• Korean Journal of Materials Research
• /
• v.14 no.12
• /
• pp.885-888
• /
• 2004

$BaMgAl_{10}O_{17}:Eu^{2+}$ for PDP blue phosphor was synthesized using SHS(Self-propagating High temperature Synthesis) method. While Al metal powder was oxidized in this combustion, $Eu_{2}O_3$ was reduced to Eu2+. Therefore the mole ratio of $Al/Al_{2}O_3$ is one of the most important variable of the reaction. When $Al/Al_{2}O_3$ is 2.5/3.75, it has not only appropriate temperature and reaction velocity, but also excellent luminescent property. The sample synthesized in this system has similar characteristics comparing to sample using conventional solid-state reaction.

• Journal of Powder Materials
• /
• v.6 no.2
• /
• pp.145-151
• /
• 1999

Nickel silicides ($Ni_5$Si$_2$, Ni$_2$Si and NiSi) have been synthesized by mechanical alloying (MA) of Ni-27.9at.9at%Si, Ni-33.3at% and Ni-50.0at% powder mixtures, respectively. From in situ thermal analysis, eash citical milling period for the formation of the three phases was observed to be 40.2, 34.9 and 57.5 min, at which there was a rapid increase in temperature. This indicates that rapid, self-propagating high-temperature synthesis (SHS) reactions were observed to produce the three phases during room-temperature high-energy ball milling of elemental powders. Each Ni silicide, Ni and Si, however, coexisted for an extended milling time even after the critical milling period. The powders mechanically alloyed after the critical period showed the rapid increase in microhardness. The Hv values were found to be higher than 1000kgf/mm$^2$. The formation of nickel silicides by mechanical alloying and the relevant reaction rates appeared to be influenced by the critical milling period and the heat of formation of the products involved ($Ni_5$Si$_2$$\rightarrow$-43.1kJ/mol.at., Ni$_2$Si$\rightarrow$-47.6kJ/mol.at., NiSi$\rightarrow$-42.4kJ/mol.at).

• Journal of the Korean Ceramic Society
• /
• v.48 no.6
• /
• pp.559-564
• /
• 2011

In order to investigate the behavior of $SiO_2$ in the molybdenum silicide powders, crystal structure of these powders was measured by XRD, in addition, surface composition and surface phase (or chemical states) and microstructure were analysed by XPS and TEM, respectively. Mo-silicide powders containing $SiO_2$ were synthesized by SHS (Self-Propagating High-Temperature Synthesis) technique. In XRD result, according to increase of $SiO_2$ contents, the crystal structure for synthesized $MoSi_2$ powders was still typical $MoSi_2$ bct without any other phases. By XPS analysis, the surface of Mo and Si source powders was covered with $MoO_3$ and $SiO_2$, respectively, and the surface of synthesized $MoSi_2$ powder was also covered with $MoO_3$ and $SiO_2$, which were stable oxides at room temperature. However, according to increase of $SiO_2$ addition, $MoSi_2$ phase in XPS spectra decreased and $SiO_2$ phase increased relatively in synthesized $MoSi_2$ powders. From the results by XPS and XRD, we found that the existent $SiO_2$ has amorphous structure. In the microstructure, the small particulates of the synthesized products added $SiO_2$ agglomerated together to form larger clusters (from ~10 nm to ~1 ${\mu}m$). From TEM, XPS, and XRD results, we found that the out layer of agglomeration of synthesized $MoSi_2$ powder is surrounded by amorphous $SiO_2$.

• Korean Chemical Engineering Research
• /
• v.57 no.4
• /
• pp.553-558
• /
• 2019

In present study, the cylindrical susceptor by the slip casting method was designed to apply high-temperature induction heating by using $(Mo,W)Si_2$ ceramics. $MoSi_2$-based materials were synthesized by SHS (Self-propagating High-temperature Synthesis) method. The phase and crystal structure of $MoSi_2$-based materials were confirmed by XRD analysis. The shape of cylindrical mold was synthesized for various thickness by using the slip casting method. Finally, the susceptor for induction heating was processed by sintering and heat treatment to form $SiO_2$ layer, which was confirmed on the surface of susceptor by SEM/EDS analysis. To evaluate the heating performance of $(Mo,W)Si_2$ cylinder susceptor, we measured the maximum surface temperature and heating rate in comparison with the rod heating element under constantly applied power. The induction heating of the $(Mo,W)Si_2$ cylinder showed excellent heating performance, reaches the maximum temperature of $1457^{\circ}C$, with the average heating rate of $19^{\circ}C/s$ at 2 kW

