show that the compressive residual stress of the surface suppress the fatigue crack opening and consequently slow crack growth rates.

• KSTLE International Journal
• /
• v.1 no.1
• /
• pp.8-11
• /
• 2000

A surface crack in a semi-infinite body under Hertzian contact was considered. The simplified method used to estimate stress intensity factor K for specimen was extended to the model which is chosen in this paper. Very satisfactory results are obtained comparing with those known and it is proved that the method is more convenient than other methods. The results of the analysis show that due to the presence of $K_I$ for unlubricated condition, mode I fracture is active in the field below the surface and the maximum $K_{I}$ is obtained when the trailing edge of Hertzian contact reaches a position over the crack. The magnitudes of stress intensity factors $K_I$ and $K_Il$ increase with increasing friction forces. For a surface crack perpendicular to the contact surface, the stress intensity factor $K_I$ reaches its maximum value at a depth very close to the surface. Driving forve fer crack initiation and propagation is $K_I$ for unlubricated condition and $K_Il$ for both fluid and boundary lubricated condition.n.

• Journal of Welding and Joining
• /
• v.22 no.4
• /
• pp.73-81
• /
• 2004

Failure mechanisms of welded joints under fatigue loads are interpreted that multiple collinear surface cracks initiating randomly along the weld toes propagate under the mutual interaction and coalescence of adjacent two cracks. To estimate fatigue crack propagation life for three types of the representative welded joints, i.e. non-load carrying cruciform, cover plate and longitudinal stiffener joint, the stress intensity factors at the front of the surface cracks have to be calculated, which are influenced strongly by the geometry of attachments, weld toes and the crack shapes. For the effective calculation of the stress intensity factors the Mk-factor was introduced which can be derived by a parametric study performed by FEM considering influence of the geometrical effects. The fatigue life of the cruciform joint was estimated by using the Mk-factors and the method considering the propagation mechanisms of the multiple surface cracks. Analysis results for the fatigue life had a good agreement with that of experiment.

• Journal of Ocean Engineering and Technology
• /
• v.14 no.1
• /
• pp.29-36
• /
• 2000

Surface micro-crack grows along intergranular or transgranular region of crystal grains. But if it meets the barrier such as sessile dislocation and precipitates it loses straightness and deflects. Investigators had many difficulties in estimating fatigue life of smooth specimen because of the random distribution growth and coalescence of surface micro-cracks. The path of surface micro-crack has irregularity due to nonhomogeneous microstructure. Euclidian geometry can't quantify the shape of surface micro-crack but fractal geometry can. Therefore in this paper fractal dimension is measured at various stage of cycle ratio and estimated cycle ratio in 2024-T3 aluminium, alloy.