• Korean Journal of Materials Research
• /
• v.20 no.11
• /
• pp.570-574
• /
• 2010

A diamond-like carbon (DLC) film deposited on a WC disk was investigated to improve disk wear resistance for injection molding of zirconia optical ferrule. The deposition of DLC films was performed using the filtered vacuum arc ion plating (FV-AIP) system with a graphite target. The coating processing was controlled with different deposition times and the other conditions for coating, such as input power, working pressure, substrate temperature, gas flow, and bias voltage, were fixed. The coating layers of DLC were characterized using FE-SEM, AFM, and Raman spectrometry; the mechanical properties were investigated with a scratch tester and a nano-indenter. The friction coefficient of the DLC coated on the WC was obtained using a pin-on-disk, according to the ASTM G163-99. The thickness of DLC films coated for 20 min. and 60 min. was about 750 nm and 300 nm, respectively. The surface roughness of DLC films coated for 60 min. was 5.9 nm. The Raman spectrum revealed that the G peak of DLC film was composed of $sp^3$ amorphous carbon bonds. The critical load (Lc) of DLC film obtained with the scratch tester was 14.6 N. The hardness and elastic modulus of DLC measured with the nano-indenter were 36.9 GPa and 585.5 GPa, respectively. The friction coefficient of DLC coated on WC decreased from 0.2 to 0.01. The wear property of DLC coated on WC was enhanced by a factor of 20.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.5
• /
• pp.357-363
• /
• 2003

The aim of this work is the synthesis of a-C:H films from methane gas using surface spark discharge at the atmospheric pressure. Properties of these films have been investigated as functions of energy W delivered per a methane molecule in the discharge. The method enables the coatings to be deposited with high growth rates (up to $100 \mu\textrm{m}$/hour) onto large-area substrates. It is shown that the films consist of spherical granules with diameter of 20∼50 nm formed in the spark channel and then deposited onto the substrate. The best film characteristics such as minimum hydrogen-to-carbon atoms ratio H/C=0.69, maximum hardness $H_{v}$ =3 ㎬, the most dense packing of the granules and highest scratch resistance has been obtained under the condition of highest energy W of 40 eV. The deposited a-C:H coatings were found to be more soft and hydrogenated compared to the diamond-like hydrogenated (a-C:H) films which obtained by traditional plasmaenhanced chemical vapor deposition methods at low pressure (＜10 Torr). Nevertheless, these coatings can be potentially used for scratch protection of soft plastic materials since they are of an order harder than plastics but still transparent (the absorption coefficient is about $10^4$∼$10^{5}$ $m^{-1}$ At the same time the proposed method for fast deposition of a-C:H films makes this process less expensive compared to the conventional techniques. This advantage can widen the application field of. these films substantially.y.

• Journal of the Korean Magnetics Society
• /
• v.10 no.6
• /
• pp.310-317
• /
• 2000

With use of (G)MR head, thermal asperity (TA) has been a big concern in drive industry. In this study, we investigated several factors of heads and disks which affects the TA sensitivity of the drive. TA experiments were conducted by introducing the particles on the drives using a particle injection chamber. It was found that the slider ABS shape can help to reduce TA or contamination in the head/media interface. However, TA sensitivity of the drive mainly depend on the intrinsic property of (G)MR sensor. GMR head is much less sensitive to TA compared with MR head. However, in case that the same bias current was applied for both of MR and GMR head, TA sensitivity of GMR head became almost identical to that of MR head. Therefore it was found that the bias current is a dominant factor in determining TA sensitivity of the head. TA sensitivity of different types of disks was also studied. The scratch resistance of the carbon overcoat layer is the one of the main factors which influence TA rejection capability of the disks.

• Journal of Mechanical Science and Technology
• /
• v.16 no.7
• /
• pp.911-918
• /
• 2002

The tribological performance of A1$_2$O$_3$/NiCr coating deposited on steel (SH45C) was investigated under lubrication. The parameters of sliding wear consist of normal load and coating thickness. Test result showed that there was no evidence of an improved bonding strength in the coating. However, the wear resistance of the A1$_2$O$_3$/NiCr coaling was significantly greater than that of the Al$_2$O$_3$ coating. It was eviclent that the residual stress for the A1$_2$O$_3$coating was higher than that of the A1$_2$O$_3$/NiCr coating from the Scratch test failure of coating. The bond coating played an important role in decreasing the residual stress. Also, it was found that the residual stress had d notable influence on the wear mechanism.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.10a
• /
• pp.89-92
• /
• 2003

Nano-scratch tests were performed on PMMA thin films spin-coated on a Si substrate using an atomic force microscopy (AFM) with loads ranging from 10nN to 100nN. At low applied loads, a ridge pattern was formed on the PMMA surface. No wear particles were observed during the pattern-forming mild wear. At high applied loads, severe wear occurred accompanied by wear particles. The film with the highest hardness showed the highest wear resistance. Friction force generated during the Scratching was closely related with surface deformation of the film.

