• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.86-94
• /
• 2000

This study was performed to investigate types and formation mechanism of cracks in two Al alloy welds, A5083 and A7N01 spot-welded by pulse Nd : YAG laser, using SEM, EPMA and Micro-XRD. In the weld zone, three types of crack were observed : center line crack({TEX}$C_{C}${/TEX}), diagonal crack({TEX}$C_{D}${/TEX}), and U shape crack({TEX}$C_{U}${/TEX}). Also, HAZ crack({TEX}$C_{H}${/TEX}) was observed in the HAZ region, furthermore, mixing crack({TEX}$C_{M}${/TEX}) consisting of diagonal crack and HAZ crack was observed. White film was formed at th hot crack region in the fractured surface after it was immersed to 10% NaOH water. In the case of A5083 alloy, white films in {TEX}$C_{C}${/TEX} crack and {TEX}$C_{D}${/TEX} crack region were composed of low melting phases, {TEX}$Fe_{2}SiAl_{8}${/TEX} and eutectic phases, $Mg_2$Al$_3$ and $Mg_2$Si. Such films observed $CuAl_2$, {TEX}$Mg_{32}(Al,Zn)_{3}${/TEX}, MgZn$_2$, $Al_2$CuMg and $Mg_2$Si were observed in the whitely etched films near {TEX}$C_{C}${/TEX} crack and {TEX}$C_{D}${/TEX} crack regions. The formation of liquid films was due to the segregation of Mg, Si, Fe in the case of A5083 alloy and Zn, Mg, Cu, Sim in the case of A7N01 alloy, respectively. The {TEX}$C_{C}${/TEX} and {TEX}$C_{D}${/TEX} cracks were regarded as a result of the occurrence of tensile strain during the welding process. The formation of {TEX}$C_{M}${/TEX} crack is likely to be due to the presence of liquid film at the grain boundary near the fusion line in the base metal as well as in the weld fusion zone during solidification. The {TEX}$C_{U}${/TEX} crack is considered a result of the collapsed keyhole through incomplete closure during rapid solidification.

• Laser Solutions
• /
• v.4 no.1
• /
• pp.39-48
• /
• 2001

This study was performed to evaluate basic characteristics of electron beam weldability for high strength aluminum alloys. The aluminum alloys used were A5083 and A6N01, and A7N01. The principal welding process parameters, such as accelerating voltage, beam current, welding speed and chamber pressure were investigated. The dimension and microstructure of welds were evaluated with OLM, and SEM (EDAX). In addition, weldability variation(cracking) due to process parameters was also evaluated. The degree of cracking in the EB fusion zone appears to be affected mainly by aspect ratio, such that as aspect ratio increases the cracking tendency also increases. The alloying element itself may also affect the hot cracking resistance, but its role is considered to be indirect effect such that the relatively higher vaporization pressure elements of Zn and Mg give deeper weld penetration and thus results in greater cracking tendency.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.1
• /
• pp.16-23
• /
• 1997

Stainless steel are widely applicable in various engineering fields for its exellent corrosion and impact ressistance. Austenitic weld metal has some ferrite for preventing solidification cracking by ASME specification. Several family of austenic stainless steel contains varying ferrite contents. But ferrite in austenic stainless steels is adversely affect weld metal toughness and since fully austenic grades are known to have good toughness. Austenic stainless steel has various alloying addition for improving corrosion resistance, impact toughness and solidification crack resistance. The effect of various alloying elements are not found to be clear in present. From this view of point, this study tried to establish the criteria of alloy design for austenic stainless steel by controlling primary solidification mode and clarifying the effect of several alloying elements.

• Journal of Welding and Joining
• /
• v.30 no.3
• /
• pp.57-65
• /
• 2012

The interest of austenitic heat resistant stainless steels containing high Si has increased because they have higher resistance of oxidation and higher strength at high temperature than STS 310. This study carried out Varestraint test for evaluation of solidification cracking sensitivity of 14 different stainless steels. As a result of Varestraint test, all specimens solidified as primary ferrite, and solidification crack sensitivity increased with adding $N_2$ to shielding gas. Nb and W had beneficial effect on solidification crack resistance in case of less than FN 2 containing, but crack sensitivity increased with Nb and W in case of more than FN 2. Ce had beneficial effect on solidification crack resistance but impaired weld bead appearance.

• Journal of Welding and Joining
• /
• v.32 no.6
• /
• pp.41-46
• /
• 2014

In this study, cracking susceptibility of laser cladding was investigated according to the processing parameters such as laser power, scan speed and feeding rate with blended powders of stellite#6 and technolase40s (WC+NiCr). The solidification microstructure of clad was composed of Co-based dendrite structures with ${\gamma}+Cr7C3$ eutectic phases at the dendritic boundaries. The crack propagation showed transgranular fracture along dendritic boundaries due to brittle chrome carbide at the eutectic phases. From results of fractography experiments, the fracture surface was typical cleavage brittle fracture in the clad and substrate. The number of clad cracks, caused by a tensile stress after the solidification, increased with increase of laser power, scan speed and feeding rate. Increase of the laser power caused large pores by facilitating WC decarburizing reaction. And the pores affected increase of crack susceptibility. High scan speed caused increment of clad cracks due to thermal stress and WC particle fractures. Also, increase of the feeding rate accompanied an amount of WC particles causing crack initiation and decarburizing reaction.

• Journal of Welding and Joining
• /
• v.21 no.5
• /
• pp.540-546
• /
• 2003

Recently Al alloys are being used gradually for structural materials of transports. In welding of Al alloys used for transports, good weldabilities as well as adequate mechanical properties of the welds should be ensured as structural materials. In this study, the welds formation, macro and microstructural characteristics, generation of defects and hardness distribution in welds of Al alloys of 5083, 6N01 and 7N01 by DCSP- and AC-GTA welding process, were investigated. The deeper penetration was obtained in all welds of the alloys by DCSP-GTAW with He gas, compared with those by using AC-GTAW. The 6N01 alloy showed high susceptibilities to solidification cracking in weld metal and liquation cracking in HAZ of the welding beads of both DCSP- and AC-GTAW process. The cracking ratio of 6N01 alloy was increased with increasing of welding current. The porosity ratios in weld metal of all alloys used were extremely low including all welding conditions of DCSP-GTAW. However, in AC-GTAW process, the porosity ratios of the welds using Ar gas showed much higher values than those using He gas.

• Proceedings of the KWS Conference
• /
• v.43
• /
• pp.85-87
• /
• 2004

• Proceedings of the KWS Conference
• /
• 2000.04a
• /
• pp.60-63
• /
• 2000

• Proceedings of the KWS Conference
• /
• 2003.11a
• /
• pp.98-100
• /
• 2003

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2000.02a
• /
• pp.101-103
• /
• 2000

In the present work, we have investigated the combined effect of high-energy milling and Agb addition on microstructure and superconducting properties for Bi-2223/Ag. tape. The addition of siver plays an important role in enhancing liquid phase formation, Resulting in densification and cracking during solidification. Further study is needed for the optimization of Ag content and heat-treatment which can reduce the cracking.