• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.141-161
• /
• 1998

The depth and patterns of demineralization according to the difference in concentration and application time of phosphoric acid were observed through the transmission electron microscope, and shear bond strengths to the acid -conditioned dentin were then measured and compared with the TEM results. To investigate the influence of polymer addition into the phosphoric acid and the effect of difference in concentration and application time of the acid, the specimens were randomly divided into 9 groups. Among the specimens, the exposed dentin surfaces were acid-conditioned with 10% polymer-thickened phosphoric acid(All Bond 2, Bisco, U.S.A.) and aqueous 10%, 20%, 30%, 40% phosphoric acid for 20 seconds, The rest of the specimens were acid-conditioned with 10% phosphoric acid for 15s, 30s, 60s, 120s respectively. The specimens were immersed in 4% glutaraldehyde in 0.1M sodium cacodylate buffer and postfixed with 1 % osmium tetroxide without decalcification and then observed under a JEOL Transmission Electron Microscope(JEM 1200 EX II, Japan). After the specimens were acid-conditioned as the above, primer and adhesive resin were applied to blot-dried dentin and shear bond strengths were then measured and analysed. The results were as follows : 1. The intertubular demineralization depth of 4.0-$5.0{\mu}m$ in 10% polymer-thickened phosphoric acid gels was similar or slightly deeper than that of 4.0-$4.5{\mu}m$ in aqueous 10% phosphoric acid solution. 2. The intertubular demineralization depth of aqueous 20%, 30% and 40% phosphoric acid solution was 6.5-$7.0{\mu}m$, 6.5-$7.5{\mu}m$ and 9.0-$15.0{\mu}m$ respectively. It showed that the depth of dentin demineralization is partly related to the concentration of phosphoric acid solution. 3. The intertubular demineralization depth of aqueous 10% phosphoric acid solution in application time for 15s, 30s, 60s and 120s was 2.5-$3.0{\mu}m$, 4.0-$6.0{\mu}m$, 6.5-$7.0{\mu}m$ and 8.5-$14.0{\mu}m$ respectively. It showed that the depth of dentin demineralization is directly related to the application time of phosphoric acid solution. 4. The partially demineralized dentin layer between demineralized collagen layer and unaffected dentin was showed to a width of 0.5-$1.0{\mu}m$ in lower concentration groups treated with aqueous 10% phosphoric acid for 20s, 60s, 120s and 20% phosphoric acid for 20s. 5. The demineralization effect at the border of intertubular-peritubular junction was less evident than that in the peritubular and intertubular dentin. The collagen fibers in the intertubular dentin had a random orientation, whereas those that lined the tubules were circumferentially aligned. The cross-linkage of dentinal collagen in demineralized collagen layer was clearly seen. 6. A statistically significant difference of bond strengths according to the difference in phosphoric acid concentration did not exist among the groups treated with 10%, 20%, 30% and 40% acid solution (P>0.05). However, bond strengths to the treated dentin with 10% phosphoric acid solution for 30s were significantly higher than that for 120s (P<0.05).

• Korean Journal of Heritage: History & Science
• /
• v.55 no.1
• /
• pp.51-61
• /
• 2022

Earthenware horn cups with horse head decorations were excavated from Tomb No. 7 of Bokcheon-dong, Dongraegu, Busan Metropolitan City. Made of earth in the shape of a horn, these cups are considered to have been used to drink alcohol or beverage. Large numbers of earthenware horn cups of various shapes were excavated from tombs located in the old territories of Silla and Gaya. A pair of earthenware horn cups were excavated from Tomb No. 7, and the two cups are almost identical in overall shapes and manufacturing techniques despite different sizes. Conservation treatment was carried out for the bigger one of the two horn cups this time. There are two cracks toward the horse head decorations around the mouth with missing parts observed. The chest of the horse touches the ground with one side decorating the horse head and the other side facing the conical mouth of the horn cup. It is in the U shape, striking a balance based on two legs attached behind. The surface of the horn cup was made with a potter's wheel, and the connection to the horse head has traces of cutting and trimming. The horse head is expressed realistically with its features including the ears, eyes, nose, and mouth well apprehended and its color is grey This study intended to investigate manufacturing techniques of the artifact by examining its internal structure through the condition survey in a non-destructive way. CT imaging was used to figure out its manufacturing techniques and to diagnose its condition, and accordingly the scientific conservation treatment was conducted to stabilize the artifact. The precise diagnosis on conservation condition found that there are two chips in the spout with their cracks extended. One of the chips is connected with separation added to the crack. The material which has been used for connection in the past was collected for the infrared spectroscopic analysis, which was identified to be nitrocellulose resin for the connection. Therefore, this conservation treatment focused on removing the old material and preventing the spread of cracks. Before conservation treatment, the condition survey and scientific examination for the artifact were carried out to secure data about the earthenware horn cup with horse head decorations(Treasure). Based on them, effective plans for its conservation treatment was sought for and then existing adhesive was safely removed, and restoration material was selected to take into account its reversibility. In addition, the conservation treatment according to optimal methodologies was conducted through the consultation meeting with experts.

