• Journal of Powder Materials
• /
• v.30 no.2
• /
• pp.146-155
• /
• 2023

The Ti-6Al-4V lattice structure is widely used in the aerospace industry owing to its high specific strength, specific stiffness, and energy absorption. The quality, performance, and surface roughness of the additively manufactured parts are significantly dependent on various process parameters. Therefore, it is important to study process parameter optimization for relative density and surface roughness control. Here, the part density and surface roughness are examined according to the hatching space, laser power, and scan rotation during laser-powder bed fusion (LPBF), and the optimal process parameters for LPBF are investigated. It has high density and low surface roughness in the specific process parameter ranges of hatching space (0.06-0.12 mm), laser power (225-325 W), and scan rotation (15°). In addition, to investigate the compressive behavior of the lattice structure, a finite element analysis is performed based on the homogenization method. Finite element analysis using the homogenization method indicates that the number of elements decreases from 437,710 to 27 and the analysis time decreases from 3,360 to 9 s. In addition, to verify the reliability of this method, stress-strain data from the compression test and analysis are compared.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.42 no.2
• /
• pp.187-195
• /
• 2022

This study investigated the effect of artesian pressure on mechanical properties of deep cement mixing (DCM)-improved specimens. Various laboratory tests such as unconfined compression test and scanning electron microscope (SEM) were conducted on DCM specimens which curied in a water tank with different artesian pressures. The artesian pressure was determined in consideration of the laboratory scale and the hydraulic gradient in field conditions. Results of experimental tests indicated that unconfined compressive strength, secant modulus, and unit weight of specimen decreased and water content tended to increase as an artesian pressure increased. The stress-strain behavior changed brittle to ductile behaviors as an artesian pressure increased. The outflow water from the water tank reacted with the phenolphthalein solution due to the leaching phenomenon of the improved specimen. SEM analysis also confirmed that a small amount of ettringite was formed between soil particles in the specimens with artesian pressure.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.29 no.6A
• /
• pp.577-585
• /
• 2009

A 9-node degenerated shell finite element(FE), which has been developed for assessment of ultimate pressure capacity and nonlinear analysis for nuclear containment building is described in this paper. Reissner-Midnlin(RM) assumptions are adopted to develop the shell FE so that transverse shear deformation effects is considered. Material model for concrete prior to cracking is constructed based on the equivalent stress-equivalent strain relationship. Tension stiffening model, shear transfer mechanism and compressive strength reduction model are used to model the material behavior of concrete after cracking. Niwa and Aoyagi-Yamada failure criteria have been adapted to find initial cracking point in compression-tension and tension-tension region, respectively. Finally, the performance of the developed program is tested and demonstrated with several examples. From the numerical tests, the present results show a good agreement with experimental data or other numerical results.

• Steel and Composite Structures
• /
• v.51 no.3
• /
• pp.243-260
• /
• 2024

Thirteen self-compacting recycled concrete filled aluminium tubular (SCRCFAT) columns were tested under concentric compression loads. The effects of the replacement ratio of the recycled concrete aggregate (RCA) and steel fibre (SF) reinforcement on the structural performance of the SCRCFAT columns were studied. A control specimen (C000) was cast with normal concrete without SF to be reference for comparison. Twelve columns were cast using RCA, six columns were cast using concrete incorporating 2% SF while the rest of columns were cast without SF. Failure mode, ductility, ultimate load capacity, axial deformation, ultimate strains, stress-strain response, and stiffness of the SCRCFAT columns were studied. The results showed that, the peak load of tested SCRCFAT columns incorporating 5-100 % RCA without SF reduced by 2.33-11.28 % compared to that of C000. Conversely, the peak load of tested SCRCFAT columns incorporating 5-100% RCA in addition to 2% SF increased by 21.1-40.25%, compared to C000. Consequently, the ultimate axial deformation (Δ) of column C100 (RCA=100% and SF 0%) increased by about 118.9 % compared to C000. The addition of 2% SF to the concrete mix decreased the axial deformation of SCRCFAT columns compared to those cast with 0% SF. Moreover, the stiffness of the columns cast without SF decreased as the RCA % increased. In contrast, the columns stiffness cast with 2% SF increased by 26.28-89.7 % over that of C000. Finally, a theoretical model was proposed to predict the ultimate loads tested SCRCFAT columns and the obtained theoretical results agreed well with the experimental results.

