• KSTLE International Journal
• /
• v.6 no.2
• /
• pp.39-44
• /
• 2005

Friction and wear properties of the Boron carbide ($B_{4}C$) coating 100 nm thickness were studied under various relative humidity (RH). The boron carbide film was deposited on silicon substrate by DC magnetron sputtering method using $B_{4}C$ target with a mixture of Ar and methane ($CH_4$) as precursor gas. Friction tests were performed using a reciprocation type friction tester at ambient environment. Steel balls of 3 mm in diameter were used as counter-specimen. The results indicated that relative humidity strongly affected the tribological properties of boron carbide coating. Friction coefficient decreased from 0.42 to 0.09 as the relative humidity increased from $5\%$ to $85\%$. Confocal microscopy was used to observe worn surfaces of the coating and wear scars on steel balls after the tests. It showed that both the coating surface and the ball were significantly worn-out even though boron carbide is much harder than the steel. Moreover, at low humidity ($5\%$) the boron carbide showed poor wear resistance which resulted in the complete removal of coating layer, whereas at the medium and high humidity conditions, it was not. X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) analyses were performed to characterize the chemical composition of the worn surfaces. We suggest that tribochemical reactions occurred during sliding in moisture air to form boric acid on the worn surface of the coating. The boric acid and the tribochemcal layer that formed on steel ball resulted in low friction and wear of boron carbide coating.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.6
• /
• pp.273-277
• /
• 2006

High velocity of oxy-fuel (HVOF) thermal spray coating is progressively replacing the other classical hard coatings such as chrome plating and ceramic coating by the classical methods, since the very toxic $Cr^{6+}$ ion is well known as carcinogen causing lung cancer, and the ceramic coatings are brittle. Co-alloy T800 powder is coated on the Inconel 718 substrates by the HVOF coating procesess developed by this laboratory. For the study of the possibility of replacing of chrome plating, the wear properties of HVOF Co-alloy T800 coatings are investigated using the reciprocating sliding tester with a counter sliding SUS 304 ball both at room and at an elevated temperature of $1000^{\circ}F\;(538^{\circ}C)$. The possibility as durability improvement coating is studied for the application to the high speed spindles vulnerable to frictional heat and wear. Wear mechanisms at the reciprocating sliding wear test are studied far the application to the systems similar to the sliding test such as high speed spindles. Wear debris and frictional coefficients of T800 coatings both at room and at an elevated temperature of $538^{\circ}C$ are drastically reduced compared to those of non-coated surface of Inconel 718 substrates. Wear traces and friction coefficients of both coated and non-coated surfaces are drastically reduced at a high temperature of $538^{\circ}C$ compared with those at room temperature. These show that the coating is highly recommendable far the durability Improvement coating on the surfaces vulnerable to frictional heat and wear.

• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.62-68
• /
• 2000

Ultra thin TiN films (50∼700nm thickness) were deposited on AISI 304 stainless steel substrates using a reactive DC magnetron sputtering deposition process to investigate their wear and friction properties. Dry sliding wear tests of the films were carried out against hardened steel and alumina counterparts using a pin-on-disk type wear tester at room temperature. Variation of friction coefficient was measured as a function of film thickness, load, sliding speed and roughness of the substrate. Worn surfaces of the film were examined by a scanning electron microscope. Wear resistance of the TiN film increased with the increase of the film thickness. The TiN film showed relatively high wear resistance in spite of its ultra thin thickness when it is mated by the steel counterpart, while it showed poor wear resistance with the alumina counterpart. The good wear resistance with the steel counterpart was explained by the formation of oxide layers on the film surface and sound interface character between the ultra thin film and the substrate.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.663-667
• /
• 2005

Surface modified carbon nanotubes were applied into the epoxy composites to investigate its tribological property. Carbon nanotubes reinforced epoxy composites were fabricated by casting. Effects to the tribological property of loading concentrations and types of surface modification of carbon nanotubes were investigated under sliding condition using linear reciprocal sliding wear tester. The results show that the small amount of carbon nanotubes into the epoxy exhibited lower weight loss than the pure epoxy. It is concluded that the effect of an enormous aspect ratio of carbon nanotubes surface area which wider than conventional fillers that react as interface for stress transfer. As increased the contents of carbon nanotubes, the weight loss from the wear test was reduced. And the surface modified carbon nanotubes show better tribological property than as produced carbon nanotubes. It is due that a surface modification of carbon nanotubes increases the interfacial bonding between carbon nanotubes and epoxy matrix through chemical bonding. Changes in worn surface morphology are also observed by optical microscope and SEM for investigating wear behaviors. Carbon nanotubes in the epoxy matrix near the surface are exposed, because it becomes the lubricating working film on the worn surface. It reduces the friction and results in the lower surface roughness morphology in the epoxy matrix as increasing the contents of the carbon nanotubes.

• Tribology and Lubricants
• /
• v.22 no.5
• /
• pp.237-242
• /
• 2006

Surfaces found in nature, including biological surfaces have been providing inspiration to modify/fabricate artificial surfaces as solutions for tribological applications. As an example, the concept of 'lotus-effect' has motivated tribologists world wide to modify/fabricate surfaces for enhanced tribological performance. These was done by creating nano/micro-scale asperities on various surfaces using ion beam milling and ion-beam assisted roughening. In order to understand the attributes of natural surfaces, which are inspirational to tribologists, we characterized the surface of two natural surfaces-Nelumbo nucifera (lotus) and Colocasia esculenta leaves. Further, we evaluated their micro-scale friction property, both in their fresh and dried conditions. The characterization of surfaces was conducted using a confocal microscope and SEM, which involved the evaluation of size and distribution of protuberances. The micro-scale friction property was evaluated using a ball-on-flat type micro-tribo tester, under reciprocating motion. A soda lime glass ball (2 mm diameter) was used in these tests. Tests were conducted at the applied normal load of $3000{\mu}N$, at a sliding speed of 1 mm/sec for a scan length of 3 mm. All experiments were conducted at ambient temperature ($24{\pm}1^{\circ}C}$) and relative humidity ($45{\pm}5%$). It was observed that the friction behaviour of the natural surfaces was influenced by their surface characteristics (morphology and distribution of protuberances) and also by the condition (fresh or dried) in which they were tested.

