• Advances in concrete construction
• /
• v.9 no.6
• /
• pp.547-556
• /
• 2020

This study aimed to develop reference materials (RMs) that are chemically stable and can simulate the flow characteristics of cement paste. To this end, the candidate components of RMs were selected considering the currently required properties of RMs. Limestone, slag, silica, and kaolin were selected as substitutes for cement, while glycerol and corn syrup were selected as matrix fluids. Moreover, distilled water was used for mixing. To select the combinations of materials that meet all the required properties of RMs, flow characteristics were first analyzed. The results revealed that silica and kaolin exhibited bilateral nonlinearity. When an analysis was conducted over time, slag exhibited chemical reactions, including strength development. Moreover, fungi were observed in all mixtures with corn syrup. On the other hand, the combination of limestone, glycerol, and water exhibited a performance that met all the required properties of RMs. Thus, limestone, glycerol, and water were selected as the components of the RMs. When the influence of each component of the RMs on flow characteristics was analyzed, it was found that limestone affects the yield value, while the ratio of water and glycerol affects the plastic viscosity. Based on this, it was possible to select the mixing ratios for the RMs that can simulate the flow characteristics of cement paste under each mixing ratio. This relationship was established as an equation, which was verified under various mixing ratios. Finally, when the flow characteristics were analyzed under various temperature conditions, cement paste and the RMs exhibited similar tendencies in terms of flow characteristics. This indicated that the combinations of the selected materials could be used as RMs that can simulate the flow characteristics of cement paste with constant quality under various mixing ratio conditions and construction environment conditions.

• Journal of Welding and Joining
• /
• v.34 no.6
• /
• pp.47-54
• /
• 2016

Post-Weld Heat Treatment (PWHT) cracking susceptibility in the weld heat-affected zone (HAZ) of reduced activation ferritic-martensitic (RAFM) steels was evaluated through stress-rupture tests. 9Cr-1W based alloys including different C, Ta and Ti content were prepared. The coarse grained heat-affected zone (CGHAZ) samples were simulated with welding condition of 30 kJ/cm heat input. CGHAZ samples consisted of martensite matrix. Stress rupture experiments were carried out using a Gleeble simulator at temperatures of $650-750^{\circ}C$ and at stress levels of 125-550 MPa, corresponding to PWHT condition. The results revealed that PWHT cracking resistance was improved by Ti addition, i.e., Ti contributed to the formation of fine and stable MX precipitates and suppression of coarse M23C6 carbides, resulting in improvement of stress rupture ductility. Meanwhile, rupture strength increased with increasing solute C content.

• Journal of Adhesion and Interface
• /
• v.1 no.1
• /
• pp.30-37
• /
• 2000

This study focused on the direct blending of bonding agents (resorcinol, hexamethylenetetramine, NaOH) into rubber compound to simplify the composite manufacturing process. The mechanism of direct blending system was studied by comparing the following two cases. The one is direct blending of bonding agents into rubber compound and then allows the reaction (Case I). The other is mixing of reactant obtained by reaction of bonding agents (Case II). According to the morphology analysis, the Case II showed the clean interfacial area between bonding agents and matrix rubber, while the Case I created the new interphase under proper processing condition. Also, the optimum adhesion strength between SBR and nylon cord could be obtained with bonding agents whose molar ratios of resprcinol/hexamethylenetetramine was 1.2/1 in the recipes.

• Polymer(Korea)
• /
• v.38 no.1
• /
• pp.62-68
• /
• 2014

To improve the compatibility of bentonite with rubber matrix, organo-modified bentonite was synthesized with a silane coupling agent, [3-(2-aminoethylamino)propyl]trimethoxysilane (AEAPTMS) in the suspension of bentonite. The structure and characteristics of organo-modified bentonite were investigated using FTIR-spectroscopy, thermogravimetric analysis (TGA) and X-ray diffraction (XRD). Ethylene-propylene-diene monomer (EPDM) rubber/organo-bentonite composites were compounded by a two-roll mill. The vulcanization and mechanical properties were studied. Results showed that the concentration of hydrochloric acid and $H_2O$ in the synthesis had significant influence on the modification of bentonite, which further contributed to the properties of the composites. Filled with 20 phr modified bentonite, the tensile strength and elongation at break of the rubber increased from 1.95 to 4.8 MPa and 300% to 500%, respectively.

• Korean Journal of Metals and Materials
• /
• v.47 no.12
• /
• pp.797-810
• /
• 2009

A study was made of the effects of a Sn addition on the microstructure and microfracture mechanism of squeeze cast AZ51-xSn magnesium alloys. Microstructural observation, in situ fracture testing, and fractographic observations were conducted on these alloys to clarify the microfracture process. The microstructural analyses indicated that $Mg_2Sn$ particles as well as $Mg_{17}Al_{12}$ particles precipitated mainly along the solidification cell boundaries; the volume fraction of these hard particles increased as the amount of added Sn increased, with increased the strength. From in situ fracture observations of the AZ51-7Sn alloy, coarse precipitates located on the cell boundaries worked as easy crack propagation sites and caused abrupt intercellular fracturing. On the other hand, the overall fracture properties of the AZ51-3Sn alloy improved because crack propagation proceeded into the Mg matrix rather than into the cell boundaries as twins developed actively, as confirmed by an R-curve analysis. These findings suggest that the addition of 3~5 wt.% Sn is effective in improving both the tensile and fracture properties on the basis of well-developed twins, the blocking of crack propagation, and crack blunting.

