• Steel and Composite Structures
• /
• v.28 no.5
• /
• pp.527-539
• /
• 2018

The use of reinforced concrete (RC) shear wall with concrete filled steel tube (CFST) columns and steel fiber reinforced concrete (SFRC) shear wall has aroused widespread attention in recent years. A new shear wall, named SFRC shear wall with CFST columns, is proposed in this paper, which makes use of CFST column and SFRC shear wall. Six SFRC shear wall with CFST columns specimens were tested under cyclic loading. The effects of test parameters including steel fiber volume fraction and concrete strength on the failure mode, strength, ductility, rigidity and dissipated energy of shear wall specimens were investigated. The results showed that all tested shear wall specimens exhibited a distinct shear failure mode. Steel fibers could effectively control the crack width and improve the distribution of cracks. The load carrying and energy dissipation capacities of specimens increased with the increase of steel fiber volume fraction and concrete strength, whilst the ductility of specimens increased with the increase of steel fiber volume fraction and the decrease of concrete strength.

• Structural Engineering and Mechanics
• /
• v.83 no.6
• /
• pp.789-798
• /
• 2022

The stud shear connector is the main force transfer member in the steel-concrete composite member, and the mechanical behavior is very complicated in the concrete. The concrete around the stud is subjected to the pry-out local pressure concentration of the stud, which can easily produce splitting mirco-cracks. In order to solve the problem of pry-out local splitting of stud shear connector, a kind of stud shear connector with constraint measure is proposed in this paper. Through the push-out test, the interface shear behavior of the new stud shear connector between steel and concrete flange plate was studied, and the difference between the new stud shear connector and the traditional stud connector was compared. The results show that the stud shear connector with constraint measure can effectively avoid the adverse effect of local pressure splitting by relying on its own constraint measure. The shear stiffness of the interface between steel and concrete flange plates is greatly improved, which provides a theoretical basis for the design of strong connection coefficient of steel-concrete composite structures.

• Journal of the Korea Concrete Institute
• /
• v.22 no.5
• /
• pp.711-718
• /
• 2010

The requirement of the maximum yield strength of shear reinforcement in the KCI-07 code is quite different to those in the ACI-08 code, EC2-02, CSA-04, and JSCE-04 codes. Eighteen RC beams having high strength shear reinforcement were tested. Test results indicated that even if the yield strength of shear reinforcement in beams was much greater than the maximum yield strength required by the KCI-07 design code, the shear reinforcement of these beams reached their yield strains. Furthermore, the shear strengths of tested beams increased almost linearly with the increase of the amount of shear reinforcement. In addition, larger numbers of diagonal cracks developed in the web of the beam having greater yield strength than the beams having lower yield strength of shear reinforcement. The maximum crack width of the beam having high strength shear reinforcement was approximately the same to the crack with of the beam having normal strength shear reinforcement.

• Journal of the Earthquake Engineering Society of Korea
• /
• v.24 no.5
• /
• pp.233-241
• /
• 2020

This paper is to investigate the retrofitting effect for a non-seismic reinforced concrete frame strengthened by perimeter steel moment frames with indirect integrity, which ameliorates the problems of the direct integrity method. To achieve this, first, full-scale tests were conducted to address the structural behavior of a two-story non-seismic reinforced concrete frame and a strengthened frame. The non-seismic frame showed a maximum strength of 185 kN because the flexural-shear failure at the bottom end of columns on the first floor was governed, and shear cracks were concentrated at the beam-column joints on the second floor. The strengthened frame possessed a maximum strength of 338 kN, which is more than 1.8 times that of the non-seismic specimen. A considerable decrease in the quantity of cracks for the strengthened frame was observed compared with the non-seismic frame, while there was the obvious appearance of the failure pattern due to the shear crack. The lateral-resisting capacity for the non-seismic bare frame and the strengthened frame may be determined per the specified shear strength of the reinforced columns in accordance with the distance to a critical section. The effective depth of the column may be referred to as the longitudinal length from the border between the column and the foundation. The lateral-resisting capacity for the non-seismic bare frame and the strengthened frame may be reasonably determined per the specified shear strength of the reinforced columns in accordance with the distance to a critical section. The effective depth of the column may be referred to as the longitudinal length from the border between the column and the foundation. The proposed method had an error of about 2.2% for the non-seismic details and about 4.4% for the strengthened frame based on the closed results versus the experimental results.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.04a
• /
• pp.280-285
• /
• 1996

The shear behavior of reinforced concrete deep beams with web opennings has been scrutinized experimentally to verify the influences of the structural parameters such as size, shape, location and reinfrocements of web openings, and shear span ratio. A total of 22 specimens has been tested under one or two point loading conditions at the laboratory. In the tests most specimens have shown shear failures with inclined cracks from the loacing points to the supports through openings. The ultimate strengths of the specimens measured from the tests have shown wide differences depending on the locations of the openings which deter the formation of the compression struts between the loading points and the supports. The effects of the reinforcements and the geomtry of the openings on the shear strengths and the crack developments have been carefully checked and analyzed.

