• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.2
• /
• pp.1-8
• /
• 2022

The corrosion of reinforcement is the main reason for the performance degradation of concrete structures. The pre-rusted parts of rebar in concrete structures are vulnerable to the corrosion, especially if the structure is exposed to wet or chlorinated environments. In this study, effects of different curing solution on corrosion behavior of the pre-rusted rebars in the cement composites were investigated. HCl(3%) and CaCl₂(10%) solution were utilized to accelerate the pre-rust of the rebar, and each pre-rust condition rebar including reference (RE) were placed in mortar cylinder. Three kinds of samples then were cured in CaCl₂ (3%) solution and tap water respectively for 120 days. Electrochemical polarization and half-cell potential measurement were used to monitor the influence of curing water on the corrosion behavior of pre-rusted steel bar in cement composite. The surface morphology and composition of corroded steel bar were analyzed by scanning electron microscope and energy dispersive X-ray diffraction. The results show that the corrosion rates of pre-rusted samples in both curing water are higher than that of non-pre-rusted samples. The corrosion rates of RE, CaCl₂ and HCl pre-rusted samples in salt water were 8.14, 4.48, 13.81 times higher than those in tap water respectively, on the 120th day.

• Journal of Adhesion and Interface
• /
• v.12 no.1
• /
• pp.34-42
• /
• 2011

The roll coating process is well-known for completely replacement coating system with an existing wet paint process for automotive which has low productivity and is not environment-friendly process. It is very important to evaluate the curing behavior, corrosion resistance and processing property as well as rheological behavior in order to realize a film flexibility and hardness simultaneously. In this study, we have synthesized the polyester resin modified with hydroxyl values and molecular weight to apply the pre-painted system, and then evaluated the curing behavior, deep drawing, tensile strength and rheological properties. It was observed that N-0375-40 of 40 (mg KOH/mol) hydroxyl values showed the most suitable for flexibility, film hardness, and curing behavior.

• Food Science of Animal Resources
• /
• v.41 no.2
• /
• pp.173-184
• /
• 2021

Clean labeling is emerging as an important issue in the food industry, particularly for meat products that contain many food additives. Among synthetic additives, nitrite is the most important additive in the meat processing industry and is related to the development of cured color and flavor, inhibition of oxidation, and control of microbial growth in processed meat products. As an alternative to synthetic nitrite, preconverted nitrite from natural microorganisms has been investigated, and the applications of pre-converted nitrite have been reported. Natural nitrate sources mainly include fruits and vegetables with high nitrate content. Celery juice or powder form have been used widely in various studies. Many types of commercial starter cultures have been developed. S. carnosus is used as a critical nitrate reducing microorganism and lactic acid bacteria or other Staphylococcus species also were used. Pre-converted nitrite has also been compared with synthetic nitrite and studies have been aimed at improving utilization by exploiting the strengths (positive consumer attitude and decreased residual nitrite content) and limiting the weaknesses (remained carcinogenic risk) of pre-converted nitrite. Moreover, as concerns regarding the use of synthetic nitrites increased, research was conducted to meet consumer demands for the use of natural nitrite from raw materials. In this report, we review and discuss various studies in which synthetic nitrite was replaced with natural materials and evaluate pre-converted nitrite technology as a natural curing approach from a clean label perspective in the manufacturing of processed meat products.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.161-164
• /
• 2004

The object of this study is vibrating compaction and curing method in the production process of Design concrete for precast concrete(Design-PC) product. From change of vibrating compaction time and pre-curing time, curing temperature which would be factors of product quality in Design-PC concrete production, and research of optimized steam curing condition from relations between curing condition and strength development, basic data of vibrating compaction time and concrete steam curing method for Design-PC will be presented.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.5
• /
• pp.63-71
• /
• 2010

This paper is about a research of steam curing which is one of the curing methods for accelerating the early-age strength of pre-cast concrete. With cylinder mold and mock-up specimen, the research was executed to study the best cycle of steam curing temperature through quantifying cycle of steam curing and maximum temperature, while the required strength is developed under the early-age. Moreover, causes and measurements for the high temperature of concrete, which is due to the steam curing, and the crack, which occurs when removing steel form, are stated. Ultimately, the economical method of producing, which satisfies early-age strength development and quality assurance while manufacturing PC structure, is stated.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.04a
• /
• pp.285-291
• /
• 1997

This study is the experimental results on the applicability of the super flowing concrete, which is the pre-cast concrete, to various cases. The primary purpose of this study is to verify the demolding strength, the handling strength of the super flowing concrete at various curing conditions, and the site quality control of the DWS (Daewoo Multi-Room Modular Construction System). From the experimental works, required strength and curing cycles are satisfied. Furthermore site quality control details and quality of the pre-cast concrete using the super flowing concrete are obtained. From now on, this study may suggest how to apply the super flowing concrete for common circumstance.

