• 한국생산제조학회지
• /
• 제25권4호
• /
• pp.253-257
• /
• 2016

The effects of re-peening on the compressive residual stress and fatigue life of Al7075-T6 were investigated. The compressive residual stress induced on the surface of components by shot peening is known to increase the fatigue life. However, the fatigue load relaxes the compressive residual stress of components. Re-peening is a technique to again induce the relaxed compressive residual stress and increase the total fatigue life of components. In this study, the re-peening process was applied to fatigue-loaded specimens. The compressive residual stress and fatigue life were examined for re-peened specimens with fatigue ratios of 30%, 50%, and 70%. The results showed that the compressive residual stress of the specimens was relaxed under the fatigue load. The re-peening process significantly increases the compressive residual stress and total fatigue life.

• 대한기계학회논문집A
• /
• 제36권11호
• /
• pp.1381-1389
• /
• 2012

본 논문에서는 쇼트피닝 가공한 알루미늄 7075-T6 재료의 부식피로향상에 대한 연구를 하였다. 사용된 알루미늄 금속은 상대적으로 가볍고 강한 재료의 특성으로 항공기 주요부품의 재료로 사용되고 있으며, 많은 연구를 통해 알루미늄을 사용하면 약 50%의 무게 감소효과를 낼 수 있다고 한다. 재료의 부식은 인장환경에서 재료의 파단시점을 앞당기고 구조물의 수명을 심각하게 감소시킨다. 따라서 알루미늄 금속의 부식 환경에서의 재료의 부식저항을 향상 시킬 수 있는 연구가 요구된다. 쇼트피닝 가공은 재료 표면에 압축잔류응력을 인가하여 재료의 피로수명을 늘리고 나아가 재료의 신뢰성을 확보하는 기술로 반복하중을 받는 많은 부품들에 이미 적용되어 사용되고 있다. 부식 환경에서는 가공 후 거칠어진 표면으로 인해 공식부식을 야기하지만, 피닝가공에 의한 표면 직하에 압축잔류응력이 부식을 억제하여 부식저항을 증가시킨다. 본 연구에서의 쇼트피닝가공된 시험편에 대한 실험결과와 선행연구에서의 쇼트피닝 가공하지 않은 알루미늄 합금 재료의 부식피로특성을 비교하였다. 실험 결과 쇼트피닝 가공은 알루미늄합금의 피로수명향상에 영향을 미치고, 압축잔류응력은 부식피로수명을 증가시킴을 알 수 있었다.