• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2000.11a
• /
• pp.79-83
• /
• 2000

Interfacial and microfailure properties of carbon liber/bismaleimide (BMI) composites were evaluated using both tensile fragmentation and compressive Broutman tests with acoustic emission (AE). Since BMI is rather difficult matrix to apply for the conventional fragmentation test because of its too low elongation and too brittle and high modulus properties, dual matrix composite system was applied. After carbon fiber/BMI composite was prepared for rod shape by controlling differing curing stage, composites rod was embedded in toughened epoxy as outer matrix. The typical microfailure modes including fiber break, matrix cracking, and interlayer failure were observed during tensile testing, whereas the diagonal slippage in fiber ends was observed during compressive test. On the other hand, AE amplitudes of BMI matrix fracture were higher than carbon fiber tincture under tensile test because BMI matrix has very brittle and high modulus. The waveform of signals coming from BMI matrix fractures was consistent with AE amplitude result under tensile tests.

• Composites Research
• /
• v.19 no.4
• /
• pp.7-14
• /
• 2006

Interfacial shear strength between epoxy and carbon fiber has been analyzed utilizing the microbond specimen with an epoxy micro-droplet adhered onto single carbon fiber. The interfacial shear stress distributions along the fiber/matrix interface were calculated by finite element analysis using three kinds of finite element models such as droplet model, circular-crosssection model and pull-out model. Conclusions were obtained as follows. (1) Interfacial shear stress distribution showed that larger stresses were concentrated in the fiber/matrix interface for microbond test than for pull-out test. Thus, debonding at the fiber/matrix interface during microbond test was liable to occur at low load level. (2) Microbond test showed higher interfacial strength which was caused by various effects of micro-droplet geometry and size as well as stress concentration in the region contacting with the micro-vise tip.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.3
• /
• pp.566-576
• /
• 1997

This study was performed to evaluate the tensile strength of solder joint in titanium and the wettability of 14K gold solder on titanium. Two pieces of titanium rod 30 mm in length and 3mm in diameter were butt-soldered with a 14K gold solder using the electric resistance heating under flux-argon atmosphere, the infrared heating under argon atmosphere, and the infrared heating under vacuum-argon atmosphere. A tensile test was performed at a crosshead speed of 0.5 mm/min, and fracture surfaces were examined by SEM. To evaluate the wettability of 14K gold solder on titanium, titanum plates of a $17{\times}17{\times}1mm$ were polished with #80-#2000 emery papers, and the spreading areas of solder 10 mg were measured by heating at 840 * for 60 seconds. The solder-matrix interface regions were etched by the solution of 10% KCN-10% (NH4)2S2O8, and analyzed by EPMA. The results obtained were summarized as follows ; 1. The maximum tensile strength was obtained when the titanium surface was polished with #2000 emery paper and soldered using the electric resistance heating under flux-argon atmosphere. Soldering strengths showed the significant difference between the electric resistance heating and the infrared heating(p<0.05). 3. The fracture surfaces showed the aspect of brittle fracture, and the failure developed along the interfaces of solder-matrix reaction zone. 4. The EPMA data for the solder-matrix interface region revealed that the diffusion of Au and Cu occurred to the titanium matrix, and the reaction zone showed the higher contents of Au, Cu and Ti than others.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.04a
• /
• pp.18-23
• /
• 1996

Since at least three-quarters of the volume of concrete is occupied by aggregate, it is not surprising that its quality is considerable importance. Not only may the aggregate limit the strength of concrete, as weak aggregate cannot porduce strong concrete, but the properties of aggregate greatly affect the durability and sructural performance of concrete. But, it is ture that aggregate strength is usually not a factor in normal concrete strength because the aggregate particle is several times stronger than the matrix and the transition zone in concrete. This study is to consider the influence the strength of concrete according to the kinds of aggregate, such as crushed river rocks, curshed rocks, high strength recycled aggregate, low strength recycled aggregate at water cement ratio 0.25. It is possible to concern the important of the mechanical role of aggegate for the high strength concrete.

• 연구논문집
• /
• s.23
• /
• pp.165-171
• /
• 1993

$Si_3N_4/Sic$. nano-composites were fabricated by hot-pressing, gas pressure sintering. The composites contained up to 50 wt. % of SiC. The mechanical properties such as strength, toughness, and hardness of the composite are compared each other. The flexural strength of the composites was improved significantly by introducing fine SiC particles into $Si_3N_4$ matrix, while the fracture toughness was not improved. The increase in flexural strength is attributed to the formation of uniformly elongated $\beta -Si_3N_4$ grains as well as the reduction of grain size.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.10a
• /
• pp.321-327
• /
• 1996

The result of an experimental study on the mechanical properties of different types of polypropylene fiber reinforced concrete are presented in this paper. This study has been performed to obtain the properties of PFRC such as slump, Vee-Bee time, compressive strength, tensile strength, flexural strength, toughness and resistance to impact. The test variables are fiber content, fiber types, fiber length and W/C ratio. Polypropylene fibers were effective in reinforcing the matrix. A remarkable increase in toughness was observed by the addition of polypropylene fibers.

