• The Journal of Advanced Prosthodontics
• /
• v.5 no.4
• /
• pp.479-484
• /
• 2013

PURPOSE. The aim of this study was to evaluate the effects of additional acid etching and curing mechanism (light-curing or self-curing) of a composite resin on the dentin bond strength and compatibility of one-step self-etching adhesives. MATERIALS AND METHODS. Sixteen human permanent molars were randomly divided into eight groups according to the adhesives used (All-Bond Universal: ABU, Clearfil S3 Bond: CS3), additional acid etching (additional acid etching performed: EO, no additional acid etching performed: EX), and composite resins (Filtek Z-250: Z250, Clearfil FII New Bond: CFNB). Group 1: ABU-EO-Z250, Group 2: ABU-EO-CFNB, Group 3: ABU-EX-Z250, Group 4: ABU-EX-CFNB, Group 5: CS3-EO-Z250, Group 6: CS3-EO-CFNB, Group 7: CS3-EX-Z250, Group 8: CS3-EX-CFNB. After bonding procedures, composite resins were built up on dentin surfaces. After 24-hour water storage, the teeth were sectioned to make 10 specimens for each group. The microtensile bond strength test was performed using a microtensile testing machine. The failure mode of the fractured specimens was examined by means of an optical microscope at ${\times}20$ magnification. The data was analyzed using a one-way ANOVA and Scheffe's post-hoc test (${\alpha}$=.05). RESULTS. Additional etching groups showed significantly higher values than the no additional etching group when using All-Bond Universal. The light-cured composite resin groups showed significantly higher values than the self-cured composite resin groups in the Clearfil S3 Bond. CONCLUSION. The additional acid etching is beneficial for the dentin bond strength when using low acidic one-step self-etch adhesives, and low acidic one-step self-etch adhesives are compatible with self-cured composite resin. The acidity of the one-step self-etch adhesives is an influencing factor in terms of the dentin bonding strength and incompatibility with a self-cured composite resin.

• The Journal of Korean Academy of Prosthodontics
• /
• v.46 no.2
• /
• pp.148-156
• /
• 2008

Statement of problems: Self-etch adhesives exhibit some clinical benefits such as ease of manipulation and reduced technique-sensitivity. Nevertheless, some concern remains regarding the bonding effectiveness of self-etch adhesives to enamel, in particular when so-called 'mild' self-etch adhesives are employed. This study compared the microtensile bond strengths to ground enamel of the two-step self-etch adhesive Clearfil SE Bond (Kuraray) to the three-step etch-and- rinse adhesive Scotchbond Multi-Purpose (3M ESPE) and the one-step self-etch adhesive iBond (Heraeus Kulzer). Purpose: The purpose of this study was to determine the effect of a preceding phosphoric acid conditioning step on the bonding effectiveness of a two-step self-etch adhesive to ground enamel. Material and methods: The two-step self-etch adhesive Clearfil SE Bond non-etch group, Clearfil SE Bond etch group with prior 35% phosphoric acid etching, and the one-step self-etch adhesive iBond group were used as experimental groups. The three-step etch-and-rinse adhesive Scotchbond Multi-Purpose was used as a control group. The facial surfaces of bovine incisors were divided in four equal parts cruciformly, and randomly distributed into each group. The facial surface of each incisor was ground with 800-grit silicon carbide paper. Each adhesive group was applied according to the manufacturer's instructions to ground enamel, after which the surface was built up using Light-Core (Bisco). After storage in distilled water at $37^{\circ}C$ for 1 week, the restored teeth were sectioned into enamel beams approximately 0.8*0.8mm in cross section using a low speed precision diamond saw (TOPMET Metsaw-LS). After storage in distilled water at $37^{\circ}C$ for 1 month, 3 months, microtensile bond strength evaluations were performed using microspecimens. The microtensile bond strength (MPa) was derived by dividing the imposed force (N) at time of fracture by the bond area ($mm^2$). The mode of failure at the interface was determined with a microscope (Microscope-B nocular, Nikon). The data of microtensile bond strength were statistically analyzed using a one-way ANOVA, followed by Least Significant Difference Post Hoc Test at a significance level of 5%. Results: The mean microtensile bond strength after 1 month of storage showed no statistically significant difference between all adhesive groups (P>0.05). After 3 months of storage, adhesion to ground enamel of iBond was not significantly different from Clearfil SE Bond etch (P>>0.05), while Clearfil SE Bond non-etch and Scotchbond Multi-Purpose demonstrated significantly lower bond strengths (P<0.05), with no significant differences between the two adhesives. Conclusion: In this study the microtensile bond strength to ground enamel of two-step self-etch adhesive Clearfil SE Bond was not significantly different from three-step etch-and-rinse adhesive Scotchbond Multi-Purpose, and prior etching with 35% phosphoric acid significantly increased the bonding effectiveness of Clearfil SE Bond to enamel at 3 months.

