• Bulletin of the Korean Chemical Society
• /
• 제33권12호
• /
• pp.4173-4179
• /
• 2012

From Neungsalli Temple located in Buyeo, ancient glass vessel fragments were discovered along with hundreds of glass beads. In this research, we used SEM-EDS to analyze glass vessel fragments and beads excavated from Neungsalli Temple. Then, we analyzed their chemical composition and examined their characteristics. In particular, we investigated a relationship between glass vessels from Neungsalli temple and Hwangnamdaechong (South tomb). The result of our experiment showed that the glass artifacts from Neungsalli temple were all soda glass. To be specific, the vessel fragments were soda-lime glass and spherical beads were high-alumina soda glass. Then, we compared glass vessel fragments from Neungsalli temple to glass vessels excavated from Hwangnamdaechong. Glass vessels from both sites turned out to be soda lime glass. We classified them further based on raw material used for soda - natron and marine plant ash.

• 보존과학회지
• /
• 제28권3호
• /
• pp.205-216
• /
• 2012

아산 밖지므레 유적 마한 분묘에서 출토된 유리 65점은 포타쉬유리군이 13점, 소다유리군이 52점으로 소다유리군이 우세하게 나타났다. 색상별로 세분하면, 감청색 유리는 포타쉬유리군과 소다유리군이 공반되는 반면 자색 유리는 포타쉬유리군이고 적색, 벽색, 녹색, 금박유리는 소다유리군으로 나타났다. 감청색 유리는 안정제의 함량이 낮은 LCA계이고 이중에 소다유리는 MgO와 $K_2O$ 함량이 낮은 LMK형으로 천연탄산소다가 원료로 사용된 것으로 판단된다. 적색 유리는 균질한 유리가 LCA-B계/HMK형이고 불균질한 유리가 HCLA계/LMK형으로 각각 해양 식물 재와 천연탄산소다가 사용되었을 가능성이 있다. 벽색과 녹색 유리는 환옥이 LCA-A계/LMHK형이고 연주옥이 LCA-B계/HMK형으로 형태에 따라 차이를 보인다. 금박구슬은 19.9~22.6K의 순도를 갖는 금박과 HCLA계/LMK형의 소다유리로 제작되었다. 즉, 아산 밖지므레 유적 유리구슬 대부분은 백제시대 타 유적에서 확인되는 유리 조성과 유사성이 높은 편이나 벽색 및 녹색 연주옥과 일부 적색 환옥은 다른 화학 조성을 보이므로 원료에 차이가 있음을 알 수 있다. 이와 같은 특성은 고대유리의 교역 체계 이해를 위한 중요한 단서를 제공할 것으로 기대된다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2008년도 International Meeting on Information Display
• /
• pp.373-376
• /
• 2008

New glass compositions for lead free, low temperature sealing glass frit was examined in $ZnO-V_2O_5-P_2O_5$ glass system which can be used sealing material for PDP to be made of soda lime glass substrates. Among many glass compositions, KFS-C glass showed low glass transition point (Tg) and good fluidity and adhesion characteristics when it was tested by flow button method at low temperature of $420^{\circ}C$. Its Tg was $317^{\circ}C$ and thermal expansion coefficient (CTE) was $70{\times}10^{-7}/K$. The glass frit was mixed with an organic vehicle to make a paste and it was dispensed and sealed with soda lime glass substrates at $420^{\circ}C$ for 10min. Sealed glass panels also showed good adhesion strength even sealed at low temperature of $420^{\circ}C$.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2000년도 춘계학술발표대회 논문집
• /
• pp.20-25
• /
• 2000

In order to study the impact fracture behavior of brittle materials, a steel-ball-impact experiment was Performed. Five kinds of materials were used in this study : soda-lime glass plates, glass/epoxy prepreg-one layer-bonded and unbonded glass plates, glass/epoxy prepreg-three layers-bonded and unbonded glass plates. Fracture patterns, the maximum stress and absorbed fracture energy were observed according to various impact velocities 40-120m/s. With increasing impact velocity, ring crack, cone crack, radial crack and lateral crack took place in the interior of glass plates. The generation of such cracks was largely reduced with glass/epoxy prepreg coating. Consequently, it is thought that the characteristics of the dynamic Impact fracture behavior could be evaluated using the absorbed fracture energy and the maximum stress measured at the back surface of glass plates.

• 한국산학기술학회논문지
• /
• 제5권2호
• /
• pp.98-102
• /
• 2004

단일이온교환 프로세스를 도입하여 soda-lime-silicate 유리에 있어서의 이온교환 거동 및 물성변화를 관찰하였다. 온도 및 시간 변화에 따라 K/sup +/ 이온의 침투깊이, 이온교환량은 증가하였으며, 이에 비례하여 밀도, 굴절률도 증가하는 경향을 보였다 이온교환 과정에서 생성된 비가교 산소로 인하여 400nm에서 흡수 현상이 관찰되었으며, 열팽창계수는 구조의 치밀화와 이력현상에 영향을 받았다.

• Tribology and Lubricants
• /
• 제13권4호
• /
• pp.18-25
• /
• 1997

The various deformation and fracture behaviors under light loads in soda-lime glass under sliding Vickers indentation have been studied. In soda-lime glass, deformation and fracture behaviors can be classified into four different patterns by applied load. At very light load (<0.1N), plastic deformation only occurred. At low loads (0.1~0.8N), median crack, appear. At intermediate loads (0.8~3.0N), median and lateral cracking occurred leading to a large chipping. At high loads (3.0~6.0N), a crushed zone was observed with median crack. The friction experiment finds that the increasing in the friction coefficients coincides with the onset of crushing in soda-lime glass.

