• Journal of the Korean Wood Science and Technology
• /
• v.39 no.2
• /
• pp.148-155
• /
• 2011

Thermal treatment techniques are used for modifying wood and wood-based materials to improve dimensional stability and hygroscopicity. This study investigated the effects of press pressure and temperature on density, vertical density profile, thickness swelling and surface hardness of eucalyptus wood boards. The experimental wood boards were prepared from Turkish River Gum ($Eucalyptus$ $camaldulensis$ Dehn.). The surface hardness value increased with increasing press pressure in the treated groups. The application of a higher pressure at the same temperature level increased the amount of swelling of wood. It means that it is not needed for application of higher pressure to enhance the dimensional stability of wood. It is expected that it is possible to produce increased hardness, dimensional stability and durability by application of hot pressing treatment. This research showed that different press pressure and temperature values should be used to improve the performance properties of eucalyptus wood so that the end-use of the wood materials could be expanded.

• Journal of the Korean Wood Science and Technology
• /
• v.23 no.2
• /
• pp.70-76
• /
• 1995

Research was conducted at the Wood Materials and Engineering Laboratory, Washington State University, Pullman, WA to evaluate the effects of the sequence of wax addition, wax level, and wax type on mechanical properties and water resistance performance of isocyanate-bonded particleboard. Mechanical properties and water resistance performance were not influenced significantly by the sequence of wax addition. Internal bond and wet modulus of rupture in bending strength were decreased significantly by increasing the wax emulsion level, but dry modulus of rupture and modulus of elasticity in bending strength were not decreased significantly by increasing the wax emulsion level. Dry internal bond, dry and wet moduli of rupture, and modulus of elasticity were not decreased by increasing the solid wax level except for wet internal bond. The addition of 1.0 and 1.5% wax level did not produce any significant additional water resistance effect when compared to the addition of 0.5% wax level. Internal bond values of boards with solid wax addition showed significantly better results than boards with just a wax emulsion added. Modulus of rupture, modulus of elasticity, and water resistance performance did not show significant difference between solid wax and wax emulsion.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.1
• /
• pp.29-36
• /
• 2009

Recycling of wood wastes or residues is a good solution for a shortage of wood resources and a rise in the price. Shipbuilding wood wastes were almost used to produce the boards by milling. However, considering the economic value and insufficient resource, recycling with milling is dissatisfied method. This study has been carried out to investigate the recycling possibility of shipbuilding wood waste. There are two kinds of shipbuilding wastes: plywood waste and solid waste. From the results of this study, the following conclusions have been made: 1. Bending properties of plywood and laminated plywood lumber were tested by Korean Standard. 2. The main fracture mode of plywood waste and laminated plywood lumber is that of simple tension. 3. The recommended application for the recycling of shipbuilding wood waste are outdoor wood furnishings, indoor wood furnishings and some wooden building construction materials: interior raw material, wooden pallet, siding, paneling, flooring. picnic table, deck components, porch swing, landscaping timbers, residential fencing, patios, and boardwalks etc.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.4
• /
• pp.388-396
• /
• 2009

In our study, the potential of okara as an ingredient of new bio-based adhesives was investigated for the production of fancy-veneered flooring boards. Okara was hydrolyzed by 1% sulfuric acid solution (AC) and 1% sodium hydroxide solution (AK). Phenol formaldehyde (PF) prepolymers were prepared as a cross-linker of okara hydrolyzates. Then, okara-based adhesive resins were formulated with 35% AC, 35% AK and 30% PF prepolymer on solid content basis. The adhesive resins were applied on high-density fiberboards (HDF) with the spread rate of $300g/m^2$. After that, oak fancy veneers are covered on the HDF, and then pressed with the pressure of $7kg/m^2$ at $120^{\circ}C$. The experimental variables were three mole ratios of formaldehyde to phenol (1.8, 2.1, 2.4), three assembly time (0, 10, 20 min), and two press time (90 sec, 120 sec), respectively. The fancy-veneered high-density fiberboards were tested by dry tensile strength, glueline failure by wetting and formaldehyde emission. Tensile strength of the boards exceeded the requirement of KS standard. The formaldehyde emissions were approached at the E0 level specified in KS standard. Based on these results, okara can be used as an ingredient of environmentally friendly adhesive resin systems for the production of flooring boards.

• Journal of the Korean Wood Science and Technology
• /
• v.17 no.1
• /
• pp.55-68
• /
• 1989

This experiment was carried out to investigate the crack of coated Nitrocellulose Lacquer on flatand edge-grained boards of Quercus acutissima, ring-porous wood, and Betula platyphylla var. japonica, diffuse-porous wood, by variations of moisture contents at 7, 13 and 21%. Cold check system was used as an accelerating method for crack development, in which one cycle of the system consisted of 10 replications of each unit cycle, $60^{\circ}C$ for 4hr followdd by $-20^{\circ}C$ for 4hr. The analysis of Nitrocellulose Lacquer characteristics was made by means of water permeation measurement, F.T.I.R. spectroscopy, N.M.R. spectroscopy, gel permeation chromatography, gas chromatography, and D.S.C. The results obtained were as follows: 1. The number of cracks increased with the increasing moisture content of board. 2. The crack of coated film on flat-grained board was fewer in number than on edge-grained board. 3. The crack occurred in Quercus acutissima was more numerous on edge-grained board but less frequent on flat-grained board compared with that in Betula platyphylla var. japonica, respectively. 4. The cold crack vertically developed to the grain both in Quercus acutissima and Betula platyphylla var. japonica. 5. Water permeability in intermediate coated film was lower than in under and top coated film, but the difference was not confirmed between under and top coated film.