• Journal of Korea Foundry Society
• /
• v.31 no.3
• /
• pp.130-136
• /
• 2011

Effects of GBF (gas bubbling filtration) treatment conditions and scrap ratio on the electric conductivity of a commercial pure aluminum for diecasting were investigated using by specific gravity and electrical conductivity measurement system, hydrogen gas analyzer, XRD, and EDS. Electrical conductivities of specimen mixed Al scrap ratio until 60% from 0% were decreased with increasing the precipitates amount and size of AlFeSi ternary intermetallic compound on the grain boundary as well as amount of porosity in the grain. On the other hand, electrical conductivities was reincreased gradually in spite of scrap ratio increase from 80% to 100%. Size of AlFeSi compound formed on the grain boundary were coarsened with the increament of scrap ratios untill 80% and GBF treatment time simultaneously.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.9 no.6
• /
• pp.71-77
• /
• 2010

Although the problems of defects and nonmetallic inclusion in metal fatigue are very complicated, it is particularly important to view these problems from the perspective that defects and inclusions are virtually equivalent to small cracks. This concept will help one to understand various fatigue phenomena caused by Ductile Cast Iron. For different ferrite-pearlite matrix structure, containing more than 90% spheroidal ratio of graphite, GCD 45-3, GCD 50, GCD 60 series and 70%, 80%, 90% spheroidal ratio of graphite, GCD 40, GCD 45-1, GCD 45-2 series, this paper has carried out image analyzer, estimated maximum and mean size of graphite, investigated correlation. It was concluded as follows. (1) A good quality of Ductile cast iron using in this experiment, the graphite was separated well. The effect of the interaction by graphite was verified by microscopic observation and by fracture mechanics investigation in surface, interior of the specimen. (2)${\sqrt{area}}_{max}$ of graphite can be used to predict fatigue limit of Ductile Cast Iron. The Statistical distribution of extreme values of ${\sqrt{area}}$ may be used as a guide line for the control of inclusion size in the steel making processes.

• Fisheries and Aquatic Sciences
• /
• v.26 no.3
• /
• pp.224-233
• /
• 2023

This research was conducted at Langgur City, Southeast Maluku Regency, Maluku Province, Eastern Indonesia from November 2020 to February 2021 to study biological aspects of roundscads (Decapterus spp.) which consist of species composition, sex ratio, gonad maturation level, size distribution, length-weight relationship and condition factor. Samples were collected at traditional fish market in Langgur City. Fish samples collected at the market were put into cool box and then brought to the laboratory for further examination. Fish samples were identified, separated based on species, dissected to determine their sex and gonad maturation stage and then measured. Totally, there were 290 specimen collected which consist of five species namely Decapterus kurroides, D. macarellus, D. macrosoma, D. muroadsi and D. russelli. Sex ratio between male and female for all species showed 1:1. Gonad maturation level showed that stage I and II have higher percentage than stage III and IV indicates immature fish more dominant compare to mature one. Among five species found, D. macarellus has larger size while the smaller belongs to D. muroadsi. Results of length-weight relationship analysis showed that roundscads inhabiting Southeast Maluku waters have isometric and negative allometric growth pattern with relative condition factor around 1.00.

• Transactions of Materials Processing
• /
• v.33 no.3
• /
• pp.178-184
• /
• 2024

In this study, we investigated the effects of extrusion ratio and extrusion temperature on the microstructure and tensile properties of extruded Mg-6Al-0.3Mn-0.3Ca-0.2Y (SEN6) alloy. As the extrusion ratio and temperature increase, dynamic recrystallization during extrusion is promoted, leading to the formation of a fully recrystallized microstructure with increased grain size. Additionally, the increases in extrusion ratio and temperature lead to texture strengthening, exhibiting a higher maximum texture intensity. The extruded materials contain three types of secondary phases, i.e., Al₈Mn₄Y, Al₂Y, and Al₂Ca, with irregular or polygonal shapes. The quantity, size, distribution, and area fraction of the second-phase particles are nearly identical between the two materials. Despite its larger grain size, the tensile yield strength of the material extruded at 450 ℃ and an extrusion ratio of 25 (450-25) is higher than that of the material extruded at 325 ℃ and an extrusion ratio of 10 (325-10), which is mainly attributed to the stronger texture hardening effect of the former. The ultimate tensile strength is similar in the two materials, owing to the higher work hardening rate in the 325-10 extrudate. Despite differences in grain size and recrystallization fraction, numerous twins are formed throughout the specimen during tensile deformation in both materials; consequently, the two materials exhibit nearly the same tensile elongation.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.10 no.6
• /
• pp.42-47
• /
• 2001

In this study, fatigue limit of ductile cast iron is evaluated based on phenomena of the microscopic observation, such as matrix structure, spheroidal ratio, size of graphite and distribution. Three different ferrite-pearlite matrix structure, GCD 45-), GCD 50, GCD 60 series, all of which contain more than 70% spheroidal ratio of graphite, were used to obtain the correlation between maximum size of graphite and fatigue strength. It was concluded as fellows. (1) In Ductile cast iron of ferrite-pearlite matrix, the fatigue limit of GCD 60 series with 73% pearlite structure was the highest. (2) From observation of the starting point of crack of all specimens, it is noted that the crack initiates, in graphite, goes through ferrite and propagates into pearlite. (3) A good quality of Ductile cast iron used in this experiment can be checked from uniformly distributed graphite. The negligible interaction effect between graphites was verified by microscopic observation and fracture mechanics investigation in surface and interior of the specimen.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.1135-1140
• /
• 2001

