• Membrane Journal
• /
• v.16 no.4
• /
• pp.286-293
• /
• 2006

Porous asymmetric membranes based on PVdF as a nascent membrane were prepared by using a phase inversion method. PVdF ion conductive composite membranes were finally made by introducing $SO_3{^-}$ from sulfuric acid after cross-linked PS with various DVB contents in the pores of PVdF. Final PVdF composite membranes were characterized by FTIR, SEM, EDS to verify $SO_3{^-}$. It was revealed that the solvent contents and ion exchange capacity (IEC) decreased with increase of the degree of cross-linking. As the degree of crosslink increases both the electric conductivity and methanol permeability decreased, which was showing the better values than Nafion 117. When DVB content was 8%, its electric conductivity ($5.58{\times}10^{-5}S/cm$) was similar to Nafion 117 ($6.03{\times}10^{-5}S/cm$). But the lower methanol permeability ($1.0{\times}10^{-6}cm^2/sec$) than that of Nafion 117 was obtained.

• Korean Chemical Engineering Research
• /
• v.49 no.2
• /
• pp.211-217
• /
• 2011

In this study, ion exchange membranes were prepared using high impact polystyrene(HIPS) with various crosslinking and sulfonation time. Degree of sulfonation(DS) of sulfonated HIPS(SHIPS) membrane was increased with sulfonation time and decreased with crosslinking time. The highest value of DS was 66%. Also, water uptake and ion exchange capacity(IEC) of SHIPS membrane were decreased with degree of crosslinking and increased with sulfonation time. Then their values were 35.2% and 1.55 meq/g, respectively. Electrical resistance and ion conductivity of the membranes were showed more excellent value with sulfonation time. The maximum value of electrical resistance and ion conductivity were $0.4\Omega{\cdot}cm^{2}$ and 0.1 S/cm, respectively. It is indicated that the SHIPS membrane has the higher performance compare with Nafion 117. Durability of SHIPS membranes in a organic solvent was increased with increasing crosslinking time. The surface roughness of HIPS membranes were confirmed with SEM that was become uneven surface with progressing sulfonation.

• Macromolecular Research
• /
• v.10 no.6
• /
• pp.304-310
• /
• 2002

In a recent study by the same authors using a DMTA (Dynamic Mechanical Thermal Analyzer), it was found that the 4-aminobenzoic arid (ABA) molecules acted as either a neutralizing agent, or a plasticizer, or a filler, depending on the order of mixing of poly(styrene-co-styrenesulfonic acid) (PSSA), ABA, and NaOH. Subsequent to that study, we here pursued the same topic, i.e., the effect of the addition of CsOH (instead of NaOH) and ABA on the morphology of PSSA, but this time, by using a small-angle X-ray scattering (SAXS) technique. In line with the previous results, the present study with the SAXS technique verified that the order of mixing has a significant effect on the morphology of ionomers. In addition, with the SAXS data and the density values of the ionomers, we attempted to calculate both the number of sulfonate ionic groups per multiplet and the size of the multiplet of the ionomer.

• Journal of the Korean Society of Radiology
• /
• v.11 no.2
• /
• pp.157-165
• /
• 2017

The active transport characteristics of $K^+$ and $Na^+$ pumping system of cell membrane model which irradiated by high energy x-ray(linac 6MeV) was investigated. The cell membrane model used in this experiment was a $Na^+$ type sulfonated copolymerized membrane of styrene and divinylbenezene. The initial flux of the ion was increased with increase of both $H^+$ ion concentration. In this experiment range(pH 1.5-5, temperature $36.5^{\circ}C$), the initial flux of $K^+$ which was not irradiated by radiation was found to be from $2.09{\times}10^{-4}$ to $1.32{\times}10^{-3}mole/cm^2{\cdot}h$ and that of $Na^+$ from $7.09{\times}10^{-4}$ to $1.09{\times}10^{-3}mole/cm^2{\cdot}h$. the initial flux of $K^+$ which was irradiated by radiation was found to be from $21.0{\times}10^{-4}$ to $16.7{\times}10^{-3}mole/cm^2{\cdot}h$ and that of $Na^+$ from $62.0{\times}10^{-4}$ to $20.6{\times}10^{-3}mole/cm^2{\cdot}h$. The ratio $K^+$/$Na^+$ of membrane was about 1.10. And the driving force of pH of irradiated membrane was significantly increased about 9-20 times than membrane which was not irradiated. As active transport of $K^+$ and $Na^+$ of cell membrane model were abnormal, cell damages were appeared at cell.

