• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.2
• /
• pp.317-326
• /
• 1997

An investigation was performed to study the matrix cracking and delamination in laminated composite plates due to transverse impact. A model was developed for predicting the initiation of the matrix cracking and the shape and size of impact-induced delamination in laminated composite plates resulting from the ballistic impact. The model consists of a stress analysis and a failure analysis. A transient finite element analysis which was based on the higher-order shear deformation theory was adopted for calculating the stresses inside the laminated composite plates during impact. A failure analysis was used to predict the initial intraply matrix cracking and the shape and size of the interface delamination in the laminates. As a results, a shear matrix cracking which was governed by the transverse interlaminar shear stress occured at the middle layer near the midplane of laminates and a bending matrix cracking which was governed by the transverse inplane stress occured at the bottom layer near the surface of laminates. In a thick laminates, a shear matrix cracking generated first at the middle layer of laminates, but in a thin laminates, a bending matrix cracking generated first at the bottom layer of laminates.

• International Journal of Concrete Structures and Materials
• /
• v.3 no.1
• /
• pp.47-56
• /
• 2009

The first diagonal cracking and ultimate shear load of reinforced girder made of ultra high performance fiber reinforced concrete (UHPFRC) were investigated in this paper. Eleven girders were tested in which eight girders failed in shear. A simplified formulation for the first diagonal cracking load was proposed. An analytical model to predict the ultimate shear load was formulated based on the two bounds theory. A fiber reinforcing parameter was constituted based on the random assumption of steel fiber uniform distribution. The predicted values were compared with the conventional predictions and the test results. The proposed equation can be used for the first cracking status analysis, while the proposed equations for computing the ultimate shear strength can be used for the ultimate failure status analysis, which can also be utilized for numerical limit analysis of reinforced UHPFRC girder. The established fiber reinforcing theoretical model can also be a reference for micro-mechanics analysis of UHPFRC.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1990.10a
• /
• pp.83-87
• /
• 1990

The effect of concrete strength on shear cracking strength in reinforced concrete beams is investigated analytically. The quantitative response of reinforced concrete beam-end-part with varing concrete stiffness, which is a function of concrete compressive strength, is examined utilizing a finite element mothod. The result indicates that the severer shear stress localization/concentration takes place in the beam having higher concrete strength. Thus the increase ratio of shear cracking strength with respect to concrete compressive strength decreases as the concrete strength becoms higher.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10b
• /
• pp.885-890
• /
• 2000

12 RC deep beams with a/d = 1.17 are reported. This paper is to study the effect of vertical and horizontal web reinforcement and web reinforcement arrangement on inclined cracking shear, ultimate shear strength, midspan deflection, and inclined crack width. Test results indicated that web reinforcement produces and arrangement seems to moderately affect inclined cracking shear, ultimate shear strength and crack width. However, addition of horizontal web reinforcement(pv = 0.0085) little or no influence on inclined cracking shear, ultimate shear strength and crack width. The member which vertical and horizontal web reinforcement concentrate on the center web considerably increases in load-carrying capacity.

• Journal of the Korea Concrete Institute
• /
• v.11 no.4
• /
• pp.43-54
• /
• 1999

Shear tests are performed on four full-scale 12.5 m proto-type models, "least depth double tee," which are resulted from the optimization process. Domestic superimposed live load regulation, domestic material properties which is available to product. Korean building code requirements, construction environments and economy are considered as the main factors to establish the process. All of the specimens tested fully comply with the shear strength requirements as specified by ACI 318-95. The research has shown following results. 1) The development length requirement of ACI 318-95 does not seem a good predictor for the estimation of bond failure in a beam with the strands below the supports. 2) The load required for the first initial coner cracking in the dap end and first web shear cracking does not seem to have any relation with the dimension and shear strength of the section in the test beams. 3) The strand slip has a direct relationship with the web shear cracking. However, the coner cracking in the dap end does not give any help for the slip in anchorage. 4) Use of whole area for bearing steel at the bottom of dap end is desired for safe bearing pressure design in the precast prestressed double tee beams. 5) The deflection of beam influences directly on the amount of strand slip at the anchorage after initiation of it, and relationship between them are very linear.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.3
• /
• pp.48-54
• /
• 2022