• Journal of Powder Materials
• /
• v.6 no.3
• /
• pp.215-223
• /
• 1999

The synthesis of $Ni_5Si_2,\;Ni_2Si$ and NiSi has been investigated by mechanical alloying (MA) of Ni-27.9at%Si, Ni-33.3at%Si and Ni-50.0at%Si powder mixtures. As-received and premilled elemental powders were subjected to MA. The as-received Ni powder was spherical and the mean particle size 48.8$\mu$m, whereas the premilled Ni powder was flaky and the mean particle diameter and thickness were found to be 125 and 5$\mu$m, respectively. The mean surface area of the premilled Mi powder particle was 3.5 times as large as that of the as-received Ni powder particle. The as-received Si powder was was 10.0$\mu$m. Self-propagating high-temperature synthesis (SHS) reaction, followed by a slow reaction (a solid state diffusion), was observed to produce each Ni silicide during MA of the as-received elemental powders. In other word , the reactants and product coexisted for a long period of MA of time. Only SHS reaction was, however, observed to produce each Ni silicide during MA of the premilled elemental powders, indicating that each Ni sillicide formed rather abruptly at a short period of MA time. The mechanisms and reaction rates for the formation of the Ni silicides appeared to be influenced by the elemental powder particle size and shape as well as the heat of formation of the products $(Ni_5Si_2$longrightarrow-43.1kJ/mol.at., $Ni_2Si$$\rightarrow$-47.6kJ/mol.at.).

• Korean Journal of Metals and Materials
• /
• v.50 no.9
• /
• pp.677-684
• /
• 2012

A feasible way to fabricate in-situ Al/TiC composites was investigated. An elemental mixture of $Al-TiO_2-C$ pellet was directly added into an Al melt at $800-920^{\circ}C$ to form TiC by self-combustion reaction. The addition of CuO initiates the self-combustion reaction to form TiC in $1-2{\mu}m$ at the melt temperature above $850^{\circ}C$. Besides the CuO addition, a diluent element of excess Al plays a significant role in the TiC formation by forming a precursor phase, $Al_3Ti$. Processing parameters such as CuO content, the amount of excess Al and the melt temperature, have affected the combustion reaction and formation of TiC, and their influences on the microstructures of in-situ Al/TiC composites are examined.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.3
• /
• pp.212-218
• /
• 2017

$Mg_xNi_yZn_{1-x-y}Fe_2O_4$ ferrite powders were prepared by self-propagating high temperature synthesis followed by classifying with an ultrasonic wet-magnetic separation unit to get high pure nano-sized particles. The $Mg_xNi_yZn_{1-x-y}Fe_2O_4$ ferrites were well formed by using several powders like iron, nickel oxide, zinc oxide and magnesium oxide at 0.1 MPa of oxygen pressure. The ultrasonic wet-magnetic separation of pre-mechanical milled ferrite powders resulted in producing the powders with average size of 800 nm. The addition of a surfactant during the wet-magnetic separation process improved productivity more than twice. The coercive force, maximum magnetization and residual magnetization of the $Mg_xNi_yZn_{1-x-y}Fe_2O_4$ nano-powders with 800 nm size were 3651 A/m, $53.92Am^2/kg$ and $4.0Am^2/kg$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.45 no.7
• /
• pp.418-422
• /
• 2008

The preparation of FeB by SHS in $B_2O_3-Mg-Fe-Fe_3O_4$ system was investigated in this study. In the preparation of FeB, the effects of the initial pressure of inert gas in reactor, the content of Mg and $Fe_3O_4$ in mixture on the reactivity and reaction products was investigated. The minimum initial pressure of inert gas in reactor for SHS reaction in this system was 25 atm, and as the pressure increased, the concentration of unreacted Mg decreased and combustion temperature increased. At the initial inert gas pressure in reactor of 25 atm, the optimum composition for the preparation of pure FeB was $1.5B_2O_3$+3.43Mg+ 1.7Fe+$0.1Fe_3O_4$. The FeB synthesized in this condition had an irregular shape and the particle size of $5\;{\mu}m$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.201.2-201.2
• /
• 2016

$Mg_xNi_yZn_{1-x-y}Fe_2O_4$ ferrite powders were prepared by self-propagating high temperature synthesis followed by classified by ultrasonic wet-magnetic separation method to get nano-sized particles with high purity. The $Mg_xNi_yZn_{1-x-y}Fe_2O_4$ ferrites were well formed by using several powders like iron, nickel oxide, zinc oxide and magnesium oxide at 0.1 MPa of oxygen pressure. The ultrasonic wet-magnetic separation of pre-mechanical milled ferrite powders produced the powders with average size of $3.7-0.8{\mu}m$. The addition of a surfactant during the separation process improved productivity more than twice. The coercive force, maximum magnetization and residual magnetization of the $Mg_xNi_yZn_{1-x-y}Fe_2O_4$ nano-powders with 810 nm size were 45.89 Oe, 53.92 emu/gOe, 0.4 emu/Oe, respectively.

• Journal of the Korean Ceramic Society
• /
• v.44 no.6 s.301
• /
• pp.338-342
• /
• 2007

Porous silicon nitride ceramics were prepared by SHS (Self-Propagating High Temperature Synthesis) from silicon powder, silicon nitride powder and pore-forming precursor. The microstructure, porosity and the flexural strength of the porous silicon nitride ceramics were varied according to the Si/Si3N4 ratio, size and amount of the pore-forming precursors. Some sample exhibited as high flexural strength as $162{\pm}24\;MPa$. The high strength is considered to result from the fine pore size and the strong bonding amoung the silicon nitride particles.