• 대한기계학회논문집A
• /
• 제21권1호
• /
• pp.83-92
• /
• 1997

In a study on the development of Cu-based sintered friction materials, the specimens pressed with various compacting pressures $(3-6 ton/cm^2/)$ have been evaluated to find the optimum condition of compacting pressure. As compacting pressure increased up to $(5 ton/cm^2/)$, mechanical properties such as density, hardness, bending strength, wear and coefficient of friction, etc. improved remarkably, but up to 6 ton/cm$^{2}$, decreased slightly because of traps of gases and water vapors in specimen. Disk assembly composed of 12 pieces of Cu-based friction materials has been compared with one of asbestos-and nonasbestos-based friction materials. In dynamic and driving tests to find burst spin strength, corrosion area rate and friction properties, etc., Cu-based sintered friction materials showed better properties than the others, especially in severe conditions because oxides such as $Cu_2O; and; SnO_2$ in the friction surface of friction materials were formed.

• Tribology and Lubricants
• /
• 제23권6호
• /
• pp.266-271
• /
• 2007

The brake performance of sintered friction materials for the high speed train was studied. In this study, newly developed sintered materials based on copper were compared with the commercial products for high speed trains. They were tested on a 1/5 scale dynamometer using low carbon steel disks. Effectiveness, fade, and recovery tests were carried out to examine friction performance and the change of disk thickness variation (DTV) during brake applications and noise propensity were also evaluated. Results showed that the two sintered friction materials exhibit similar friction coefficients and braking performance, whereas the newly developed friction material was superior in terms of DTV generation and noise propensity to the commercial friction material. The improvement of the newly developed friction material was attributed to the high graphite content which reduced the stick-slip phenomena and prevented uneven disk wear by producing friction films on the counter disk.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1997년도 제25회 춘계학술대회
• /
• pp.53-61
• /
• 1997

The effect of sintering condition on tribological behavior in the Cu-base sintered friction materials was studied through pin-on-disk type wear tester. Especially, the experiment was focused on making a comparative study between presstwed sintering and pressureless sintering. Pressureless sintering process showes more stable friction coefficient and lower wear rate than pressure sintering process. This result is related to pore size and density of pore in the sintered materials.

• Tribology and Lubricants
• /
• 제29권4호
• /
• pp.242-247
• /
• 2013

This study aims to establish the fundamental basis for the design of materials used in high-speed trains, by using a lab-scale dynamometer to evaluate the characteristic behavior of metallic sintered friction materials in relation to the shape of graphite. The test results clearly demonstrate that when flake graphite and granular graphite are added equivalently, the average coefficient of friction is much lower, and it is less influenced by speed variation; moreover, friction wear is observed to be insignificantly low. Adding flake graphite increases the coefficient of friction, which leads to higher friction wear. In addition, the roughness of the disc surface was equivalent regardless of the shape of the graphite.

• 대한기계학회논문집A
• /
• 제20권1호
• /
• pp.44-52
• /
• 1996

Influence of frictional and mechanical properties was studied with the content(8-18 wt.%) and shapes(flake of irregular) of graphite that was used as lubricant components of copper-based sintered materials. The density, hardness and bending strength of friction materials with the shape of flake graphite were lower and decreased rapidly than that of irregular, as the content of graphite increases up to 18 wt.%. In friction test, wear rate was about 2.0-$2.5{\times}10^{-7}\textrm{cm}^3$/kgf.m and coefficient of friction was 0.30-0.37, independent on graphite content and shape. As the temperature of friction materials increased, wear rate decreased rapidly because oxides such as $Cu_2O$ and $SnO_2$ in the surface of friction material were formed.

• 한국기계가공학회지
• /
• 제3권3호
• /
• pp.5-10
• /
• 2004

The effect of bronze sintered friction materials on frictional and mechanical properties is studied with the content(8~18 wt,%) and shapes (flake and irregular) of graphite that is used as solid lubricants to meet diverse characteristics such as low coefficient of friction, low wear rate and high bending strength. The content and shapes of graphite are optimized by statistical experiments. Friction test was carried out measure friction coefficient, temperature dependence and wear rate. As a result of experiments, the density, hardness and bending strength with a shape of flake graphite are lower and decrease rapidly than that of Irregular, as the content of graphite increases up to 18 wt% Aftei friction test, coefficient of friction is 0.3~0 4 and wear rate is $0.32{\sim}2.98{\times}10^{-7}cm^3/kg{\cdot}m$. When the content of graphite increases, coefficient of friction increases In a shape of flake graphite and decreases in a shape of irregular graphite.

• Tribology and Lubricants
• /
• 제29권1호
• /
• pp.19-26
• /
• 2013

Cu-matrix sintered brake pads and low-alloy heat-resistant steel are commonly applied to basic brake systems in high-energy moving machines. In this research, we analyzed the tribological characteristics to determine the influence of the air velocity between the disk and pad. At a low brake pressure with airflow, the friction stability was decreased as a result of the lack of tribofilm formation at the disk surface. However, there were no significant changes in the friction coefficient under any of the test conditions. The wear rates of the friction materials were decreased with an increase in the airflow velocity. As a result, the airflow velocity influenced the friction stability, as well as the wear rate of the friction materials and disk, but not the friction coefficient.

• Tribology and Lubricants
• /
• 제29권2호
• /
• pp.98-104
• /
• 2013

Cu-matrix-sintered brake pads and heat-resistant low-alloy steel are commonly applied to basic brake systems in high-energy moving machines. We analyzed how the tribological characteristics are influenced by the inertial mass. A high inertial mass decreased the friction coefficient by about 15% compared to a low inertial mass under all velocity conditions. The wear rates of the friction materials increased with the inertial mass. Thus, the inertial mass influences the friction coefficient and wear rate of the friction materials and disk but not the friction stability.

• Tribology and Lubricants
• /
• 제30권6호
• /
• pp.330-336
• /
• 2014

Sintered metallic brake pads and low alloy heat resistance steel disks are applied to mechanical brake systems in high energy moving machines that are associated with recently developed 200km/h trains. This has led to the speed-up of conventional urban rapid transit. In this study, we use a lab-scale dynamometer to investigate the effects of the composition of friction materials on the tribological characteristics of sintered metallic brake pads and low alloy heat resistance steel under dry sliding conditions. We conduct test under a continuous pressure of 5.5 MPa at various speeds. To determine the optimal composition of friction materials for 200 km/h train, we test and the evaluate frictional characteristics such as friction coefficients, friction stability, wear rate, and the temperature of friction material, which depend on the relative composition of the Cu-Sn and Fe components. The results clearly demonstrate that the average friction coefficient is lower for all speed conditions, when a large quantity of iron power is added. The specimen of 25 wt% iron powder that was added decreased the wear of the friction materials and the roughness of the disc surface. However when 35 wt% iron powder was added, the disc roughness and the wear rate of friction materials increased By increasing the amount of iron powder, the surface roughness, and temperature of the friction materials increased, so the average friction coefficients decreased. An oxidation layer of $Fe_2O_3$ was formed on both friction surfaces.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1995년도 특별강연 및 추계학술발표 개요집
• /
• pp.165-169
• /
• 1995

This paper deals with determining the proper friction welding condition and analyzing mechanical in of friction welded joints of sintered carbide tool materials (SKNM50 for the blade part of press punch) to alloy steel (SCM440 for the shank part of press punch), the alloy steel to aluminum(A6061 for the interlayer material between the blade part and the shank) and sintered carbide tool materials to aluminum. And also acoustic emission test will be carried out during fiction welding to evaluate the weld quality.