• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.4
• /
• pp.121-128
• /
• 2007

The present study evaluates the resistance to sulfate attack of cement matrix with or without silica fume. The main variable was the replacement levels of silica fume. In order to introduce sulfate attack to cement matrix, mortars and pastes was exposed to sodium sulfate solution for 510 days. Visual examination, expansion and compressive strength loss of mortars in addition to characteristics of pore for the paste samples were regularly investigated. From the test results, it was clearly observed that the cement matrix with silica fume was very resistant to sulfate attack irrespective of the replacement levels of silica fume. However, the severe deterioration due to sulfate attack was found in cement matrix without silica fume.

• Asian-Australasian Journal of Animal Sciences
• /
• v.31 no.6
• /
• pp.873-880
• /
• 2018

Objective: The objective of this experiment was to compare the effects of adding 130 mg/kg Cu from either copper sulfate (CS) or tribasic copper chloride (TBCC) on growth performance, mineral deposition in tissues, and the excretion in feces of pigs as well as changes in the mineral contents in tissues and feces when the supplemental Cu level was decreased from 130 mg/kg to 10 mg/kg. Methods: A total of 72 pigs ($32.6{\pm}1.2kg$) were randomly assigned to a CS diet or a TBCC diet with 6 pens per treatment. The trial lasted 102 d and included 3 phases (phase 1, 1 to 30 d; phase 2, 31 to 81 d; and phase 3, 82 to 102 d). The supplemental levels of Cu in the 2 treatments were 130 mg/kg in phase 1 and 2 and 10 mg/kg in phase 3. Results: The results showed that pigs fed the CS diet tended to have higher average daily gain than pigs fed the TBCC diet during d 1 to 81 (p<0.10). Compared with CS, TBCC increased the activities of aspartate transaminase (AST), ceruloplasmin, and superoxide dismutase in serum on d 30 (p<0.05). The TBCC decreased the Cu level in the liver on d 81 (p<0.05) and increased the Mn level in the liver on d 102 (p<0.05). The concentration of Cu in feces sharply decreased when the supplemental Cu level in diet changed from 130 mg/kg to 10 mg/kg in both diets (p<0.05). Conclusion: The result suggested that TBCC and CS had no significant difference on growth performance but TBCC had higher activities of AST and antioxidant enzymes and lower liver Cu than CS when pigs fed diets with 130 mg Cu /kg diet.

• Journal of the Society of Disaster Information
• /
• v.15 no.2
• /
• pp.239-248
• /
• 2019

Purpose: This study aims to enhance the resistance against sulfate attack compared to ordinary Portland cement (OPC) concrete by using liquid crystal display (LCD) as binder. Method: The fundamental properties including compressive strength and porosity of concrete replaced by LCD up to 15% at increments of 5% and in turn, the weight, volume, and strength loss of LCD-mixed concrete was analyzed. Results: For the concrete substituted by 5% of LCD, it showed the highest compressive strength at 28 days of curing, and particular at immersion of $Na_2SO_4$ solution, it was achieved the lowest loss of weight, volume and strength due to an decreased porosity at capillaries. In contrast, there is no distinct difference of the sulfate attack resistance between LCD-mixed concretes under exposure of $MgSO_4$ solution, excepted for OPC concrete. Conclusion: In this study, comparison of resistance to sulfate attack between LCD-mixed concretes, and it would be proposed the possibility of LCD usage as binder through long-term verification with extended replacement ratio and identification of changes of hydrates in the cement matrix.

• International Journal of Concrete Structures and Materials
• /
• v.9 no.2
• /
• pp.145-158
• /
• 2015

The consequence of sulfate attack on geopolymer concrete, made from an alkali activated natural pozzolan (AANP) has been studied in this paper. Changes in the compressive strength, expansion and capillary water absorption of specimens have been investigated combined with phases determination by means of X-ray diffraction. At the end of present investigation which was to evaluate the performance of natural alumina silica based geopolymer concrete in sodium and magnesium sulfate solution, the loss of compressive strength and percentage of expansion of AANP concrete was recorded up to 19.4 % and 0.074, respectively.

• Journal of the Korea Concrete Institute
• /
• v.16 no.1 s.79
• /
• pp.130-138
• /
• 2004

The primary factors that affecting concrete sulfate resistance are the chemistry of the Portland cement and the chemistryandreplacementlevelofmineraladmixtures. In order to investigate the effect of those on the sulfate attack the testing program involved the testing of several different mortar mixes using the standardized test, ASTM C 1012. four different cements were evaluated including one Type I cement, two Type I-II cements, and one Type V cement. Mortar mixes were also made with mineral admixtures as each cement was combined with three different types of mineral admixtures. One Class F fly ash and one Class C fly ash was added in various percent volumetric replacement levels. The expansion measurements of mortar bars were taken and compared with expansion criteria recommended from past experience to investigate the effect of each factor.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.953-956
• /
• 2006

Sulfate resistance of mortar specimens with or without alkali-free accelerator exposed to sulfate solutions for 360 days was investigated. Test results confirms a negative effect of alkali-free accelerator on the sulfate deterioration, irrespective of attacking sources. Based on the ASTM C1012 expansion test, the experimental findings demonstrated that higher $C_3A$ content in cement led to the higher expansion, especially in the mortar specimens with alkali-free accelerator.

