• Journal of the Korea Concrete Institute
• /
• v.22 no.2
• /
• pp.219-228
• /
• 2010

It has been well known that concrete structures exposed to acid and sulfate environments such as sewer, sewage and wastewater, soil, groundwater, and seawater etc. show significant decrease in their durability due to chemical attack. Such deleterious acid and sulfate attacks lead to expansion and cracking in concrete, and thus, eventually result in damage to concrete matrix by forming expansive hydration products due to the reaction between portland cement hydration products and acid and sulfate ions. Objectives of this experimental research are to investigate the effect of mineral admixtures on the resistance to acid and sulfate attack in concrete and to suggest high-resistance concrete mix against acid and sulfate attack. For this purpose, concretes specimens with three types of cement (ordinary portland cement (OPC), binary blended cement (BBC), and ternary blended cement (TBC) composed of different types and proportions of admixtures) were prepared at water-biner ratios of 32% and 43%. The concrete specimens were immersed in fresh water, 5% sulfuric acid, 10% sodium sulfate, and 10% magnesium sulfate solutions for 28, 56, 91, 182, and 365 days, respectively. To evaluate the resistance to acid and sulfate for concrete specimens, visual appearance changes were observed and compressive strength ratios and mass change ratios were measured. It was observed from the test results that the resistance against sulfuric acid and sodium sulfate solutions of the concretes containing mineral admixtures were much better than that of OPC concrete, but in the case of magnesium sulfate solution the concretes containing mineral admixtures was less resistant than OPC concrete due to formation of magnesium silicate hydrate (M-S-H) which is non-cementitious.

• Journal of the Korea Concrete Institute
• /
• v.27 no.6
• /
• pp.641-649
• /
• 2015

The purpose of this study was to assess the durability of high-strength concrete with high volume mineral admixture (HVMAC) derived from previous studies within ternary blended concrete (TBC) and normal concrete (NC). Four durability evaluation types such as chloride penetration resistance, freezing and thawing resistance, carbonation resistance in two pre-treatment conditions, and sulfuric acid and sulfate resistance using 5% sulfuric acid ($H_2SO_4$), 10% sodium sulfate ($Na_2SO_4$), and 10% magnesium sulfate ($MgSO_4$) solution were selected and performed in this study. HVMAC showed the excellent chloride penetration resistance in any age and the freezing and thawing durability close to 100%. In addition, HVMAC affected more reduction in carbonation resistance than TBC. When the curing time was increased, to create a concrete internal organization densely improved resistance to carbonation. HVMAC also showed the most superior in sulfuric acid and sulfate resistance. As the reduction of calcium hydroxide and $C_3A$ to apply a large amount of admixture reduced the swelling and cracking of concrete, the strength reduction and mass change of concrete was found to be small indicated.

• Journal of Korean Society of Environmental Engineers
• /
• v.27 no.1
• /
• pp.36-42
• /
• 2005

This study examined the feasibility of producing sulfuric acid and ammonia water from ammonium sulfate solution using two-compartment electrodialysis with a bipolar membrane (EDBM). Electrodialysis experiments were carried out with 20 wt% ammonium sulfate at different current densities and sulfuric acid concentrations in a concentrate compartment. The current efficiency increased with the current density from 25 to $100\;mA/cm^2$. Nevertheless, the efficiency was relatively low compared with that of general desalting electrodialysis, owing to the diffusion of sulfuric acid from the concentrate compartment to the diluate. The diffusion rate through the anion exchange membrane increased with the sulfuric acid concentration in the concentrate compartment, which decreased the current efficiency. Conversely, the electrical resistance decreased with increasing current density owing to the Joulian heat generated during water dissociation in the transition region of the bipolar membrane under a high electric field. From the experimental results, we concluded that operating at a higher current density is effective from the perspective of current efficiency and electrical resistance when producing sulfuric acid and ammonia water from ammonium sulfate using a two-compartment EDBM process. Further studies on the effects of increasing the sulfuric acid concentration on current efficiency are required to apply the EDBM process practically.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.179-180
• /
• 2022

In this study, analyzed the effect of using CGS before and after the pre-treatment process as fine aggregate on the resistance to sulfate attack in concrete. As a result of the analysis, Although it showed a similar tendency to Plain (CS100), it is judged that it is necessary to analyze the resistance to sulfate attack due to the increase in immersion periods such as 180 days and 365 days.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.421-424
• /
• 2008

The purpose of this experimental research is to investigate the influence of cement types on the resistance to acid and sulfate. For this purpose, concrete specimens with three types of cement such as ordinary portland cement(OPC), binary blended cement(BBC), and ternary blended cement(TBC) were made for water-binder(W/B) ratios of 32% and 43%, and then according to JSTM C 7401, the appearance change and ratio of mass change of them were estimated through the immersion tests by 5% sulfuric acid, 10% sodium sulfate, and 10% magnesium sulfate solution, respectively. It was observed from the test result that the resistance against acid and sulfate increased with decreasing W/B ratio and those of BBC and TBC concretes were better than the case of OPC concrete from immersion tests of 91 days.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.27-32
• /
• 2002

