• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.1065-1068
• /
• 2008

Marine bridges are readily deteriorated due to the exposure to marine environment. The concrete deterioration occurred by corrosion of steel in concrete is mainly relevant to chloride in seawater. Chloride ions penetrate through porous concrete, and then reach to the reinforcing steel, and finally corroded them. The corrosion by-products(rusts) increase the volume as much as 6 to 10 times of origin steel. this creates expanding pressure and tensile stress, which cause the structures cracking and spalling. Sometimes the rebar corrosion is accelerated, and then collapsed catastrophically. In order to prevent corrosion damage, it is important to understand well regarding the reason of concrete corrosion, the quantification of its damage, and protection method/system to stop or to mitigate the corrosion. In this study, slab specimens were fabricated to evaluate the effect of cathodic protection which was simulated to marine bridges, and/or port structures. Zn-mesh sacrificial anode has been applied as a chathodic protection system and accelerated test conditions, i.e. temperature and salt concentration have been used in this study.

• Journal of Ocean Engineering and Technology
• /
• v.25 no.2
• /
• pp.85-91
• /
• 2011

Many protection methods such as surface coating, electric protection, or other methods have been applied to the numerous steel structures widely used in continental and marine areas to control their corrosion, which is done from an economic point of view. Most of these steel structures are primarily protected by coating methods. However, some steel piles under seawater are protected by the electric protection method, that is, either using an impressed current or a sacrificial anode method. Furthermore, environmental contamination may cause a severely corrosive environment, which, in turn, causes the accelerated corrosion of steel structures. Subsequently, coated steel structures could deteriorate more rapidly than the designed lifetime because of the acid rain caused by air pollution, etc. Therefore, a coating of marine paint exposed to seawater, that is, underwater hardening painting, is increasingly required to be fast drying as well as highly corrosion resistant. In this study, five types of underwater hardening paints were prepared with different resin series and additives. Their corrosion and water resistances were investigated using electrochemical methods such as corrosion potential, polarization curves, impedance and cyclic voltammogram measurements, etc. Even though it is generally accepted that the corrosion resistance of bare steel tends to increase with a shift of the corrosion potential in the noble direction, the corrosion resistance of a sample with a coating exhibited a relatively better tendency when it had a lower corrosion potential in this study. The corrosion current density was also decreased with a decrease in the diffusion limiting current density, which may mean that there is some relationship between corrosion and water resistance. The S sample of the ceramic resin series showed the relatively best corrosion and water resistance among those of samples, while the worst corrosion and water resistance were observed for the R sample of the epoxy resin series. The corrosion and water resistance of those samples tended to deteriorate with an increase in the immersion days, and their corrosion and water resistances were considered to be apparently improved by the types of resin and additives.