• Corrosion Science and Technology
• /
• v.16 no.1
• /
• pp.8-14
• /
• 2017

The corrosion behavior of a ferritic/martensitic steel T91 exposed to an aqueous solution containing chloride and sulfate ions is investigated depending on the stimulated all-volatile treatment (AVT) and under oxygenated treatment (OT) conditions. The corrosion of T91 steel under OT condition is severe, while the corrosion under AVT condition is not. The co-existence of chloride and sulfate ions has antagonistic effect on the corrosion of T91 steel in both AVT and OT conditions. Unlike to corrosion resistance in the aqueous solution, OT pretreatment provides T91 steel lower oxidation-resistance than VAT pretreatment. From scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDS) and X-ray diffraction (XRD) analysis, the lower corrosion resistance in the aqueous solution by VAT conditions possibly is due to the formation of pits. In addition, the lower oxidation resistance of T91 steel pretreated by OT conditions is explained as follows: the cracks formed during the immersion under OT conditions accelerated peeling-off rate of the oxide film.

• Advances in concrete construction
• /
• v.8 no.2
• /
• pp.119-126
• /
• 2019

This paper reports an experimental investigation conducted to evaluate the durability performance of concrete mixtures prepared utilizing blends of Type I Portland cement (OPC) and natural pozzolans (NPs) obtained from three different sources in Saudi Arabia. The control concrete mixture containing OPC alone as the binder and three concrete mixtures incorporating NPs were prepared keeping water/binder ratio of 0.4 (by weight), binder content of $370kg/m^3$, and fine/total aggregate ratio of 0.38 (by weight) invariant. The compressive strength and durability properties that included depth of water penetration, depth of carbonation, chloride diffusion coefficient, and resistance to reinforcement corrosion and sulfate attack were determined. Results of this study indicate that at all ages, the compressive strength of NP-admixed concrete mixtures was slightly less than that of the concrete containing OPC alone. However, the concrete mixtures containing NP exhibited lower depth of water penetration and chloride diffusion coefficient and more resistance to reinforcement corrosion and sulfate attack as compared to OPC. NP-admixed concrete showed relatively more depth of carbonation than OPC when subjected to accelerated carbonation. The results of this investigation indicates the viability of utilizing of Saudi natural pozzolans for improving the durability characteristics of concrete subjected to chloride and sulfate exposures.

• Advances in concrete construction
• /
• v.7 no.3
• /
• pp.175-181
• /
• 2019

Low-calcium fly ash (LCFA) were used to prepare cement/LCFA specimens in this study. The basic physical properties including water demand, fluidity, setting time, soundness and drying shrinkage of cement/LCFA paste were investigated. The effects of curing time, immersion time and wet-dry cycles in 3% $Na_2SO_4$ solution on the compressive strength and the microstructures of specimens were also discussed. The results show that LCFA increases the water demand, setting time, soundness of cement paste samples. 50% and 60% LCFA replacement ratio decrease the drying shrinkage of hardened cement paste. The compressive strength of plain cement specimens decreases at the later immersion stage in 3% $Na_2SO_4$ solution. The addition of LCFA can decrease this strength reduction of cement specimens. For all specimens with LCFA, the compressive strength increases with increasing immersion time. During the wet-dry cycles, the compressive strength of plain cement specimens decreases with increasing wet-dry cycles. However, the pores in the specimens with 30% and 40% LCFA at early ages could be large enough for the crystal of sodium sulfate, which leads to the compressive strength increase with the increase of wet-dry cycles in 3% $Na_2SO_4$ solution. The microstructures of cement/LCFA specimens are in good agreement with the compressive strength.

• Steel and Composite Structures
• /
• v.29 no.2
• /
• pp.201-218
• /
• 2018

In this study, the effects of magnesium sulfate on the mechanical performance and the durability of confined and unconfined geopolymer concrete (GPC) specimens were investigated. The carbon and basalt fiber reinforced polymer (FRP) fabrics with 1-layer and 3-layers were used to evaluate the performances of the specimens under static and cyclic loading in the ambient and magnesium sulfate environments. In addition, the use of FRP materials as a rehabilitation technique was also studied. For the geopolymerization process of GPC specimens, the alkaline activator has selected a mixture of sodium silicate solution ($Na_2SiO_3$) and sodium hydroxide solution (NaOH) with a ratio ($Na_2SiO_3/NaOH$) of 2.5. In addition to GPC specimens, an ordinary concrete (NC) specimens were also produced as a reference specimens and some of the GPC and NC specimens were immersed in 5% magnesium sulfate solutions. The mechanical performance and the durability of the specimens were evaluated by visual appearance, weight change, static and cyclic loading, and failure modes of the specimens under magnesium sulfate and ambient environments. In addition, the microscopic changes of the specimens due to sulfate attack were also assessed by scanning electron microscopy (SEM) to understand the macroscale behavior of the specimens. Results indicated that geopolymer specimens produced with nano-silica and fly ash showed superior performance than the NC specimens in the sulfate environment. In addition, confined specimens with FRP fabrics significantly improved the compressive strength, ductility and durability resistance of the specimens and the improvement was found higher with the increased number of FRP layers. Specimens wrapped with carbon FRP fabrics showed better mechanical performance and durability properties than the specimens wrapped with basalt FRP fabrics. Both FRP materials can be used as a rehabilitation material in the sulfate environment.