The purpose of this study is to investigate the shrinkage properties of high strength concrete according to the S/A ratio at early age. The main parameters are as follows : S/A ratio is 30, 35, 38, 41, 45%, W/B ratio 24.9%, SF/B ratio 8%. FA/B 15%. The size of specimen is l0$\times$10$\times$40cm and the shrinkage is measured by the embedded gage at each end of the specimens. From the test, it was found that the slump-flow of concrete was high, and also autogenous shrinkage increased and drying shrinkage decreased as S/A ratio increased.

• Preventive Nutrition and Food Science
• /
• v.3 no.3
• /
• pp.292-294
• /
• 1998

Surimi sol and gel were prepared by mixing egg albumin, starch, oil and carrageenan, which are used as representative ingredients in the surimi composite, at different ratio. Structural properties in surimi composite were investigated by examining the phase changes and dispersion pattern (average particle size, size range and the averge number of particle) of the particulate ingredients in sol and gel with an image analyzer. A staining technique of the specimen containing egg albumin in surimi gel was developed by adjusting pH of a toluidine staining solution. Image analysis revealed that size and density of ingredient particles were function of the level and dispersion of ingredients except of starch-incorporated surimi gel which showed maximum particle size at 6%.

• Journal of the Korean Geosynthetics Society
• /
• v.13 no.2
• /
• pp.49-57
• /
• 2014

In this study, in order to take advantage of samples collected in the Jangbogo station, and to grasp the liquefaction resistance characteristics of the dynamic load was performed cyclic triaxial test. Also, through the comparison with the existing literature. The test results, for the relationship between number of cycles for the same cyclic shear stress ratio and the cyclic shear stress ratio to produce an axial strain of 5%, in all samples, the cyclic shear stress ratio to liquefaction for the specimen, which has been liquefied, was increased, whereas number of cycles were reduced. The cyclic shear stress ratio of samples first decrease up to the fine content of about 10%. After this strength level, there is a little increase in cyclic shear stress ratio with increasing fine content. In addition, the cyclic shear stress ratio between cohesive strength, mean particle size, and friction angle decrease but some time later, there was a tendency that cyclic shear stress ratio is a little increased.

• Journal of the Korean Society for Precision Engineering
• /
• v.19 no.12
• /
• pp.127-133
• /
• 2002

The objective of this study is to investigate fatigue life and fatigue crack propagation behavior The experiment of fatigue life for MMC have been carried out for the stress ratio R＝0.1 at 20Hz. Fatigue lift limit of AC4CH alloy is about 70 ㎫ and Fatigue limit of MMC has been increment to 120 ㎫, therefore, fatigue limits of MMC is about 71 % higher than that of AC4CH alloy Crack propagation tests on half-size CT specimen of thickness 12.5mm were conducted by using sinusoidal waveform. The crack length was monitored by compliance method. Test conditions were at 0.1 and 0.05 of load ratio at 10Hz of loading frequency and test load was 2.3kN. The effects of stress ratio on the fatigue crack propagation behavior for MMC was discussed within the Paris law. As the results of this study, Fatigue crack propagation increased with increasing the load ratio.

• Advances in concrete construction
• /
• v.12 no.5
• /
• pp.399-409
• /
• 2021

The existing method to improve the coordination performance of the inner and outer parts of concrete-encased concrete-filled steel tube (CFST) composite columns by increasing the volume-stirrup ratio causes difficulties in construction due to over-dense stirrups. Thus, this paper proposes an open polygonal composite stirrup with high strength and high ductility CRB600H reinforced rebar, and seventeen specimens were constructed, and their axial compressive performance was tested. The main parameters considered were the volume-stirrup ratio, the steel tube size, the stirrup type and the stirrup strength. The test results indicated: For the specimens restrained by open octagonal composite stirrups, compared with the specimen of 0.5% volume-stirrup ratio, the compressive bearing capacity increased by 14.6%, 15.7% and 21.5% for volume-stirrup ratio of 0.73%, 1.07% and 1.61%, respectively. For the specimens restrained by open composite rectangle stirrups, compared with the specimen of 0.79% volume-stirrup ratio, the compressive bearing capacity increased by 7.5%, 6.1%, and -1.4% for volume-stirrup ratio of 1.12%, 1.58% and 2.24%, respectively. The restraint ability and the bearing capacity of the octagonal composite stirrup are better than other stirrup types. The specimens equipped with open polygonal composite stirrup not only had a higher ductility than those with the traditional closed-loop stirrup, but they also had a higher axial bearing capacity than those with an HPB300 strength grades stirrup. Therefore, the open composite stirrup can be used in practical engineering. A new calculation method was proposed based on the stress-strain models for confined concrete under different restrain conditions, and the predicted value was close to the experimental value.