• Structural Engineering and Mechanics
• /
• v.11 no.3
• /
• pp.301-314
• /
• 2001

The purpose of this experimental study is to investigate the damage mechanism due to shear-fatigue behavior of high-strength reinforced concrete beams under repeated loading. The relationship between the number of cycles and the deflection or strain, the crack growths and modes of failure with the increase of number of cycles, fatigue strength, and S-N curve were observed through a fatigue test. Based on the fatigue test results, high-strength reinforced concrete beams failed at 57-66 percent of static ultimate strength for 2 million cycles. The fatigue strength at 2 million cycles from S-N curves was shown as about 60 percent of static ultimate strength. Compared to normal-strength reinforced concrete beams, fatigue capacity of high-strength reinforced concrete beams was similar to or lower than fatigue capacity of normal-strength reinforced concrete beams. Fatigue capacity of normal-strength reinforced concrete beams improved by over 60 percent.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.04a
• /
• pp.399-404
• /
• 2000

This paper are the mechanical characteristics of eccentrically loaded normal strength and high strength reinforced concrete columns based on the test results. The columns are $120\times120$mmat the mid-section and are haunched at the ends to apply the eccentric loading and prevent premature failure. Variables are concrete strengths(361, 672, 974 kgf/$\textrm{cm}^2$), $\textrm{cm}^2$longitudinal reinforcement ratios (1.98, 3.54, 1 5.53%), spacing of lateral reinforcement (30, 60, 120mm), and eccentricities (24, 40mm). As a results, the main conclusions obtained from the comparison and analysis for the strength tendency, deformation and ductility of high strength reinforced concrete columns with variables are as follows; As the concrete compressive strength concrete and lateral reinforcement increases, the ductility index of high strength reinforced concrete columns decrease, but it increase with the increase of eccentricity and longitudinal reinforcement ratio. The confinement ratio must be greater than 20 percent in order for the level of ductility between high strength reinforced concrete columns and normal strength reinforced concrete columns to be almost equal.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.549-552
• /
• 2006

Generally the ultra-high strength steel reinforced concrete has rich mix composition composed of high-strength type mineral admixtures and as a result of very low water-binder ratio(about under w/b=25%), it reveals ultra-high compressive strength(about over 100Mpa). Also, in order to obtain sufficient toughness after construction, we usually mix a large quantity steel fiber with ultra-high strength steel reinforced concrete therefore we must use proper mixer for workability. When we make the ultra-high strength steel reinforced concrete we need more long mixing time or much super-plasticizer than when we manufacture normal concrete. These bring about economical problems and performance deterioration. Therefore, in this study, in order to manufacture easily ultra-high strength steel reinforced concrete we develope a dedicated mixer for ultra-high strength steel reinforced concrete with high speed type. It carried out the examination for comparison between the dedicated and general type mixer, the analysis and counterplan of the point at issue when we manufacture ultra-high strength steel reinforced concrete by the dedicated mixer.

• Journal of the Korea Institute of Building Construction
• /
• v.13 no.1
• /
• pp.58-65
• /
• 2013

Currently, many high-rise buildings are built in Korea for land-efficient utilization and vista. In high-rise buildings this tall, the use of high-strength concrete is essential to reduce the cross-section of structure members and secure axial load. However, this high strength concrete is vulnerable to spalling by fire, due to the water vapor pressure caused by the very high temperature in fire. To prevent this, the main method used is to reinforce the concrete with fiber. However, there has been little research on the pumpability of fiber reinforced high strength concrete. For this reason, this study features a performance review based on the properties and pumpability of fiber reinforced high strength concrete. In addition, the parameter of rheology was measured by extracting mortar from the concrete, and friction factor was measured through a 400 m horizontal pipe pumping test using the fiber reinforced high strength concrete. The basic information on fiber reinforced high strength concrete that we obtain through the experiments and review will contribute to the field.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1993.10a
• /
• pp.220-225
• /
• 1993

This paper is an experimental study on shear capacity of the high strength lightweight reinforced concrete beams with shear-depth ratio between 1.5 and 2.5. Thirteen T & rectangular beams were tested to determine their diagonal cracking and ultimate shear capacity. The major variables are shear span-depth ratio (a/d=1.5, 2.0, 2.5), concrete compressive strength(f'c=210, 24., 270㎏/㎠) and tensile steel ratio( =0.6, 1.2%). Based on results obtained from experiment of high strength lightweight reinforced concrete Beam & normal concrete, the following conclusions were drawn. (1) The shear capacity of high-strength lightweight concrete is less 15% than that of normal concrete under same condition. (2) As the results of Comparing this experimental datas with other various formulas. It is regarded that ACI 318-89 shear strength formula related tensile strength is proper to design formula of shear strength of high-strength lightweight reinforced concrete using lightweight concrete.