• The Korean Journal of Ceramics
• /
• v.3 no.3
• /
• pp.208-212
• /
• 1997

Shear-induced phase transformation behavior of chemically stabilized $\beta$-cristobalite was studied by the fiber push-out technique. To obtain the critical grain size for phase transformation, the hot-pressed polycrystalline $\beta$-cristobalite, which was used as the interphase between fiber and matrix, was annealed at $1300^{\circ}C$ for 10h. Two types of fibers, mullite and sapphire fiber, were used in this study. Debonding between mullite fiber and cristobalite interphase occurred at a critical load of 230 MPa. Static friction and fiber sliding were continuously followed by debonding. Shear-induced transformation induced cracks in the cristobalite interphase at the debonding stage. In the case of the sapphire fiber, the debonding occurred at a lower load of 180 MPa due to the residual stress in the interface caused by the difference in thermal expansion coefficients between the fiber and the cristobalite interphase. The load was insufficient for shear-induced phase transformation.

• Structural Engineering and Mechanics
• /
• v.72 no.1
• /
• pp.19-30
• /
• 2019

The mechanical behavior of Fiber Reinforced Cementitious Composites (FRCC) under direct shear is studied through experiment and analytical simulation. The cementitious composite considered contains 55% replacement of cement with fly ash and 2% (volume ratio) of short discontinuous synthetic fibers (in the form of mass reinforcement, comprising PVA - Polyvinyl Alcohol fibers). This class of cementitious materials exhibits ductility under tension with the formation of multiple fine cracks and significant delay of crack stabilization (i.e., localization of cracking at a single location). One of the behavioral parameters that concern structural design is the shear strength of this new type of fiber reinforced composites. This aspect was studied in the present work with the use of Push-off tests. The shear strength is then compared to the materials' tensile and splitting strength values.

• Computers and Concrete
• /
• v.29 no.1
• /
• pp.31-45
• /
• 2022

Experimental and numerical simulation were used to investigate the effects of angle and number of T shape non-persistent crack on the shear behaviour of crack's bridge area under uniaxial compressive test. concrete samples with dimension of 150 mm×150 mm×40 mm were prepared. Within the specimen, T shape non-persistent notches were provided. 16 different configuration systems were prepared for T shape non-persistent crack based on two and three cracks. In these configurations, the length of cracks were taken as 4 cm and 2 cm based on the cracks configuration systems. The angle of larger crack related to horizontal axis was 0°, 30°, 60° and 90°. Similar to cracks configuration systems in the experimental tests, 28 models with different T shape non-persistent crack angle were prepared in numerical model. The length of cracks were taken as 4 cm and 2 cm based on the cracks configuration systems. The angle of larger crack related to horizontal axis was 0°, 15°, 30°, 45°, 60°, 75° and 90°. Tensile strength of concrete was 1 MPa. The axial load was applied to the model. Displacement loading rate was controlled to 0.005 mm/s. Results indicated that the failure process was significantly controled by the T shape non-persistent crack angle and crack number. The compressive strengths of the specimens were related to the fracture pattern and failure mechanism of the discontinuities. Furthermore, it was shown that the compressive behaviour of discontinuities is related to the number of the induced tensile cracks which are increased by increasing the crack number and crack angle. The strength of samples decreased by increasing the crack number. In addition, the failure pattern and failure strength are similar in both methods i.e. the experimental testing and the numerical simulation methods (PFC2D).

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04a
• /
• pp.379-384
• /
• 1998

To overcome the common deficiencies found in such two-way slabs, such as excessive cracking around columns, excessive deflections and low punching shear strength, it was proposed to investigate the strategic reinforcing steel distribution detailings. Concentration of the top mat of flexural reinforcement result in a higher punching shear resistance, higher post cracking stiffness, a more uniform distribution of strains in the top bars and smaller cracks at all levels of loading.

• Structural Engineering and Mechanics
• /
• v.9 no.5
• /
• pp.505-518
• /
• 2000

A major cause of premature debonding of tension face plates is shear peeling (Jones et al. 1988, Swamy et al. 1989, Ziraba et al. 1994, Zhang et al. 1995), that is debonding at the plate ends that is associated with the formation of shear diagonal cracks that are caused by the action of vertical shear forces. It is shown in this paper how side plated beams are less prone to shear peeling than tension face plated beams, as the side plate automatically increases the resistance of the reinforced concrete beam to shear peeling. Tests are used to determine the increase in the shear peeling resistance that the side plates provide, and also the effect of vertical shear forces on the pure flexural peeling strength that was determined in the companion paper. Design rules are then developed to prevent premature debonding of the plate ends due to peeling and they are applied to the strengthening and stiffening of continuous reinforced concrete beams. It is shown how these design rules for side plated beams can be adapted to allow for propped and unpropped construction and the time effects of creep and shrinkage, and how side plates can be used in conjunction with tension face plates.