• Korean Journal of Heritage: History & Science
• /
• v.56 no.3
• /
• pp.158-171
• /
• 2023

Pottery filled with organic materials was excavated from the G-2 building site of Yongjangseong Fortress, Jingo, a relic of the Goryeo Dynasty. In this study, the characteristics of organic material were confirmed by a scientific analysis of organic material in pottery found at the palace in Yongjangseong, Jindo. In addition, it was intended to review the analysis method to identify the natural resin and to secure characteristic components(biomarkers) for each natural resin and use them as basic data in the future. The organic materials in the pottery were analyzed using attenuated total reflectance Fourier-transformed infrared spectroscopy(ATR-FTIR) and gas chromatography mass spectrometry(GC-MS). The infrared spectral characteristics were estimated to be natural resin, and biomarkers of organic materials were identified as sesquiterpene-based compounds(C₁₅H₂₄, MW 204) and derivatives. The lacquer(T.vemicifluum) is composed mainly of alkenes, alkanes, and catechol. Pine resin(P.densiflora), on the other hand, is primarily composed of diterpenoid(abietic acid, pimaric acid) and Whangchil(yellow lacquer) is identified to have sesquiterpenes(such as selinene, muurolene, calamenene) as its main components. So, the organic material in the pottery can be identified as Whangchil by comparing their compounds with modern resin materials from Dendropanax. morbifera that correspond with the results. Whangchil, which is exuded from the Dendropanax. morbifera, has been used as a natural coating materials since ancient times, and it has been confirmed that the characteristic components are well preserved even 700 years later. It can be assumed that the interior Whangchil was stored not for use as a coating, but rather for ritual purposes when the building was constructed, because the pottery was found near the cornerstone. Furthermore, based on simplified sample preparation using pyrolysis-gas chromatography mass spectrometry(Py-GC-MS), the thermal decomposition products were found to be similar to the characteristic components, suggesting that this method can be applied to the identification of natural resins used in historic artifacts.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.2
• /
• pp.38-45
• /
• 1999

This study was to figure out proper Formaldehyde/Urea molar ratio of UF resin with satisfactory bonding strength of plywood and properties of particleboard. The six kinds of UF resins were manufactured with F/U molar ratio 1.0, 1.2, 1.4, 1.6, 1.8, and 2.0. The boards were made of three kinds of raw materials : Veneer, Sliver-Particle and Strand-Particle. Manufacturing condition of plywood : amount of mixing resin was 150g/$m^2$. The fourty secs/mm simple-pressing schedule in the pressure 10kgf/$m^2$ was applied for 480mm${\times}$700mm board at the temperature of $110^{\circ}C$ in a hot press. Manufacturing condition of particleboard : Target density was 0.65g/$cm^2$. The stepwise 9 minutes- multi-pressing schedule in the maximum pressure 40kgf/$cm^2$, the minimum pressure 15kgf/$cm^2$ was applied for $480mm{\times}634mm{\times}12mm$ board at the temperature of $150^{\circ}C$ in a hot press. The results are as follows : I. In bonding strength, plywood which was made by F/U molar ratio 1.2 showed the highest value. Other molar ratio resin also gave the satisfied value of KS standard, 7.5kgf/$cm^2$. 2. In internal bond strength of particleboard, Sliver-Particleboard(SLPB) and Strand-Particleboard(STPB) varied respectively from 5.9kgf/$cm^2$ to 4.8kgf/$cm^2$, from 6.7kgf/$cm^2$ to 5.4kgf/$cm^2$. SLPB with F/U=1.2 and STPB with F/U=1.6 had higher IB value. Also, both SLPB and STPB showed lower IB value in F/U molar ratio 2.0 and 1.0. 3. SLPB and STPB with six kinds of UF resin respectively satisfied bending strength of KS standard 150 Type(130kgf/$cm^2$) and 200 Type(180kgf/$cm^2$). Bending strength data for both of SLPB and STPB showed little or no loss from F/U=1.8 to F/U=1.2. Also, STPB was approximately two times higher than that of SLPB. Therefore, the raw material's shape had more effect on bending strength than the FlU molar ratio. 4. F/U=1.6 and 1.4 showed the lower thickness swelling in SLPB and STPB. All of STPBs satisfied thickness swelling of KS standard, under 12%.