• Journal of Welding and Joining
• /
• v.32 no.6
• /
• pp.47-55
• /
• 2014

The purpose of the study is to produce a mechanically improved weld and minimum variation of color through comparing unpulsed and pulsed GTAW (Gas Tungsten Arc Welding) for pure titanium (CP grade7) tube. Pulsed GTAW using 60 A peak current and 20 A background current (1:9) achieved the wider window of welding conditions having part and full penetration without burn-through than the case of unpulsed GTAW. Moreover, the pulsed welding reduced a discoloration on the back bead of the weld and the size of microstructures (basket weave and serrated ${\alpha}$). That is because the pulsed welding has it's a low heat input and severe weld flow induced from electric current variation. Furthermore, the pulsed welding improved the bending property of the welded Ti tube. The enhanced bending property for the pulsed GTAW was due to the insignificant discoloration on the weld surface with maintaining the metal polish.

• Journal of Ocean Engineering and Technology
• /
• v.12 no.2 s.28
• /
• pp.57-64
• /
• 1998

This study is concerned with criterion for membrane to shell conversion in two-dimensional elastic-plastic finite element analysis using membrane/shell mixed element. It is well known that in the sheet metal forming some parts of the sheet deform under almost pure stretching (membrane) conditions, whereas other parts in contact with sharp tooling surfaces can develop significant bending strains. The membrane analysis has a short computational time however, in the membrane analysis the bending effects can not be condidered at all. On the other hand, the shell analysis allows the consideration of bending effects, but involves too much computational time. So Onatel),2), Yang et al3),4) developed the membrane/shell mixed element. Onate introduced the energy ratio parameter and Yang et al introduced the ratio of thickness to radius of curvature as the criterion. In the present study we propose a new criterion by using the angle between both side elements in the nodal point.

• Steel and Composite Structures
• /
• v.8 no.2
• /
• pp.145-158
• /
• 2008

In slender sections there is a substantial post-buckling strength provided after the formation of local buckling waves. These waves happened due to normal stresses or shear stresses or both. In this study, a numerical investigation of the behavior of slender I-section beams in combined pure bending and shear has been described. The studied cases were assumed to be prevented from lateral torsional buckling. To achieve this aim, a finite element model that simulates the geometric and material nonlinear nature of the problem has been developed. Moreover, the initial geometric imperfections were included in the model. Different flange and web width-thickness ratios as well as web panel aspect ratios have been considered to draw complete set of interaction diagrams. Results reflect the interaction behavior between flange and web in resisting the combined action of moments and shear. In addition, the web panel aspect ratio will not significantly affect the combined ultimate shear-bending strength as well as the post local buckling strength gained by the section. Results are compared with that predicted by both the Eurocode 3 and the American Iron and Steel specifications, AISI-2001. Finally, an empirical interaction equation has been proposed.

• Korean Journal of Materials Research
• /
• v.24 no.1
• /
• pp.13-18
• /
• 2014

In order to clarify the effect of Nb addition on the ductile-brittle transition property of sintered TiC, TiC-10 mol% Nb composites were researched using a three-point bending test at temperatures from room temperature to 2020 K, and the fracture surface was observed by scanning electron microscopy. It was found that the Nb addition decreases the ductile-brittle transition temperature of sintered TiC by 300 K and increases the ductility. The room temperature bending strength was maintained at up to 1800 K, but drastically dropped at higher temperatures in pure TiC. The strength increased moderately to a value of 320MPa at 1600 K in TiC-10 mol% Nb composites, which is 40% of the room temperature strength. Pores were observed in both the grains and the grain boundaries. It can be seen that, as Nb was added, the size of the grain decreased. The ductile-brittle transition temperature in TiC-10 mol% Nb composites was determined to be 1550 K. Above 1970 K, yieldpoint behavior was observed. When the grain boundary and cleavage strengths exceed the yield strength, plastic deformation is observed at about the same stress level in bending as in compression. The effect of Nb addition is discussed from the viewpoint of ability for plastic deformation.

• Steel and Composite Structures
• /
• v.43 no.4
• /
• pp.483-500
• /
• 2022

Cold-formed steel wall panels sheathed with gypsum plasterboard have shown superior thermal and structural performance in fire. Recent damage caused by fire events in Australia has increased the need for accurate fire resistance ratings of wall systems used in low- and mid-rise construction. Past fire research has mostly focused on light gauge steel framed (LSF) walls under uniform axial compression and LSF floors under pure bending. However, in reality, LSF wall studs may be subject to both compression and bending actions due to eccentric loading at the wall to-roof or wall-to-floor connections. In order to investigate the fire resistance of LSF walls under the effects of these loading eccentricities, four full-scale standard fire tests were conducted on 3 m × 3 m LSF wall specimens lined with two 16 mm gypsum plasterboards under different combinations of axial compression and lateral load ratios. The findings show that the loading eccentricity can adversely affect the fire resistance level of the LSF wall depending on the magnitude of the eccentricity, the resultant compressive stresses in the hot and cold flanges of the wall studs caused by combined loading and the temperatures of the hot and cold flanges of the studs. Structural fire designers should consider the effects of loading eccentricity in the design of LSF walls to eliminate their potential failures in fire.