• Journal of the Korean Wood Science and Technology
• /
• v.14 no.1
• /
• pp.3-44
• /
• 1986

In order to obtain the basic physical and mechanical properties of steel wire reinforced particleboard, particleboards were formed with large particles through 2.11 mm (12 meshes) and retained on 1.27mm (20 meshes) sieves and small particles through 1.27mm (20 meshes) and retained on 0.42mm (60 meshes) sieves from the plywood mill wastes of meranti (Shorea spp.) in the form of pallmanchips, applying urea-formaldehyde resin as an adhesive on the particle surface in 10 percent on the oven dried weight of particles, and arranging steel wires of 1mm in diameter 5,10,15,20, and 25mm in longitudinal and transverse direction with crossing in the mid of the board depth in single layer boards, 10mm in longitudinal or transverse direction without crossing in two layers and 10mm in longitudinal and transverse directions with and without crossing in three steel wire layers boards. The stepwise 9-minutes-multi-pressing schedule in 5 minutes at 35 kgf/$cm^2$, 2.5 minutes at 25 kgf/$cm^2$. and 1.5 minutes at 15 kgf/$cm^2$ was applied for $300{\times}200{\times}13$mm board at the temperature of 160$^{\circ}C$ in a hot press. Specific gravity, thickness swelling, bending properties of modulus of rupture (MOR), modulus of elasticity(MOE), work to proportional limit, and work to ultimate load, internal bond (IB), and screw holding power(SHP) of the reinforced boards were analyzed on the wire openings and wire layers. The results obtained are summarized as follows; 1) In specific gravity, particleboards with large particles and small particles had higher value with more steel wire placements and more steel layers composition, 2) Particleboards with large particles in accordance with more steel wire liners composition gave very poor thickness swelling. 3) The mechanical properties of particleboards formed with large or small particles were reinforced with more steel wire layers. Therefore, bending strength was improved in modulus of rupture, modulus of elasticity, and work to ultimate load. Especiallv, particleboards with two or three steel wire layers showed the tension lamination effect when the steels in lower steel wire layer were oriented parallel to the board length. 4) The modulus of rupture, modulus of elasticity, and work to ultimate load in bending varied with opening area, distance of lengthwise wires multipled by distance of transverse wires. Particleboards formed with large particles resulted in higher value in modulus of rupture with 1.5-3 $cm^2$ opening area, 1-2cm distance between transverse wires, and 1.5-2.5cm distance between lengthwise wires. Particle boards formed with small particles showed higher value with 0.5-1.5$cm^2$ or 3.75-6.25 $cm^2$ opening area, 0.5 or 2.5cm distance between transverse wires. 5) In modulus of elasticity, particleboards formed with large particles with one steel wire layer suggested higher value with 5-3$cm^2$ opening area, 1-2.5cm distance between transverse wires and also 1-2.5 cm distance between lengthwise wires. Particleboards formed with small particles showed higher value with 0.75-1.25$cm^2$ or 3-6.25$cm^2$ opening area and 0.5 or 2.5cm distance between transverse wires. 6) Particleboards formed with large particles gaved higher value in work to ultimate load with 1-3$cm^2$ opening area. Particleboards formed with small particles showed increasing tendancy with decreasing opening area. 7) In internal bond and screw holding power, particleboards formed with large particles had increasing value in two and three steel wire layers compositions, but particleboards formed with small particles showed no difference. Particleboards formed with large particles containing one steel wire layer showed no difference in internal bond and screw holding power, and particleboards formed with small panicles containing one steel wire layer resulted in increasing value in internal bond and decreasing value in screw holding power in accordance with increase in opening area.