• Progress in Superconductivity
• /
• 제3권1호
• /
• pp.36-40
• /
• 2001

We have studied vortex dynamics in$ Bi_2$$Sr_2$$CaCu_2$O$_{8}$single crystals of unirradiated and irradiated samples by using 100 $\times$ $100\mu\textrm{m}^2$Hall sensor. Doses equivalent magnetic fields are 20 G, 100 G and 1 kG. In the magnetization measurement, a second magnetization peak (SMP) was observed in unirradiated, 20 G dose and 100 G dose samples in contrast to 1 kG dose sample. In the unirradiated sample, the SMP was observed in the range of 18 K ~ 35 K and the amplitude of the SMP decreased with increasing temperature. With increase of the irradiation dose, temperature region and sharpness of the SMP were reduced. In the magnetic relaxation measurement, we observed that the normalized relaxation rate S decreased with increasing the irradiation dose. Our results suggest that the vortex dynamics is not greatly affected by low-density columnar defects.s.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2001년도 High Temperature Superconductivity Vol.XI
• /
• pp.22-22
• /
• 2001

• 한국자기학회지
• /
• 제20권6호
• /
• pp.228-233
• /
• 2010

본 연구에서는 비정질 CoFeHfO 박막 재료의 두께 변화에 따른 고주파 손실 특성을 분석하기 위하여 57~1368 nm 두께의 CoFeHfO 박막 재료에 대해 마이크로파 투자율 특성을 분석하였다. 두께가 405 nm이하에서 허수부 투자율은 2.95 GHz에서 하나의 공진주파수를 보이지만, 405 nm 이상에서는 2.97 GHz와 547 MHz에서 두 개의 공진주파수를 보인다. 저자장하에서 측정한 토오크 곡선 결과로부터 547 MHz에서 발생되는 공진주파수는 CoFeHfO 재료의 자화 용이축들의 각도 분포에 기인하는 것으로 자기장의 세기에 따라서 급격하게 감소하는 특성을 보인다. 따라서 두께가 400 nm 이상의 CoFeHfO 박막 재료를 2 GHz 대역에서 작동하는 초소형 마이크로파 부품에 적용하기 위해서는 자화 용이축의 분포각도를 최소화시켜야 한다.