• Composites Research
• /
• v.20 no.6
• /
• pp.8-14
• /
• 2007

Debonding failure characteristics of the composite skin-stiffener specimens were experimentally investigated. The influences of bonding methods, types of stiffener shape and various secondary bonding parameters were evaluated. Present test results combined with the previous test results[1] showed that the failure displacement of the skin-stiffener specimens well evaluates the skin-stiffener debonding failure strength of the composite stiffened panels. The specimens with an open type stiffener had lower bending stiffness and larger failure displacement than those with a closed type stiffener. Secondary bonding and co-curing with adhesive had better failure strength than co-curing without adhesive film. Secondary bonded specimens failed by adhesive failure and co-cured specimens failed by delamination failure. As the bondline thickness was thinner, the skin-stiffener specimens had higher failure strength. The fillets had no influence on failure strength of the specimens. The influence of the surface roughness was shown according to types of stiffener shape.

• Composites Research
• /
• v.31 no.6
• /
• pp.323-331
• /
• 2018

The effect of stainless steel jagged-pin reinforcement on the pull-off strength of the composite hat-joint was studied by the test. The pins were physically and chemically surface-treated and inserted in the thickness direction over the interface where the skin and stiffener meet. The specimens including the jagged-pins were made by co-curing process. Diameters of the jagged-pins were 0.3, 0.5 and 0.7 mm. The pin areal densities were set to 0.5 and 2.0% based on the interface area where the skin and stiffener meet. The specimens using 0.3 mm diameter normal (un-jagged) pins with 2.0% areal density were additionally fabricated and tested to investigate the pin shape effect on the pull-off strength. The pull-off strengths of specimens reinforced with 0.5% areal density by 0.3, 0.5, and 0.7 mm diameter pins were 45, 19 and 9% higher than those of un-reinforced specimens, respectively. In case with 2.0% pin areal density, the strengths were 127, 45, and 11% higher than those of un-reinforced specimens, respectively. The test results show that the higher pin areal density results in the higher strength when the pin diameter is the same. When the pin areal density is the same, the smaller pin diameter leads to higher strength. When the joints using jagged-pins and normal pins in 2.0% areal density with 0.3 mm diameter, the joints of jagged-pins showed the 64% higher strength. From the results of this study, it was confirmed that jagged-pin reinforcement can be an effective method for improving the pull-off strength of composite hat-joint.