• Structural Engineering and Mechanics
• /
• v.66 no.4
• /
• pp.477-485
• /
• 2018

This study aims to investigate the influence of individual and hybrid fiber on the local bond-slip behavior of medium and high strength concrete after exposure to different high temperatures. Tests were conducted on local pullout specimens (150 mm cubes) with a reinforcing bar embedded in the center section. The embedment lengths in the pullout specimens were three times the bar diameter. The parameters investigated include concrete type (control group: ordinary concrete; experimental group: fiber concrete), concrete strength, fiber type and targeted temperature. The test results showed that the ultimate bond stress in the local bond stress versus slip curve of the high strength fiber reinforced concrete was higher than that of the medium strength fiber reinforced concrete. In addition, the use of hybrid combinations of steel fiber and polypropylene fiber can enhance the residual bond strength ratio of high strength concrete.

• Computers and Concrete
• /
• v.11 no.6
• /
• pp.531-539
• /
• 2013

An experimental investigation of mechanical properties of jute fiber-reinforced concrete (JFRC) has been reported for making a suitable construction material in terms of fiber reinforcement. Two jute fiber reinforced concretes, called jute fiber reinforced normal strength concrete (JFRNSC) and jute fiber-reinforced high-fluidity concrete (JFRHFC), were tested in compression, flexure and splitting tension. Compressive, flexural and splitting tensile strengths of specimens were investigated to four levels of jute fiber contents by volume fraction. From the test results, Jute fiber can be successfully used for normal strength concrete (NSC) and high-fluidity concrete (HFC). Particularly, HFC with jute fibers shows relatively higher improvement of strength property than that of normal strength concrete.

• Journal of the Korea Concrete Institute
• /
• v.11 no.6
• /
• pp.35-46
• /
• 1999

The steel fiber reinforced concrete may affect substantially to the tension stiffening at post cracking behavior. Even if several tension stiffening models exist, they are for plain and normal strength concrete. Thus, the development of tension stiffening models for steel fibrous high strength RC members are necessary at this time when steel fiber reinforced and high strength concretes are common in use. This paper presents tension stiffening effects from experimental results on direct tension members with the main variables such as concrete strength, concrete cover depth, steel fiber quantity and aspect ratio. The comparison of existing models against experimental results indicated that linear reduced model closely estimated the test results at normal strength level but overestimated at high strength level. Discontinuity stress reduced model underestimated at both strength levels. These existing models were not valid enough in applying at steel fibrous high strength concrete because they couldn't consider the concrete strength nor section area. Thus, new tension stiffening models for high strength and steel fiber reinforced concrete were proposed from the analysis of experimental results, considering concrete strength, rebar diameter, concrete cover depth, and steel fiber reinforcement.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10a
• /
• pp.501-506
• /
• 1998

This paper is an experimental study on the flexural strength and ductility capacity of reinforced high performance concrete beams with the concrete which has compressive strength of 600~700kg/$\textrm{cm}^2$, slump value of 20~25cm and slump-flow value of 60~70cm. Total 8 beams with different tensile reinforcement ratio and pattern of loading were tested. Form the results of reinforced high performance concrete beams, the equivalent stress block parameters proposed by MacGregor et al. or New Zealand code are recommended to use. Also, an extreme fiber concrete compressive strain of reinforced high performance concrete beams are distributed 0.0033~0.0048. In reinforced high performance concrete beams, reinforcement ratio in order to insure curvature ductility index 2 and 4 propose by ACI code should be less than those of reinforced normal strength concrete beams.

• Journal of the Korea Concrete Institute
• /
• v.12 no.2
• /
• pp.71-78
• /
• 2000

This paper presents a study on the flexural rigidity of reinforced high strength concrete beams. Thirty six beams with different compressive strength of concrete, tensile reinforcement ratio, compressive reinforcement ratio, and pattern of loadings(1 point loading and 2 points loading) were tested to evaluate the effective moment of inertia. According to the experimental results, the eqation(1) proposed by ACI code for the effective moment of inertia overestimated that of simply supported reinforced high strength concrete beams. Thus, in this paper, an empirical equation(3) is proposed as a lower bound of 90% confidence limit to estimate the effective moment of inertia of simply supported reinforced high strength concrete beams.