• 소성∙가공
• /
• 제24권4호
• /
• pp.287-292
• /
• 2015

The possibility of chemical precipitation for recycled ammonium paratungstate (APT) was studied. WO₃ particles were synthesized by chemical precipitation method using a 1:2 weight ratio of APT:DI-water. At the 500℃ sintering temperature, the X-ray diffraction results showed that APT completely decomposed to WO₃. For the granulated powder WC-Co, vacuum heat treatment at proper temperatures increases tap density and flow-ability. Hardness of the WC-Co thermal spray coating layer was measured in the range HV 831~1266. Spray conditions for the best characteristic values were an oxygen flow rate=1500 scfh, a fuel flow rate = 5.25gph and a gun distance = 320mm.

• 한국생산제조학회지
• /
• 제24권1호
• /
• pp.23-30
• /
• 2015

The scanning quality can be influenced by reflective abilities of a surface. Transparency and glossiness of a surface can highly limit the scanning results. Various techniques have been developed to solve problems of reflective and transparent surfaces. As one of the most feasible and convenient solutions, a thin layer of coating with proper specifications is sprayed on surface for eliminating the problems of the surfaces. As the main goal is to keep the object geometry unchanged, then it is important to coat the surface with layers less than one micrometer in thickness. For this purpose, a newly designed atomization-based spray system has been developed and tested in sets of experiments to study its efficiency on scanning results while objects with the surface are in use. This paper presents the spray design process and then studies and compares the 3D scanning results of the surfaces coated with atomization-based and aerosol sprays.

• Journal of Welding and Joining
• /
• 제33권1호
• /
• pp.49-53
• /
• 2015

An experimental study was conducted to investigate the effect of carbon nanotubes on the zinc corrosion resistance of sealing layer formed on the Tungsten Carbide spray coating. Using the nanotubes, a sealing agent in the form of solid-liquid suspensions was made and applied to the surface of spray coating. A series of experiments, consisted of three stages such as preparation of test piece, molten-pot immersion test, and evaluation of micro structure, were undertaken to demonstrate complicated interaction existing between zinc ions and sealing layer containing the nanotubes. Experimental results showed newly developed sealing layer were less susceptible to corrosion and thus coated layer was well protected even in the case of 10 days exposure. Comparison of the micro structure after molten pot test also indicated that carbon nanotubes still remained in the matrix and organized more reliable frame work constituted with boron nitride and chromium compound. It was revealed that carbon nanotubes in the sealing layer played positive role to enhance zinc corrosion resistance in the perspective of both fibrous structure and inherent chemical stability.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2011년도 춘계학술대회 및 Fine pattern PCB 표면 처리 기술 워크샵
• /
• pp.196-197
• /
• 2011

Rudder, one of the most important component in the marine vessel, is now being decreased life time to serve due to cavitation erosion, vortex current, high flow speed suffer from ship speed going up dramatically. In this study, 10 kinds of thermal spray coating materials(2 of Zn alloy series, 3 of Al alloy series, 3 of Cu alloy series, 2 of STS alloy series) are chosen to apply on specimens and analyze micro structure, metallic composition, properties(porosity, oxidation) by using visual observation, XRD, EDX etc.. Additionally, to refine the characteristic of corrosion endurance for thermal spray coating layer, compared with thermal spray process and 5 kinds of heavy duty painting and AC paint (Anti-Corrosion Paint). Based on above mentioned experimental results, a priority of all coated specimens on corrosion-erosion endurances finalized and summarized there by desirable composition and process of thermal sprayed material properly.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 봄 학술논문 발표대회
• /
• pp.59-60
• /
• 2022

When a metal sprayed film of several hundred ㎛ on the concrete surface is possible to 80 dB of shielding effect electromagnetic waves (ElectroMagnetic Pulse, EMP). Therefore, in this study, as a way to secure EMP shielding performance by applying a metal spray coating showing excellent EMP shielding performance to a concrete structure, the metal spray welding efficiency and thin film adhesion performance according to the concrete spray direction and surface treatment method were evaluated. Metal sprayed efficieny according to the metal spraying direction and method was confirmed that the difference was insignificant by applying the roughening agent. However, the method of strengthening the concrete surface and applying the sealing agent show maximum adhesion strength of 3.98 MPa compared to other methods, and it is judged that this method can be utilized for the metal spraying method for concrete EMP shielding.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1997년도 제26회 추계학술대회
• /
• pp.183-190
• /
• 1997

The wear behaviors of $Al_2O_3-40%TiO_2$ deposited on casting aluminum alloy(ASTM A356) by plasma spray against SiC ball have been investigated experimentally. Friction and wear tests are carried out at room temperature. The friction coefficient of $Al_2O_3-40%TiO_2$ coating is lower than that of pure $Al_2O_3$ coating(APS). It is found that low friction correspond to low wear and high friction to high wear in the experimental result. The thickness of $Al_2O_3-40%TiO_2$ coatings indicated the existence of the optimal coating thickness. It is found that a voids and porosities of coating surface result in the crack generated. As the tensile stresses in coating increased with the increased friction coefficient. The columnar grain of coating will be fractured to achieve the critical stress. It is found that the cohesive of splats and the porosity of surface play a role in wear characteristics. It is suggested that the mismatch of thermal expansion of substrate and coating play an important role in wear performance. Tensile and compressire under thermo-mechanical stress may be occurred by the mismatch between thermal expansion of substrate and coating. This crack propagation above interface is observed in SEM.