• The Journal of Korean Academy of Prosthodontics
• /
• v.44 no.4
• /
• pp.383-393
• /
• 2006

Statement of problem : Limited research on flowable resin has been undertaken on its application directly on dentin associated with the adhesive systems. Purpose : This study was to evaluate the shear bond strengh and fracture aspect of flowable resin on human dentin with various types of dentin bonding adhesives with thermo cycling effect. Materials and methods: Filtek-Flow(3M ESPE, USA) was used as flowable resin and Eighty human molars were randomly divided into 4 groups : three dentin bonding adhesives (Scotchbond-Multipurpose : 3-step contentional system, One-Step : One-bottle system. Prompt L-Pop : All-in-one, self-etching primer) and 32% etching treatment without bonding adhesive as a control group. For evaluating their durability of bonding, each group was subdivided : storaging in the water at 37$^{\circ}C$(24 hours) and thermocycling (0$^{\circ}C$-55$^{\circ}C$, 30 seconds intervals, 1000 cycle). Shear bond strength tests were performed and resin-dentin interface and fracture mode were observed. Results were analysed by one-way ANOVA and Scheffe's multiple range test. Results and Conclusion : 1. At 0 cycle, the mean shear bond strength of One-Step exhibited the highest value of all groups(p<0.05), and there were no significant differences between Prompt L-Pop and Scotchbond-Multipurpose, Scotchbond-Multipurpose and control(p>0.05). After 1000 thermocycling, One-Step exhibited higher value than other groups(p<0.05), and there were no significant differences among other groups (p>0.05). 2. The shear bond strength of each group was significantly decreased after thermocycling except Scotchbond-Multipurpose (p>0.05). 3. The most common failure mode was adhesive type and mixed type, next in order.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.44 no.4
• /
• pp.419-426
• /
• 2017

Attachment of the orthodontic bracket conducted during the window opening procedure can result in failure due to various adverse conditions such as blood or saliva contamination, or other wet conditions. For the success of the bracket attachment, reduction of total operation time is crucial. The purpose of this literature is to evaluate the differences between the final resultant shear bond strength of the conventional method of using phosphoric acid and self-etching primer, and that of the operation time-reduced method in which the curing step is omitted subsequent to the primer application. A total of 40 human maxillary incisors were prepared. Group I(control group) and II were etched with 37% phosphoric acid and Group III and IV were conditioned with self-etching primer. Attachment of the group I and III was conducted by manufacturer's instructions. The operation time of Group II and IV was reduced by eliminating the curing step after the primer application. The resultant shear bond strength of each group was measured and an adhesive remnant index (ARI) was recorded. The mean shear bond strength of group I, II, III, and IV were 14.16 MPa, 8.33 MPa, 8.29 MPa, and 6.48 MPa respectively. Significant differences could only be found between the control group and the experimental groups (p < 0.05). The ARI indicated no significant difference among all groups.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.5
• /
• pp.350-357
• /
• 2017

PURPOSE. The object of the present study was to evaluate the shear bonding strength of composite to PEKK by applying several methods of surface treatment associated with various bonding materials. MATERIALS AND METHODS. One hundred and fifty PEKK specimens were assigned randomly to fifteen groups (n = 10) with the combination of three different surface treatments (95% sulfuric acid etching, airborne abrasion with $50{\mu}m$ alumina, and airborne abrasion with $110{\mu}m$ silica-coating alumina) and five different bonding materials (Luxatemp Glaze & Bond, Visio.link, All-Bond Universal, Single Bond Universal, and Monobond Plus with Heliobond). After surface treatment, surface roughness and contact angles were examined. Topography modifications after surface treatment were assessed with scanning electron microscopy. Resin composite was mounted on each specimen and then subjected to shear bond strength (SBS) test. SBS data were analyzed statistically using two-way ANOVA, and post-hoc Tukey's test (P<.05). RESULTS. Regardless of bonding materials, mechanical surface treatment groups yielded significantly higher shear bonding strength values than chemical surface treatment groups. Unlike other adhesives, MDP and silane containing self-etching universal adhesive (Single Bond Universal) showed an effective shear bonding strength regardless of surface treatment method. CONCLUSION. Mechanical surface treatment behaves better in terms of PEKK bonding. In addition, self-etching universal adhesive (Single Bond Universal) can be an alternative bonding material to PEKK irrespective of surface treatment method.

• Proceedings of the KACD Conference
• /
• 2001.11a
• /
• pp.560.1-560
• /
• 2001

To evaluate the micro-shear bond strength of current adhesive systems to cervical and mid-coronal enamel. Materials and Two commercially available resin adhesives were investigated; a self-etching primer system(Clearfil SE Bond, Kyraray) and a one-bottle adhesive system(Single Bond, 3M) intended for use with the total-etch wet-bonding technique were employed. Two regions of enamel, cervical and mid-coronal regions, were chosen from the buccal surface of extracted molars and were then bonded with each adhesive system and submitted to the micro-shear bond test.(중략)

• Restorative Dentistry and Endodontics
• /
• v.29 no.2
• /
• pp.185-190
• /
• 2004