• The Journal of Korean Academy of Prosthodontics
• /
• v.43 no.4
• /
• pp.415-425
• /
• 2005

Statement of problem : Fracture of composite resin core will be occulted by progress of crack. Bonding interface of different materials has large possibility of starting point of crack line. Therefore, the bond strength of glass fiber post to composite resin core is important for prevention of fracture. Purpose: This in vitro study tried to find out how to get the higher strength of glass fiber post to composite resin core through surveying the maximum load that fractures the post and cote complex. Materials and methods: 40 specimens made with glass fiber Posts(Style $post^{(R)}$, Metalor, Swiss) and composite resin core ($Z-100^{(R)}$, 3M, USA) were prepared and loaded to failure with push-out type shear-bond strength test in a universal test machine. The maximum fracture load and fracture mode were investigated in the specimens that were restored with four different surface treatments. With the data. ANOVA test was used to validate the significance between the test groups, and Bonferroni method was used to check if there is any significant statistical difference between each test group. Evely analysis was approved with 95% reliance. Results: On measuring the maximum fracture load of specimens, both the treatments of sandblasted and acid-etched one statistically showed the strength increase rather than the control group (p<0.005). The scanning electric microscope revealed that sand blasting made more micro-retention form not only on the resin matrix but on the glass fiber, and acid-etching contributed to increase in surface retention form, eliminated the inorganic particles in resin matrix. Specimen fracture modes investigation represented that sand blasted groups showed lower bonding failure than no-sand blasted groups. Conclusion: Referring to the values of maximum fracture load of specimens, the bonding strength was increased by sand blasting and acid-etching.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.14 no.1
• /
• pp.53-58
• /
• 2000

In this paper, the variable mechanical strength and dielectric breakdown strength of epoxy composites were measured at boiling absorption condition in order to observe the influences of moisture in out door use. Also, in order to improve water resistance of matrix resin, IPN(interpenetrating polymer network) method which had been already reported, was introduced and the influence was investigated. As Adding filter(SiO2) classified by o[phr], 50[phr] and 100[phr] to two kinds of matrix resin, six kinds of specimens were manufactured. As a result, it was confirmed that the moisture absorption rate was increased and mechanical strength and dielectric breakdown strength were degraded with boiling time and filler content increasing. On the other hand, it was confirmed that moisture absorption rates were decreased and the degrading rates of mechanical strength and dielectric breakdown strength were lowered according to improvement of adhesion strength in case of IPN specimens.

• Composites Research
• /
• v.22 no.3
• /
• pp.82-88
• /
• 2009

The effect of open and filled holes on the strength behavior of carbon fiber reinforced polymeric (CFRP) composites was investigated. The strength was measured at room temperature dry, cold temperature dry, $-55^{\circ}C$, and elevated temperature wet, $108.3^{\circ}C$ on several different laminate configurations. Based on the experimental data presented, it is shown that the filled hole tensile strength is larger than that of open hole by reducing damage around the hole due to the constraint imposed by the fastener. The tensile strength at cold temperature dry, $-55^{\circ}C$ is increased with the brittleness by the thermal expansion coefficient of fiber and matrix. The compressive strength at elevated temperature wet, $108.3^{\circ}C$ is decreased by the cause of interfacial deterioration between fiber and matrix with moisture absorption.

• Korean Journal of Materials Research
• /
• v.20 no.9
• /
• pp.467-471
• /
• 2010

Composites of ceramic powders and an elastomer-based matrix were prepared by mixing $CaCO_3$ powders with polyethylene and polypropylene elastomers, and their mechanical and sound insulation properties were measured. $CaCO_3$ powders with 0.7 ${\mu}m$ and 35 ${\mu}m$ particle size were added to elastomers up to 80 wt%. Scanning electron microscopy photographs showed uniform distribution of the $CaCO_3$ powders in the matrix. While density and surface hardness increased, melt index, tensile strength and elongation of the composites decreased as the amount of added $CaCO_3$ powders increased. As more $CaCO_3$ powders were added sound transmission loss of the composites increased owing to the increase of density. Addition of 0.7 ${\mu}m$ sized $CaCO_3$ powders resulted in a slightly higher transmission loss than the addition of 35 ${\mu}m$ sized powders because of the increased interface area between the elastomer matrix and the $CaCO_3$ powders. Composites with a polyethylene matrix showed higher transmission loss than those with a polypropylene matrix because the tensile strength and hardness of the polyethylene-based composites were low and their elongation was high.