This research describes a quantitative procedure used to estimate the effect of concrete cracking on stiffness degradation of concrete shear walls and provides analytical references for the seismic design of concrete shear walls. As preliminary research on the seismic response of concrete shear walls, nonlinear transient analysis was performed with commercial FE software. The study presents the nonlinear time history analysis results in terms of concrete damage and cracking behavior induced by seismic input motions. By varying the input motions, concrete strength and shear wall thickness, the seismic responses of a shear wall were examined with nonlinear time history analysis, and the progressive cracking behavior and corresponding hysteresis loop were described. Based on the analysis results, frequency and stiffness degradation of the shear wall from progressive concrete damage and cracking were captured with respect to the seismic levels. The results of this study suggest that stiffness degradation from concrete cracking should be appropriately considered when determining the seismic capacity of RC shear wall structures.

• Computers and Concrete
• /
• v.12 no.5
• /
• pp.697-715
• /
• 2013

Numerous studies have been conducted to understand the shear behavior of reinforced concrete (RC) beams since it is a complex phenomenon. The diagonal cracking strength of a RC beam is critical since it is essential for determining the minimum amount of stirrups and the contribution of concrete to the shear strength of the beam. Most of the existing equations predicting the diagonal cracking strength of RC beams are based on experimental data. A powerful computational tool for analyzing experimental data is an artificial neural network (ANN). Its advantage over conventional methods for empirical modeling is that it does not require any functional form and it can be easily updated whenever additional data is available. An ANN model was developed for predicting the diagonal cracking strength of RC slender beams without stirrups. It is shown that the performance of the ANN model over the experimental data considered in this study is better than the performances of six design code equations and twelve equations proposed by various researchers. In addition, a parametric study was conducted to study the effects of various parameters on the diagonal cracking strength of RC slender beams without stirrups upon verifying the model.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.377-380
• /
• 1999

This paper dscribes an experimental investigation into the cause of flexural-shear failure in RC beams. The experimental variables are bottom flange width and tension bar location. Then these test results were compared and analyzed to deduce the major cause of critical-shear cracking. As a result, it was found that the propagation of the critical shear crack depended exclusively on the intensity of horizontal cracking.

• Structural Engineering and Mechanics
• /
• v.56 no.2
• /
• pp.317-340
• /
• 2015

Design codes have specified the minimum shear reinforcement requirement for reinforced concrete (RC) and prestressed concrete (PSC) members to prevent brittle and premature shear failure. They are, however, very different from one another, and particularly, ACI318 code allows the required minimum shear reinforcement to be reduced in PSC members, compared to that in RC members, by specifying the additional equation for PSC members whose basis is not clear. In this paper, the minimum shear reinforcement ratio for PSC members was proposed, which can provide a sufficient reserved shear strength and deformation capacity. The proposed equation was also verified by the test results of PSC specimens lightly reinforced in shear, comparing to design codes and other proposed equations from previous studies.

• Magazine of the Korea Concrete Institute
• /
• v.6 no.2
• /
• pp.118-128
• /
• 1994

There have been conducted a lot of works on shear behavior of steel fiber reinforced concrete beams. Fiber reinforced concrete beams without shear reinforcement were tested to determine their cracking shear strengths and ultimate shear capacities. Results of tests on 14 reinforced concrete beams (including 11 containing steel fibers) are reported. Two parameters were varied in the study, namely, the volume fraction of fibers and shear span-to-depth ratio.The effects of fiber incorporation on failure modes, deflections, cracking shear strength, and ul~imate shear strength have been examined. Resistance to shear stresses have been found to be improved by the inclusion of fibers, The mode of failure changed from shear to flexure when the shear span-to-depth ratio exceeds 3.4. Based on these investigations, a method of computing the shear strength of steel fiber reinforced concrete beam is suggested. The comparisons between computed values and expenmentally observed values are shown to verify the proposed theoretical treatment and steel fibers efficiency.