• Korean Journal of Metals and Materials
• /
• v.50 no.9
• /
• pp.697-702
• /
• 2012

In this study, unidirectional and plain woven carbon fiber reinforced magnesium matrix composite laminates were fabricated by the liquid pressing infiltration process, and evolutions of the microstructure and compressive strength of the composite laminates under corrosion were investigated by static immersion tests. In the case of the unidirectional composite laminate, the main microstructural damage during immersion appeared as a form of corrosion induced cracks, which were formed at both CF/Mg interfaces and the interfaces between layers. On the otherhand, wrap/fill interface cracks were mainly formed in the plain woven composite laminate, without any cracks at the CF/Mg interface. The formation of these cracks was considered to be associated with internal thermal residual stress, which was generated during cooling after the fabrication process of these materials. As a consequence of the corrosion induced cracks, the thickness of both laminates increased in directions vertical to the fibers with increasing immersion time. With increasing immersion time, the compressive strengths of both composite laminates also decreased continuously. It was found that the plain woven composite laminates have superior corrosion resistance and stability under a corrosive condition than unidirectional laminates.

• Textile Coloration and Finishing
• /
• v.34 no.2
• /
• pp.109-116
• /
• 2022

Tire codes are made of materials such as hemp, cotton, rayon, nylon, steel, polyester, glass, and aramid are fiber reinforcement materials that go inside rubber to increase durability, driveability, and stability of vehicle tires. The reinforcement of the tire cord may construct a composite material using tires such as automobiles, trucks, aircraft, bicycles, and fibrous materials such as electric belts and hoses as reinforcement materials. Therefore, it is essential to ensure that the adhesive force between the rubber and the reinforced fiber exhibits the desired physical properties in the rubber composite material made of a rubber matrix with reinforced fibers. This study is a study on the heat treatment conditions for improving the adhesion strength of the tire cord and the reinforced fiber for tires. The core technology of the drying process is a uniform drying technology, which has a great influence on the quality of the reinforcement. Therefore, the uniform airflow distribution is determined by the geometry and operating conditions of the dryer. Therefore, this study carried out a numerical analysis of the shape of a drying nozzle for improving the performance of hot air drying in a dryer used for drying the coated reinforced fibers. In addition, the flow characteristics were examined through numerical analysis of the study on the change in the shape of the chamber affecting drying.

• Journal of the Semiconductor & Display Technology
• /
• v.21 no.4
• /
• pp.33-38
• /
• 2022

With an attempt to suppress the moiré phenomenon caused by the interference between the black matrix of a display panel and the metal grid of a camera, we have fabricated an anti-moiré filter using light diffusing particles (LDPs) with the average diameter of 20 ㎛. It is demonstrated that the anti-moiré filter coated on a glass substrate (370 mm × 470 mm) using a table slot-die coater reduces the moiré intensity to a great extent when the area covered by LDPs is 50%. To quantify the intensity of moiré phenomenon, we have measured the lightness ratio and found that it is reduced from 132.12 down to 105.71 by the filter. To find the optimum area covered by LDPs, we have performed ray tracing simulations using Mie scatters as a substitute for LDPs. From the simulated irradiation distribution, we have calculated the standard deviation (SD) and contrast ratio (CR) to evaluate the moiré strength. As expected, the SD and CR values decrease with increasing covered area by LDPs. However, there exists a trade-off between the transmittance of the filter and its capability of reducing the moiré intensity in determining the area covered by LDPs.

• Journal of the Korean Institute of Gas
• /
• v.5 no.2 s.14
• /
• pp.14-21
• /
• 2001

In order to investigate the damage mechanism of the coupler transferring LPG, microstructural observation and chemical analysis of the couplers operated for the long time in the LPG stations and virgin 6/4 forged-brass corrosion-tested were conducted. Their microstructure was consisted of two phases that bright $\beta$ precipitates were irregularly dispersed in $\alpha$ matrix. The chemical compositions of oxide layer on the surface of the used coupler were composed of S, C, O, Al, Si, etc. as well as Cu and Zn. In environmental corrosion tests of both $10\%$ HCl and Mattsson solutions, no apparent deviations in mechanical impact strength of forged-brass was observed. While, in U-bend stress corrosion cracking specimen, some microcracks were observed.

• Elastomers and Composites
• /
• v.42 no.4
• /
• pp.224-231
• /
• 2007

Polyurethane (PU) was prepared with the compositions of polytetramethylene glycol (PTMG) having two different molecular weight (250, 1000 g/mol). The optimum composition of PTMG 250/1000 was 60/40 based on the mechanical properties. PU/organoclay nanocomposites were prepared with several kinds of organoclay. The mechanical properties of nanocomposite prepared with 93A were considerable. The improvement in tensile strength and modulus for PU/organoclay nanocomposite with the application of ultrasound compared to the PU/organoclay nanocomposite without the application of ultrasound was factors of 1.2, and hardness (shore A type) increased from 90 to 95. The difference in thermal degradation was not observed. The results of transmission electron micrographs and X-ray measurements suggest that the intercalated organoclay in PU matrix was observed.