Recently, railway industry has been developed not only functional parts such as acceleration and high performance of the railway but also emotional parts such as improved ride comfort and blocking noise. However, some important components of railway such as wheel and rail always had exposed too much operation time, cyclic load and rolling contact directly. The variations of load, vibration and chemical compositions were caused of wheel and rail having a lot of different types of contact fatigue damages. Therefore, It is necessary to improve inspection and maintenance technology in order to ensure safety and reliability of railway. Many researchers have already been reported the technology. Magnetic camera, one of the non-destructive testing technique can be used to inspect and evaluate the changes of magnetic field in ferromagnetic and paramagnetic materials with cracks. When an electromagnetic is applied to a specimen, a magnetic field will be distorted around a crack on the specimen. In present paper, the distribution of magnetic property in wheel with cracks using magnetic camera had investigated. The crack can be detected and evaluated by distribution analysis of magnetic field. The magnetic camera technique can be detected and evaluated the crack by rolling contact fatigue.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2011.06a
• /
• pp.1551-1552
• /
• 2011

• Tribology and Lubricants
• /
• v.22 no.6
• /
• pp.320-328
• /
• 2006

In this study, the simulation of rolling contact fatigue based on stress analysis is conducted under Elastohydrodynamic Lubrication state. To predict a crack initiation life accurately, it is necessary to calculate contact stress and subsurface stresses accurately. Contact stresses are obtained by contact analysis of a semi-infinile solid based on the use of influence functions and the subsurface stress field is obtained using rectangular patch solutions. And a numerical algorithm using Newton-Rapson method was constructed to calculate the Elastohydrodynamic lubrication pressure. Based on these stress values, several multiaxial high-cycle fatigue criteria are used and the critical loads corresponding to fatigue limits are calculated.

• Journal of the Korean Society for Precision Engineering
• /
• v.28 no.5
• /
• pp.565-571
• /
• 2011

Because most fatigue cracks in wheel and rail take place by rolling contact of wheel and rail in railroad industry, it is critical to understand the rolling contact phenomena, especially for the three-dimensional situation. This paper presents an approach to steady-state rolling contact problem of three-dimensional contact bodies, with or without tangential force, based on the finite element method. The steady-state conditions are controlled by the applied relative slip and tangential force. The three-dimensional distribution of tangential traction and contact stresses on the contact surface are investigated. Results show that the distribution of tangential traction and contact stresses on the contact surface varies rapidly as a result of the variation of stick-slip region. The tangential traction is very close in form to Carter's distribution.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2013.05a
• /
• pp.1583-1584
• /
• 2013

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2010.11a
• /
• pp.1055-1056
• /
• 2010

• Transactions of the Korean Society of Automotive Engineers
• /
• v.15 no.5
• /
• pp.133-138
• /
• 2007

Surface pitting is a major failure mode for gears. The contact fatigue life analysis of transmission gear considering running-in process is presented in this paper. Surface roughness change of rolling test is used in a life analysis. Contact stresses are obtained by contact analysis of a semi-infinite solid based on the use of influence functions; the subsurface stress field is obtained using rectangular patch solutions. Mesoscopic multiaxial fatigue criterion which can yield satisfactory results for non-proportional loading is then applied to predict fatigue damage. Suitable counting method and damage rule were used to calculate the fatigue life of random loading caused by rough surface. The life analysis considering running-in is in good agreement with the experimental results.

• Tribology and Lubricants
• /
• v.15 no.2
• /
• pp.150-155
• /
• 1999

The rolling fatigue lives (RFL) of five kinds of silicon nitride balls were investigated. Four kinds of Si$_3$N$_4$balls were fabricated using different raw materials, sintering aids and sintering conditions. Commercially available Si$_3$N$_4$ball was also studied for comparison. All the balls were finished up to the dimensional accuracy of Grade 10 defined in KS B 2001 (Steel Balls fer Ball Bearings) with a size of 9.525 mm. RFL tests were then conducted under the initial theoretical maximum contact stress 6.38 GPa and the spindle speed 10,000 rpm. Gear oil was provided by oiled race as lubricant. The results of RFL test indicated the prerequisitic conditions for the long rolling life of Si$_3$N$_4$ball : (1) the high density, (2) microstructures consisted of small uniformly distributed grains, (3) little glassy phase in grainboundary, and (4) little crystalline phase and secondary phase that induces residual thermal stress due to the differences of thermal expansion coefficient with Si$_3$N$_4$phase.

• Proceedings of the KSR Conference
• /
• 2008.11b
• /
• pp.874-882
• /
• 2008

In a domestic, HSR-350x which has the maximum speed 350km/h was developed and then next, the next generation high speed train which has the maximum speed 400km/h has still been developing. With developing the next generation high speed railway, there need to be a general plan to make sure of dynamic safety though the a study on the crack and failure of rail by rolling contact fatigue. Therefore, this study investigated occurring stress of rail according to the track quality, train velocity, wheel radius, track stiffness, distance between sleepers, axial force using Eisenmann's equations. For the more, via the finite element method, it investigated shear force on the rail head which could be changed by the early crack length, angle and temperature. As a result, this study confirmed the main elements which effect on the fatigue life cycle of rail.

• Korean Journal of Materials Research
• /
• v.7 no.1
• /
• pp.62-68
• /
• 1997

In the first part of the paper, the crack growth process in rolling contact fatigue has been investigated on ring type plate specimens, in which crack growth is two dimensional and cracks are observed on the side surface of the specimens. The results have shown that cracks are initated from the contact surface in tensile mode in the direction approximately normal to the contact surface and after some short length of growth, shear mode growth occurs from the tip of the crack and it grows until the separation of the surface layer, namely flakung type failure, occurs. In the second part, mode U fatigue crack growth tests have been made by using an apparatus designed based on the concept that the subsurface fatigue crack growth in rolling contact fatigue is the mode U fatigue crack growth under the stress state where the tensile mode growth is suppressed by compression stress. The rest results have shown that the mode U fatigue crack growth occurs if the superposed compression stress is enough to suppress the tensile mode growth.