• Journal of Ocean Engineering and Technology
• /
• v.22 no.2
• /
• pp.85-90
• /
• 2008

Ships in bad weather conditions are likely to be subjected to accidental loads, such as high bending moment, collision, and grounding. Once she has damage to her hull, her ultimate strength will be reduced. This paper discusses an investigation of the effect of collision damage on the ultimate strength of a ship structure by performing a series of collapse tests. For the experiment, five box-girder models with stiffeners were prepared with a cross section of $720mm\;{\times}\;720mm$ and a length of 900mm. Of the five, one had no damage and four had an ellipse shaped damage area that represented the shape of the bulbous bow of a colliding ship. The amount of damage size was different between models. Among the damaged models, the damage in three of them was made by cutting the plate and stiffener, and in one by pressing to represent collision damage. Experiments were carried out under a pure bending load and the applied load and displacements were recorded. The ultimate strength was reduced as the damage size increased, as expected. The one with the largest amount of damage had damage to 30% of the depth, and its ultimate strength was reduced by 19% compared to the undamaged one. The pressed one has higher ultimate strength than those that were cut. This might be due to the fact that the plate around the pressed damage area contributes to the ultimate strength, whereas the cut one has no plate to contribute.

• Publications of The Korean Astronomical Society
• /
• v.27 no.4
• /
• pp.177-179
• /
• 2012

We present Spitzer IRS spectroscopy of $CO_2$ ice toward 19 young stellar objects (YSOs) with luminosity lower than $1L_{\odot}$. Pure $CO_2$ ice forms only at elevated temperatures, T > 20 K, and thus at higher luminosities. Current internal luminosities of YSOs with L < $1L_{\odot}$ do not provide such conditions out to radii of typical envelopes. Significant amounts of pure $CO_2$ ice would signify a higher past luminosity. We analyze $15.2{\mu}m$ $CO_2$ ice bending mode absorption lines in comparison to the laboratory data. We decompose pure $CO_2$ ice from 12 out of 19 young low luminosity sources. The presence of the pure $CO_2$ ice component indicates high dust temperature and hence high luminosity in the past. The sum of all the ice components (total $CO_2$ ice amount) can be explained by a long period of low luminosity stage between episodic accretion bursts as predicted in an episodic accretion scenario. Chemical modeling shows that the episodic accretion scenario explains the observed total $CO_2$ ice amount best.

• Composites Research
• /
• v.23 no.3
• /
• pp.31-36
• /
• 2010

A new material, carbon-nanofiber/polypyrrole (CNF/PPy) composite films, with different CNF weight ratios were fabricated electrochemically. Compared to the fabrication process based on simple physical mixing, the flexibility of the new film has been improved much better than the previous similar material. Pure PPy films were also fabricated by the new electrochemical process for the comparison of difference. Several SEM images were taken at two locations (electrode-side and solution-side) and at the cross section of the samples. Electrical conductivity of the composite films was measured by the four-probe method. The conductivity of the pure PPy film 0.013cm thick was 79.33S/cm. The CNF/PPy composite film with 5% CNF showed a conductivity of 93S/cm. One with 10% CNF showed a conductivity of 126 S/cm. The conductivity of PPy improves, as the CNF weight ratio increases. The good conductivity of CNF/PPy composites makes them a candidate for a small bending actuator. A bending sensor consists of PPy and PVDF, which can be operated in the air, was designed and the bending deflection was calculated using FEM.

• Structural Engineering and Mechanics
• /
• v.48 no.4
• /
• pp.519-545
• /
• 2013

An outline of the Timoshenko beam theory is presented. Two differential equations of motion in terms of deflection and rotation are comprised into single equation with deflection and analytical solutions of natural vibrations for different boundary conditions are given. Double frequency phenomenon for simply supported beam is investigated. The Timoshenko beam theory is modified by decomposition of total deflection into pure bending deflection and shear deflection, and total rotation into bending rotation and axial shear angle. The governing equations are condensed into two independent equations of motion, one for flexural and another for axial shear vibrations. Flexural vibrations of a simply supported, clamped and free beam are analysed by both theories and the same natural frequencies are obtained. That fact is proved in an analytical way. Axial shear vibrations are analogous to stretching vibrations on an axial elastic support, resulting in an additional response spectrum, as a novelty. Relationship between parameters in beam response functions of all type of vibrations is analysed.

• Journal of the Korean Ceramic Society
• /
• v.42 no.6 s.277
• /
• pp.443-447
• /
• 2005

Fracture behavior was investigated in the $Al_2O_3-TiO_2(3 wt{\%})-LaPO_4(25 wt{\%}$) composite ceramics. To improve the fracture toughness of alumina ceramics, $TiO_2$ and $LaPO_4$ as a second phase were introduced. The samples were made by conventional powder processing method. Green compacts were sintered at $1600^{\circ}C$ for 2 h in air. Fracture toughness was tested using Indentation Strength Bending(ISB) method. From the bending test, enhanced fracture toughness was found in the composite, compared to the pure and $TiO_2$-doped alumina. The main factor of the enhancement of fracture toughness seems to be attributed to the weak interphase role of the $LaPO_4$ as a particulate type.