• Journal of the Korean Ceramic Society
• /
• v.32 no.12
• /
• pp.1337-1348
• /
• 1995

TZP/SUS- and ZT/SUS-functionally gradient materials (FGM) were fabricated by pressureless sintering in Ar-atmosphere. The sintering defects such as warping, frustrum formation, splitting and cracking which originated from shrinkage and sintering behaviors of metal and ceramics different from each other could be controlled by the adjustment with respect to the particle size and phase type of zirconia. The residual stresses generated on the metal and ceramic regions in FGM were characterized with X-ray diffraction method, and relaxed as the thickness and number of compositional gradient layer were increased. The residual stress states in TZP/SUS-FGM have irregular patterns by means of the different sintering behavior and cracking at ceramic-monolith. While in ZT/SUS-FGM, compressive stress is induced on ceramic-monolith by the volume expansion of monoclinic ZrO2 at phase transformation. Also, compressive stress is induced on metal-monolith by the constraint of warping which may be created to the metal direction by the difference of coefficient of thermal expansions. As a consequence, it has been verified that the residual stress generated on FGM is dominantly influenced by the thickness and number of compositional gradient layer, and the sintering defects and residual stress can be controlled by the constraint of the difference of shrinkage and sintering behaviors of each component.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.274-275
• /
• 2006

The sintering behavior of titanium-titanium nitride nanocomposite powders has been studied by dilatometry. Titanium. titanium nitride nanocomposite powders were produced by the reactive milling of micron sized titanium powder $(12\;{\mu}m)$ in nitrogen atmosphere. The Ti-TiN nanocomposite powders milled for various durations along with the initial micron sized Ti powders were then sintered in the temperature range of $450-1000^{\circ}C$ by a constant rate of heating $(10^{\circ}C/min)$. The linear shrinkage, shrinkage rate, activation energy for sintering and microstructure has been studied and discussed as a function of milling time.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1992.05b
• /
• pp.126-126
• /
• 1992

Solid and liquid sintering behaviors of mechanically alloyed 75W-25Cu powders have been studied by using a dilatometry technique. The sintering was performed under hydrogen atmosphere of 1 atm with a heating rate of 3 $^{\circ}C$/min. The mechanically alloyed 75W-25Cu powders were prepared by high energy ball milling process under argon atmosphere of 1 atm with alloying times of 0 to 400 h. To compare with the sintering behaviors of mechanically alloyed powders, pure Cu and W powders were also sintered under the above conditions, As the mechanical alloying time increased from 0 to 400 h, the shrinkage behavior of the alloyed powders was enhanced during the sintering, and staring temperature of liquid sintering decreased from 1083 to 1068 $^{\circ}C$. The saturation temperature, above which the shrinkage was completed, of liquid phase sintering decreased from 1248 to 1148 $^{\circ}C$ with increasing mechanical alloying time from 200 to 400 h. The residual stress of the mechanically alloyed powder was measured by X-raydiffractometer. The microstructure of sintered spcimen was observed by optical and scanning electron microscope. From these results, variations of solid and liquid sintering behaviors with mechanical alloying time were discussed in terms of the amount of residual stress and the distribution of W and Cu powders in the mechanically alloyed powder.

• Journal of Powder Materials
• /
• v.21 no.2
• /
• pp.102-107
• /
• 2014

A high temperature dilatometer attached to a graphite furnace is built and used to study the sintering behavior of $B_4C$. Pristine and carbon doped $B_4C$ compacts are sintered at various soaking temperatures and their shrinkage profiles are detected simultaneously using the dilatometer. Carbon additions enhance the sinterability of $B_4C$ with sintering to more than 97% of the theoretical density, while pristine $B_4C$ compacts could not be sintered above 91% due to particle coarsening. The shrinkage profiles of $B_4C$ reveal that the effect of carbon on the sinterability of $B_4C$ can be seen mostly below $1950^{\circ}C$. The high temperature dilatometer delivers very useful information which is impossible to obtain with conventional furnaces.

• Journal of the Korean Ceramic Society
• /
• v.31 no.11
• /
• pp.1265-1270
• /
• 1994

Ultra-fine hydroxyapatite powder were synthesized by the hydrothermal reaction at 10 atm, 3 hrs of Ca(OH)2 suspension with (NH4)2HPO4 solution, and were characterized sintering behavior. Sintered bodies of hydroxyapatite powders which synthesized by hydrothermal reaction method has less weight loss, less sintering shrinkage and superior mechanical property, and was more dense than sintered bodies of hydroxyapatite powder which synthesized by wet method. Sintered bodies were hydroxyapatite single phase. When soack in Ringer's solution for 2 weeks, hydroxyapatite powders preserved hydroxyapatite and sintered body absorbed trace of Ca2+ ion with soaked time.

