• 수산해양교육연구
• /
• 제28권6호
• /
• pp.1875-1881
• /
• 2016

The wear behavior for the two types of composites, those are epoxy matrix composites filled with silica particles and aluminium matrix composites filled with SiC particles, were compared to investigate the wear mechanism for these composites. Especially, the effect of the volume fraction for the epoxy matrix composites and the particle size for the aluminium matrix composites according to the apply load and sliding velocity were investigated. Wear tests of the pin-on-disc mode were carried out and followed by scanning electron microscope observations for the worn surface. The addition of the fillers in the composites were improved the wear resistance significantly and changed the wear mechanism for the both composites. These results were identified by the observation of the worn surface after testing.

• Composites Research
• /
• 제16권3호
• /
• pp.75-84
• /
• 2003

본 연구의 목적은 가압주조법에 의해 제조된 Saffil/Al, Saffil/$\textrm{Al}_2\textrm{O}_3$/Al, Saffil/SiC/Al 과 같은 혼합금속 복합재료의 마모 물성을 조사하고자 하는 것이다. 마모 시험은 건조와 윤활상태 하에서 pin-on-disk 형태의 마모 시험기로 수행되었다. 세가지 금속복합재료의 마모 물성시험에서 Saffil섬유, $\textrm{Al}_2\textrm{O}_3$입자, SiC입자의 효과들을 조사하였다. 마모 메커니즘은 복합재료의 마모된 표면들을 관찰하여 분석하였다. 마모과정 동안 마찰계수(COF)의 변화는 컴퓨터에서 자동적으로 기록되었으며, 건조 조건에서 Saffi1/SiC/Al은 고온과 높은 하중 하에서 가장 좋은 마모 저항을 보여주었다. 한편 Saffil/ Al과 Saffi1/$\textrm{Al}_2\textrm{O}_3$/Al의 마모 저항은 비슷한 결과를 보였다. 건조조건에서 적당한 하중과 상온에서 지배적인 마모 메커니즘은 연삭 마모이며, 하중이나 온도가 증가함에 따라 응착마모로 변화되며, 고온에서는 융착마모를 나타내었다. 건조 상태에서 세가지 복합재료를 비교시 액체 파라핀에 의한 윤활시험시 마모 특성이 가장 좋은 결과를 나타내었다. 윤활조건에서는 Saffil/Al복합재료가 가장 좋은 마모 저항성을 보였으며, 이 경우 마찰계수도 가장 작게 나타났다. 윤활 조건에서 금속복합재료의 주요 마모 메커니즘은 microploughing 이었으나, microcracking 역시 다른 정도에서는 미소 균열도 발생한다.

• Tribology and Lubricants
• /
• 제35권6호
• /
• pp.356-361
• /
• 2019

The friction and wear between machine components directly influence the energy loss and failure in various machines. Therefore, there is always a demand for finding methods to reduce friction and wear. Of the possible methods, lubrication is a widely used method for reducing friction and wear. In the case of lubrication, it is important to analyze the tribological behavior in the boundary lubrication because most of friction and wear occurs in the boundary lubrication regime. Cast iron has been regarded as a good material for industrial applications due to the excellent mechanical properties and high productivity. Especially, nodular cast iron is a material that shows better mechanical properties and wear-resistance compared with cast iron due to inclusion of spheroidal graphite. In this work, we investigated the tribological characteristics of nodular cast iron with respect to different counter parts in boundary lubrication regime. Sliding tests were conducted with SUJ2, ZrO₂, Si₃N₄ balls as counter parts using a pin-on-disk type tribotester. The results showed different friction and wear behaviors with different counter parts. The case of ZrO₂ showed the lowest wear rate in specimen and no significant ball wear. In case of SUJ2, it showed similar wear rate with ZrO₂ case in specimen and the highest friction coefficient. The case of Si₃N₄ showed the lowest friction coefficient, 33% lower than the case of SUJ2. It showed 16.9 times larger wear rate in specimen and 43% larger wear rate in ball compared to that of the SUJ2 case.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 proceedings of the second asia international conference on tribology
• /
• pp.153-154
• /
• 2002

Wear map of silver coatings on AISI 52100 has been constructed to delineate the wear transition behavior with the change in operating conditions in various environments. Three main regimes were clearly identified: (i) elastic/plastic deformation of silver coating without failure. (ii) mild wear regime after initial failure of silver coating and (iii) severe wear regime. In the mild wear regime, the contact surfaces were covered with transfer layers of agglomerated wear particles. The transfer layer acted as a protective layer and resulted in low friction even after the initial failure of the coated films, whose characteristics were strongly dependent on both the operating and environmental conditions. Also, the existence of the critical sliding speed, above which no transfer layer was able to form, was discussed in the work.