자가산부식 접착제 (self-etching primer)는 법랑질과 상아질을 동시에 산부식과 프라이머 처리를 함으로 임상 시술 시간을 단축시킬 뿐만 아니라, 임상과정 중 발생할 수 있는 술자의 실수 및 타액등에 의한 오염의 가능성을 줄일 수 있는 장점을 가지고 있다. 그러나 약산을 이용한 산부식법이 법랑질에 대해 탈회효과 및 접착강도에 있어 논란이 되고 있다. 이에 본 연구에서는 인산을 이용한 추가적인 산부식 및 자가산부식 접착제의 적용시간을 달리할 경우 법랑질에 대한 접착강도의 변화를 알아보고자 하였다. 135개의 발거한 우치의 법랑질 면을 ＃600사포로 연마한 후 9개의 군으로 분류하였다. 각 군은 부가적인 32% 인산을 처리하지 않은 군 (1~3군), 15초간 처리한 군 (4~6군), 60초간 처리한 군 (7~9군)으로 나누고, 이를 다시 Clearfil SE Bond의 프라이머로 5초 (1, 4, 7군), 20초 (2, 5, 8군), 60초 (3, 6, 9군)간 처리한 군으로 분류하였다. 접착제 처리한 면에 Clearfil AP-X 복합레진을 접착하고 24시간 경과 후 전단응력 강도를 측정하였다. 결과는 One-way ANOVA 처리후 Duncan's multiple range test로 사후검증하였다. 동일한 자가산부식 프라이머 처리 시간을 가진 군에서 산 부식을 한 경우가 그렇지 않은 군에 비해 높은 접착강도를 나타내었으며 인산부식 시간의 차이에 의한 영향은 없었다.(1 < 4, 7군/ 2 < 5, 8군/ 3 < 6, 9군). 자가산부식제의 프라이머 적용 시간에 의한 효과는 1군(5초 적용)을 제외한 나머지 군의 경우 동일한 인산 처리군에서는 차이가 없는 것으로 나타났다.(1군 < 2, 3군/ 4＝5＝6군/ 7＝8＝9군). Clearfil SE Bond 접착제의 법랑질에 대한 접착강도는 부가적인 산부식을 통하여 증가시킬 수 있으며 프라이머의 적용 시간에 의한 효과는 제조자의 지시에 의한 시간 이상 적용할 경우 차이가 없는 것으로 나타났다.

• Proceedings of the KACD Conference
• /
• 2008.05a
• /
• pp.224-234
• /
• 2008

The purpose of this study was to compare the normal and two times of application time of six self-etching primers applied to enamel using microshear bond strength (uSBS) test and the finding of scanning electronic microscope (SEM). Crown of sixty human molars were bisected mesiodistally and buccal and lingual enamel of crowns were partially exposed and polished with 600 grit SiC papers. They were divided into one of two equal groups subdivided into one of six equal groups (n = 10) by self-etching primer adhesives. After the same manufacture's adhesive resin and composites were bonded on the enamel surface of each group, the bonded specimens were subjected to uSBS testing and also observed under SEM. In conclusion, generally two times of primer application time increased the enamel uSBS, especially with the statistical increase of bond strength in adhesives involving high-pH primers.

• Restorative Dentistry and Endodontics
• /
• v.33 no.3
• /
• pp.224-234
• /
• 2008

The purpose of this study was to compare the normal and two times of application time of six self-etching primers applied to enamel using microshear bond strength (uSBS) test and the finding of scanning electronic microscope (SEM). Crown of sixty human molars were bisected mesiodistally and buccal and lingual enamel of crowns were partially exposed and polished with 600 grit SiC papers. They were divided into one of two equal groups subdivided into one of six equal groups (n = 10) by self-etching primer adhesives. After the same manufacture's adhesive resin and composites were bonded on the enamel surface of each group, the bonded specimens were subjected to uSBS testing and also observed under SEM. In conclusion, generally two times of primer application time increased the enamel uSBS, especially with the statistical increase of bond strength in adhesives involving high-pH primers.

• Restorative Dentistry and Endodontics
• /
• v.34 no.5
• /
• pp.397-405
• /
• 2009

This study compared the effect of an activator, intermediate bonding resin and low-viscosity flowable resin on the microtensile bond strength of a self-curing composite resin used with two-step total etching adhesives. Twenty extracted permanent molars were used. The teeth were assigned randomly to nine groups (n=10) according to the adhesive system and application of additional methods (activator, intermediate adhesive, flowable resin). The bonding agents and additional applications of each group were applied to the dentin surfaces. Self-curing composite resin buildups were made for each tooth to form a core, 5mm in height. The restored teeth were then stored in distilled water at room temperature for 24h before sectioning. The microtensile bond strength of all specimens was examined. The data was analyzed statistically by one-way ANOVA and a Scheffe's test. The application of an intermediate bonding resin (Optibond FL adhesive) and low-viscosity flowable resin (Tetric N-flow) produced higher bond strength than that with the activator in all groups. Regardless of the method selected, Optibond solo plus produced the lowest ${\mu}TBS$ to dentin. The failure modes of the tested dentin bonding agents were mostly adhesive failure but there were some cases showed cohesive failure in the resin.