In this research influences of type and concentration of alkali activator and curing condition on the hydration, and properties of alkali activated blast furnace slag(AAS) concrete were investigated. Sodium carbonate and sulfate were used as alkali activators and their concentration were 4~10 weight percent with Na$_2$O equivalent to binder. The curing conditions were standard curing using 23$^{\circ}C$ water and activated curing chamber at $65^{\circ}C$. Results show that in case of sodium carbonate addition high early strengths were gained by activation of early hydration, but later strength gained was slight. On the other side sodium sulfate strengths were continuously increased with adding amount and ages. Steam curing activated early hydration so that early strengths were improved but later strengths were similar to standard curing. The strength reduction of AAS mortar with sodium sulfate was less than OPC mortar in 5% sulfuric acid solution so that AAS concrete can be useful for acid-resistance concrete.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2015.05a
• /
• pp.84-85
• /
• 2015

The aim of this study is to develop crack self-healing concrete and repair materials with the sulfate resistance using geo-materials and by-products for practical industrial application. Research has been done on the healing of cracks in aged concrete, but it seems that very little is known about the actual healing mechanism and its conditions. In this research, the essential properties of geo-materials with pozzolanic reaction for self-healing were analyzed and discussed.

• Advances in concrete construction
• /
• v.6 no.4
• /
• pp.345-362
• /
• 2018

In this paper, mechanical and short-term durability properties of fly ash and slag based geopolymer concretes (FAGPC-SGPC) were investigated. The alkaline solution was prepared with a mixture of sodium silicate solution ($Na_2SiO_3$) and sodium hydroxide solution (NaOH) for geopolymer concretes. Ordinary Portland Cement (OPC) concrete was also produced for comparison. Main objective of the study was to examine the usability of geopolymer concretes instead of the ordinary Portland cement concrete for structural use. In addition to this, this study was aimed to make a contribution to standardization process of the geopolymer concretes in the construction industry. For this purpose; SGPC, FAGPC and OPC specimens were exposed to sulfuric acid ($H_2SO_4$), magnesium sulfate ($MgSO_4$) and sea water (NaCl) solutions with concentrations of 5%, 5% and 3.5%, respectively. Visual inspection and weight change of the specimens were evaluated in terms of durability aspects. For the mechanical aspects; compression, splitting tensile and flexural strength tests were conducted before and after the chemical attacks to investigate the residual mechanical strengths of geopolymer concretes under chemical attacks. Results indicated that SGPC (100% slag) is stronger and durable than the FAGPC due to more stable and strong cross-linked alumina-silicate polymer structure. In addition, FAGPC specimens (100% fly ash) showed better durability resistance than the OPC specimens. However, FAGPC specimens (100% fly ash) demonstrated lower mechanical performance as compared to OPC specimens due to low reactivity of fly ash particles, low amount of calcium and more porous structure. Among the chemical environments, sulfuric acid ($H_2SO_4$) was most dangerous environment for all concrete types.

• Journal of the Korean institute of surface engineering
• /
• v.26 no.4
• /
• pp.163-174
• /
• 1993

The effect of gelatine on the electrodeposition of copper in cupric sulfate-sulfuric acid solution was investi-gated using an ac impedance technique. In the presence of gelatine, the charge transfer resistance was in-creased and the electrical double layer capacitance was decreased. A model was suggested to explain the im-pedance spectra and it fitted well the experimental data. Also the uniformity of deposit thickness was in-creased while the grain size was decreased by the addition of gelatine.

• Journal of the Korean Ceramic Society
• /
• v.44 no.11
• /
• pp.633-638
• /
• 2007

The setting time of alkali activated slag cement tends to be much faster than ordinary Portland cement, and its compressive strength had been higher from the 1 day but became lower than that of the cement on the 28 days. According to the results of the surface observation, weight loss, compressed strength, and erosion depth tests on the sulphuric acid solution. It has been drawn that alkali activated slag cement has a higher sulphate resistance than ordinary Portland cement, and in particular, the alkali activated slag cement added 5 wt% alumina cement has little deterioration on the sulphuric acid solution. The reason why the alkali activated slag cement has higher sulphate resistance than other hardened cement pastes is that it has no $Ca(OH)_2$ reactive to sulphate ion, and there is little $CaSO_4{\cdot}2H_2O$ production causing volume expansion, unlike other pastes. And it is supposed that $Al(OH)_3$ hydrates with high sulphate resistance, which is produced by adding the alumina cement increases the sulfate resistance.