• Composites Research
• /
• v.33 no.6
• /
• pp.365-370
• /
• 2020

The icing formation at aircraft occur problems such as increasing weight of the body, fuel efficiency reduction, drag reduction, the error of sensor, and etc. The viscosity of polyurethane (PU) topcoat was measured at 60℃ in real time to set the pre-curing time. SiO2 nanoparticles were dispersed in ethanol using ultra-sonication method. The SiO2/ethanol solution was sprayed on PU topcoat that was not cured fully with different pre-curing conditions. Surface roughness of SiO2/PU nanocomposites were measured using surface roughness tester and the surface roughness data was visualized using 3D mapping. The adhesion property between SiO2 and PU topcoat was evaluated using adhesion pull-off test. The static contact angle was measured using distilled water to evaluate the hydrophobicity. Finally, the pre-curing time of PU topcoat was optimized to exhibit the hydrophobicity of SiO2/PU topcoat.

• The Journal of Korean Academy of Prosthodontics
• /
• v.40 no.3
• /
• pp.236-245
• /
• 2002

The acrylic resin was first introduced as denture base materials in 1937 and it is commonly used for denture base fabrication nowadays. Three different curing cycles (Conventional curing cycle, short curing cycle and long curing cycle) and three commercially available heat-activated acrylic resins (Vertex RS, Lucitone 199 and ProBase Hot) were investigated to find the curing cycle and material that showed the minimum shrinkage of the resin during polymerization process. A brass master mold was fabricated and duplicated by additional silicone impression material. Stone molds were made by pouring of type III dental stone (SILKY-ROCK YELLOW, Whip-Mix, Louisville, Kentucky). It was embedded in the flask. Strain gauge and thermocouple were embedded in the specimen. Strain gauge and thermocouple were connected to signal conditioning amplifier and data was recorded by pre-programmed software. The parameters ESmax (Maximum expansion strain), Sb (Strain measured just before deflasking procedure), Sa (Strain measured just after deflasking procedure) and Sf (Strain measured at the end of the experiment) were measured. ${\Delta}$S was calculated from Sb and Sa (${\Delta}$S=Sb-Sa). In the experiment concerned about materials, the parameters 90-ESmax (Maximum expansion strain measured during early 90 minutes of curing procedure), 180-ESmax (Maximum expansion strain measured from 90 minutes to 180 minutes), Sb, Sa, ${\Delta}$S and Sf were measured and the following conclusions were made. 1. The ESmax value of conventional curing cycle showed the largest value and the 180-ESmax value of Lucitone 199 showed the smallest value. 90-ESmax values showed no significant difference (p<0.05). 2. ${\Delta}$S values of conventional curing cycle showed the positive values. ${\Delta}$S values of short curing cycle and long curing cycle showed the negative values. All three materials cured by conventional curing cycle showed the positive values. 3. The Sf values of long curing cycle and ProBase Hot (cured by conventional curing cycle) showed the smallest values.

• Journal of Adhesion and Interface
• /
• v.10 no.4
• /
• pp.155-161
• /
• 2009

The most upcoming technical issue of automotive coating is the compact coating process. Pre-primed coating is the outstanding technology eliminating electro-deposition and primer coating process. The main properties of pre-primed coating for automotive are flexibility, corrosion resistance, and weldability. Therefore, we synthesized the conventional polyester, elastomeric polyester and polyvinylidene fluoride resins and evaluated their properties to use as weldable pre-primed automotive coatings. As the results of flexibility and curing behavior, the elastomeric polyester coating was most appropriate to use for the pre-primed automotive coatings.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.232-235
• /
• 2002

Recently developed liquid silicone rubber (LSR) can be cured by platinum catalyzed additional hydrosilylation mechanism and has the advantage of no byproduct compared to traditional millable peroxide curing silicone rubber. We investigated the characteristics of dielectric breakdown of silicone rubber and adhesion properties between semi-conductive LSR and insulating LSR for high voltage application of pre-molded joint (PMJ). In order to understand the dielectric breakdown characteristics, we used the sheet samples and the paired type rogowski insert electrode system. The breakdown strength and adhesion strength of LSR (E-3) were superior to those of several silicone rubbers. Adhesion strength could be improved by curing at high temperature without post-curing process or enhanced by post-curing process. When LSR (E-3) was cured at $(150^{\circ}C{\times}10min$ semi-conductive )${\times}$ ($175^{\circ}C{\times}10min$ insulation), it showed the high breakdown strength with low standard deviation, and good adhesion strength. In this results, we could apply this process to the fabrication of PMJ without post-curing.