• Advances in concrete construction
• /
• v.17 no.5
• /
• pp.273-284
• /
• 2024

The steel-concrete composite system has been playing a vital role in the construction sector for the past two decades. By using steel and concrete together, we achieve strong load resistance with minimal deflection and bending stress. The study focuses on the numerical and analytical behaviour of concrete encased steel castellated beams and compared them with previous experiments. The study used five composite beams, including one control reinforced concrete beam (CC), one fully concrete encased steel beam (FCES), and three fully concrete encased castellated beams. The major variable is the opening configuration of the castellated beam, such as openings along the longitudinal axis, above the longitudinal axis, and below the longitudinal axis. The 150 mm × 250 mm cross section and 2000 mm in length of beams were used. Using the finite element software ANSYS, we conduct nonlinear finite element analysis for the entire beam and compare it with test data. The numerical load carrying capacity of concrete encased steel castellated beam with a hexagonal opening above the longitudinal axis (FCESCB H2) is 160 kN is closer to the experimental observation. Von Mises strain of FCESB is 0.004232, which is lower than CB and composite castellated beam. The ductility factor and energy absorption capacity of FCESB are 5.090 and 1688.47 kNm. It was observed that the configuration of the opening will influence the strength of the composite beam. Plastic moment methods were employed to estimate the ultimate load carrying capacity of the beam. In the analytical study the beams were assumed as perfectly plastic. The ultimate analytical load carrying capacity of FCESCB H2 is 21.87% higher than FCESB. It found that performing FCESCB H2 is superior to the entire specimen.

• Journal of the Korea Concrete Institute
• /
• v.23 no.5
• /
• pp.581-590
• /
• 2011

Since ultra-high performance cementitious composites (UHPCC) not only represents high early age shrinkage strain due to its low water-to-binder ratio (W/B) and high fineness admixture usage but also reduces the cross section of structure from the higher mechanical properties, it generally has more shrinkage cracks from the restraints of formwork and reinforcing bars. In this study, free and restrained shrinkage experiments were conducted to evaluate the suitability of incorporating both expansive admixture (EA) and shrinkage reducing agent (SRA). The test results indi-cated that approximately 40~44% of free shrinkage strain was decreased. Also, the results showed that 35% and 47% of residual tensile stresses were relieved by synergetic effect of SRA and EA, respectively. Residual tensile stresses from ringtest were relaxed by approximately 61% and 64% of elastic shrinkage stresses due to SRA and EA, respectively, because of the tensile creep effect. Therefore, the creep effect should be considered to precisely estimate the restrained shrinkage behavior of concrete structures. The degree of restraint of UHPCC was approximately in the range of 0.78~0.85. The addition of combined EA and SRA showed minute influence on the degree of restraint. However, the effect decreased when thicker concrete ring was used. Tensile creep strains were measured and compared to the predicted values from 4-parametric prediction model considering time dependent restrained forces.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.24 no.2
• /
• pp.83-93
• /
• 1988