• Clean Technology
• /
• v.11 no.3
• /
• pp.153-164
• /
• 2005

This study found a reliable evaluation for four kinds of pb-Free plating solutions and it's layers, through pure Sn, SnAg, SnBi and SnCu. These four kind of solutions are widely used to pb-Free plating. Hull-cell, Harring-blum, coverage, throwing power, current efficiency, stability, life-time, composition, hardness, roughness, abrasion, scratch, solderability, corrosion, contact angle, morphology, SIR(Surface insulation resistance) and Whisker test were experimented. Also, Using ICP, XRF, FE-SEM, EDS, temperature/humidity chamber, solderability tester, hardness tester, roughness tester, abrasion tester, salt spray tester, contact angle tester, SIR tester, and microscope. In this paper could be shown the systematic and various analysis for reliability about four kinds of pb-Free plating solutions, processes and it's deposit surface.

• Journal of the Korean institute of surface engineering
• /
• v.28 no.6
• /
• pp.343-351
• /
• 1995

Titanium nitride films have been prepared on various substrates (silicon wafer, HSS) by cathode arc ion plating process to measure microhardness, adhesion and wear-resistant behaviors by changing the substrate bias voltages (0∼-300V), thickness and roughness. Microhardnesses were measured by micro vickers hardness tester, the adhesion strengths were evaluated by acoustic signals through the scratch test with incremental applied load. As the substrate bias voltages were increased, the ｛111｝ orientation was predominant, the microhardnesses and adhesion strengths of tool steel were observed to be stronger than those of without subatrate bias voltage. Adhesion strengths of the substrate bias were 4-7 times higher than those of without the substrate bias, confirmed by SEM with EDX. Wear resistances were used pin-on-disk tribotester and TiN costing reduced the abrasive wear. As the substrate bias was increased, the weight loss and the friction coefficient was decreased.

• KSTLE International Journal
• /
• v.9 no.1_2
• /
• pp.31-35
• /
• 2008

DLC (Diamond Like Carbon) films have predominant tribological properties like a high hardness, low friction and high chemical resistance; therefore, DLC films are applied in a wide range of industrial fields. This paper evaluated the characteristics of DLC films deposited on bearing steel with different hardness by RF-PECVD (Radio Frequency - Plasma Enhanced Chemical Vapor Deposition) method. Si-interlayer was deposited on bearing steel to improve adhesion strength by RF-Sputtering method. The DLC film structures were analyzed with Raman spectra and Gaussian function. Adhesion strength of DLC films was measured with a scratch tester. Friction and wear test were carried out with a ball-on -disc type to investigate the tribological characteristics. Experimental results showed that DLC films deposited on bearing steel under same deposition condition have typical structure DLC films regardless of hardness of bearing steel. Adhesion strength of DLC film is increased with a hardness of bearing steel. Friction coefficient of DLC film showed lower at the high hardness of bearing steel.

• Journal of the Semiconductor & Display Technology
• /
• v.13 no.1
• /
• pp.35-41
• /
• 2014

UV curable transparent hard coating materials have been developed to improve the mechanical and optical properties of PET substrate. The coating materials were synthesized using various urethane acrylate oligomers, monomers, photo initiators, and leveling agents. The materials were coated on PET substrates and UV cured. The hard coated PET films were shown to have the good scratch resistance and transparency. When the urethane acrylate oligomer with more functional groups was introduced into the coating solution, the mechanical and optical properties were improved. However the higher concentration of 9-functional oligomer resulted in the decrease of workability. The addition of trimethylolpropane ethoxylate$(EO/OH)_9$ triacrylate(TMPETA) to coating solution improved the workability and properties. As a result, the UV cured film from the formulation of urethane acrylate oligomer with 9-functional groups, TMPETA as a monomer, IRACURE 754 as a photo initiator and BYK-340 as a leveling agent showed the best mechanical and optical properties in this study.

• Corrosion Science and Technology
• /
• v.10 no.2
• /
• pp.65-70
• /
• 2011

DLC is considered as the candidate material for application of moving parts in automotive components relatively in high pressure and temperature operating conditions for its high hardness with self lubrication and chemical inertness. The properties of interlayer between the substrate and the DLC film were studied. Arc ion plating method have been employed to deposit onto substrate and sputtering method was used for synthesizing DLC onto interlayer. Among these six types of interlayer, deposited DLC film onto TiCN showed excellent value for characteristics. From the results of analysis for physical properties of DLC films, it seems that the adhesion forces were more important factors than intrinsic mechanical properties such as hardness, roughness and wear resistance of DLC films. AFM(Atomic Force Microscope) was used for understanding roughness of DLC films. Hardnesses of the coating layers were identified by nano-indentation method and adhesions were checked by scratch method.