• 한국공작기계학회논문집
• /
• 제14권2호
• /
• pp.1-7
• /
• 2005

In order to determine the wear Properties of PECVD ceramic coatings, wear process was evaluated using the coated pin of Falex Tribosystem. Coating materials deposited wear the TiC, TiN and Ti(CN). An experimental process was established to determine the tribological characteristics of friction and wear behavior under the variation of applied load, temperature and sliding distance by the Falex test machine. The experimental results indicate that TiN coating compared with TiC coating on e materials have e excellent friction and wear characteristics. However TiC coating compared i친 TiN coatings have a low friction coefficient with steel and good thermal stability, and Ti(CN) has the excellent anti-wear properly as well as the superiority of extreme pressure property. Compound coating compared wi simple coatings show improved tribological characteristics.

• Tribology and Lubricants
• /
• 제21권1호
• /
• pp.16-20
• /
• 2005

Friction and wear characteristics between two steel surfaces under fretting condition are investigated experimentally. The fretting damage caused by low-amplitude oscillatory sliding can be classified into three regimes of gross-slip, mixed-slip and partial-slip due to stick-slip phenomenon. One of the most important characteristics of fretting wear is the transition from gross-slip to mixed-slip. This study was focused on getting the degree of stick-slip out of the friction transition under fretting condition. Fretting wear is divided into three conditions of gross-slip/mixed-slip/partial-slip. The criteria for the division are friction and displacement amplitude, wear scar morphology and dissipated energy. In this test, friction force and displacement were measured for detecting the transition from mixed-slip to gross-slip and qualitatively predicting the degree of the wear.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1997년도 한국재료학회 추계학술발표회
• /
• pp.45-45
• /
• 1997

• 한국생산제조학회지
• /
• 제9권3호
• /
• pp.41-47
• /
• 2000

The atmospheric humidity is varied between 30% and 90% with season in Korea. Thus the influence of humidity on the behavior of wear for tools and dies. This paper presents the influence of atmospheric humidity on the wear of carbon the un-lubricated pin-on-disk sliding contact. it was found that the severe wear is dominant at a low humidity and the mild wear is strongly related with the carbon concentration of the steel at a high humidity in this study. The experiments were carried out in a chamber where the humidity was accurately maintained by humidifier. To investigate the relationship three different carbon steels such as 1020, 1041, and 1034 steels were used.

• 한국재료학회지
• /
• 제8권12호
• /
• pp.1138-1145
• /
• 1998

Ni계 경면합금인 Deloro 50의 마모거동을 15ksi와 30ksi 접촉응력하의 여러 마모조건에서 조사하였다. 상온대기중에서 Deloro 50는 15ksi 응력에서도 극심한 응착마모가 발생하는 매우 낮은 마모저항성을 보였는데 이는 fcc 결정구조를 갖는 Deloro 50 기지상의 경도와 가공경화율이 strain-induced 상변태를 이웅한 hcp 결정구조의 Stellite 6보다 낮기 때문으로 생각된다. 상온 수중에서 Deloro 50는 15ksi 응력에서 Stellite 6와 비슷한 마모저항성을 보였는데 이는 물이 미세요철간의 금속간 접촉을 억제하였기 때문으로 생각된다. 그러나, 30ksi의 높은 접촉응력에서는 상온 대기중길 같은 응착마모가 발생하는 것으로 보아, 30ksi의 높은 응력에서는 물의 응착마모 억제 효과가 없었기 때문으로 생각된다. $300^{\circ}C$ 대기중에서 Deloro 50는 30ksi의 높은 접촉응력에서도 Stellite 6보다 우수한 마모저항성을 보였는데 이는 고온에서 마모시 생성되는 복합산화물층이 효과적으로 금속간 접촉을 방해하여 응착마모를 억제하였기 때문으로 생각된다.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 제35회 춘계학술대회
• /
• pp.96-102
• /
• 2002

This paper was studied on the wear-corrosion behavior of ductile cast iron in the acidic environment. In the dry atmosphere and variety of pH solution, wear-corrosion characteristics and friction coefficient of GCD 60 with various sliding speed and distance were investigated. And electrochemical polarization test of GCD 60 was examined in the environment of various pH value. The main results are as following : In the dry atmosphere, boundary friction appears below nearly 5 $kg_{f}$ of contact load, and it is considered that solid friction occurs over nearly 5 $kg_{f}$ of contact load. As pH value becomes low, wear-corrosion loss in the aqueous solution increases. As the corrosion environment is acidified, corrosion potential of GCD 60 becomes noble, polarization resistance becomes low, and corrosion current density increases.