• 한국재료학회지
• /
• 제20권10호
• /
• pp.524-534
• /
• 2010

Glass was fabricated using refused coal ore obtained from the Dogye coal mine in Samcheok. We additionally used soda ash and calcium carbonate to make a glass with the chemical composition of soda-lime glass, and we also used white, brown, and green glass cullet to make various kinds of colored glass. Transparent glass was fabricated by melting batch materials including refused coal ore at $1550^{\circ}C$ for 1 hr in an electrical furnace. The light transmittance and color chromaticity were measured by a UV/VIS/NIR spectrometer. Transparent glass with a light transmittance of over 80% was fabricated using normal refused coal ore and white glass cullet. Various kinds of colored glass with a light transmittance of 30-80% were fabricated using refused coal ore and brown or green glass cullet. The light transmittance of the mixed color glass samples, fabricated using normal refused coal ore and brown glass cullet and green glass cullet, indicated 30-47%, a relatively low value, in the condition of a cullet ratio of 20-50%. The characteristics of the color chromaticity of the glass samples were indicated in a chromaticity diagram by x-coordinates, y-coordinates, Y (lightness). The values of x-coordinates and y-coordinates were moved with a regular directional property according to the kind and amount of glass cullet. Therefore, we concluded that refused coal ore can be used for raw materials of color glass products like art glass and glass tile.

• 대한치과기공학회지
• /
• 제30권2호
• /
• pp.39-45
• /
• 2008

Titanium and its alloys are widely used as dental implants materials because of their excellent mechanical properties. However, the alumina and zirconia ceramics are preferred to use as the substitute of Ti implants because there is a problems in esthetics and biocompatibility in Ti implant. The the glass infiltrated alumina ceramics are studied to increase the toughness and biocompatibility. The 45S5 and soda-lime glass powder was mixed with ethanol at ratio of 1:1 and brushed on the surface of alumina. Then it was heat treated in the electric furnace at $1400^{\circ}C$ from 30 min. to 5 hours. The glass powder was controlled from 200 to $350{\mu}m$ using ball milling. After heat treatment, the glass infiltrated specimen was tested in universal testing machine to measure the bending strength. The surface microstructure of each specimen was observed with SEM. The biocompatibility of 45S5 and soda-lime glass coated alumina was investigated using PBS at $36.5^{\circ}C$ incubator. The specimen was immersed in PBS for 3, 5, 7, 10 days. After that, the surface morphology was investigated with SEM. As the results of experiment, the 45S5 bioglass infiltrated alumina show the increase of bending strength according to the increasing of heat treatment time from 30 min. to 5 hours at $1400^{\circ}C$ Finally the 1370N bending strength of alumina increased to 1958N at 5 hours heat treatment, which shows 1.4 times higher. In contrast to this, the soda lime glass infiltrated alumina ceramics shows the convex curve according to heat treatment time. Thus it shows maximum bending strength of 1820N at 1 hour heat treatment of $1400^{\circ}C$ It gives 1.3 times higher. However, the bending strength of soda lime glass infiltrated alumina is decreasing with increasing heat treatment time after 1 hour. The precipitation on the surface of 45S5 glass infiltrated alumina was revealed as a sodium phosphate ($Na_{6}P_{6}O_{24}6H_{2}O$) and the amount of precipitation is increasing with increasing of immersion time in PBS. In contrast to this, there is no precipitation are observed on the surface of soda lime glass infiltrated alumina. This implies that 45S5 glass infiltrated alumina brings more biocompatible when it is implanted in human body.

• 한국세라믹학회지
• /
• 제52권2호
• /
• pp.133-136
• /
• 2015

The outward diffusion of $Na^+$ ions in iron-bearing soda lime silicate glass via oxidation heat treatment before the ion exchange process is artificially induced in order to increase the amount of ions exchanged during the ion exchange process. The effect of the addition process is analyzed through measuring the bending strength, the weight change, and the inter-diffusion coefficient after the ion exchange process. The glass strength is increased when the outward diffusion of $Na^+$ ions via oxidation heat treatment before the ion exchange process is added. For the glass subjected to the additional process, the weight change and diffusion depth increase compared with the glass not subjected to the process. The interdiffusion coefficient is also slightly increased as a result of the additional process.

• 한국세라믹학회지
• /
• 제56권5호
• /
• pp.483-488
• /
• 2019

We studied whether chemical strengthening can heal the flaws on soda-lime silicate glass. Artificial surface cracks were introduced on the glass by sharp indentation with various loads of 0.1 to 10 N. Then, the glasses with flaws were treated by ion-exchanging in KNO₃ melt. The change in the dimension of the crack on glass was measured by a digital microscope and a scanning electron microscope. The chemical strengthening treatment enhances the strength of the glass with flaws. It is thought that the melted KNO₃ not only forms the depth of the compressed layer of 7.5 ㎛, but also heals the cracks by infiltrating them and expanding the glass on both sides of the cracks. The critical length (2c) of the cracks on soda-lime glass that can be healed by chemical strengthening is 50 ㎛ or less.