• Macromolecular Research
• /
• v.17 no.9
• /
• pp.658-665
• /
• 2009

This study examined the effects of the sodium salts of aliphatic dicarboxylic acids (DCAs) on the dynamic mechanical properties and morphology of two sets of poly(styrene-co-sodium methacrylate) (MNa) and poly(styrene-co-sodium styrenesulfonate) (SNa) ionomers. When the DCA content was relatively low, the ionic moduli of the MNa and SNa ionomers increased but the matrix and cluster glass transition temperature ($T_g$) did not change significantly. The increasing ionic modulus was almost independent of the type of the ionic groups of the ionomer, and the chain length of DCAs. When a large amount of the sodium succinate (DCA4) was added to the MNa and SNa ionomers, the ionic moduli of the two ionomers increased strongly but the matrix and cluster $T_g's$ increased slightly and significantly, respectively. In the case of sodium hexadecanedioate (DCA 16), DCA 16 increased the ionic moduli of the two ionomers. The addition of DCA16 changed the matrix and cluster $T_g's$ of the MNa ionomer slightly, but decreased the cluster $T_g$ of the SNa ionomer significantly with no change in the matrix $T_g$. In addition, the DCA-containing ionomers showed an X-ray diffraction peak indicating the presence of ordered domains of DC As in the ionomers. Hence, DCA4 acts mainly as a reinforcing filler in MNa and SNa systems. In the case of DCA 16, it initially behaved like a filler but also functioned as a preferential plasticizer for the clusters at high content.

• Analytical Science and Technology
• /
• v.17 no.1
• /
• pp.60-68
• /
• 2004

The core-shell polyolefin nonwovon fabric (PNF), wherein the PNF comprises at least about 60% of polyethylene having a melting temperature at ${\sim}132^{\circ}C$ and no more than about 40% of second polypropylene having a lower melting temperature at ${\sim}162^{\circ}C$. The sulfonic acid group for battery separators were prepared by radiation-induced grafting of styrene onto PNF and by the subsequent sulfonation of polystyrene graft chains. The sulfonated PNF was characterized by XPS, SEM, DSC, TGA and porosimeter. The electrochemical properties such as electrolyte retension, electrical resistance, and transport number of the $K^+ions$ were evaluated after sulfonation. It was found that the electrolyte retension increased, whereas the electrical resistance decreased with increasing sulfonic acid content. The transport number of $K^+$ in PNF with sulfonic acid of 0.22 ~ 3.60 mmol/g was to be 0.90 ~ 0.93.

• Polymer(Korea)
• /
• v.33 no.6
• /
• pp.608-614
• /
• 2009

The cation-exchange membrane which was sulfonated styrene-ethylene/buthlene-styrene(SEBS) block copolymer containing the high impact polystyrene (HIPS) was prepared via post-sulfonation and casting method using the epoxidized polybutadiene and divinylbenzene as crosslinking agents. Post-sulfonation was carried out with sulfuric acid as sulfonating agent and silver sulfate as initiator in the nitrogen atmosphere. The basic properties of membranes, degree of sulfonation (DS), water uptake, ion-exchange capacity (IEC), electrical resistance, and modulus have been examined. DS of membrane increased with increasing the sulfonation time. The maximum DS of membrane containing 10 wt% HIPS was 83.6 %. The water uptake and IEC of membranes gradually increased as increasing the DS. The maximum water uptake and IEC of membranes were 43.8 % and 1.14 meq/g, respectively. The lowest electrical resistance of membrane containing the 20 wt% HIPS was $83\;\Omega{\cdot}cm^2$. The electrical conductivity of membrane containing 10 wt% HIPS was $1.22\times10^{-4}S/cm$. The modulus of membrane increased with increasing DS and these values were 153 and $204\;kgf/cm^2$ before and after sulfonation, respectively.

• Journal of the Korean Society of Radiology
• /
• v.16 no.2
• /
• pp.141-150
• /
• 2022

The initial co-transport and counter-transport permeate transport characteristics of calcium ion at epithelial cell membrane model in parathyroid which irradiated by high energy x-ray(linac 6 MV) was investigated. The epithelial cell membrane model used in this experiment was a polysulfonated copolymerized membrane of poly(PS-DVB: polystyrene-divinylbenzene). The difference of sorbed water in membrane, fixed carrier concentration(SO₃^2-), initial pH value, OH^- concentration were occurred at difference of Ca²⁺concentration and quantity of parathyroid hormone, respectively. The initial co-transport and counter-transport permeate flux of Cl^-, OH^-, Ca²⁺ on fixed carrier concentration(SO₃^2-) and initial pH value of irradiated membrane was found to be decreased than non-irradiated membrane. The initial co-transport and counter-transport permeate flux of Ca²⁺ on fixed carrier concentration (SO₃^2-), initial pH value, OH^- concentration in irradiated membrane were found to be decreased about 2.68 ~ 6.87 times, about 1.42 ~ 1.63 times, about 2.07 ~ 1.672 times than non-irradiated membrane, respectively. As a result, the quantity of parathyroid hormone was decreased at irradiated membrane than non-irradiated membrane. The decrease of parathyroid hormone was occurred at hypoparathyroidism and osteoporosis, parathyroiditis, and so on. As the parathyroid hormone in epithelial cell membrane model were abnormal, cell damages were appeared at cell.