Recent Experimental results show that the J integral can be effectively used to obtain a valid parameter for predicting plane strain and plane stress fracture. However, only a few research results have been reported for the effect of thickness where the plane strain state can not be assumed. A purpose of this study is to find the behavior of fracture touhness and tearing modulus varing the specimen thickness. The type of specimen in the present study is compact tension (CT). The thicknesses of the low carbon steel specimens that are used in the experiments are 5, 10, 15, 20 and 25mm. The measurement of crack length is taken by optical measurements method. From the study, the followings are found; 1) The fracture toughness and the tearing modulus which are obtained by using Yoon's and Simpson's formula show more conservative than that by using Rice's and Merkel's. 2) The fracture toughness is increase in specimen thickness which is reached 15mm. Beyond this thickness the fracture toughness is decreased in specimen thickness. 3) In the case of CT specimen with the thickness ranging from 5 to 25mm, the tearing modulus which is applied the same J integral equation is almost constant. 4) By using Yoon's formula, the correlation of the plane slress fracture toughness J sub(C) with specimen thickness B is expressed as the following formula. J sub(C)/J sub(IC)=1.7-15.1(B/W)+112.9(B/W) super(2) -301.3(B/W) super(3) +260.6(B/W) super(4)

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.1
• /
• pp.147-157
• /
• 2018

The basis of capacity design has been explicitly or implicitly regulated in most bridge design specifications. It is to guarantee ductile failure of entire bridge system by preventing brittle failure of pier members and any other structural members until the columns provides fully enough plastic rotation capacity. Brittle shear is regarded as a mode of failure that should be avoided in reinforced concrete bridge pier design. To provide ductility behavior of column, the one of important factors is that flexural hinge of column must be detailed to ensure adequate and dependable shear strength and deformation capacity. Eight small scale circular reinforced concrete columns were tested under cyclic lateral load with 4.5 aspect ratio. The test variables are longitudinal steel ratio, transverse steel ratio, and axial load ratio. Eight flexurally dominated columns were tested. In all specimens, initial flexural-shear cracks occurred at 1.5% drift ratio. The multiple flexural-shear crack width and length gradually increased until the final stage. The angles of the major inclined cracks measured from the vertical column axis ranged between 42 and 48 degrees. In particular, this study focused on assessing transverse reinforcement contribution to the column shear strength. Transverse reinforcement contribution measured during test. Each three components of transverse reinforcement contribution, axial force contribution and concrete contribution were investigated and compared. It was assessed that the concrete stresses of all specimen were larger than stress limit of Korea Bridge Design Specifications.

• Composites Research
• /
• v.36 no.3
• /
• pp.199-204
• /
• 2023

A combination of a metallic mesh and an adhesive layer of metallic particle/epoxy composite was introduced as an intermediate layer to enhance the adhesion between cold-sprayed particles and fiber-reinforced composites (FRCs). Aluminum was considered for both the metallic particles in the adhesive and the metallic mesh. To predict the mechanical characteristics of the intermediate bond layer under a high strain rate, the properties of the adhesive layer needed to be calculated or measured. Therefore, in this study, the Al particle/epoxy adhesive was homogenized by using a rule of mixture. To verify the homogenization, the penetration depth, and the thickness decrease after the cold spray deposition from the undeformed surface, was monitored with FE analysis and compared with experimental observation. The comparison displayed that the penetration depth was comparable to the diameters of one cold spray particle, and thus the homogenization approach can be reasonable for the prediction of the stress level of particulate polymer composite interlayer under a high strain rate for cold spray processing.

• Journal of the Korea Concrete Institute
• /
• v.24 no.6
• /
• pp.727-735
• /
• 2012

Recently, a high-strength strand of 2400 MPa was developed using domestic technologies. In 2011, KS D 7002 was revised to cover the newly developed high-strength strands to support their practical usage. Presently, however, discussions and evaluations are not sufficient on the mechanical properties of the strands and their performance in structural members. Also, there were no detailed reviews on the need to revise the current design code for practical use of the high-strength strands. In this study, flexural behavior of a member with the high-strength strands was estimated through sectional analysis and a review and comparison of the domestic and foreign design codes were conducted considering the analysis results. Also, the need for the revision of the design code was discussed. Such discussion especially focused on the estimation of the stress in strand, which related with various issues such as determination methods for yield point of strands, time-dependent loss of prestressing force, estimation of stress in strand at member failure, and net strain limit for ductile failure of member. The discussion revealed that some parts in the design code need a revision and the further studies are required.