• 한국표면공학회지
• /
• 제26권2호
• /
• pp.55-62
• /
• 1993

The effect of interlayer coating thickness of Ni and Ti on corrosion behavior was studied for TiN ion plat-ed steel plate. Interlayer coating was carried out in a single and bi-layer to a various thickness combination prior to final TiN coating. Corrosion behavior was evaluated by anodic polarization test in 1N H2SO4 as well as salt spray test. Ni interlayer coating was effectived in reducing corrosion current density of active region and Ti interlayer coating over Ni coating reduced the anodic corrosion current density by an order of 4 with increasing the thickness of Ti up to$ 3\mu\textrm{m}$. The improvement of corrosion resistance by Ni/Ti interlayer coating was attributed to the effective prevention of penetration of active corrosion agent resulting from the inherent corrosion resistance of Ni and Ti. Putting corrosion behavior was observed from salt spray test result for all specimens and corrosion resistance at salt atmosphere was enhanced with increasing Ni and Ti thickness, Cor-lay TiN coating was spalled out by the generation of corrosion products.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2022년도 가을 학술논문 발표대회
• /
• pp.81-82
• /
• 2022

Al and Zn are used to protect the steel structures from corrosion. In the present studies, 15Al-85Zn alloy wires has been used for the deposition of coating by arc thermal spray process. Moreover, this process of coating exhibited severe defects formation, therefore, this coating was post-treated with different concentrations i.e. 0.05, 0.1 and 0.5M sodium hexa meta phosphate (Na6[(PO3)6]: SHMP) to fill to defects of deposited coatings and assessed their corrosion resistance in 3.5 wt.% NaCl solution with exposure periods. After the treatment, the porosity of the coating reduced significantly by formation of composite oxide films onto the coating surface. Initially, 0.5 M SHMP treated coating exhibited highest in total impedance due to significant reduction of porosity but once the exposure periods are extended, the composite oxides are dissolved, thus, total impedance is decreased.

• 한국산학기술학회논문지
• /
• 제15권1호
• /
• pp.32-38
• /
• 2014

본 연구에서는 해수용 열교환기 적용을 위한 열분사 코팅의 침지부식 특성 및 열확산율을 조사하기 위해 실험이 수행되었다. 코팅은 아연과 알루미늄을 열분사 코팅한 뒤 실리콘 및 에폭시 수지를 추가 도포한 총 8개의 시편이며 이를 $70^{\circ}C$ 3.5%w NaCl 수용액에 2주간 침지하여 침지 전후의 부식특성 변화를 관찰하였다. 코팅의 부식특성 변화를 관찰하기 위하여 AC 임피던스 측정, SEM 촬영 등을 진행하였으며 레이저 확산법을 이용하여 침지 전후의 열확산율을 측정 및 비교하였다. 침지실험 결과로부터 실리콘 및 에폭시가 추가된 코팅 시편은 표면에 블리스터가 생성되지 않았으며 이에 실러 추가 코팅에 따른 내부식성 향상효과가 있는 것으로 확인되었다.

• Korean Chemical Engineering Research
• /
• 제49권6호
• /
• pp.710-714
• /
• 2011

본 연구에서는 열 플라스마 용사 코팅 법을 사용하여 고체산화물 연료전지에서 사용되는 $La_{0.8}Ca_{0.2}CrO_{3}$(LCC), $La_{0.8}Sr_{0.2}CrO_{3}$(LSC), $La_{0.8}Ca_{0.2}CrO_{0.9}Co_{0.1}O_{3}$(LCCC) 세라믹 연결재를 코팅하여 코팅 층의 특성평가를 수행하였다. 열 플라즈마 코팅에 앞서 각 세라믹 연결재 입자의 특성평가를 위해 X선 회절, 미세 구조, 입자 측정 및 비표면적 분석을 수행하였다. 세라믹 연결재 입자의 특성평가 후, 열 플라스마 용사 코팅 법을 사용하여 연료극 지지체 위에 코팅하였으며, 코팅 층의 특성을 평가하기 위해 코팅 층의 표면, 파단면 분석, 가스 누출 속도 및 전기 전도도 측정을 수행하였다. 이러한 특성 평가 결과를 바탕으로 열 플라스마 용사 코팅 법을 통해 코팅된 LCCC 코팅 층이 고체산화물 연료전지의 세라믹 연결재로서 적합함을 확인하였다.