• Journal of Powder Materials
• /
• v.10 no.3
• /
• pp.172-175
• /
• 2003

Mechanically-alloyed NiAl powder was sintered by Spark-Plasma Sintering (SPS) process. Densification and behavior mechanical property were determined from the experimental results and analysis ,such as changes in linear shrinkage, shrinkage rate, microstructure, and phase during sintering process, Victors hardness, and transver.ie-rupture-strength (TRS). Above 97% relative density was obtained after sintering at 115$0^{\circ}C$ for 5 min. Crystallite size determined by the Scherrer method was approximately 50 nm. From the X-ray diffraction analysis it was confirmed that the sintered bodies were composed mainly of NiAl phase together with Ni$_3$Al phase. Measured Vickers hardness and TRS value were 555$\pm$10 $H_v$ and 1393$\pm$75 MPa , respectively.

• Journal of the Korean Ceramic Society
• /
• v.31 no.4
• /
• pp.448-456
• /
• 1994

The reaction-sintered alumina and zirconia-alumina ceramics were fabricated from the Al/Al2O3 or Zl/ZrO2(Ca-PSZ) powder mixtures via the attrition milling. And the effects of the milling characteristics of used raw powders on reaction sintering were investigated. After attrition milling and isopressing at 400 MPa the Al/Al2O3 specimen was oxidated at 1200℃ for 8 hours followed by sintering at 1550℃ for 3 hours. Because mixed powders of flake-type Al with coarse alumina was much more effectively comminuted than the globular-type Al with coarse alumina powders, it's sintered body of more than 97% theoretical density was achived, but low contents of Al leads to relatively higher shrinkage of about 8%. And because coarse alumina particles was much more beneficial in cutting and reducing the ductile Al particles, using the coarse alumina powder was much more effective in reaction sintering. Fused Ca-PSZ powder was reaction sintered with Al at 1550℃ for 3 hours and low shrinkage ZrO2-Al2O3 composites were fabricated. But because Al/Ca-PSZ powder mixtures were not effectively milled the reaction sintering and densification was difficult. And the Ca ion in Ca-PSZ grains diffused into alumina grains during sintering so that the unstabilization of Ca-PSZ body was occured which gave the microcracks in the specimens.

• Journal of Applied Reliability
• /
• v.15 no.3
• /
• pp.216-221
• /
• 2015

Sintering behavior of 3%yttria-stabilized zirconia was comparatively studied using a spray-dried powder produced by a domestic and global company. Quality of the sintered block was analysed in terms of relative density, shrinkage rate, grain growth, hardness, and fracture toughness. Relative density, shrinkage rate, and hardness value of the finally sintered block was similar between domestic and global zirconia powder, respectively. But, flexural strength of the domestic powder specimen was about 70% of the sintered block produced by using a global powder. The poor sintering quality of the domestic powder was discussed in relation with compressibility of the spray-dried granule-type powder and the amount of monoclinic phase in the as-received powder.

• Journal of the Korean Society for Heat Treatment
• /
• v.11 no.3
• /
• pp.177-185
• /
• 1998

The purpose of this research is to investigate the effects of Co, Co-Ti addition on the sintering characteristic of $(Ti_{1-x}Alx)N$ material synthesized by the direct nitriding method for a application as a cermet material. The observed shrinkage rates of $(Ti_{1-x}Alx)N$ pellets increase with the additive (Co, Co-Ti) content, temperature and time, and also the pellets with the same additive content exhibit the shrinkage behavior that depends on the Ti/Al ratio. However, although the shrinkage rates in this study is the mast higher (36%), the density of the sintered $(Ti_{1-x}Alx)N$ pellet is below 80% density in theory because of the partial segregation and the dense band defect of AlCo compound. Consequentely, it is considered that Co was not effective as a binder material because the wettability of liquid Co metal on $(Ti_{1-x}Alx)N$ materials is poor, In $(Ti_{1-x}Alx)N$ with Ti-Co additive, the stoichiometric TiN is transformed by the under-stoichiometric TiNx(x<1.0) during sintering, leading to the good properties such as hardnees and hot oxidation.

• Journal of the Korean Ceramic Society
• /
• v.29 no.6
• /
• pp.419-430
• /
• 1992

Fabrication possibility of low-shrinkage alumina without oxidation and wetting agent was presented on the basis of observation about oxidation behavior, microstructure and physical characteristics of such reaction agents free Al2O3-Al system. The composition less than Al 10w/o where Al can act as a sintering agent for Al2O3 was excluded. Under the condition of present experiments oxidation of Al2O3-Al system was dependent not on holding time but mainly on oxidation temperature. In thes case of Al powder not comminuted effectively during powder mixing of Al2O3-Al, columnar structure which would act as a hindrance to the densification during sintering developed more during oxidation with higher Al contents, and which made the fabrication of low-shrinkage Al2O3 ceramics impossible. If Al powder was comminuted effectively due to co-mixed Al2O3 characteristics, densification was improved because of no columnar structure and made the fabrication of sintered body with -2.7% dimensional change and 81% relative density possible. As a result, it is possible to fabricate dense low-shrinkage Al2O3 ceramics without oxidation and wetting agent under conditions such as smaller particle size of Al, Al contents below 50v/o, higher green density of Al2O3-Al compact and the use of Al2O3 powder used for high-density ceramics.