• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.149-150
• /
• 2022

In Korea, there is no clearly established technology for diagnosing and evaluating the damage depth of concrete structures created by fire. There have been cases of repairing, reinforcing, and demolishing degraded structures without diagnosing the damage depth. The commonly used phenolphthalein-based carbonate thickness measurement does not satisfy the complete disappearance condition of Ca(OH)₂ in the interval where the relatively stationary flow declines after exposure to high temperatures. Even a small amount of Portlandite[Ca(OH)₂] reacts with a red color, and the damage depth is misjudged. It was confirmed by X-ray diffraction and scanning electron microscope that Ca(OH)₂ existed from 300℃ to 500℃ where the residual compressive strength decreased.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.3
• /
• pp.83-91
• /
• 2019

The purpose of this study is to assess a fire-damaged concrete structure using a digital camera and image processing software. To simulate it, mortar and paste samples of W/C=0.5(general strength) and 0.3(high strength) were put into an electric furnace and simulated from $100^{\circ}C$ to $1000^{\circ}C$. Here, the paste was processed into a powder to measure CIELAB chromaticity, and the samples were taken with a digital camera. The RGB chromaticity was measured by color intensity analyzer software. As a result, the residual compressive strength of W/C=0.5 and 0.3 was 87.2 % and 86.7 % at the heating temperature of $400^{\circ}C$. However there was a sudden decrease in strength at the temperature above $500^{\circ}C$, while the residual compressive strength of W/C=0.5 and 0.3 was 55.2 % and 51.9 % of residual strength. At the temperature $700^{\circ}C$ or higher, W/C=0.5 and W/C=0.3 show 26.3% and 27.8% of residual strength, so that the durability of the structure could not be secured. The results of $L^*a^*b$ color analysis show that $b^*$ increases rapidly after $700^{\circ}C$. It is analyzed that the intensity of yellow becomes strong after $700^{\circ}C$. Further, the RGB analysis found that the histogram kurtosis and frequency of Red and Green increases after $700^{\circ}C$. It is analyzed that number of Red and Green pixels are increased. Therefore, it is deemed possible to estimate the degree of damage by checking the change in yellow($b^*$ or R+G) when analyzing the chromaticity of the fire-damaged concrete structures.

• Journal of the Korea Concrete Institute
• /
• v.18 no.3 s.93
• /
• pp.431-438
• /
• 2006

The determination of the depth of deteriorated concrete is one of the main problems in the structural assessment of concrete structures that have been subjected to a fire. This information is particularly important in order to optimize the future operations of repair/strengthening, or in decision-making concerning a possible demolition. The purpose of this study is to propose evaluation technique of damaged depth of concrete exposed at high temperature. In order to evaluate damaged depth of core picked at member under fire, the 24 specimens have been made with variables of concrete strength(20 MPa, 40 MPa, 60 MPa) and heating exposure condition in 600 and 800 for 2 hours. Color change analysis and water absorption after heating have been measured and split tensile stress test was performed to ka the residual compressive strength against the depth of specimen. The results show that the deeper of the depth from heating face, water absorption ratio is smaller and residual stress ratio is larger and the color of heated face is changed to red color. Using this technique at damage evaluation of fired structure, We evaluate damaged depth of member under fire and determine the reasonable strengthening range.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.4
• /
• pp.311-318
• /
• 2018

When reinforced concrete structures are exposed to fire, their mechanical properties such as compressive strength, elasticity coefficient and rebar yield strength, are degraded. Therefore, the structure's damage assessment is essential in determining whether to dismantle or augment the structure after a fire. In this study, the confinement effect of lateral reinforcement of RC column according to the numbers of fire exposure face and stirrup was verified by fire resistant test with the heating temperatures of $400^{\circ}C$, $600^{\circ}C$ and $800^{\circ}C$. The test results showed that the peak stress decreases and peak strain increases as the temperature is getting higher, also transverse ties are helpful in improving the compressive resistance of concrete subjected to high temperature. Based on the results of this study, the residual stress of confined concrete under thermal damage is higher at the condition of more lateral reinforcement ratio and less fire exposure faces. The decreasing ratio of elastic modulus of more confined and less exposure faces from the relationship of load and displacement was also smaller than that of opposite conditions.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.1
• /
• pp.47-56
• /
• 2017

In this study, the higher temperature thermal property of the fly ash-blast furnace slag system Geopolymer including alumina aggregate was investigated whether that Geopolymer will be or not useful as thermal-resistant construction materials. Under every mixing conditions, the crack on the surface of hardened body was not observed up to $800^{\circ}C$ and it corresponded with fact that level of changes was not significant before and after heating process. Residual compressive strength is most high when mixing Blast-Furnace Slag ratio is 60 wt% until temperature reaches $800^{\circ}C$. The major hydrates of hardened body of Geopolymer; amorphous halo pattern between $20{\sim}35^{\circ}$ (2theta) and mullite ($3Al_2O_3{\cdot}2SiO_2$) and quartz ($SiO_2$) was found during the experiment. Amorphous halo pattern was a aluminosilicate gel generated by geopolymeric polycondensation and it was found that the halo pattern of aluminosilicate gel was preserved up to $800^{\circ}C$. The patterns of aluminosilicate gel disappeared from $1,000^{\circ}C$ and crystal phases like gehlenite, calcium silicate, calcium aluminum oxide, microcline was observed with the increase of exposure temperature.