• Korean Journal of Materials Research
• /
• v.18 no.5
• /
• pp.283-288
• /
• 2008

The effect of sintering aids and glass-frit on the densification and resistivity of silver paste was investigated in an effort to enhance the sintered density and electrical conductivity of the silver electrode. To prepare Pb-free silver paste for use at low sintering temperatures, two commercial silver powders ($0.8\;{\mu}m$ and $1.6\;{\mu}m$ in size) and 5wt.% lab-synthesized nanoparticles (30-50 nm in size) as a sintering aids were mixed with 3 wt.% or 6 wt.% of glass frit ($Bi_2O_3$-based) using a solvent and three roll mills. Thick films from the silver paste were prepared by means of screen printing on an alumina substrate followed by sintering at $450^{\circ}C$ to $550^{\circ}C$ for 15 min. Silver thick films from the paste with bimodal particles showed a high packing density, high densification during sintering and low resistivity compared to films created using monomodal particles. Silver nanoparticles as a sintering aid enhanced the densification of commercial silver powder at a low sintering temperature and induced low resistivity in the silver thick film. The glass frit also enhanced the densification of the films through liquid phase sintering; however, the optimum content of glass frit is necessary to ensure that a dense microstructure and low resistivity are obtained, as excessive glass-frit can provoke low conductivity due to the interconnection of the glass phase with the high resistivity between the silver particles.

• Composites Research
• /
• v.31 no.2
• /
• pp.76-81
• /
• 2018

In this study, the elemental mercury removal behaviors of silver-plated porous carbons materials were investigated. The pore structures and total pore volumes of the hybrid materials were analyzed by $N_2$ adsorption/desorption analysis at 77 K. The pore structures and surface morphologies of the hybrid materials were characterized by XRD and SEM, respectively. The elemental mercury adsorption capacities of all silver-plated porous carbons hybrid materials were higher than those of the as-received samples, despite the fact that the specific surface areas and total pore volumes decreased with increasing metal loading time. It was found that silver nanoparticles showed excellent elemental mercury removal behaviors in carbonaceous hybrid materials.

• Molecular & Cellular Toxicology
• /
• v.5 no.1
• /
• pp.23-31
• /
• 2009

To compare the effects of nanometer-sized silver ions and support materials (nano-silver coating material, NM-silver) and silver ions, we exposed zebrafish embryos to both types of nano-silver ions and compared the acute responses during embryogenesis. The amount of silver in the NM-silver (17.16%) was greater than that in the silver ion (4.56%). Both of these materials have different atomic compositions. The silver ion-exposed groups (10 and 20 ppt) showed lower survival rates than the NM-silver-exposed groups (10 and 20 ppt). NM-silver penetrated the skin and blood tube of zebrafish larvae as aggregated particles, whereas, silver ions penetrated the organelles, nucleus and yolk in a spread-out pattern. Micro-array analysis of RNA from zebrafish larvae (72 hours post-fertilization) that were treated with either NM-silver or silver ions, showed alteration in expression of the BMP, activin, TGF-$\beta$, and $GSK3{\beta}$ genes pathway. Additionally, $GSK3{\beta}$ gene pathway for apoptosis that was related with left-right asymmetry. Gene expression changes in the NM-silver or silver ions-treated zebrafish embryo led to phenotypic changes in the hatched larvae, reflecting increased apoptosis and incomplete formation of an axis.

• Journal of the Korean Ceramic Society
• /
• v.41 no.10 s.269
• /
• pp.788-791
• /
• 2004

We have studied the fabrication of silver micro lines using the silver nano sol on ITO substrate by an ink-jet method. The average particles size of $10wt\%$ silver nano sol synthesized with polyelectrolytes was smaller than 10 nm. The pattern formation of silver nano sol on the substrate closely related with the contact angle of the silver nano sol. The dot shaped of silver nano sol on bare ITO substrate was formed due to the high contact angle of silver nano sol. When ITO substrates was treated with 100 ppm polyethylenimine for silver nano sol patterning, fine silver micro lines of $60{\sim}100{\mu}m$ width was fabricated by ink-jet method.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.1552-1555
• /
• 2005