• Tribology and Lubricants
• /
• v.22 no.5
• /
• pp.276-281
• /
• 2006

The fractal dimension is quantitatively to define the irregular characteristic of the shape in natural. It can be useful in describing morphological characteristics of various wear particles. This paper was undertaken to diagnose failure condition for sliding members in lubrication by fractal dimension. It will be possible to diagnose wear mechanism, friction and damage state of machines through analysis of shape characteristics for wear particle on driving condition by fractal parameters. In this study, the calculating and analyzing methods of fractal dimensions were constructed for the condition monitoring and wear particle analysis in lubricant condition. So, we carried out the Friction and wear test with the ball on disk type tester, and the fractal parameters of wear particle in lubricated conditions were calculated. Fractal parameters were defined as texture fractal dimension ($D_{t}$), structure fractal dimension ($D_{s}$) and total fractal dimension (D).

• Tribology and Lubricants
• /
• v.15 no.2
• /
• pp.184-192
• /
• 1999

Various compositions of$ Cr_2$$O_3$/Mo composite powders were fabricated using spray-drying method and plasma-spray coatings of these powders were prepared to understand their tribological properties. Experiments were conducted using a reciprocal type tribo-tester at room temperature under dry sliding condition. The worn surface of coated specimens were observed using SEM (Scanning Electron Microscopy) and chemical compositions were analyzed using XRD (X-ray Diffractometry) and XPS (X-ray Photoelectron Spectroscopy). The results showed that friction coefficient of the Mo added specimens were lower than that of $Cr_2$$O_3$specimen. However $Cr_2$$O_3$specimen showed the lowest wear loss. Wear protecting layer were observed at the worn surface of coated specimens with Mo addition. From the XPS analysis, the mixed phases of $Cr_2$$O_3$ $CrO_3$and $MoO_3$were founded in the wear protecting layer.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2000.11a
• /
• pp.406-413
• /
• 2000

The friction and wear behaviors of Magnetron Sputtered MoS$_2$films were investigated by using a pin on disk type tester which was designed and manufactured for this experiment. The experiment was conducted by using silicon nitride (Si$_3$N$_4$) as a pin material and Magnetron Sputtered MoS$_2$on bearing steel (STB2) as a disk material, under operating conditions that include different surface roughness (Polishing specimen, Grinding specimen)(2types), linear sliding velocities in the range of 22, 44, 66mm/sec (3types), normal loads vary from 9.8N, 19.6N, 29.4N(3types), corresponding to contact pressures of 1.9∼2.7GPa and atmospheric conditions of high vacuum( 1.3${\times}$10$\^$-4/Pa), medium vacuum( 1.3${\times}$10$\^$-l/Pa), ambient air(10$\^$5/Pa)(3types). We investigated fracture mechanism in magnetron sputtered MoS$_2$films with Magnetron Sputtering method in each experiment.

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.520-528
• /
• 1994

An investigation was carried out to understand the effect of the amount of free silicon on the tribological properties of Si-SiC. The specimens of dense Si-SiC composites with various amount of free silicon were fabricated in the temperature of 175$0^{\circ}C$ after molding under various pressure. Wear properties were measured by ball-on-plate wear tester under the constant weight of 4 Kgf at constant sliding speed of 500 mm/sec in water. As the result, the Rockwell hardness and fracture strength of Si-SiC composites remained nearly constant up to 16.62 vol% of free silicon in the Si-SiC microstructure. The Si-SiC composites containing the free silicon of 16.62 vol% was considered to be prominent in the tribological properties, which had the friction coefficient of 0.08 and the specific wear rate of 2.4$\times$10-8$\textrm{mm}^2$Kgf-1. The analysis of the wear surface indicated the complicated processes occuring on the surface such as fine polishing, abrasion, microfracture.

• Safety and Health at Work
• /
• v.3 no.1
• /
• pp.22-30
• /
• 2012

Objectives: To challenge the problem of slipperiness, various slipmeters have been developed to assess slip hazard. The performance of in-situ slipmeter is, however, still unclear under the various floor conditions. The main objectives of this study were to evaluate the performance of three kinds of slipmeters under real conditions, and to find their dynamic and kinematic characteristics, which were compared with gait test results. Methods: Four common restaurant floor materials were tested under five contaminants. Slipmeters and human gaits were measured by high speed camera and force plate to find and compare their dynamic and kinematic characteristics. Results: The contact pressures and built-up ratio were below those of subjects. The sliding velocity of British Pendulum Tester was above those of subjects, while those of BOT-3000 and English XL were below those of subjects. From the three meters, the English XL showed the highest overall correlation coefficient (r = 0.964) between slip index and $R_a$, while the rest did not show statistical significance with surface roughness parameters ($R_a$, $R_z$). The English XL only showed statistical significance (p < 0.01) between slip index and contaminants. The static coefficient of friction obtained with the BOT-3000 showed good consistency and repeatability (CV < 0.1) as compared to the results for the BPT (CV > 0.2) and English XL (CV < 0.2). Conclusion: It is unclear whether surface roughness can be a reliable and objective indicator of the friction coefficient under real floor conditions, and the viscosity of contaminants can affect the friction coefficient of the same floors. Therefore, to evaluate slipperiness, the performance of the slipmeters needed to improve.