We have studied the inkjet patterning of synthesized aqueous silver nano-sol on interface-controlled ITO glass substrate. Furthermore, we designed the conductive ink for direct inkjet patterning on bare ITO glass substrate. The first, the highly concentrated polymeric dispersant-assisted silver nano sol was prepared by variation of molecular weight and control of initial nucleation and growth of silver nanoparticles. The high concentration of batch-synthesized silver nano sol was possible to 40 wt%. At the same time the particle size of silver nanoparticles was below $10{\sim}20nm$. The second, the synthesized silver nano sol was inkjet - patterned on ITO glass substrate. The connectivity and width of fine line depended largely on the wettability of silver nano sol on ITO glass substrate, which was controlled by surfactant. The relationship was understood by wetting angle. The fine line of silver electrode as fine as $50{\sim}100\;{\mu}m$ was successfully formed on ITO glass substrate. The last, the direct inkjet-patternable silver nano sol on bare ITO glass substrate was designed also.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.1
• /
• pp.12-17
• /
• 2021

Among the various precious metals, silver is used in various fields because of its low price than other precious metals. However, the surface of silver remains after rain in the atmosphere containing sulfur ions and chlorine ions, causing silver corrosion and discoloration. Existing documents have developed a anode to prevent corrosion but that are concentrated on secondary batteries. This study tried to prevent corrosion and discoloration of silver by using an Al sacrificial anode. Sulfuric acid decreased the potential of silver and increased the current density at active polarization and OCP. The amount of corrosion of silver with the Al sacrificial anode was reduced from 0.5 % to 6.5%. When silver is used for decoration outside, corrosion and discoloration of silver can be suppressed by installing an Al anode.

• 한국초전도학회:학술대회논문집
• /
• 2008.08a
• /
• pp.68-68
• /
• 2008

• Bulletin of the Korean Chemical Society
• /
• v.35 no.10
• /
• pp.2979-2984
• /
• 2014

Silver nanoparticles have been synthesized by liquid-phase and alcohol reduction methods. Silver-doped silica-complex nanoparticles were prepared using a sol-gel process. The formation, structure, morphology, and particle size of the nanoparticles have been studied using several techniques. Silver nanoparticles of size of 30-40 nm were formed successfully by alcohol reduction. TEM images show that both the concentration and the molecular weight of polyvinyl pyrrolidone (PVP) considerably affect the size of the emerging silver nanoparticles. The number of silver-doped silica-complex particles increased by a mercapto-group treatment that showed a narrower size distribution than that of silica treated with amino groups. The silver/polyester and silver-doped silica/polyester masterbatch chips showed excellent antibacterial activity against Staphylococcus aureus and Escherichia coli.

• Korean Journal of Metals and Materials
• /
• v.48 no.6
• /
• pp.570-574
• /
• 2010

Silver conducting films were formed from nano-sized silver powders and glass frits prepared by flame spray pyrolysis. The mean sizes of the silver powders and glass frits were 73 and 63 nm, respectively. Nano-sized glass frits improved the adhesion strength of the silver conducting film to the glass substrate. The densities of the silver conducting films increased by increasing the glass contents of the films at firing temperatures of 400 and $500{^{\circ}C}$. The specific resistances of the silver conducting films with 5 wt.% glass of silver component were 7.8, 4.2 and 2.4 cm at firing temperatures of 400, 450 and $500{^{\circ}C}$.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.3
• /
• pp.725-730
• /
• 2014

The effect the diameter of silver nanorod arrays whose distance between the nanorods was uniform at 65 nm have on Surface-enhanced Raman Scattering (SERS) has been studied by varying the diameter from 28 to 51 nm. Nanorod length was fixed at approximately 62 nm, which is the optimum length for SERS by excitation with a 632.8 nm laser line. The transverse and longitudinal modes of the surface plasmon of these silver nanorods were near 400 and 630 nm, respectively. The extinction of the longitudinal mode increased with increasing nanorod diameter, while the transverse mode did not change significantly. High-quality SERS spectra of p-aminothiophenol and benzenethiol adsorbed on the tips of the silver nanorods were observed by excitation with a 632.8 nm laser line. The SERS enhancement increased with increasing nanorod diameter. We concluded that the SERS enhancement increases when the diameter of silver nanorods is increased mainly by increasing the excitation efficiency of the longitudinal mode. The enhancement factor for the silver nanorods with a 51 nm diameter was approximately $2{\times}10^7$.